Role of lattice defects and crystallite morphology in the UV and visible-light-induced photo-catalytic properties of combustion-prepared TiO2

The physico-chemical, photo-physical and micro-structural properties responsible for the strikingly different photocatalytic behavior of combustion-prepared TiO2 (c.TiO2) and Degussa P25 (d.TiO2) samples are elucidated in this study. Electron microscopy and selected area electron diffraction micrographs revealed that the two samples exhibited different morphologies. The grains of c.TiO2 were spherical and comprised of 5-6 nm size primary particle. On the other hand, d.TiO2 consisted of large (0.5-3.0 mu m) size and irregular shape aggregates having primary particles of 15-40 nm cross-sectional diameter. The ESR study revealed that the presence of certain defect states in c.TiO2 helped in stabilization of O-. and Ti3+-OH type species during room-temperature UV-irradiation. No such paramagnetic species were however formed over d.TiO2 under similar conditions. C1s and Ti 2p XPS spectra provide evidence for the presence of some lattice vacancies in c.TiO2 and also for the bulk Ti4+ -> Ti3+ conversion during its UV-irradiation. Compared to d.TiO2, c.TiO2 displayed considerably higher activity for discoloration of methyl orange but very poor activity for splitting of water, both under UV and visible light radiations. This is attributed to enhanced surface adsorption of dye molecules over c.TiO2, because of its textural features and also the presence of photo-active ion-radicals. On the other hand, the poor activity of c.TiO2 for water splitting is related to certain defect-induced inter-band charge trapping states in the close vicinity of valence and conduction bands of c.TiO2, as revealed by thermoluminescence spectroscopy. Further, the dispersion of nanosize gold particles gave rise to augmented activity of both the catalysts, particularly for water splitting. This is explained by the promotional role of Au-0 or Au-0/TiO2 interfacial sites in the adsorption and charge-adsorbate interaction processes. (C) 2011 Elsevier B.V. All rights reserved.

Synthesis and photocatalytic performance of quasi-fibrous ZnO

The combustion of oxidizer zinc nitrate and fuel oxalic acid results in quasi-fibrous zinc oxide. The processing parameters including oxidizer to fuel ratio, time and temperature were optimized for the resultant crystal structure and morphology. Pure hexagonal phase formation does not depend on the fuel ratio, but a stoichiometric ratio of oxidizer to fuel at 450 degrees C and 30 min results in highly crystalline ZnO with 3 mu m length and 0.5 mu m width. This quasi-fiber originates from partial fusion of near spherical, similar to 60 nm particles during the rapid rate of reaction in the combustion process. Transmission electron microscopic analysis confirms the anisotropic primary particle orientation and pore distribution within the developed quasi-fibrous particles. The degradation of methyl orange was assessed by degrading the dye in the presence of the synthesized ZnO (2.95 eV) under both UV and visible light. Quasi-fibrous zinc oxide exhibits effective photocatalytic efficiency under visible light irradiation.

Facile synthesis of PbWO4: Applications in photoluminescence and photocatalytic degradation of organic dyes under visible light

Stolzite polymorph of PbWO4 catalyst was prepared by the facile room temperature precipitation method. Structural parameters were refined by the Rietveld analysis using powder X-ray data. PbWO4 was crystallized in the scheelite-type tetragonal structure with space group I4(1)/a (No. 88). Field emission scanning electron microscopy revealed leaf like morphology. Photoluminescence spectra exhibit broad blue emission (425 nm) under the excitation of 356 nm. The photocatalytic degradation of Methylene blue, Rhodamine B and Methyl orange dyes were measured under visible illumination. The 100% dye degradation was observed for MB and RhB dyes within 60 and 105 min. The rate constant was found to be in the decreasing order of MB > RhB > MO which followed the 1st order kinetic mechanism. Therefore, PbWO4 can be a potential candidate for blue component in white LEDs and also acts as a catalyst for the treatment of toxic and non-biodegradable organic pollutants in water. (C) 2014 Elsevier B.V. All rights reserved.

