Marine Collagen Reinforcement of Calcium Phosphate Bone Cements: A Biological Assessment

Induction of in vivo responses by implanted biomaterials is of great interest in the medical device field. Calcium phosphate bone cements (CPCs) can potentially promote natural bone remodelling and ingrowth in vivo and, as such are becoming more common place in a range of orthopaedic procedures. However, concerns remain regarding their mechanical and handling properties. Compressive modulus and fracture toughness of CPCs can be improved, without compromising injectability and setting time, through the incorporation of bovine collagen fibres1. Incorporation of marine derived collagen fibres has also yielded similar improvements2. It is hypothesised that, due to its role in bone formation and function, that incorporation of collagen in CPCs will also result in biological benefits.
The biological properties of α-TCP-CPC were largely unchanged by the incorporation of marine derived collagen. However, as a result of significant improvements to the mechanical properties, its incorporation may still result in a suitable alternative to some commercially available bone cements.

The Role of Water Content and Paste Proportion on Physico-mechanical Properties of Alkali Activated Fly Ash–Ggbs Concrete

The growth of the construction industry worldwide poses a serious concern on the sustainability of the building material production chain, mainly due to the carbon emissions related to the production of Portland cement. On the other hand, valuable materials from waste streams, particularly from the metallurgical industry, are not used at their full potential. Alkali activated concrete (AAC) has emerged in the last years as a promising alternative to traditional Portland cement based concrete for some applications. However, despite showing remarkable strength and durability potential, its utilisation is not widespread, mainly due to the lack of broadly accepted standards for the selection of suitable mix recipes fulfilling design requirements, in particular workability, setting time and strength. In this paper, a contribution towards the design development of AAC synthetized from pulverised fuel ash (60%) and ground granulated blast furnace slag (40%) activated with a solution of sodium hydroxide and sodium silicate is proposed. Results from a first batch of mixes indicated that water content influences the setting time and that paste content is a key parameter for controlling strength development and workability. The investigation indicated that, for the given raw materials and activator compositions, a minimum water to solid (w/s) ratio of 0.37 was needed for an initial setting time of about 1 hour. Further work with paste content in the range of 30% to 33% determined the relationship between workability and strength development and w/s ratio and paste content. Strengths in the range of 50 - 60 MPa were achieved.

Sustainable binders for concrete: a structured approach from waste screening to binder composition development

Worldwide, the building sector requires the production of 4 billion tonnes of cement annually, consuming more than 40% of global energy. Alkali activated “cementless” binders have recently emerged as a novel eco-friendly construction material with a promising potential to replace ordinary Portland cement. These binders consist of a class of inorganic polymer formed mainly by the reaction between an alkaline solution and an aluminosilicate source. Precursor materials for this reaction can be found in secondary material streams from different industrial sectors, from energy to agro-alimentary. However, the suitability of these materials in developing the polymerisation reaction must be assessed through a detailed chemical and physical characterisation, ensuring the availability of required chemical species in the appropriate quantity and physical state. Furthermore, the binder composition needs to be defined in terms of proper alkali activation dosages, water content in the mix, and curing conditions. The mix design must satisfy mechanical requirements and compliance to desired engineering properties (workability, setting time) for ensuring the suitability of the binder in replacing Portland cement in concrete applications. This paper offers a structured approach for the development of secondary material-based binders, from their identification to mix design and production procedure development. Essential features of precursor material can be determined through chemical and physical characterisation methods and advanced microscope techniques. Important mixing parameters and binder properties requirements are examined and some examples of developed binders are reported.

Sustainable concrete: design and testing

Producing concrete with secondary raw materials is an excellent way to contribute to a moresustainable world, provided that this concrete has at least the same performance during itsservice life as concrete made with the primary raw materials it replaces. Secondary rawmaterials for Light Weight (LW) aggregates (rigid polyurethane foams, shredded tire rubberand mixed plastic scraps) have been combined with secondary raw materials for the binder(fly ash, slag and perlite tailings) making sustainable concretes that were investigated fortheir suitability as LW, highly insulating concrete for four different types of applications.Compliance to desired engineering properties (workability, setting time) was not alwaysfeasible: it was mostly the low workability of the mixtures that limited their application.Contrary to well established cements, steering the workability by adding water was not anoption for these binders that rely on alkali-activation. Eight successful mixtures have beentested further. The results have shown that it is possible to produce a non-structuralsustainable concrete with good mechanical and thermal insulation properties.Design of concrete made with novel materials is currently not feasible without extensiveexperimentation as no design rules exist other than empirically derived rules based ontraditional materials. As a radical different approach, a flexible concrete mix design has beendeveloped with which the concrete can be modelled in the fresh and hardened state. Thenumerical concrete mix design method proves a promising tool in designing concrete forperformance demands such as elasticity parameters and thermal conductivity

