Spectroscopic ellipsometry investigations of the optical properties of manganese doped bismuth vanadate thin films

The optical properties of Bi(2)V(1-x)MnxO(5.5-x) (x=0.05, 0.1, 0.15 and 0.2 at.%) thin films fabricated by pulsed laser deposition on platinized Silicon Substrates were Studied in UV-visible spectral region (1.51-4.17 CV) using spectroscopic ellipsometry. The optical constants and thicknesses of these films have been obtained by fitting the ellipsometric data (Psi and Delta) using a multilayer four-phase model system and a relaxed Lorentz oscillator dispersion relation. The surface roughness and film thickness obtained by spectroscopic ellipsometry were found to be consistent with the results obtained by atomic force and scanning electron microscopy. The refractive index measured at 650 nm does not show any marginal increase with Mn content. Further, the extinction coefficient does not show much decrease with increasing Mn content. An increase in optical band gap energy from 2.52 to 2.77 eV with increasing Mn Content from x = 0.05 to 0.15 was attributed to the increase in oxygen ion vacancy disorder. (C) 2009 Elsevier Ltd. All rights reserved.

Redistribution of subcellular calcium in rat liver on administration of vanadate

Mitochondria isolated from the livers of rats administered with sodium meta-, ortho-, or polyvanadate, but not vanadyl sulphate, exhibited enhanced Ca2+ — stimulated respiration and uptake of calcium. These effects were shown also by mitochondria isolated from livers perfused with polyvanadate. The concentration of acid-soluble calcium decreased significantly in the mitochondrial fraction on vanadate treatment, while that in the cytosol showed a corresponding increase. Phenoxybenzamine, an antagonist to a-adrenergic receptors, effectively inhibited vanadate-induced Ca2+ mobilization, but surgical sympathectomy was without effect. This is the first demonstration of vanadate mimicking agr-adrenergic agonists in vivo.

Increase in alpha-glycerophosphate dehydrogenase and other oxidoreductase activities of hepatic mitochondria on administration of vanadate to the rat

Liver mitochondria isolated from vanadate-administered rats showed increased (20-25%) rates of oxidation of both NAD(+)-linked substrates and succinate. Respiratory control index and ADP/O were unaffected by the treatment. Dormant and uncoupler-stimulated ATPase activity also was not affected by vanadate administration. Membrane-bound, electron-transport-linked dehydrogenase activities (both NAD(+)- and succinate-dependent) increased by 15-20% on vanadate treatment. Mitochondrial alpha-glycerophosphate dehydrogenase activity increased by 50% on vanadate administration. The above effects of vanadate on oxidoreductase activities could be prevented by the prior administration of antagonists to alpha-adrenergic receptors. Substrate-dependent H2O2 generation by mitochondria also showed an increase on vanadate administration.

Occurrence of Lipid Peroxidation in Brain Microsomes in the Presence of NADH and Vanadate

Oxidation of NADH by rat brain microsomes was stimulated severalfold on addition of vanadate. During the reaction, vanadate was reduced, oxygen was consumed, and H2O2 was generated with a stoichiometry of 1:1 for NADH/O2, as in the case of other membranes. Extra oxygen was found to be consumed over that needed for H2O2 generation specifically when brain microsomes were used. This appears to be due to the peroxidation of lipids known to be accompanied by a large consumption of oxygen. Occurrence of lipid peroxidation in brain microsomes in the presence of NADH and vanadate has been demonstrated. This activity was obtained specifically with the polymeric form of vanadate and with NADH, and was inhibited by the divalent cations Cu2+, Mn2+, and Ca2+, by dihydroxy-phenolic compounds, and by hemin in a concentration-dependent fashion. In the presence of a small concentration of vanadate, addition of an increasing concentration of Fe2+ gave increasing lipid peroxidation. After undergoing lipid peroxidation in the presence of NADH and vanadate, the binding of quinuclidinyl benzylate, a muscarinic antagonist, to brain membranes was decreased.

Structural, optical and electrical characteristics of transparent bismuth vanadate films deposited on indium tin oxide coated glass substrates

Bismuth vanadate (BVO) thin films were fabricated on indium tin oxide (ITO) coated glass substrates using pulsed laser ablation technique and investigated their structural, optical and electrical properties. The use of the indium tin oxide coated glass substrate resulted in reducing the leakage current characteristics of crystalline BVO thin films. The X-ray diffraction (XRD) studies confirmed the monophasic nature of the post annealed (500 A degrees C/1 h) films. The atomic force microscopy indicated the homogeneous distribution of crystallites in the as-deposited films. The as-deposited and the post annealed films were almost 90% transparent (380-900 nm) as confirmed by optical transmission studies. Dielectric constant of around 52 was attained accompanied by the low dielectric loss of 0.002 at 10 kHz for post annealed films. The leakage current of the post annealed BVO films on ITO coated glass substrates measured at room temperature was 8.1 x 10(-8) A at an applied electric field of 33 kV/cm, which was lower than that of the films with platinum and SrRuO3 as the bottom electrodes.

