Crystallization at room temperature from amorphous to trigonal selenium as a byproduct of the synthesis of water dispersible zinc selenide

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Microwave Hydrothermal Synthesis and Photocatalytic Performance of ZnO and M:ZnO Nanostructures (M = V, Fe, Co)

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Synthesis and photoluminescence behavior of Bi4Ti3O12 powders obtained by the complex polymerization method

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

SiO2-GeO2 soot preform as a core for Eu2O3 nanocoating: Synthesis and photophysical study

Nowadays solid state chemists have the possibility of work with low temperature strategies to obtain solid state materials with appropriate physical and chemical properties for useful technological applications. Photonic core shell materials having a core and shell domains composed by a variety of compounds have been synthesized by different methods. In this work we used silica-germania soot prepared by vapor-phase axial deposition as a core where a nanoshell of Eu2O3 was deposited. A new sol-gel like method was used to obtain the Eu2O3 nanoshell coating the SiO2-GeO2 particles, which was prepared by the polymeric precursor method. The photophysical properties of Eu3+ were used to obtain information about the rare earth surrounding in the SiO2-GeO2@Eu2O3 material during the sintering process. The sintering process was followed by the luminescence spectra of Eu3+ and all the samples present the characteristic emission related to the D-5(0) -> F-7(J) (J=0, 1, 2, 3 and 4). The ratios of the D-5(0) -> F-7(2)/D-5(0) -> F-7(1) emission intensity for the SiO2-GeO2@Eu2O3 systems were calculated and it was observed an increase in its values, indicating a low symmetry around the Eu3+ as the temperature increases.

(Sr,Tm)ZrO3 powders prepared by the polymeric precursor method: Synthesis, optical properties and morphological characteristics

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Synthesis and functionalization of magnetite nanoparticles with different amino-functional alkoxysilanes

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Microwave-assisted hydrothermal synthesis of nanocrystalline SnO powders

Tin oxide (SnO) powders were obtained by the microwave-assisted hydrothermal synthesis technique using SnCl2 center dot 2H(2)O as a precursor. By changing the hydrothermal processing time, temperature, the type of mineralizing agent (NaOH, KOH or NH4 OH) and its concentration, SnO crystals having different sizes and morphologies could be achieved. The powders were characterized by X-ray diffraction (X-ray), Field Emission Scanning Electron Microscopy (FE-SEM), High Resolution Transmission Electron Microscopy (HR-TEM) and Selected Area Electron Diffraction (SAED). The results showed that plate-like form is the characteristic morphology of growth and the TEM analyses indicate the growth direction as (200). (c) 2007 Elsevier B.V. All rights reserved.

BaMoO(4) powders processed in domestic microwave-hydrothermal: Synthesis, characterization and photoluminescence at room temperature

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Mechanochemical synthesis of lead magnesium niobate ceramics in iron media

The possibility of mechanochemical synthesis of the lead magnesium niobate (PMN) powders of the composition Pb(Mg(1/3)Nb(2/3))O(3) in iron vials was investigated. According to X-ray and energy-dispersive spectroscopy (EDS) analysis of the obtained powder mixtures, milling in iron vials resulted in incorporation of Fe and formation of PFN of composition Pb(Fe(1/2)Nb(1/2))O(3) simultaneously with formation of PMN. Relative amounts of PMN and PFN were determined based on values of Curie temperature and lattice constant of perovskite phase. Although only 1 wt pct of Fe was incorporated, a stoichiometry of the system was significantly changed, resulting in formation of pyrochlore phase and excess MgO. Single-phase perovskite was obtained when the excess of PbO and Nb(2)O(5) was added during mechanochemical synthesis. Because the dielectric properties were worse than expected, the alternative ways for improvement of dielectric properties were tried and discussed.

Urea-Based Synthesis of Zinc Oxide Nanostructures at Low Temperature

The preparation of nanometer-sized structures of zinc oxide (ZnO) from zinc acetate and urea as raw materials was performed using conventional water bath heating and a microwave hydrothermal (MH) method in an aqueous solution. The oxide formation is controlled by decomposition of the added urea in the sealed autoclave. The influence of urea and the synthesis method on the final product formation are discussed. Broadband photoluminescence (PL) behavior in visible-range spectra was observed with a maximum peak centered in the green region which was attributed to different defects and the structural changes involved with ZnO crystals which were produced during the nucleation process.