Alkali activated fuel ash and slag mixes:optimization study from paste to concrete building blocks

Alkali activated binders, based on ash and slag, also known as geopolymers, can play a key role in reducing the carbon footprint of the construction sector by replacing ordinary Portland cement in some concretes. Since 1970s, research effort has been ongoing in many research institutions. In this study, pulverized fuel ash (pfa) from a UK power plant, ground granulated blast furnace slag (ggbs) and combinations of the two have been investigated as geopolymer binders for concrete applications. Activators used were sodium hydroxide and sodium silicate solutions. Mortars with sand/binder ratio of 2.75 with several pfa and ggbs combinations have been mixed and tested. The optimization of alkali dosage (defined as the Na2O/binder mass ratio) and modulus (defined as the Na2O/SiO2 mass ratio) resulted in strengths in excess of 70 MPa for tested mortars. Setting time and workability have been considered for the identification of the best combination of pfa/ggbs and alkali activator dosage for different precast concrete products. Geopolymer concrete building blocks have been replicated in laboratory and a real scale factory trial has been successfully carried out. Ongoing microstructural characterization is aiming to identify reaction products arising from pfa/ggbs combinations.

PMMA-co-EHA cements for osteoprotheses

The main purpose of this thesis was to produce new formulations of PMMA-co- EHA and study its feasibility as being an alternative to traditional PMMA bone cements. Thus, were originally produced several co-polymers of PMMA-co-EHA and its mechanical properties and in vitro behaviour were evaluated. The copolymers were obtained by radical polymerization and several formulations were produced by partial replacement of MMA (up to about 50%) for EHA. Overall, the results suggest that the partial replacement of MMA by EHA decreased the modulus of the materials and, consequently, increased its flexibility. Then, PMMA commercial beads were added to PMMA-co-EHA formulations (to get bone cement) and the general properties of the resulting bone cements were evaluated. In general, the results revealed that the partial replacement of MMA by EHA led to beneficial changes in curing parameters (there was a reduction of the peak temperature and an increase of curing/setting time), in the in vitro behaviour (the water capacity increased) and in the mechanical properties (the bending strength increased) of new cements. The in vitro cellular response of new formulations of PMMA-co-EHA was compared with that of traditional PMMA bone cement. To this end, we tested the cell adhesion and proliferation of osteoblast-like MG63 cells and human cells from bone marrow. The results revealed that both types of cells were able to attach and proliferate in both formulations. The only exception was observed for the formulation prepared with the highest percentage of EHA, where a few cells that adhere failed to proliferate. Moreover, it was found that increasing the amount of EHA in cement led to an increasing inhibition of cell growth, especially during the first week of culture. This was related to increased water uptake capacity by the new formulations and consequent release of some of its toxic components. Finally, PMMA commercial beads were partially replaced by HA particles and the influence of this substitution on the curing parameters, the mechanical properties and in vitro behaviour of the resulting composites was also evaluated. Incorporation of HA into the bone cements induced a number of significant changes in its final properties: 1) decrease the peak temperature; 2) increase of curing time, 3) increasing the value of elastic modulus accompanied by decrease of the strength/tension. This last finding was related to poor interfacial adhesion between the various components of the bone cements and a heterogeneous distribution (possible agglomeration) of HA particles.

