The tensile fracture of mild steel

The fibrous and cleavage tensile fracture of an annealed mild steel was investigated. Round tensile specimens of two geometries, one straight and one with a circumferential notch, were pulled at temperatures between room temperature and liquid nitrogen temperature. Tensile fractures occurred at average strains from 0.02 to 0.87. The mechanism of fibrous fracture at room temperature was investigated metallographically. The stress-strain values at which fibrous and cleavage fractures are initiated were determined.

Many fine microcracks, which are associated with pearlite colonies and inclusion stringers, develop prior to fibrous fracture. The macrofracture, which leads to final separation of the tensile specimen, is initiated by the propagation of a microcrack beyond the microstructural feature with which it is associated. Thus, the fibrous fracture of mild steel does not develop by the gradual growth and coalescence of voids that are large enough to be visible in the optical microscope. When the microcracks begin to open and propagate, final fracture quickly follows. Axial cracks are a prominent feature of the macrofracture that forms in the interior of the specimen immediately before final fracture.

The Bridgman distribution of stresses is not valid in a notched tensile specimen. Fibrous and cleavage fractures occur at approximately the same value of maximum tensile stress. When the maximum tensile stress that is necessary for cleavage fracture is plotted against the corresponding maximum tensile strain, the result is an unique locus.

Effect of particle concentration on erosion rate of mild steel bends in a pneumatic conveyor

Particle concentration is known as a main factor that affects erosion rate of pipe bends in pneumatic conveyors. With consideration of different bend radii, the effect of particle concentration on weight loss of mild steel bends has been investigated in an industrial scale test rig. Experimental results show that there was a significant reduction of the specific erosion rate for high particle concentrations. This reduction was considered to be as a result of the shielding effect during the particle impacts. An empirical model is given. Also a theoretical study of scaling on the shielding effect, and comparisons with some existing models, are presented. It is found that the reduction in specific erosion rate (relative to particle concentration) has a stronger relationship in conveying pipelines than has been found in the erosion tester. © 2004 Elsevier B.V. All rights reserved.

Long-term anticorrosion behaviour of polyaniline on mild steel

Anticorrosion performances of polyaniline emeraldine base/epoxy resin (EB/ER) coating on mild steel in 3.5% NaCl solutions of various pH values were investigated by electrochemical impedance spectroscopy (EIS) for 150 days. In neutral solution (pH 6.1), EB/ER coating offered very efficient corrosion protection with respect to pure ER coating, especially when EB content was 5-10%. The impedance at 0.1 Hz of the coating increased in the first 1-40 immersion days and then remained constant above 10(9) Omega cm(2) until 150 days, which in combination with the observation of a Fe2O3/Fe3O4 passive film formed on steel confirmed that the protection of EB was mainly anodic. In acidic or basic solution (pH 1 or 13), EB/ER coating also performed much better than pure ER coating. However, these media weakened the corrosion resistance due to breakdown of the passive film or deterioration of the ER binder.

Polyaniline for corrosion prevention of mild steel coupled with copper

Polyaniline emeraldine base/epoxy resin (EB/ER) coating was investigated for corrosion protection of mild steel coupled with copper in 3.5% NaCl solution. EB/ER coating with 5-10 wt% EB had long-term corrosion resistance on both uncoupled steel and copper due to the passivation effect of EB on the metal surfaces. During the 150 immersion days, the impedance at 0.1 Hz for the coating increased in the first 1-40 days and subsequently remained constant above 10(9) Omega cm(2), whereas that for pure ER coating fell below 10(6) Omega cm(2) after only 30 or 40 days. Immersion tests on coated steel-copper galvanic couple showed that EB/ER coating offered 100 times more protection than ER coating against steel dissolution and coating delamination on copper, which was mainly attributed to the passive metal oxide films formed by EB blocking both the anodic and cathodic reactions. Salt spray tests showed that 100 mu m EB/ER coating protected steel-copper couple for at least 2000 h.

Adsorption and Corrosion Inhibition Behavior of Mild Steel by One Derivative of Benzoic-Triazole in Acidic Solution

A newly synthesized benzoic-triazole derivative 3,5-dimethylbenzoic acid [1,2,4]triazol-l-ylmethyl ester (DBT) was investigated as a corrosion inhibitor of mild steel in 1 M HCl solution using weight loss measurements, potentiodynamic polarization, SEM, and EIS methods. The results revealed that DBT was an excellent inhibitor, and the inhibition efficiencies obtained from weight loss and electrochemical experiments were in good agreement. Using the potentiodynamic polarization technique, the inhibitor was proved to have a mixed-type character for mild steel by suppressing both anodic and cathodic reactions on the metal surface. The number of water molecules (X) replaced by a molecule of organic adsorbate was determined from the Flory-Huggins, Dhar-Flory-Huggins, and Bockris-Swinkels substitutional adsorption isotherms applied to the data obtained from the gravimetric experiments performed on a mild steel specimen in 1 M HCl solution at 298 K.

Inhibition Effect of 2,3,5-Triphenyl-2H-tetrazolium Chloride and 2,4,6-Tri(2-pyridyl)-s-triazine on the Corrosion of Mild Steel in 1 mol/L HCl and Mechanism Study (II)

The inhibitory effect of 2,3,5-triphenyl-2H-tetrazolium chloride (TTC) and 2,4,6-tri(2-pyridyl)-s-triazine (TPT) molecules on the corrosion of mild steel in 1 mol/L HCl and microcosmic inhibitory mechanism were investigated by X-ray photoelectron spectroscopy and ellipsometry. XPS results showed that C Is and N Is peaks of TTC, C Is and N Is peaks of TPT and their integral areas were obtained, which suggested the layer of the inhibitors (TTC or TPT) should have effectively protected the mild steel surface from the corrosion; and the depression from the inhibitors for the corrosion of mild steel surface was studied using ellipsometry combined with potentiodynamic polarization and the phasic difference was gained, which displayed the inhibitory coverage of the inhibitors formed.

