Propriedades fisicas do monocristal fe/mgo(100) e estudo da expansao termica da superficie da ag(100)

In this work we have developed a way to grow Fe/MgO(100) monocrystals by magnetron sputtering DC. We investigated the growing in a temperature range among 100 oC and 300 oC. Structural and magneto-crystalline properties were studied by different experimental techniques. Thickness and surface roughness of the films were investigated by atomic force microscopy, while magneto-crystalline properties were investigated by magneto-optical Kerr effect and ferromagnetic resonance. Our results show that as we increase the deposition temperature, the magneto-crystalline anisotropy of the films also increases, following the equation of Avrami. The best temperature value to make a film is 300 oC. As the main result, we built a base of magnetoresistence devices and as an aplication, we present measurements of Fe/Cr/Fe trilayer coupling. In a second work we investigated the temperature dependence of the first three interlayer spacings of Ag(100) surface using low energy electron diffraction. A linear expansion model of crystal surface was used and the values of Debye temperatures of the first two layers and thermal expansion coefficient were determinated. A relaxation of 1% was found for Ag(100) surface and these results are matched with faces (110) and (111) of the silver. iv

Estudo espectro eletroquímico de sistemas estruturados argila-corante

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Finite-momentum condensate of magnetic excitons in a bilayer quantum Hall system

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Magnetic field induced lattice effects in a quasi-two-dimensional organic conductor close to the Mott metal-insulator transition

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

New layered double hydroxides intercalated with substituted pyrroles. 1. In situ polymerization of 4-(1H-pyrrol-1-yl)benzoate

The two-dimensional hybrid organic-inorganic materials Zn-2-Cr and Zn-2-Al-LDHs (Layered Double Hydroxides) containing 4-(1H-pyrrol-1yl)benzoate anions as the interlayer anions were synthesized by the co-precipitation method at constant pH followed by subsequent hydrothermal treatment for 72 h. The materials were characterized by PXRD, C-13 CP-MAS NMR, ESR, TGA, and TEM. The basal spacing found by the X-ray diffraction technique is coincident with the formation of bilayers of the intercalated anions. Solid-state C-13 NMR and ESR data strongly suggest the partial in situ polymerization of the 4-(1H-pyrrol-1yl)benzoate anions during coprecipitation. (c) 2006 Elsevier Ltd. All rights reserved.

New layered double hydroxides intercalated with substituted pyrroles. 2. 3-(Pyrrol-1-yl)-propanoate and 7-(pyrrol-1-yl)-heptanoate LDHs

We report the synthesis and characterization of organic-inorganic hybrid materials: Zn-2-Al-LDHs (layered double hydroxides) containing 3-(1H-pyrrol-1-yl)-propanoate and 7-(1H-pyrrol-l-yl)-heptanoate as the interlayer anions. The LDHs were synthesized by the co-precipitation method at constant pH followed by hydrothermal treatment for 72 h. The materials were characterized by PXRD, C-13 CP-MAS NMR, TGA, and ESR. The basal spacing found by PXRD technique is coincident with the formation of bilayers of the intercalated anions. The solid state C-13 NMR showed that the interlayered anions remain identical after intercalation. ESR data suggest that the monomers connect each other in a limited number of guests when a thermal treatment is applied. The inorganic LDH sheets delay the temperature of degradation of the monomers. (c) 2006 Elsevier Ltd. All rights reserved.

Thermal behaviour of intercalated 8-hydroxyquinoline (oxine) in montmorillonite clay

The composite montmorillonite-8-hydroxyquinoline (Swy-1-8-HQ) was prepared by two different processes and studied by using thermogravimetric analysis (TG/DTG and DSC), as well as helpful techniques as fluorescence in the UV-visible region and X-ray diffraction. The composites developed fluorescent appearance, however with quantum poor efficiency and they exhibited distinct TG and DSC thermal behavior. The fluorescence data of spectra associated to the TG/DT curves allowed to suggest that the 8-HQ was present in the composites in two different circumstances: 1 - intercalated in the interlayer spaces (Swy-1-8-HQ2), rigidly associated to the Substrate feasible as a monolayer with the aromatic rings parallel to the silica layer; and/or, 2 - adsorbed on the Surface (Swy-1-8-HQ1), either as a bilayer formation or tilting of the molecules to the silicate layer sheet. All results confirmed above are in agreement with X-ray diffraction patterns, once the interlayer space increases when 8-HQ is incorporated. The experimental results confirm the formation of the composites in agreement with the method used in the preparation.

