On the investigation of singular stress field around radial cracks in annulii subjected to diametrical tension

Results of photoelastic investigation conducted on annulii containing a radial crack at inner edge and subjected to diametrical tension are reported. The cracks are oriented at 90°, 60° and 45° to the loading direction. The Stress-Intensity Factors (SIFs) were determined by analysing the crack-tip stress fields. Smith and Smith's method [Engng Fracture Mech.4, 357–366 (1972)] and a modified method developed earlier by the authors (to be published) were adopted in the evaluation of SIFs.

Mixed-mode stress intensity factors for arbitrarily oriented cracks in cylindrical shells under axial pull and torsion

Results of photoelastic investigations conducted on cylindrical tubes (made of Araldite material) containing cracks oriented at 0°, 30°, 45°, 60° and 90° to the axis of the tube and subjected to axial and torsional loads are reported. The stress-intensity factors (SIFs) were determined by analysing the crack-tip stress fields. Smith and Smith's method [Engng Fracture Mech.4, 357–366 (1972)] and a new method developed by the authors by modifying Rakesh et al.'s method [Proc. 26th Congress of ISTAM, India (1981)] were employed to evaluate the mixed-mode SIFs.

Studies of moisture induced crosslinking in a novel vinyl ether maleic anhydride copolymer

A novel vinyl ether, 2,2-dimethyl-4-vinyioxymethyl-1,3-dioxol (DMVMD), that has a dimethyl ketal protected vicinal diol functionality was synthesizied from readily available starting materials, such as glycerol, acetone and acetylene. Copolymerisation of DMVMD with maleic anhydride (MAH) in various molar ratios was carried out using a free radical initiator. The composition of the copolymer was established by conductometric titration, and was found to be 1:1 irrespective of the monomer feed composition thus establishing its alternating nature. The copolymer formed clear free standing films upon solvent casting which became insoluble upon prolonged exposure to ambeint atmosphere. The insolubility is ascribed to moisture induced crosslinking. A plausible mechanism for the crosslinking involves the hydrolysis of some of the anhydride groups, followed by acid catalysed deketalization, and then by the reaction of the alcoholic groups, thus generated, with the residual anhydride to give ester crosslinks. This hypothesis was confirmed both by model reactions and insitu FT-IR studies.

Development of design charts for stress intensity factors at tips of multi-site cracks in unstiffened curved panels

Multi-site damage need to be addressed and evaluated in order to assess the integrity of aging aircraft structures. One of the problems recognized in the recent times is the effect of interaction between two or more cracks in the close neighborhood in such structures. The present paper deals with such a problem and presents numerical estimates of stress intensity factors at a crack tip in an un-stiffened curved panel with a secondary crack in the vicinity of a primary crack. The results are presented in the form of design charts. These results should be useful in evaluation in the damage tolerance evaluation of aircraft structures with multi-site damage. (C) 2014 Elsevier Ltd. All rights reserved.

Laboratory study on cracks in saturated sands

It has been reported([1]) that when a loosely packed column of saturated sand in a vertical cylindrical container is shock loaded axially by dropping to the floor, large horizontal cracks initiate, grow and eventually fade away in the sand as it settles under gravity. This paper shows that a similar phenomenon can also be observed when shock loading is replaced by forcing water to percolate upward through the sand column. It is believed that our result sheds further light on the physics of formation of these cracks.

Simulations and Experiments of Stochastic Characteristics for Collective Short Fatigue Cracks in Steels

Stochastic characteristics prevail in the process of short fatigue crack progression. This paper presents a method taking into account the balance of crack number density to describe the stochastic behaviour of short crack collective evolution. The results from the simulation illustrate the stochastic development of short cracks. The experiments on two types of steels show the random distribution for collective short cracks with the number of cracks and the maximum crack length as a function of different locations on specimen surface. The experiments also give the variation of total number of short cracks with fatigue cycles. The test results are consistent with numerical simulations.

Formation Mechanism of Cracks in Saturated Sand

The formation mechanism of “water film” (or crack) in saturated sand is analyzed theoretically and numerically. The theoretical analysis shows that there will be no stable “water film” in the saturated sand if the strength of the skeleton is zero and no positions are choked. It is shown by numerical simulation that stable water films initiate and grow if the choking state keeps unchanged once the fluid velocities decrease to zero in the liquefied sand column. The developments of “water film” based on the model presented in this paper are compared with experimental results.

