987 resultados para FERROMAGNETIC MONOLAYER FE(110)


Relevância:

20.00% 20.00%

Publicador:

Resumo:

In1−xMnxSb crystals are grown with different Mn doping concentrations (x = 0.006, 0.01, 0.02, and 0.04) beyond the equilibrium solubility limit by the horizontal Bridgman technique. Structural, magnetic, and magnetotransport properties of the grown crystals are studied in the temperature range 1.4–300 K. Negative magnetoresistance and anomalous Hall effect are observed below 10 K. The anomalous Hall coefficient is found to be negative. The temperature dependence of the magnetization measurement shows a magnetic ordering below 10 K, which could arise from InMnSb alloy formation. Also, the saturation in magnetization observed even at room temperature suggests the existence of ferromagnetic MnSb clusters in the crystals, which has been verified by scanning electron microscopy studies. The carrier concentration increases with Mn doping, and this results in a decrease of resistivity. The carrier concentration and mobility at room temperature for the doped crystals are ∼ 2×1019 cm−3 and ∼ 200 cm2/V s, respectively. The observed anomalous Hall effect suggests the carrier mediated ferromagnetism below 10 K in In1−xMnxSb crystals.

Relevância:

20.00% 20.00%

Publicador:

Resumo:

Colossal electroresistance and current induced resistivity switching have been measured in the ferromagnetic insulating (FMI) state of single crystal manganite La0.82Ca0.18MnO3. The sample has a Curie transition temperature TC = 165 K and the FMI state is realized for temperatures T<100 K. The electroresistance (ER), arising from a strong nonlinear resistivity, attains a large value ( ≈ 100%) in the FMI state. However, this is accompanied by a collapse of the magnetoresistance (MR) to a small value even in magnetic field (H) of 10 T. This demonstrates that the mechanisms that give rise to ER and MR are effectively decoupled.

Relevância:

20.00% 20.00%

Publicador:

Resumo:

We have prepared crystalline nanowires (diameter ∼ 50 nm, length ∼ a few microns) of the charge-ordering manganite Pr0.5Ca0.5MnO3 using a low reaction temperature hydrothermal method and characterized them using x-ray diffraction, transmission electron microscopy, superconducting quantum interference device (SQUID) magnetometry and electron magnetic resonance measurements. While the bulk sample shows a charge ordering transition at 245 K and an antiferromagnetic transition at 175 K, SQUID magnetometry and electron magnetic resonance experiments reveal that in the nanowires phase, a ferromagnetic transition occurs at ∼ 105 K. Further, the antiferromagnetic transition disappears and the charge ordering transition is suppressed. This result is particularly significant since the charge order in Pr0.5Ca0.5MnO3 is known to be very robust, magnetic fields as high as 27 T being needed to melt it.

Relevância:

20.00% 20.00%

Publicador:

Resumo:

Highly (110) preferred orientated antiferroelectric PbZrO3 (PZ) and La-modified PZ thin films have been fabricated on Pt/Ti/SiO2/Si substrates using sol-gel process. Dielectric properties, electric field induced ferroelectric polarization, and the temperature dependence of the dielectric response have been explored as a function of composition. The Tc has been observed to decrease by ∼ 17 °C per 1 mol % of La doping. Double hysteresis loops were seen with zero remnant polarization and with coercive fields in between 176 and 193 kV/cm at 80 °C for antiferroelectric to ferroelectric phase transformation. These slim loops have been explained by the high orientation of the films along the polar direction of the antiparallel dipoles of a tetragonal primitive cell and by the strong electrostatic interaction between La ions and oxygen ions in an ABO3 perovskite unit cell. High quality films exhibited very low loss factor less than 0.015 at room temperature and pure PZ; 1 and 2 mol % La doped PZs have shown the room temperature dielectric constant of 135, 219, and 142 at the frequency of 10 kHz. The passive layer effects in these films have been explained by Curie constants and Curie temperatures. The ac conductivity and the corresponding Arrhenius plots have been shown and explained in terms of doping effect and electrode resistance.