Degradação de corante por partículas de ferro zero suportadas em sílica

A água é um bem essencial a todos os seres vivos. Porém, o homem não tem dado o valor e atenção necessários para a preservação dessa riqueza. Por mais que o ser humano não faça a água desaparecer do planeta, ele tem contribuído e muito para o decréscimo de sua qualidade. Dentre as várias atividades antropogênicas, que tem contribuído para a poluição das águas, destaca-se a atividade industrial. A indústria têxtil, por exemplo, libera enormes volumes de dejetos, destacando-se os corantes, além deles prejudicarem a ocorrência de fotossíntese, apresentam elevada toxicidade ao meio marinho. Com isso, este trabalho visa estudar a degradação do corante Alaranjado de Metila via catálise heterogênea. Neste estudo, foram realizadas a preparação e a caracterização de partículas metálicas estabilizadas em sílica, sendo essas partículas com diferentes teores de ferro (50 %wt, 25 %wt e 5 %wt) aderido ao suporte. Após o preparo dos catalisadores realizou-se o estudo de sua eficiência frente a diferentes parâmetros como: quantidade de catalisador, temperatura e pH. Por meio dos testes realizados foi possível observar que a quantidade do catalisador influência a reação de redução do corante Alaranjado de Metila. Porém, quando se atinge o ponto de saturação, mesmo que se adicione mais catalisador não é possível aumentar a degradação. Através da variação da temperatura, observou-se que quanto maior a temperatura maior a degradação do corante. Isso pode ser explicado devido o aumento do número de colisões entre os sítios ativos do catalisador e as moléculas do corante. E por meio da variação de pH, concluiu-se que pHs ácidos permitem que a reação de redução do corante ocorra mais rápido e pHs elevados tornam a reação de degradação do corante mais lenta, porém ainda assim ocorrem de forma satisfatória. O catalisador pôde ser reutilizado por até 3 vezes, sem nenhum tratamento prévio. Os catalisadores a 50 %wt, assim como, a 25 %wt foram capazes de degradar o corante de forma eficiente, porém o catalisador a 5 %wt não se mostrou ser eficaz. Foram realizados testes sob radiação microondas e a reação de redução ocorreu de forma muito eficaz, apresentando 100% de degradação em apenas 2 minutos. Além disso, realizou-se o estudo cinético, onde segundo dados experimentais, as reações foram classificadas como sendo de primeira ordem

Enhanced photocatalytic activity of TiO2 nano-structured thin film with a silver hierarchical configuration

TiO2 sol-gels with various Ag/TiO2 molar ratios from 0 to 0.9% were used to fabricate silver-modified nano-structured TiO2 thin films using a layer-by-layer dip-coating (LLDC) technique. This technique allows obtaining TiO2 nano-structured thin films with a silver hierarchical configuration. The coating of pure TiO2 sol-gel and Ag-modified sol-gel was marked as T and A, respectively. According to the coating order and the nature of the TiO2 sol-gel, four types of the TiO2 thin films were constructed, and marked as AT (bottom layer was Ag modified, surface layer was pure TiO,), TA (bottom layer was pure TiO,, surface layer was Ag modified), TT (pure TiO, thin film) and AA (TiO, thin film was uniformly Ag modified). These thin films were characterized by means of linear sweep voltammetry (LSV), X-ray diffraction (XRD), scanning electron microscopy (SEM), electrochemical impedance spectroscopy and transient photocurrent (I-ph). LSV confirmed the existence of Ago state in the TiO, thin film. SEM and XRD experiments indicated that the sizes of the TiO,, nanoparticles of the resulting films were in the order of TT > AT > TA > AA, suggesting the gradient Ag distribution in the films. The SEM and XRD results also confirmed that Ag had an inhibition effect on the size growth of anatase nanoparticles. Photocatalytic activities of the resulting thin films were also evaluated in the photocatalytic degradation process of methyl orange. The preliminary results demonstrated the sequence of the photocatalytic activity of the resulting films was AT > TA > AA > TT. This suggested that the silver hierarchical configuration can be used to improve the photocatalytic activity of TiO2 thin film.

Effect of dopant concentration on photocatalytic activity of TiO2 film doped by Mn non-uniformly

The thin films of TiO2 doped by Mn non-uniformly were prepared by sol-gel method under process control. In our preceding study, we investigated in detail, the effect of doping mode on the photocatalytic activity of TiO2 films showing that Mn non-uniform doping can greatly enhance the activity. In this study we looked at the effect of doping concentration on the photocatalytic activity of the TiO2 films. In this paper, the thin films were characterized by UV-vis spectrophotometer and electrochemical workstation. The activity of the photocatalyst was also evaluated by photocatalytic degradation rate of aqueous methyl orange under UV radiation. The results illustrate that the TiO2 thin film doped by Mn non-uniformly at the optimal dopant concentration (0.7 at %) is of the highest activity, and on the contrary, the activity of those doped uniformly is decreased. As a comparison, in 80 min, the degradation rate of methyl orange is 62 %, 12 % and 34 % for Mn non-uniform doping film (0.7 at %), the uniform doping film (0.7 at %) and pure titanium dioxide film, respectively. We have seen that, for the doping and the pure TiO2 films, the stronger signals of open circuit potential and transient photocurrent, the better photocatalytic activity. We also discusse the effect of dopant concentration on the photocatalytic activity of the TiO2 films in terms of effective separation of the photon-generated carriers in the semiconductor. (C) Versita Warsaw and Springer-Verlag Berlin Heidelberg. All rights reserved.