Synthesis and characterization of β-RbSc(CrO4)2

Synthesis and crystallographic data are reported for the double rubidium-scandium chromate RbSc(CrO4)2. The parameters of the orthorhombic cell are a = 14.836(2) A ̊; b = 5.627(1) A ̊ and c = 8.835(4) A ̊, Z = 4. The compound is closely related to the lamellar double chromates with other alkali metal cations, iron, lanthanides and yttrium offering the advantage of obtaining inorganic materials for electronics. © 1995.

Synthesis and sintering of ultra fine NaNbO3 powder by use of polymeric precursors

Ultra-fine NaNbO3 powder was prepared by the use of polymeric precursors. X-ray diffraction (XRD) results showed that this niobate nucleates from the amorphous precursor, with no intermediate phases, at low temperature (500°C). Studies by XRD and nitrogen adsorption/desorption showed that powders with high crystallinity ( ≈ 100%) and high surface areas (>20 m2/g) are obtained after calcination at 700°C for 5 h. Compacts of calcined powders showed high sinterability reaching 98% of theoretical density when sintered at 1190°C for 3 h.

Synthesis of PbTiO3 by use of polymeric precursors

Lead titanate powders were synthesized through the use of polymeric precursors according to the Pechini Process. The polymeric precursor was calcined at temperatures ranging from 300 to 600°C for 1 or 2 h. X-ray diffraction (XRD) showed that lead titanate crystallizes from the precursor at temperatures as low as 400°C. No intermediate carbonate phase was detected by Fourier transform infrared spectroscopy (FTIR) or by XRD. A powder with mean particle size of 150 nm was obtained after calcination of the precursor at 600°C for 1 h. © 1998 Elsevier Science B.V. All rights reserved.

Synthesis of manganese porphyrinosilica imprinted with templates using the sol-gel process

The optimized conditions for the preparation of a new manganese porphyrinosilica-template material are reported. The manganese porphyrinosilica-template was prepared by the sol-gel process, by the reaction of -SO2Cl groups present in the phenyl rings of MnTDC(SO2Cl)PPCl with 3-aminopropyltriethoxysilane. The reaction produces a precursor porphyrinopropylsilyl species, which were then polymerized with tetraethoxysilane. The presence of manganese porphyrin on xerogel is confirmed by ultraviolet visible absorption spectroscopy and thermogravimetric analysis (TGA). The prepared materials have surface areas between 19 and 674 m2 g-1. Electron spectroscopy imaging of the materials show that manganese distribution in the xerogel is uniform. Both manganese(III) porphyrinosilica-template and a similar iron(III) porphyrinosilica-template can catalyze the epoxidation of cyclooctene using iodozylbenzene as oxygen donor. The metalloporphyrinosilica-template presents catalytic activity similar to that of metaloporphyrin in solution. © 2000 Elsevier Science B.V. All rights reserved.

Synthesis and crystal phase evaluation of hydroxylapatite using the rietveld-maximum entropy method

Bioceramic systems based on hydroxylapatite (HAP) are an important class of bioactive materials that may promote bone regeneration. The aim of this research was to evaluate how the stoichiometry of HAP influences its microstructural properties when diagnosed using the combined Rietveld method and Maximum entropy method (MEM). The Rietveld Method (RM) is recognizably a powerful tool used to obtain structural and microstructural information of polycrystalline samples analyzed by x-ray diffraction. Latterly have combined the RM with the maximum entropy method (MEM), with the goal of improve structural refinement results. The MEM provides high resolution maps of electron density and their analysis leave the accurate localization of atoms inside of unit cell. Like that, cycles Rietveld-MEM allow an excellent structural refinement In this work, a hydroxylapatite sample obtained by emulsion method had its structure refined using one cycle Rietveld-MEM with x-ray diffraction data. The indices obtained in initial refinement was Rwp = 7.50%, Re = 6.56%, S - 1.14% e RB = 1.03%. After MEM refinement and electron densities maps analysis to correction of atomics positions, the news indicators of Rietveld refinement quality was Rwp = 7.35%, Re = 6.56%, S = 1.12% and RB = 0.75%. The excellent result obtained to RB shows the efficiency of MEM as auxiliary in the refinement of structure of hydroxylapatite by RM.