Characterization of oxygen free radicals generated during vanadate-stimulated NADH oxidation

The oxidation of NADH and accompanying reduction of oxygen to H2O2 stimulated by polyvanadate was markedly inhibited by SOD and cytochrome c. The presence of decavanadate, the polymeric form, is necessary for obtaining the microsomal enzyme-catalyzed activity. The accompanying activity of reduction of cytochrome c was found to be SOD-insensitive and therefore does not represent superoxide formation. The reduction of cytochrome c by vanadyl sulfate was also SOD-insensitive. In the presence of H2O2 all the forms of vanadate were able to oxidize reduced cytochrome c, which was sensitive to mannitol, tris and also catalase, indicating H202-dependent generation of hydroxyl radicals. Using ESR and spin trapping technique only hydroxyl radicals, but not superoxide anion radicals, were detected during polyvanadate-dependent NADH oxidation.

Microstructural and dielectric properties of KCl-added bismuth vanadate ceramics

The effect of KCI addition on the microstructural, structural and dielectric properties of bismuth vanadate, Bi2VO5.5 (BiV) has been examined. The average grain size of BN ceramics increases with increase in KCl content (from an average grain size of TO to 80 mu m) as a result of the increased liquid-phase formation of KCI, at the grain boundaries. Differential scanning calorimetry (DSC) carried out on the KCl-added samples indicates an upward shift in the transition temperature (T-c), from 723 K (for BN) to 734 K (for 5 mol% KCl-added BiV). On further increase in the KCI content, T-c shifts down to about 722 K for 10 mol%. This trend is consistent with that of the lattice strain data. The relative permittivity as well as the dielectric loss decrease by more than half of the original values upon the addition of KCI. The relative permittivities of the KCl-added ceramics are comparable with the values predicted by the logarithmic mixture rule. Impedance analyses suggest that the grain boundary resistance of the KCl-added BiV ceramics is higher by two orders of magnitude than that of BN ceramics. The KCl-added BN ceramics exhibit ferroelectric domains and the domain density decreases as the grain boundary region is approached.

Mechanically activated synthesis of nanocrystalline powders of ferroelectric bismuth vanadate

Mechanical milling of a stoichiometric mixture of Bi2O3 and V2O5 yielded nanosized powders of bismuth vanadate, Bi2VO5.5 (BN). Structural evolution of the desired BiV phase, through an intermediate product (BiVO4), was monitored by subjecting the powders, ball milled for various durations to X-ray powder diffraction (XRD), differential thermal analysis (DTA), and transmission electron microscopic (TEM) studies. XRD studies indicate that the relative amount of the BiV phase present in the ball-milled mixture increases with increase in milling time and its formation reaches completion within 54 h of milling. Assynthesized powders were found to stabilize in the high-temperature tetragonal (gamma) phase. DTA analyses of the powders milled for various durations suggest that the BN phase-formation temperature decreases with increase in milling time. The nanometric size (30 nm) of the crystallites in the final product was confirmed by TEM and XRD studies. TEM studies clearly demonstrate the growth of BiV on Bi2O3 crystallites. (C) 1999 Academic Press.

Preparation and characterization of nanocrystalline powders of bismuth vanadate

The influence of mechanical activation on the formation of Bi2VO5.5 bismuth vanadate (BiV) phase, was investigated by ball-milling a stoichiometric mixture of bismuth oxide and vanadium pentoxide. The structural evolution of the desired BN phase, via an intermediate BiVO4,phase, was investigated using X-ray powder diffraction; (XRD), differential thermal analysis (DTA) and transmission electron microscopy (TEM). Milling for 54h. yielded monophasic gamma-BiV powders with an average crystallite size of 30 nm. The electron paramagnetic resonance (EPR) peaks associated with the V4+ ions are stronger and broader in nanocrystalline (n) BN than in the conventionally prepared microcrystalline (m) BN, suggesting theta significant portion of V5+ has been transformed to V4+ during milling. The optical bandgap of n-BiV was found to be higher than that of m-BiV. High density (97% of the theoretical density), fine-grained (average grain-size of 2 tun) ceramics with uniform grain-size distribution could be fabricated using n-BiV powders. These fine-grained ceramics exhibit improved dielectric, pyre and ferroelectric properties. (C) 1999 Elsevier Science S.A. All rights reserved.

Synthesis and structure of La14V6CuO36.5: a transparent Cu(I) vanadate containing [OCuO](3-) sticks

The title compound, La14V6CuO36.5, was prepared from a stoichiometric mixture of La2O3,V2O5, and CuO at 1050-1080 degreesC. The compound forms transparent, pale green crystals and was characterized by wavelength dispersive spectroscopy and single crystal X-ray diffraction. The structure contains isolated VO43- tetrahedra and [OCuO](3-) sticks dispersed in a lanthanum oxide network. Films of La14V6CuO36.5 were grown on R-plane sapphire by using pulsed laser deposition. Rutherford backscattering spectroscopic and X-ray diffraction analyses of the films showed oriented growth of the title phase, a similar to5 eV optical band gap and n-type conductivity. The compound is an example of a transparent copper(I) oxide.