A simple method to prepare titania nanomaterials of core-shell structure, hollow nanospheres and mesoporous nanoparticles

A simple method to prepare titania nanomaterials of core-shell structure, hollow nanospheres and mesoporous nanoparticles has been developed. The core-shell nanostructures with NH4Cl as core and TiO2 center dot xH(2)O-NH4Cl as shell were prepared in nonaqueous system by the deposition on the surface of the aggregated NH4Cl crystals, which could be transformed into mesoporous anatase nanoparticles or hollow nanospheres by calcination at 500A degrees C or extraction with methanol, respectively. The hierarchical mesoporous nanostructures benefited the photocatalytic activities of the resultant titania nanomaterials, demonstrated by the UV light photodegradation of Methyl Orange.

Development of a doped titania immobilised thin film multi tubular photoreactor

This paper describes a novel doped titania immobilised thin film multi tubular photoreactor which has been developed for use with liquid, vapour or gas phase media. In designing photocatalytic reactors measuring active surface area of photocatalyst within the unit is one of the critical design parameters. This dictate greatly limits the applicability of any semi-conductor photocatalyst in industrial applications, as a large surface area equates to a powder catalyst. This demonstration of a thin film coating, doped with a rare earth element, novel photoreactor design produces a photocatalytic degradation of a model pollutant (methyl orange) which displayed a comparable degradation achieved with P25 TiO2. The use of lanthanide doping is reported here in the titania sol gel as it is thought to increase the electron hole separation therefore widening the potential useful wavelengths within the electromagnetic spectrum. Increasing doping from 0.5% to 1.0% increased photocatalytic degradation by ∼17% under visible irradiation. A linear relationship has been seen between increasing reactor volume and degradation which would not normally be observed in a typical suspended reactor system. © 2012 Elsevier B.V.

Supramolecular polymers azo-containing : photo-responsive block copolymer elastomers and homopolymers

Beaucoup d'efforts dans le domaine des matériaux polymères sont déployés pour développer de nouveaux matériaux fonctionnels pour des applications spécifiques, souvent très sophistiquées, en employant des méthodes simplifiées de synthèse et de préparation. Cette thèse porte sur les polymères photosensibles – i.e. des matériaux fonctionnels qui répondent de diverses manières à la lumière – qui sont préparés à l'aide de la chimie supramoléculaire – i.e. une méthode de préparation qui repose sur l'auto-assemblage spontané de motifs moléculaires plus simples via des interactions non covalentes pour former le matériau final désiré. Deux types de matériaux photosensibles ont été ciblés, à savoir les élastomères thermoplastiques à base de copolymères à blocs (TPE) et les complexes d'homopolymères photosensibles. Les TPEs sont des matériaux bien connus, et même commercialisés, qui sont généralement composés d’un copolymère tribloc, avec un bloc central très flexible et des blocs terminaux rigides qui présentent une séparation de phase menant à des domaines durs isolés, composés des blocs terminaux rigides, dans une matrice molle formée du bloc central flexible, et ils ont l'avantage d'être recyclable. Pour la première fois, au meilleur de notre connaissance, nous avons préparé ces matériaux avec des propriétés photosensibles, basé sur la complexation supramoléculaire entre un copolymère tribloc simple parent et une petite molécule possédant une fonctionnalité photosensible via un groupe azobenzène. Plus précisément, il s’agit de la complexation ionique entre la forme quaternisée d'un copolymère à blocs, le poly(méthacrylate de diméthylaminoéthyle)-poly(acrylate de n-butyle)-poly(méthacrylate de diméthylaminoéthyle) (PDM-PnBA-PDM), synthétisé par polymérisation radicalaire par transfert d’atomes (ATRP), et l'orange de méthyle (MO), un composé azo disponible commercialement comportant un groupement SO3 -. Le PnBA possède une température de transition vitreuse en dessous de la température ambiante (-46 °C) et les blocs terminaux de PDM complexés avec le MO ont une température de transition vitreuse élevée (140-180 °C, en fonction de la masse molaire). Des tests simples d'élasticité montrent que les copolymères à blocs complexés avec des fractions massiques allant de 20 à 30% présentent un caractère élastomère. Des mesures d’AFM et de TEM (microscopie à force atomique et électronique à ii transmission) de films préparés à l’aide de la méthode de la tournette, montrent une corrélation entre le caractère élastomère et les morphologies où les blocs rigides forment une phase minoritaire dispersée (domaines sphériques ou cylindriques courts). Une phase dure continue (morphologie inversée) est observée pour une fraction massique en blocs rigides d'environ 37%, ce qui est beaucoup plus faible que celle observée pour les copolymères à blocs neutres, dû aux interactions ioniques. La réversibilité de la photoisomérisation a été démontrée pour ces matériaux, à la fois en solution et sous forme de film. La synthèse du copolymère à blocs PDM-PnBA-PDM a ensuite été optimisée en utilisant la technique d'échange d'halogène en ATRP, ainsi qu’en apportant d'autres modifications à la recette de polymérisation. Des produits monodisperses ont été obtenus à la fois pour la macroamorceur et le copolymère à blocs. À partir d'un seul copolymère à blocs parent, une série de copolymères à blocs partiellement/complètement quaternisés et complexés ont été préparés. Des tests préliminaires de traction sur les copolymères à blocs complexés avec le MO ont montré que leur élasticité est corrélée avec la fraction massique du bloc dur, qui peut être ajustée par le degré de quaternisation et de complexation. Finalement, une série de complexes d'homopolymères auto-assemblés à partir du PDM et de trois dérivés azobenzènes portant des groupes (OH, COOH et SO3) capables d'interactions directionnelles avec le groupement amino du PDM ont été préparés, où les dérivés azo sont associés avec le PDM, respectivement, via des interactions hydrogène, des liaisons ioniques combinées à une liaison hydrogène à travers un transfert de proton (acidebase), et des interactions purement ioniques. L'influence de la teneur en azo et du type de liaison sur la facilité d’inscription des réseaux de diffraction (SRG) a été étudiée. L’efficacité de diffraction des SRGs et la profondeur des réseaux inscrits à partir de films préparés à la méthode de la tournette montrent que la liaison ionique et une teneur élevée en azo conduit à une formation plus efficace des SRGs.