Cimentos de fosfato de magnésio: consolidação e caracterização

A reação entre o óxido de magnésio (MgO) e o fosfato de monoamónio (MAP), à temperatura ambiente, origina os cimentos de fosfato de magnésio, materiais caracterizados pela sua presa rápida e pelas excelentes propriedades mecânicas adquiridas precocemente. As propriedades finais são dependentes, essencialmente, da composição do cimento (razão molar magnésia:fosfato e utilização de retardantes de presa) mas também são influenciadas pela reatividade da magnésia utilizada. Neste trabalho, a reação foi caracterizada através do estudo da influência da razão molar MgO:MAP (variando de 1:1 até 8:1), da presença e teor de aditivos retardantes (ácido bórico, ácido cítrico e tripolifosfato de sódio) e da variação da área superficial específica da magnésia (conseguida por calcinação do óxido), no tempo de presa, na temperatura máxima atingida e nas fases cristalinas finais formadas. A reação de presa pode ser comparada à hidratação do cimento Portland, com a existência de 4 estágios (reação inicial, indução, aceleração e desaceleração), com a diferença que estes estágios ocorrem a velocidade muito mais alta nos cimentos de fosfato de magnésio. Este estudo foi realizado utilizando a espetroscopia de impedâncias, acompanhada pela monitorização da evolução de temperatura ao longo do tempo de reação e, por paragem de reação, identificando as fases cristalinas formadas. A investigação do mecanismo de reação foi complementada com a observação da microestrutura dos cimentos formados e permitiu concluir que a origem da magnésia usada não afeta a reação nem as propriedades do cimento final. A metodologia de superfície de resposta foi utilizada para o estudo e otimização das características finais do produto, tendo-se mostrado um método muito eficaz. Para o estudo da variação da área superficial específica da magnésia com as condições de calcinação (temperatura e tempo de patamar) usou-se o planeamento fatorial de experiências tendo sido obtido um modelo matemático que relaciona a resposta da área superficial específica da magnésia com as condições de calcinação. As propriedades finais dos cimentos (resistência mecânica à compressão e absorção de água) foram estudadas utilizando o planeamento simplex de experiências, que permitiu encontrar modelos que relacionam a propriedade em estudo com os valores das variáveis (razão molar MgO:MAP, área superficial específica da magnésia e quantidade de ácido bórico). Estes modelos podem ser usados para formular composições e produzir cimentos com propriedades finais específicas.

Rheological characteristics of suwari and kamaboko gels made of surimi from Indian major carps

The gel strength, compressibility and folding characteristic of suwari (set) and kamaboko (set and cooked) gels prepared from rohu (Labeo rohita), catla (Catla catla) and mrigal (Cirrhinus mrigala) surimi were examined to understand the occurrence of suwari and modori phenomena in surimi from major freshwater carps. Suwari setting of gels did not take place at lower temperatures. Suwari gels showed good gel strength at 50 °C for rohu and at 60 °C for catla and mrigal after 30 min setting time. Incubation for 60 min decreased the gel strength at 60 °C for rohu and catla. Setting at 25 °C followed by cooking at 90 °C increased the gel strength. Increased setting temperature, however, decreased the gel strength of cooked gels. Gel strength and compressibility data were supported by folding characteristics.

Rheological characteristics of suwari and kamaboko gels made of surimi from Indian major carps

The gel strength, compressibility and folding characteristic of suwari (set) and kamaboko (set and cooked) gels prepared from rohu (Labeo rohita), catla (Catla catla) and mrigal (Cirrhinus mrigala) surimi were examined to understand the occurrence of suwari and modori phenomena in surimi from major freshwater carps. Suwari setting of gels did not take place at lower temperatures. Suwari gels showed good gel strength at 50 C for rohu and at 60 C for catla and mrigal after 30 min setting time

Síntese, aplicação e avaliação do efeito do teor de fósforo da celulose fosfatada em argamassa de alvenaria com aditivo comercial a base de hidroxi-etil-metil celulose (HEMC)

Generally, cellulose ethers improves mortar properties such as water retention, workability and setting time, along with adherence to the substrate. However, a major disadvantage of the addition of cellulose ethers in mortars is the delay in hydration of the cement. In this paper a cellulose phosphate (Cp) was synthesized water soluble and has been evaluated the effect of their incorporation into mortar based on Portland cement. Cellulose phosphate obtained was characterized by spectrophotometry Fourier transform infrared (FTIR), X-ray diffraction (XRD), elemental analysis and scanning electron microscopy (SEM). Mortar compositions were formulated with varying phosphorus content in cellulose and cellulose phosphate concentrations, when used in partial or total replacement of the commercial additive based hydroxyethyl methyl cellulose (HEMC). The mortars formulated with additives were prepared and characterized by: testing in the fresh state (consistency index, water retention, bulk density and air content incorporated) and in the hardened state (absorption by capillarity, density, flexural and compression strength). In mixtures the proportion of sand:cement of 1:5 (v / v) and factor a / c = 1.31 and water were held constant. Overall, the results showed that the celluloses phosphates employed in mortars added acted significantly when partially substituting the commercial additive. With regard to consistency index, water retention and bulk density in the fresh state and absorption by capillarity and bulk density apparent in the hardened state, showed no appreciable differences as compared to the commercial additive. The incorporated air content in the fresh state reduced markedly, but did not affect other properties. The mortars with cellulose phosphate, partially replacing the commercial additive showed an improvement of the properties of flexural strength and compressive strength