Interactions of Penny-Shaped Cracks in Three-Dimensional Solids

The interaction of arbitrarily distributed penny-shaped cracks in three-dimensional solids is analyzed in this paper. Using oblate spheroidal coordinates and displacement functions, an analytic method is developed in which the opening and the sliding displacements on each crack surface are taken as the basic unknown functions. The basic unknown functions can be expanded in series of Legendre polynomials with unknown coefficients. Based on superposition technique, a set of governing equations for the unknown coefficients are formulated from the traction free conditions on each crack surface. The boundary collocation procedure and the average method for crack-surface tractions are used for solving the governing equations. The solution can be obtained for quite closely located cracks. Numerical examples are given for several crack problems. By comparing the present results with other existing results, one can conclude that the present method provides a direct and efficient approach to deal with three-dimensional solids containing multiple cracks.

On the mechanism of the formation of horizontal cracks in a vertical column of saturated sand

Extended horizontal cracks have! been observed experimentally in a vertical column of saturated sand when a flow of water is forced to percolate upward through it. This paper provides a theory for this phenomenon. It will be shown that the presence of inhomogeneity in permeability along the length of the column is essential for such cracks to develop. It will also be shown that small initial inhomogeneity may be magnified through the transport of the finer component of the sand by percolation. Under certain conditions liquefaction takes place at a section of the sand column causing a crack to initiate and grow there. This theory is found to be in good qualitative agreement with the experimental findings.

Interacting multiple cracks in piezoelectric materials

In this paper, a method is presented to calculate the plane electro-elastic fields in piezoelectric materials with multiple cracks. The cracks may be distributed randomly in locations, orientations and sizes. In the method, each crack is treated as a continuous distributed dislocations with the density function to be determined according to the conditions of external loads and crack surfaces. Some numerical examples are given to show the interacting effect among multiple cracks.

On the Formation of Periodic Segmentation Cracks in a Coating Plated on a Substrate with Periodic Subsurface Inclusions

The mechanism of the formation of periodic segmentation cracks of a coating plated on a substrate with periodic subsurface inclusions (PSI) is investigated. The internal stress in coating and subsequently the strain energy release rate (SERR) of the segmentation cracks are computed with finite element method (FEM). And the effect of the geometrical parameters of the PSI is studied. The results indicate that the ratio of the width of the inclusion to the period of the repeated structure has an optimum value, at which the maximum internal tensile stress and SERR arise. On the other hand, the ratio of the max-thickness of the inclusion to the thickness of the coating has a threshold value, above which the further increase of this ratio should seldom influence the internal stress or the SERR.

Orientation preference and fractal character of short fatigue cracks in a weld metal

Short fatigue crack behaviour in a weld metal has been further investigated. The Schmid factor and the fractal dimension of short cracks on iso-stress specimens subjected to reversed bending have been determined and then applied to account for the distribution and orientation characteristics of short fatigue cracks. The result indicates that the orientation preference of short cracks is attributed to the large values of Schmid factor at relevant grains. The Schmid factors of most slip systems, which produced short cracks, are less than or equal to 0.4. Crack length measurements reveal that short crack path, compared to that of long crack, possesses a more stable and relatively larger value of fractal dimension. This is regarded as one of the typical features of short cracks.

Initiation and propagation of short fatigue cracks in a weld metal

Fatigue tests were performed using a purpose designed triangular shaped specimen to investigate the initiation and propagation of short fatigue cracks in a weld metal. It was observed that short fatigue cracks evolved from slip bands and were predominantly within ferrite grains. As the test progressed, the short crack density increased with minor changes in crack length. The growth of short cracks, in the early stage resulted mainly from coalescence with other existing cracks. The mechanism of short crack behaviour is discussed.

Cracks in saturated sand

The formation mechanism of water film (or crack) in saturated sand is analyzed numerically It is shown that there will be no stable "water film" in the saturated sand even if the strength of the skeleton is zero and no positions are choked. The stable water films initiate and grow if the choking state keeps unchangeable once the fluid velocities of one position decreases to zero in a liquefied sand column. A simplified method for evaluating the thickness of water film is presented according to a solidification wave theory. The theoretical results obtained by the simplified method are compared with the numerical results and the experimental results of Kokusho.