Dielectric anomaly in strontium borate-bismuth vanadate glass nanocomposite

Transparent glass nanocomposites in the pseudo binary system (100 - x) SrB4O7 (SBO)-x Bi2VO5.5 (BiV) (0 less than or equal to n less than or equal to 70) were prepared by the splat quenching technique. The nano-crystallization of bismuth vanadate (BiV) in 50 SBO-50 BiV (in mol%) glass composite has been demonstrated. These were characterized for their structural, thermal and dielectric properties. As-quenched composites under study have been confirmed to be amorphous by X-ray powder diffraction (XRD) studies. The glass transition temperature (T-g) and crystallization temperatures (T-er) were determined using differential thermal analyses (DTA), High resolution transmission electron microscopic (HRTEM) studies carried out on heat-treated samples reveal the presence of spherical nanosize crystallites of Bi2VO5.5 (BiV) dispersed in the glassy matrix of SrB4O7 (SSO). The dielectric constant (epsilon (r)) and the dielectric loss (D) measurements were carried out on the as-quenched and heat-treated glass nanocomposite samples in the frequency range 100 Hz-10 MHz. The as-quenched and the heat-treated at two different temperatures (720 and 820 K) samples exhibited broad dielectric anomalies in the vicinity of the ferroelectric-to-paraelectric transition temperature of the parent BiV ceramics. The Curie-Weiss law was found to be valid at a temperature above the transition temperature, establishing the diffused nature of the transition. (C) 2001 Elsevier Science Ltd. All rights reserved.

Analysis of oxide and vanadate supports for catalytic hydrogen combustion: Kinetic and mechanistic investigations

Combustion synthesized oxide and vanadate compounds (CeO2, Fe2O3, CeVO4, and FeVO4) were tested for catalytic hydrogen combustion. The compounds were characterized by X-ray diffraction and X-ray photoelectron spectroscopy. All the four compounds showed good activity and stability for catalytic hydrogen combustion and more than 95% conversion was observed over all the compounds within 500 degrees C. The mechanisms for the reaction over the different classes of compounds (cerium-based and iron-based compounds) were proposed on the basis of spectroscopic observations. The main difference in the mechanisms was in the nature of adsorption of H2 over the sites. The elementary processes for the reaction were proposed, corresponding rate expressions were derived, and the rate parameters for the reaction were estimated using nonlinear regression. Langmuir-Hinshelwood and Eley-Rideal mechanisms were also tested for the reaction and the proposed mechanism was compared with these mechanisms. (c) 2011 American Institute of Chemical Engineers AIChE J, 2012

Study of the effect of alkali mixture on V-O bond length in Oxyfluoro Vanadate glasses using Raman spectroscopy

Raman spectroscopic study on Oxyfluoro Vanadate glasses containing various proportions of lithium fluoride and rubidium fluoride was carried out to see an effect of mixture of alkali on vanadium-oxygen (V-O) bond length. Glasses with a general formula 40V(2)O(5) - 30BaF(2) - (30 - x) LiF - xRbF (x = 0-30) were prepared. Room temperature Raman spectra of these glass samples were recorded in back scattering geometry. The data presented is in ``reduced Raman intensity'' form with maximum peak scaled to 100. We have used v = Aexp(BR), where A and B are fitting parameters, to correlate the bond length R with Raman scattering frequency v. We observed that variation in bond length and its distribution about a most probable value can be correlated to the alkali environment present in these glasses. We also observed that all rubidium environment around the network forming unit is more homogenous than all lithium environment.

Role of Crystal Field in Mixed Alkali Metal Effect: Electron Paramagnetic Resonance Study of Mixed Alkali Metal Oxyfluoro Vanadate Glasses

The mixed alkali metal effect is a long-standing problem in glasses. Electron paramagnetic resonance (EPR) is used by several researchers to study the mixed alkali metal effect, but a detailed analysis of the nearest neighbor environment of the glass former using spin-Hamiltonian parameters was elusive. In this study we have prepared a series of vanadate glasses having general formula (mol %) 40 V2O5-30BaF(2)-(30 - x)LiF-xRbF with x = 5, 10, 15, 20, 25, and 30. Spin-Hamiltonian parameters of V4+ ions were extracted by simulating and fitting to the experimental spectra using EasySpin. From the analysis of these parameters it is observed that the replacement of lithium ions by rubidium ions follows a ``preferential substitution model''. Using this proposed model, we were able to account for the observed variation in the ratio of the g parameter, which goes through a maximum. This reflects an asymmetric to symmetric changeover of. the alkali metal ion environment around the vanadium site. Further, this model also accounts for the variation in oxidation state of vanadium ion, which was confirmed from the variation in signal intensity of EPR spectra.