Desenvolvimento de um sistema misto de pasta à base de geopolímero e cimento portland para correção de perda de circulação

The materials engineering includes processes and products involving several areas of engineering, allowing them to prepare materials that fulfill the needs of various new products. In this case, this work aims to study a system composed of cement paste and geopolymers, which can contribute to solving an engineering problem that directly involves the exploitation of oil wells subject to loss of circulation. To correct it, has been already proposed the use of granular materials, fibers, reducing the drilling fluid or cement paste density and even surface and downhole mixed systems. In this work, we proposed the development of a slurry mixed system, the first was a cement-based slurry and the second a geopolymer-based slurry. The cement-based slurry was formulated with low density and extenders, 12.0 ppg (1.438 g/cm ³), showing great thixotropic characteristics. It was added nano silica at concentrations of 0.5, 1.0 and 1.5 gps (66.88, 133.76 and 200.64 L/m3) and CaCl2 at concentrations of 0.5, 1, 0 and 1.5%. The second system is a geopolymer-based paste formulated from molar ratios of 3.5 (nSiO2/nAl2O3), 0.27 (nK2O/nSiO2), 1.07 (nK2O/nAl2O3) and 13.99 (nH2O/nK2O). Finally, we performed a mixture of these two systems, for their application for correction of circulation lost. To characterize the raw materials, XRD, XRF, FTIR analysis and titration were performed. The both systems were characterized in tests based on API RP10B. Compressive strength tests were conducted after curing for 24 hours, 7 and 28 days at 58 °C on the cement-based system and the geopolymer-based system. From the mixtures have been performed mixability tests and micro structural characterizations (XRD, SEM and TG). The results showed that the nano silica, when combined with CaCl2 modified the rheological properties of the cement slurry and from the concentration of 1.5 gpc (200.64 L / m³) it was possible to obtain stable systems. The system mixture caused a change in the microstructure of the material by favoring the rate of geopolymer formation to hinder the C3S phase hydration, thus, the production of CSH phases and Portlandite were harmed. Through the mixability tests it can be concluded that the system, due to reduced setting time of the mixture, can be applied to plug lost circulation zones when mixed downhole

Compósitos Portland-biopolímeros para cimentação de poços de petróleo

The oil production in mature areas can be improved by advanced recovery techniques. In special, steam injection reduces the viscosity of heavy oils, thus improving its flow to surrounding wells. On the other hand, the usually high temperatures and pressures involved in the process may lead to cement cracking, negatively affecting both the mechanical stability and zonal isolation provided by the cement sheath of the well. The addition of plastic materials to the cement is an alternative to prevent this scenario. Composite slurries consisting of Portland cement and a natural biopolymer were studied. Samples containing different contents of biopolymer dispersed in a Portland cement matrix were prepared and evaluated by mechanical and rheological tests in order to assess their behavior according to API (American Petroleum Institute) guidelines. FEM was also applied to map the stress distribution encountered by the cement at bottom bole. The slurries were prepared according to a factorial experiment plan by varying three parameters, i.e., cement age, contents of biopolymer and water-to-cement ratio. The results revealed that the addition of the biopolymer reduced the volume of free water and the setting time of the slurry. In addition, tensile strength, compressive strength and toughness improved by 30% comparing hardened composites to plain Portland slurries. FEM results suggested that the stresses developed at bottomhole may be 10 to 100 times higher than the strength of the cement as evaluated in the lab by unconfined mechanical testing. An alternative approach is proposed to adapt the testing methodology used to evaluate the mechanical behavior of oilwell cement slurries by simulating the confined conditions encountered at bottornhole

Análise comparativa entre as propriedades do gesso obtido de rejeito da produção de sal e gesso comerciais