Study of an organically modified clay: Selective adsorption of heavy metal ions and voltammetric determination of mercury(II)

In this work, a hydrophilic clay, Na-montmorillonite from Wyoming, USA, was rendered organophilic by exchanging the inorganic interlayer cations for hexaclecyltrimethylammonium ions (HDTA), with the formulae of [(CH3)(3)N(C16H33)](+) ion. Based on fact that organo-clay has high affinities for non-ionic organic molecules, 1,3,4-thiadiazole-2,5-dithiol was loaded oil the HDTA-montmorillonite surface, resulting in the 1,3,4-thiadiazole-2,5-dithiol-HDTA-montmorillonite complex (TDD-organo-clay).The following properties of TDD-organo-clay are discussed: selective adsorption of heavy metal ions measured by batch and chromatographic column techniques, and utilization as preconcentration agent in a chemically modified carbon paste electrode (CMCPE) for determination of mercury(II).The main point of this paper is the construction of a selective sensor, a carbon paste electrode modified with TDD-organo-clay, its properties and its application to the determination of mercury(II) ions, as this element belongs to the most toxic metals. The chemical selectivity of this functional group and the selectivity of voltammetry were combined for preconcentration and determination. (c) 2005 Elsevier B.V. All rights reserved.

Synthesis, characterization and electrochemical study of layered double hydroxides intercalated with 2-thiophenecarboxylate anions

The synthesis, characterization, and electrochemical study of the Zn(II)-Al(III) and Zn(II)-Cr(III) Layered Double Hydroxides (LDHs) containing 2-thiopenecarboxylate as the interlayer anions are described. The LDHs were prepared by the constant pH coprecipitation technique followed by hydrothermal treatment for 72 h. The materials were analyzed by PXRD, FT-IR, C-13 CP-MAS, EDX, TEM, and CV. The presence of the organic heterocyclic anions was confirmed by FT-IR and the related solid-state C-13 NMR data strongly suggested that these were dimerised during coprecipitation. Accordingly, the basal spacing found by the X-ray technique was similar to 15.3 Angstrom, a distance coincident with the formation of bilayers of the intercalated anions. The structural organization of all the new materials was greatly enhanced by hydrothermal treatment, as shown by PXRD. The improved organization of the bilayered structures had a strong influence in the electrochemical behaviour of clay-modified electrodes produced with these materials, such as the diminished resistance to the ionic flow through the LDHs films. (C) 2003 Elsevier Ltd. All rights reserved.

Partially exchanged organophilic bentonites

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Bacterial cellulose membrane as flexible substrate for organic light emitting devices

Bacterial cellulose (BC) membranes produced by gram-negative, acetic acid bacteria (Gluconacetobacter xylinus), were used as flexible substrates for the fabrication of Organic Light Emitting Diodes (OLED). In order to achieve the necessary conductive properties indium tin oxide (ITO) thin films were deposited onto the membrane at room temperature using radio frequency (r.f) magnetron sputtering with an r.f. power of 30 W, at pressure of 8 mPa in Ar atmosphere without any subsequent thermal treatment. Visible light transmittance of about 40% was observed. Resistivity, mobility and carrier concentration of deposited ITO films were 4.90 x 10(-4) Ohm cm, 8.08 cm(2)/V-s and -1.5 x 10(21) cm(-3), respectively, comparable with commercial ITO substrates. In order to demonstrate the feasibility of devices based on BC membranes three OLEDs with different substrates were produced: a reference one with commercial ITO on glass, a second one with a SiO(2) thin film interlayer between the BC membrane and the ITO layer and a third one just with ITO deposited directly on the BC membrane. The observed OLED luminance ratio was: 1; 0.5; 0.25 respectively, with 2400 cd/m(2) as the value for the reference OLED. These preliminary results show clearly that the functionalized biopolymer, biodegradable, biocompatible bacterial cellulose membranes can be successfully used as substrate in flexible organic optoelectronic devices. (C) 2008 Elsevier B.V. All rights reserved.

Pore structure characterization of kaolin, metakaolin, and their acid-treated products using small-angle X-ray scattering

Pore structure of dealuminated kaolin and metakaolin was studied by small-angle X-ray scattering (SAXS). Both parent kaolin and metakaolin have about 10% of the total pore volume provided by globular pores with 105 Å mean pore size. Their surface area is about 14 m2/g. Acid dealumination of kaolin causes an increase of its globular pore volume without an appreciable change in the mean pore size, its surface area increasing up to about 90 m2/g. Acid dealumination of metakaolin enhances the globular pore volume, although there is generation of slit-shaped pores with a narrow thickness distribution whose mean value is 14 Å. This interlayer spacing causes an increase in surface area of about 190 m2/g by SAXS. © 1994.

