An experimental evaluation of prediction models for the mechanical behavior of unreinforced, lime-mortar masonry under compression

This paper contributes to the understanding of lime-mortar masonry strength and deformation (which determine durability and allowable stresses/stiffness in design codes) by measuring the mechanical properties of brick bound with lime and lime-cement mortars. Based on the regression analysis of experimental results, models to estimate lime-mortar masonry compressive strength are proposed (less accurate for hydrated lime (CL90s) masonry due to the disparity between mortar and brick strengths). Also, three relationships between masonry elastic modulus and its compressive strength are proposed for cement-lime; hydraulic lime (NHL3.5 and 5); and hydrated/feebly hydraulic lime masonries respectively.

Disagreement between the experimental results and former mathematical prediction models (proposed primarily for cement masonry) is caused by a lack of provision for the significant deformation of lime masonry and the relative changes in strength and stiffness between mortar and brick over time (at 6 months and 1 year, the NHL 3.5 and 5 mortars are often stronger than the brick). Eurocode 6 provided the best predictions for the compressive strength of lime and cement-lime masonry based on the strength of their components. All models vastly overestimated the strength of CL90s masonry at 28 days however, Eurocode 6 became an accurate predictor after 6 months, when the mortar had acquired most of its final strength and stiffness.

The experimental results agreed with former stress-strain curves. It was evidenced that mortar strongly impacts masonry deformation, and that the masonry stress/strain relationship becomes increasingly non-linear as mortar strength lowers. It was also noted that, the influence of masonry stiffness on its compressive strength becomes smaller as the mortar hydraulicity increases.

Design of experiments applied to the mix design process of polymer mortar materials modified with GFRP recyclates

In this work, the effect of incorporation of recycled glass fibre reinforced plastics (GFRP) waste materials, obtained by means of shredding and milling processes, on mechanical behavior of polyester polymer mortar (PM) materials was assessed. For this purpose, different contents of GFRP recyclates (between 4% up to 12% in mass), were incorporated into polyester PM materials as sand aggregates and filler replacements. The effect of silane coupling agent addition to resin binder was also evaluated. Applied waste material was proceeding from the shredding of the leftovers resultant from the cutting and assembly processes of GFRP pultrusion profiles. Currently, these leftovers, jointly with unfinished products and scrap resulting from pultrusion manufacturing process, are landfilled, with supplementary added costs. Thus, besides the evident environmental benefits, a viable and feasible solution for these wastes would also conduct to significant economic advantages. Design of experiments and data treatment were accomplish by means of full factorial design approach and analysis of variance ANOVA. Experimental results were promising toward the recyclability of GFRP waste materials as aggregates and reinforcement for PM materials, with significant improvements on mechanical properties with regard to non-modified formulations.

Measuring CO2 emissions induced by online and brick-and-mortar retailing

We develop a method for empirically measuring the difference in carbon footprint between traditional and online retailing (“e-tailing”) from entry point to a geographical area to consumer residence. The method only requires data on the locations of brick-and-mortar stores, online delivery points, and residences of the region’s population, and on the goods transportation networks in the studied region. Such data are readily available in most countries, so the method is not country or region specific. The method has been evaluated using data from the Dalecarlia region in Sweden, and is shown to be robust to all assumptions made. In our empirical example, the results indicate that the average distance from consumer residence to a brick-and-mortar retailer is 48.54 km in the studied region, while the average distance to an online delivery point is 6.7 km. The results also indicate that e-tailing increases the average distance traveled from the regional entry point to the delivery point from 47.15 km for a brick-and-mortar store to 122.75 km for the online delivery points. However, as professional carriers transport the products in bulk to stores or online delivery points, which is more efficient than consumers’ transporting the products to their residences, the results indicate that consumers switching from traditional to e-tailing on average reduce their CO2 footprints by 84% when buying standard consumer electronics products. 

Measuring CO2 emissions induced by online and brick-and-mortar retailing

We develop a method for empirically measuring the difference in carbon footprint between traditional and online retailing (“e-tailing”) from entry point to a geographical area to consumer residence. The method only requires data on the locations of brick-and-mortar stores, online delivery points, and residences of the region’s population, and on the goods transportation networks in the studied region. Such data are readily available in most countries, so the method is not country or region specific. The method has been evaluated using data from the Dalecarlia region in Sweden, and is shown to be robust to all assumptions made. In our empirical example, the results indicate that the average distance from consumer residence to a brick-and-mortar retailer is 48.54 km in the studied region, while the average distance to an online delivery point is 6.7 km. The results also indicate that e-tailing increases the average distance traveled from the regional entry point to the delivery point from 47.15 km for a brick-and-mortar store to 122.75 km for the online delivery points. However, as professional carriers transport the products in bulk to stores or online delivery points, which is more efficient than consumers’ transporting the products to their residences, the results indicate that consumers switching from traditional to e-tailing on average reduce their CO2 footprints by 84% when buying standard consumer electronics products. 

Dynamic mechanical properties for polyurethane elastomers applied in elastomeric mortar

Dynamic mechanical properties of a polyurethane (PU) elastomer and a mortar processed with the same elastomer (modified polytetramethylene ether glycol (PTMEG)) were studied. The results obtained showed that the liquid aromatic amine ETHACURE (R) 300, used as cure agent, can be used to substitute the aromatic amine MOCA (R), which is usually used as cure agent in high performance elastomers. The resulting mortar produced with ETHACURE (R) 300 presents similar dynamic-mechanical thermal properties when compared with MOCA (R). However, dynamic-mechanical thermal analysis studies showed that the mortar developed with ETHACURE (R) 300 presents some advantages such as the low values of tan d, indicating a good capacity of recovery of the strain after retreating an applied force. (c) 2012 Wiley Periodicals, Inc. J Appl Polym Sci, 2012

Nationalization of the carbonaceous mortar for injection in the CNS's blast furnaces hearths

The consumption of the carbonaceous mortar for injection in the CSN's blast furnaces hearth has increased in the last years, as a function of the modern situation of the blast furnaces com paign. Allied to the growing consumption background, the devaluation of the Brazilian currency stroke hardly the importation costs of this product.