Relevância:

20.00% 20.00%

Publicador:

Resumo:

Atomistic simulation of initial < 100 > oriented FCC Cu nanowires shows a novel coupled temperature-pressure dependent reorientation from < 100 > to < 110 > phase. A temperature-pressure-induced solid-solid < 100 > to < 110 > reorientation diagram is generated for Cu nanowire with varying cross-sectional sizes. A critical pressure is reported for Cu nanowires with varying cross-sectional sizes, above which an initial < 100 > oriented nanowire shows temperature independent reorientation into the < 110 > phase. The effect of surface stresses on the < 100 > to < 110 > reorientation is also studied. The results indicate that above a critical cross-sectional size for a given temperature-pressure, < 100 > to < 110 > reorientation is not possible. It is also reported here that for a given applied pressure, an increase in temperature is required for the < 100 > to < 110 > reorientation with increasing cross-sectional size of the nanowire. The temperature-pressure-induced solid-solid < 100 > to < 110 > reorientation diagram reported in the present paper could further be used as guidelines for controlling the reorientations/shape memory in nano-scale applications of FCC metallic nanowires.

Relevância:

20.00% 20.00%

Publicador:

Resumo:

Base metal substituted Sn(0.95)M(0.05)O(2-delta) (M = Cu, Fe, Mn, Co) catalysts were synthesized by the solution combustion method and characterized by XRD, XPS, TEM and BET surface area analysis. The catalytic activities of these materials were investigated by performing CO oxidation. The rates and the apparent activation energies of the reaction for CO oxidation were determined for each catalyst. All the substituted catalysts showed high rates and lower activation energies for the oxidation of CO as compared to unsubstituted SnO(2). The rate was found to be much higher over copper substituted SnO(2) as compared to other studied catalysts. 100% CO conversion was obtained below 225 degrees C over this catalyst. A bifunctional reaction mechanism was developed that accounts for CO adsorption on base metal and support ions and O(2) dissociation on the oxide ion vacancy. The kinetic parameters were determined by fitting the model to the experimental data. The high rates of the CO oxidation reactions at low temperatures were rationalized by the high dissociative chemisorption of adsorbed O(2) over these catalysts.

Relevância:

20.00% 20.00%

Publicador:

Resumo:

The W, V, Ce, Zr, Fe, and Cu metal ion substituted nanocrystalline anatase TiO2 was prepared by solution combustion method and characterized by XRD, Raman, BET, EPR, XPS, IR TGA, UV absorption, and photoluminescence measurements. The structural studies indicate that the solid solution formation was limited to a narrow range of concentrations of the dopant ions. The photocatalytic degradation of 4-nitrophenol under UV and solar exposure was investigated with Ti1-xMxO2±δ. The degradation rates of 4-nitrophenol with these catalysts were lesser than the degradation rates of 4-nitrophenol with undoped TiO2 both with UV exposure and solar radiation. However, the photocatalytic activities of most metal ion doped TiO2 are higher than the activity of the commercial TiO2, Degussa P25. The decrease in photocatalytic activity is correlated with decrease in photoluminescence due to electron states of metal ions within the band gap of TiO2.

Relevância:

20.00% 20.00%

Publicador:

Resumo:

We have synthesized 5-7 nm size, highly crystalline TiO2 which absorbs radiation in the visible region of solar spectrum. The material shows higher photocatalytic activity both in UV and visible region of the solar radiation compared to commercial Degussa P25 TiO2. Transition metal ion substitution for Ti4+ creates mid-gap, states which act as recombination centers for electron-hole induced by photons thus reducing photocatalytic activity. However, Pt, Pd and Cu ion substituted TiO2 are excellent CO oxidation and NO reduction catalysts at temperatures less than 100 degrees C.

Relevância:

20.00% 20.00%

Publicador:

Resumo:

We prepared thin films composed of pure TiO2 or TiO2 with an Fe additive (at concentrations of 0.2-0.8 wt%) via a simple and cost effective sol gel process, and tested their antifungal properties (against Candida albicans (MTCC-1637), Candida tropicalis (MTCC-184), Candida parapsilosis (MTCC-2509), and Candida glabrata (MTCC-3019) and antibacterial properties (against Staphylococcus faecalis (NCIM-2604) Staphylococcus epidermidis (NCIM-2493), Staphylococcus aureus (NCIL-2122), and Bacillus subtilis (NCIM-2549)). The films were deposited on glass and Si substrates and subjected to annealing at 400 degrees C for 3 h in ambient air. The film structural and morphological properties were investigated by X-ray photoelectron spectroscopy profilometry and scanning electron microscopy, respectively. Antifungal and antibacterial tests were conducted using the drop test method. Among the species examined, Candida albicans (MTCC-1637), and Staphylococcus aureus (NCIL-2122) showed complete colony formation inhibition after exposure for 4 h for the TiO2 loaded with 0.8 wt% Fe thin films. These results indicate that increasing the Fe concentration increased the antimicrobial activity, with complete inhibition of colony formation after 4 h exposure.