Synthesis, structure, and thermal stability of poly(methyl methacrylate)-co- poly(3-tri(methoxysilyil)propyl methacrylate)/ montmorillonite nanocomposites

The structure and the thermodegradation behavior of both poly(methyl methacrylate)-co-poly(3-tri(methoxysilyil)propyl methacrylate) polymer modified with silyl groups and of intercalated poly(methyl methacrylate)-co-poly(3- tri(methoxysilyil)propyl methacrylate)/Cloisite 15A™ nanocomposite have been in situ probed. The structural feature were comparatively studied by Fourier transform infrared spectroscopy (FTIR), 13C and 29Si nuclear magnetic resonance (NMR), and small angle X-ray scattering (SAXS) measurements. The intercalation of polymer in the interlayer galleries was evidenced by the increment of the basal distance from 31 to 45 Å. The variation of this interlayer distance as function of temperature was followed by in situ SAXS. Pristine polymer decomposition pathway depends on the atmosphere, presenting two steps under air and three under N2. The nanocomposites are more stable than polymer, and this thermal improvement is proportional to the clay loading. The experimental results indicate that clay nanoparticles play several different roles in polymer stabilization, among them, diffusion barrier, charring, and suppression of degradation steps by chemical reactions between polymer and clay. Charring is atmosphere dependent, occurring more pronounced under air. © 2012 Society of Plastics Engineers.

Thermal stability of ionene polymers

Two different cationic polymers of the same chemical type and with very similar chemical structures were reacted with a natural bentonite over a wide range of polymer/clay ratios. This study involved the synthesis of cationic aliphatic ammonium polyionenes, specifically 3,6-ionene and 3,6-dodecylionene. Ionenes are ion-containing polymers that contain quaternary nitrogen atoms in the main macromolecular chain as opposed to a pendant chain. The CHN content, basal spacing, and elemental composition of each of the polymer-clay complexes were analyzed by X-ray diffraction, X-ray fluorescence, and thermogravimetry. All the polycations reacted to form interlayer complexes with clay, which displaced more Na+ and little Ca2+. Sodium and calcium were both present as interlayer cations in the clay and its complexes. The TG/DTG curves show that both polymers underwent thermal degradation in more than one stage. Specifically, 3,6-ionene was found to undergo two stages of decomposition and 3,6-dodecylionene undergo three stages. The behavior of the TG/DTG curves and the activation energy values suggest that 3,6-dodecylionene (E = 174,85 kJ mol-1) complexes have greater thermal stability than 3,6-ionene (E = 115,52 kJ mol-1) complexes. The mechanism of degradation suggests a direct interaction with the dodecyl chain containing 12 carbons, which are present in 3,6-dodecylionene but not in 3,6-ionene. © 2012 Akadémiai Kiadó, Budapest, Hungary.

XAS/WAXS time-resolved phase speciation of chlorine LDH thermal transformation: Emerging roles of isovalent metal substitution

The XAS/WAXS time-resolved method was applied for unraveling the complex mechanisms arising from the evolution of several metastable intermediates during the degradation of chlorine layered double hydroxide (LDH) upon heating to 450 °C, i.e., Zn2Al(OH)6·nH2O, ZnCuAl(OH)6·nH2O, Zn2Al 0.75Fe0.25(OH)6·nH2O, and ZnCuAl0.5Fe0.5(OH)6·nH2O. After a contraction of the interlamellar distance, attributed to the loss of intracrystalline water molecules, this distance experiences an expansion (T > 175-225 °C) before the breakdown of the lamellar framework around 275-295 °C. Amorphous prenucleus clusters with crystallo-chemical local order of zinc-based oxide and zinc-based spinel phases, and if any of copper-based oxide, are formed at T > 175-225 °C well before the loss of stacking of LDH layers. This distance expansion has been ascribed to the migration of Zn II from octahedral layers to tetrahedral sites in the interlayer space, nucleating the nano-ZnO or nano-ZnM2O4 (M = Al or Fe) amorphous prenuclei. The transformation of these nano-ZnO clusters toward ZnO crystallites proceeds through an agglomeration process occurring before the complete loss of layer stacking for Zn2Al(OH)6· nH2O and Zn2Al0.75Fe0.25(OH) 6·nH2O. For ZnCuAl(OH)6·nH 2O and ZnCuAl0.5Fe0.5(OH)6· nH2O, a cooperative effect between the formation of nano-CuO and nano-ZnAl2O4 amorphous clusters facilitates the topochemical transformation of LDH to spinel due to the contribution of octahedral CuII vacancy to ZnII diffusion. © 2013 American Chemical Society.