The environmental impacts, caused by the solid residues generation, are an often quoted concern nowadays. Some of these residues, which are originated from different human activities, can be fully reused, reducing the effects of the poor waste management on the environment. During the salt production process, the first formed crystals are discarded as industrial waste. This is mainly made of gypsum that is a calcium sulfate dihydrate (CaSO4.2H2O). The gypsum in question may go through a calcination process due to the plaster (CaSO4.0,5H2O) production and then the application on the cement industry. Considering the necessity of development and application for these industrial wastes, this paper aims to analyze the plaster, called Salgesso, from the gypsum that was generated during the salt production, and its use viability on the civil construction industry in order to create environmental and economical benefits. For characterization, the following experiments were performed: X-ray Fluorescence (XRF), X-ray Diffraction (XRD), thermal analysis (TG/DTG) and Scanning Electron Microscopy (SEM) with EDS. The following tests were also performed to obtain the mechanical characteristics: Thinness Modulus, Unit Mass, Setting Time and Compressive Resistance. Three commercial plasters used on civil construction were taken as references. All of these tests were performed according to the current standards. It was noticed that although there were some conflicting findings between the salt and commercial plasters in all of the studied properties, the Salgesso has its values within the standard limits. However, there is the possibility to improve them by doing a more effective calcination process. Three commercial plasters, used in construction, were used as reference material. All tests were performed according to standards in force. It was observed that although some tests present conflicting findings between the salt and gypsum plasters commercial properties in all of the studied Salgesso have values within the limits imposed by the standard, but can be improved simply by calcination process more effective

Adição de geomanta e tecido não tecido de polipropileno em cimentos geopoliméricos de pega rápida

Geopolymers are cementing materials that depict a number of advantages compared to Portland cement. Contrary to the latter, geopolymers are synthesized at room temperature, thus significantly reducing the emission of CO2 to the atmosphere. Moreover, the composition and synthesis reactions can be tailored to adjust the setting time of the material as well as its compressive mechanical strength. It is then possible to produce geopolymeric cements with short setting times and high compressive strength, although relatively brittle. The objective of the present study was to produce and characterize composite materials by reinforcing fastsetting geopolymeric matrixes with polypropylene geosynthetics (geomats and geotextiles) in an attempt to improve the toughness and tensile strength of the cementing material. Geosynthetics have been increasingly used to reinforce engineering structures, providing higher strength and better toughness. In particular, polypropylene nonwoven and geomats depict other attractive properties such as low density, durability, impact absorption and resistance to abrasion. Fast-setting geopolymers were then synthesized and reinforced with polypropylene nonwoven and geomats. The mechanical strength of the materials, reinforced or not, was characterized. The results showed that relatively short setting times and adequate flowing behavior were achieved by adjusting the composition of the geopolymer. In addition, it is possible to improve the fracture resistance of geopolymeric cements by adding polypropylene geosynthetics. The best results were achieved by reinforcing geopolymer with polypropylene TNT

Otimização do tempo e temperatura no processamento da gipsita oriunda dos cristalizadores da produção de sal para obter gesso de uso na construção civil

During the process of the salt production, the first the salt crystals formed are disposed of as industrial waste. This waste is formed basically by gypsum, composed of calcium sulfate dihydrate (CaSO4.2H2O), known as carago cru or malacacheta . After be submitted the process of calcination to produce gypsum (CaSO4.0,5H2O), can be made possible its application in cement industry. This work aims to optimize the time and temperature for the process of calcination of the gypsum (carago) for get beta plaster according to the specifications of the norms of civil construction. The experiments involved the chemical and mineralogical characterization of the gypsum (carago) from the crystallizers, and of the plaster that is produced in the salt industry located in Mossoró, through the following techniques: x-ray diffraction (XRD), x-ray fluorescence (FRX), thermogravimetric analysis (TG/DTG) and scanning electron microscopy (SEM) with EDS. For optimization of time and temperature of the process of calcination was used the planning three factorial with levels with response surfaces of compressive mechanical tests and setting time, according norms NBR-13207: Plasters for civil construction and x-ray diffraction of plasters (carago) beta obtained in calcination. The STATISTICA software 7.0 was used for the calculations to relate the experimental data for a statistical model. The process for optimization of calcination of gypsum (carago) occurred in the temperature range from 120° C to 160° C and the time in the range of 90 to 210 minutes in the oven at atmospheric pressure, it was found that with the increase of values of temperature of 160° C and time calcination of 210 minutes to get the results of tests of resistance to compression with values above 10 MPa which conform to the standard required (> 8.40) and that the X-ray diffractograms the predominance of the phase of hemidrato beta, getting a beta plaster of good quality and which is in accordance with the norms in force, giving a by-product of the salt industry employability in civil construction