Corrosion inhibition of mild steel in acidic solution by some oxo-triazole derivatives

The oxo-triazole derivative (DTP) was synthesized and its inhibiting action on the corrosion of mild steel in sulphuric acid was investigated by means of weight loss, potentiodynamic polarization, EIS and SEM. The results revealed that DTP was an excellent inhibitor and the inhibition efficiencies obtained from weight loss experiment and electrochemical experiment were in good agreement. Potentiodynamic polarization studies clearly revealed that DTP acted essentially as the mixed-type inhibitor. Thermodynamic and kinetic parameters were obtained from weight loss of the different experimental temperatures, which suggested that at different temperatures (298-333 K) the adsorption of DTP on metal surface obeyed Langmuir adsorption isotherm model. (C) 2009 Elsevier Ltd. All rights reserved.

The effect of some triazole derivatives as inhibitors for the corrosion of mild steel in 1 M hydrochloric acid

Corrosion inhibition by some new triazole derivatives on mild steel in 1 M hydrochloric acid solutions has been investigated by weight loss test, electrochemical measurement, scanning electronic microscope analysis and quantum chemical calculations. The results indicate that these compounds act as mixed-type inhibitors retarding the anodic and cathodic corrosion reactions and do not change the mechanism of either hydrogen evolution reaction or mild steel dissolution. The studied compounds following the Langmuir adsorption isotherm, and the thermodynamic parameters were determined and discussed. The effect of molecular structure on the inhibition efficiency has been investigated by ab initio quantum chemical calculations. The electronic properties such as highest occupied molecular orbital (HOMO), lowest unoccupied molecular orbital (LUMO) energy levels, energy gap (LUMO-HOMO), dipole moment and molecular orbital densities were calculated. (C) 2009 Published by Elsevier B.V.

Berberine as a natural source inhibitor for mild steel in 1 M H2SO4

Berberine was abstracted from coptis chinensis and its inhibition efficiency on corrosion of mild steel in 1 M H2SO4 was investigated through weight loss experiment, electrochemical techniques and scanning electronic microscope (SEM) with energy disperse spectrometer (EDS). The weight loss results showed that berbefine is an excellent corrosion inhibitor for mild steel immersed in 1M H2SO4. Potentiodynamic curves suggested that berbefine suppressed both cathodic and anodic processes for its concentrations higher than 1.0 x 10(-4) M and mainly cathodic reaction was suppressed for lower concentrations. The Nyquist diagrams of impedance for mild steel in 1 M H2SO4 containing berbefine with different concentrations showed one capacitive loop, and the polarization resistance increased with the inhibitor concentration rising. A good fit to Flory-Huggins isotherm was obtained between surface coverage degree and inhibitor concentration. The surface morphology and EDS analysis for mild steel specimens in sulfuric acid in the absence and presence of the inhibitor also proved the results obtained by the weight loss and electrochemical experiments. The correlation of inhibition effect and molecular structure of berberine was then discussed by quantum chemistry study. (c) 2005 Elsevier B.V. All rights reserved.

Electrochemical, SEM/EDS and quantum chemical study of phthalocyanines as corrosion inhibitors for mild steel in 1 mol/l HCl

The inhibition effect of metal-free phthalocyanine (H2Pc), copper phthalocyanine (CuPc) and copper phthalocyanine tetrasulfuric tetrasodium salt (CuPc center dot S(4)center dot Na-4) on mild steel in I mol/l HCl in the concentration range of 1.0 X 10(-5) to 1.0 X 10(-3) mol/l was investigated by electrochemical test, scanning electron microscope with energy dispersive spectrometer (SEM/EDS) and quantum chemical method. The potentiodynamic polarization curves of mild steel in hydrochloric acid containing these compounds showed both cathodic and anodic processes of steel corrosion were suppressed, and the Nyquist plots of impedance expressed mainly as a capacitive loop with different compounds and concentrations. For all these phthalocyanines, the inhibition efficiency increased with the increase in inhibitor concentration, while the inhibition efficiencies for these three phthalocyanines with the same concentration decreased in the order Of CuPc center dot S(4)center dot Na-4 > CuPc > H2Pc according to the electrochemical measurement results. The SEM/EDS analysis indicated that there are more lightly corroded and oxidative steel surface for the specimens after immersion in acid solution containing 1.0 x 10(-3) mol/l phthalocyanines than that in blank. The quantum chemical calculation results showed that the inhibition efficiency of these phthalocyanines increased with decrease in molecule's LUMO energy, which was different from the micro-cyclic compounds. (c) 2005 Elsevier B.V. All rights reserved.

Corrosion of mild steel in different granularity seabed sediment saturated with seawater

In order to investigate the corrosion of pipeline materials in Seabed Sediment (SBS) environment, weight-loss and electrochemical measurements in saturated sand and mud cells with seawater were performed for a simulation. The used electrochemical measurements included linear polarization resistance (LPR) and potentiodynamic scanning measurement. It was showed that the corrosion rate of mild steel in the present condition was lower than the corrosion rate of other marine environment corrosion zones of it; that the granularity of SBS could affect the corrosion behavior greatly; that with increasing grain size of SBS, the corrosion rate increased. Integrated over the results of the weight loss and polarization curves, the oxygen diffusion (oxygen as a depolarizant agent) mechanism was proposed and discussed.