Influence of pH on slow crack growth of dental porcelains

Objectives. To evaluate the effect of pH of storage medium on slow crack growth (SCG) parameters of dental porcelains. Methods. Two porcelains were selected: with (UD) and without (VM7) leucite particles, in order to assess if the microstructure would affect the response of the material to the pH variation. Disc specimens were produced following manufacturers` instructions. Specimens were stored in artificial saliva in pHs 3.5, 7.0 or 10.0 for 10 days and after that the fatigue parameters (n: SCG susceptibility coefficient and sigma(0): scaling parameter) were obtained by the dynamic fatigue test using the same pH of storage. Microstructural analysis of the materials was also performed. Results. For VM7, the values of n obtained in the different pHs were similar and varied from 29.9 to 31.2. The sigma(0) value obtained in pH 7.0 for VM7 was higher than that obtained in the other pHs, which were similar. For porcelain UD, n values obtained in pHs 7.0 and 10.0 were similar (40.8 and 39.6, respectively), and higher than that obtained in pH 3.5 (26.5). With respect to sigma(0), the value obtained for porcelain UD in pH 10.0 was lower than those obtained in pHs 3.5 and 7.0, which were similar. Significance. The effect of pH on the stress corrosion susceptibility (n) depended on the porcelain studied. While the n value of VM7 was not affected by the pH, UD presented lower n value in acid pH. For both porcelains, storage in acid or basic pH resulted in strength degradation. (C) 2007 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Influence of dentin on pH of 2% chlorhexidine gel and calcium hydroxide alone or in combination

The aims of endodontic treatment in cases of apical periodontitis are to reduce as much as possible the number of microorganisms inside the root canal system and to inactivate toxins produced by them. Most of the times, these objectives are not achieved solely by chemomechanical preparation, and intracanal dressing may be necessary. In these cases, calcium hydroxide is used as a root canal dressing due to its well-known and recognized antimicrobial activity. Chlorhexidine has a wide spectrum of antimicrobial activity and its association with calcium hydroxide has been recommended in an attempt to amplify antimicrobial effects of calcium hydroxide. It is also known that dentin exerts a buffering effect under wide pH variations, and may be responsible for decreasing the antimicrobial activity of drugs inside the root canal. The objectives of this study were to assess the pH of 2% chlorhexidine gel and calcium hydroxide alone or in combination, as well as the influence of dentin on the pH of these compounds. Dentin powder was obtained from bovine teeth and added as 1.8% to the volume of the medications. All substances were individually stored in plastic flasks, in triplicate. A pH meter was used at five different moments to assess pH in viscous medium: immediately after preparation and after 24 h, and 7, 14, and 21 days. Results were analyzed by paired Student`s t-test. Statistically significant differences were observed in the 2% chlorhexidine gel group alone or associated with calcium hydroxide and added of dentin powder (P < 0.05). Mean pH values indicated the influence of dentin powder because of a significant increase in pH. Calcium hydroxide with propylene glycol as the vehicle always showed high pH, demonstrating that this compound was not affected by the presence of dentin.

Effect of sodium, amine and stannous fluoride at the same concentration and different pH on in vitro erosion

Objective: This study aimed to compare the effects 0.5% and 1% sodium, amine and stannous fluoride at different pH on enamel erosion in vitro. Methods: Bovine enamel samples were submitted to a cyclic de- and remineralisation for 3 days. Each day, the samples were exposed for 120 min to pooled human saliva and subsequently treated with one of the fluoride solutions for 3 min: amine fluoride (AmF, 0.5% and 1% F(-)), sodium fluoride (NaF, 0.5% and 1% F(-)), each at pH 3.9 and 7.0, and stannous fluoride (SnF(2), 0.5% and 1% F-), at pH: 3.9. Additionally, two groups were treated with fluoride-free placebo solutions (pH: 3.9 and 7.0) and one group served as control (no fluoridation). Ten specimens each group were inserted in a so-called artificial mouth and eroded six times daily with hydrochloric acid (pH 2.6) for 90 s each intermitted by exposure to artificial saliva (1 h). After 3 days, enamel loss was analyzed profilometrically and evaluated statistically by ANOVA. Results: Only the acidic 0.5% and 1% SnF(2) and 1% AmF solutions were able to reduce erosive enamel loss significantly, while all other solutions and placebos did not differ significantly from the control. Between the acidic SnF(2) and the 1% AmF solutions no significant differences could be detected. Conclusion: At the same concentrations, acidic SnF(2) and AmF may be more effective than NaF to protect enamel against erosion. (C) 2009 Elsevier Ltd. All rights reserved.

The Effect of Different Fluoride Concentrations and pH of Dentifrices on Plaque and Nail Fluoride Levels in Young Children

To evaluate the influence of dentifrice pH and fluoride (F) concentration on F uptake by plaque and nails, two sets of 5-to 6-year-old children were randomly allocated into four groups, according to the type of dentifrice they had been using for 1 year: (1) experimental liquid dentifrice (ELD), 1,100 ppm F, pH 7.0; (2) ELD, 1,100 ppm F, pH 4.5; (3) ELD, 550 ppm F, pH 4.5, and (4) commercial toothpaste, 1,100 ppm F, pH 7.0. In one set of children, nails were clipped. In the second, plaque samples were collected 1 h after the last use of dentifrice. F concentration in plaque and nails was analyzed. Plaque F concentration was significantly lower in group 4 than in groups 1-3. Nail F concentration was significantly higher in group 4, and significantly lower in group 3, than in group 1 or 2. Plaque F uptake was influenced significantly by dentifrice consistency and nonsignificantly by pH and F concentration. Reduction of dentifrice pH did not affect nail F concentration. Copyright (C) 2009 S. Karger AG, Basel

pH, Calcium Ion Release, and Setting Time of an Experimental Mineral Trioxide Aggregate-based Root Canal Sealer

Introduction: An experimental mineral trioxide aggregate sealer (MTAS) has been developed for use as a root canal sealer. The aim of this study was to evaluate the setting time, pH, and calcium ion release of MTAS compared with white Portland cement (CPB-40; Votorantin Cimentos, Camargo Correa SA, Pedro Leopoldo, MG, Brazil), white MTA Angelus (MTA; Angelus, Londrina, PR, Brazil), and AH Plus (Dentsply DeTrey, Konstanz, Germany). Methods: For the evaluation of setting time, each material was analyzed using Gilmore-type needles. Polyethylene tubes with the materials were immersed in distilled water for the measurement of pH (digital pH meter) and calcium release (atomic absorption spectrophotometry). The evaluations were performed at 3, 6, 12, 24, and 48 hours and 7, 14, and 28 days. Data were analyzed by analysis of variance and the Tukey test at 5% significance level. Results: MTAS showed higher calcium release at all experimental periods, a greater increase in pH up to 48 hours and the longest setting time. Conclusions: MTAS presented favorable properties for its indication as a root canal sealer. (J Endod 2011;37:844-846)