Relevância:

20.00% 20.00%

Publicador:

Resumo:

We present numerical studies of a model for CO oxidation on the surface of Pt(110) proposed in Ref. 1. The model shows several interesting regimes, some of which exhibit spatiotemporal chaos. The time series of the CO concentration at a given point consists of a sequence of pulses. We concentrate on interpulse intervals theta and show that their distribution P(theta) approaches a delta function continuously as the system goes from a state M, with meandering spirals, to a state S, with spatially frozen spiral cores. This should be verifiable experimentally.

Relevância:

20.00% 20.00%

Publicador:

Resumo:

Diffusion-couple experiments are conducted in the Fe-Pt system. The phase boundary compositions of the phases measured in this study are found to be different than the compositions published previously. In the gamma-FePt solid solution, the interdiffusion coefficient increases with the Pt content up to 25 at. pct Pt. Fe is the faster diffusing species in this phase. The trend in the interdiffusion coefficient is explained with the help of calculated driving force for diffusion. To reduce errors, the average interdiffusion coefficients are calculated in the FePt and FePt3 compounds.

Relevância:

20.00% 20.00%

Publicador:

Resumo:

Zn(1-x)Fe(x)O(1+0.5x) (x = 0.5-5 mol%) nanoparticles were synthesized by a low temperature solution combustion route. The structural characterization of these nanoparticles by PXRD, SEM and TEM confirmed the phase purity of the samples and indicated a reduction in the particle size with increase in Fe content. A small increase in micro strain in the Fe doped nanocrystals is observed from W-H plots. EPR spectrum exhibits an intense resonance signal with effective g values at g approximate to 2.0 with a sextet hyperfine structure (hfs) besides a weak signal at g approximate to 4.13. The signal at g approximate to 2.0 with a sextet hyperfine structure might be due to manganese impurity where as the resonance signal at g approximate to 4.13 is due to iron. The optical band gap E-g was found to decrease with increase of Fe content. Raman spectra exhibit two non-polar optical phonon (E-2) modes at low and high frequencies at 100 and 435 cm(-1) in Fe doped samples. These modes broaden and disappear with increase of Fe do pant concentration. TL measurements of gamma-irradiated (1-5 kGy) samples show a main glow peak at 368 degrees C at a warming rate of 6.7 degrees Cs-1. The thermal activation parameters were estimated from Glow peak shape method. The average activation energy was found to be in the range 0.34-2.81 eV. (C) 2012 Elsevier B.V. All rights reserved.

Relevância:

20.00% 20.00%

Publicador:

Resumo:

A strong electron-phonon interaction which limits the electronic mobility of semiconductors can also have significant effects on phonon frequencies. The latter is the key to the use of Raman spectroscopy for nondestructive characterization of doping in graphene-based devices. Using in situ Raman scattering from a single-layer MoS2 electrochemically top-gated field-effect transistor (FET), we show softening and broadening of the A(1g) phonon with electron doping, whereas the other Raman-active E-2g(1) mode remains essentially inert. Confirming these results with first-principles density functional theory based calculations, we use group theoretical arguments to explain why the A(1g) mode specifically exhibits a strong sensitivity to electron doping. Our work opens up the use of Raman spectroscopy in probing the level of doping in single-layer MoS2-based FETs, which have a high on-off ratio and are of technological significance.

Relevância:

20.00% 20.00%

Publicador:

Resumo:

Magnetoelectric multiferroic BiFeO3 (BFO) was synthesized by a simple carbonate precipitation technique of metal nitrate solutions. X-ray powder diffraction and thermo-gravimetric analysis (TGA) revealed that the precipitate consists of an intimate mixture of crystalline bismuth carbonate and an amorphous hydroxide of iron. The precipitate yielded BiFeO3 at an optimal calcination temperature of similar to 560A degrees C. Energy dispersive X-ray (EDX) analysis showed 1:1 ratio between Bi and Fe in the oxide. X-ray photoelectron spectroscopy (XPS) studies confirmed that Fe to be in +3 oxidation states both in the precipitated powder and BiFeO3. The synthesized BFO exhibits a very weak ferromagnetic correlation at room temperature and the degree of which increases slightly on cooling down to 10 K suggesting alteration in the long range spatial modulation of the spins arrangement as compared to the bulk BiFeO3.