Mortar added by tyre rubber residues: Characterisation in fresh and hardened state

Due to the progressive increase of vehicles, the number of used tires is globally one of the serious environmental problems faced now. Therefore, several researches have being developed for its reuse. The use of tires' rubber in the concrete is a possible form of its application, aiming at the recycling of this material and the improvement of certain properties, as tenacity, impact resistance, thermal and acoustic isolation. This article presents conclusions that several researchers obtained using the rubberized concrete. Thus there were researched several works enclosing the period of 1993 to 2003, presenting then the results of some characteristics of this concrete such as: physical properties in fresh and hardened state, mechanical properties and properties that remit the durability. The bibliographical revision has as objective to subsidize future researches that can contribute to improve the use of this concrete in civil construction.

Properties of Mortar Using Cubes, Prism Halves, and Cylinder Specimens

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Durability of mixed mortar lining containing Dregs-Grits

The improper disposal of industrial waste and exploitation of natural resources has resulted in the scarcity of river sand and environmental degradation, such as river erosions and pollution. This study aimed to assess the durability of mixed mortar lining walls and ceilings, containing 0 (default), 10 and 20% of dregs-grits compounds-waste of the pulp industry-in substitution with river sand. This was done with tests that simulated both natural and artificial conditions: Direct solar incidence (testing ultraviolet radiation), attack by spraying solution (salt spray test), natural warming of the walls and ceilings incidence by indirect solar (thermal degradation) and residential fires (thermogravimetric test), in compliance with both national and/or international standards. The grout containing dregs-grits compounds showed similarity to standard (0%) for testing thermal degradability, thermogravimetric and ultraviolet radiation, but shows significantly less durability when exposed to salty environments.

Cement-base bearing pads mortar for connections in the precast concrete: study of surface roughness

Bearing pads are used in precast concrete connections to avoid concentrated stresses in the contact area between the precast elements. In the present research, the bearing pads are Portland cement mortar with styrene-butadiene latex (SB), lightweight aggregate (expanded vermiculite-term) and short fibers (polypropylene, glass and PVA), in order to obtain a material with low modulus of elasticity and high tenacity, compared with normal Portland cement mortar. The objective of this paper is to analyze the influence of surface roughness on the pads and test other types of polypropylene fibers. Tests were carried out to characterize the composite and test on bearing pads. Characterization tests show compressive strength of 41MPa and modulus of elasticity of 12.8GPa. The bearing pads tests present 30% reduction of stiffness in relation to a reference mortar. The bearing pads with roughness on both sides present a reduction up to 30% in stiffness and an increase in accumulated deformation of more than 120%, regarding bearing pads with both sides smooth.

Expansion of mortar bars in the presence of potassium acetate deicer

Carboxylate-based deicing and anti-icing chemicals became widely used in the mid 1990s, replacing more environmentally burdensome chemicals. Within a few years of their adoption, distress of portland cement concrete runways was reported by a few airports using the new chemicals. Distress manifested characteristics identical to that of alkali silica reactivity (ASR), but onset occurred early in the pavement’s operating life and with pavements thought to contain innocuous aggregate. The carboxylate-based deicing chemicals were suspected of exacerbating ASR-like expansion. Innocuous, moderately, and highly reactive aggregates were tested using modified ASTM C1260 and ASTM C1567 procedures with soak solutions containing deicer solutions and sodium hydroxide or potassium hydroxide. ASR-like expansion is exacerbated in the presence of potassium acetate. The expansion rate produced by a given aggregate is also a function of the alkali hydroxide used. Petrographic analyses were performed on thin sections prepared from mortar bars used in the experiments. Expansion occurred via two mechanisms; rupture of aggregate grains and expansion of paste.

Development of corrosion of steel bars embedded in mortar made with slag from secondary metallurgy

The aim of this work is to study the evolution of the corrosion rate of reinforcements embedded in mortar specimens that have been partly or fully replaced by the sand ladle furnace white slag. Prisms are manufactured mortar 6cm x 8cm x 2cm in which are embedded reinforcing steel bars of 6mm diameter B500SD. At the time of mixing were added varying amounts of chloride ion content by weight of cement (0%, 0.4%, 0.8%, 1.2%, 2%). The specimens were made totally or partially replacing the white slag, getting four different mixes depending on the degree of substitution. After curing the specimens for 28 days in moist chambers proceeded to dry up naturally. Here are gradually dampened by its conservation in a moist chamber, periodically measuring the corrosion rate of the bars using the technique of polarization curve. The results, in terms of corrosion current and corrosion potential, were compared with those obtained on standard samples, without replacement by slag aggregate. The analysis of results allows us to know, depending on the type of mortar used, the chloride threshold with the depassivation produced steel and the corrosion rates achieved in steels in the active state in terms of mortar moisture, obtained from qualitatively using gravimetric techniques. The results achieved to date support the conclusion that no significant differences in the behavior against corrosion induced by chloride ions, between the steel bars embedded in standard samples and the steel bars embedded in samples including with aggregates from slag. Both the chloride threshold resulting in the depassivation steel as the corrosion rate reached through the bars in an active state are very similar in both types of mortars when they have the same moisture content.