Raman evidence of the interaction between multiwalled carbon nanotubes and nanostructured TiO(2)

Nanocomposites of carbon nanotubes and titanium dioxide (TiO(2)) have attracted much attention due to their photocatalytic properties. Although many examples in the literature have visualized these nanocomposites by electron microscopic images, spectroscopic characterization is still lacking with regard to the interaction between the carbon nanotube and TiO(2). In this work, we show evidence of the attachment of nanostructured TiO(2) to multiwalled carbon nanotubes(MWNTs) by Raman spectroscopy. The nanostructured TiO(2) was characterized by both full-width at half-maximum (FWHM) and the Raman shift of the TiO(2) band at ca 144 cm(-1), whereas the average diameter of the crystallite was estimated as approximately 7 nm. Comparison of the Raman spectra of the MWNTs and MWNTs/TiO(2) shows a clear inversion of the relative intensities of the G and D bands, suggesting a substantial chemical modification of the outermost tubes due to the attachment of nanostructured TiO(2). To complement the nanocomposite characterization, scanning electronic microscopy and X-ray diffraction were performed. Copyright (C) 2011 John Wiley & Sons, Ltd.

Surface-enhanced Raman study of electrochemical and photocatalytic degradation of the azo dye Janus Green B

The photocatalytic degradation of Janus Green B azo dye over silver modified titanium dioxide films was investigated by surface-enhanced Raman spectroscopy (SERS). An optimized SERS-active substrate was employed to study the photodegradation reaction of Janus Green B. Considering that photocatalytic degradation processes of organic molecules adsorbed on TiO2 might involve either their oxidation or reduction reaction, the vibrational spectroelectrochemical study of the dye was also performed, in order to clarify the transformations involved in initial steps of its photochemical decomposition. In order to understand the changes in Raman spectra of Janus Green B after photodegradation and/or electrochemical processes, a vibrational assignment of the main Raman active modes of the dye was carried out, based on a detailed resonance Raman profile. Products formed by electrochemical and photochemical degradation processes were compared. The obtained results revealed that the first steps of the degradation process of Janus Green B involve a reductive mechanism. (C) 2007 Published by Elsevier B.V.

Estudos de sorção de um corante aniônico modelo em partículas de quitosana reticulada

Textile activity results in effluents with a variety of dyes. Among the several processes for dye-uptaking from these wastewaters, sorption is one of the most effective methods, chitosan being a very promising alternative for this end. The sorption of Methyl Orange by chitosan crosslinked particles was approached using equilibrium and kinetic analyses at different pH s. Besides the standard pseudo-order analysis normally effectuated (i.e. pseudo-first-order and pseudo-second-order), a novel approach involving a pseudo-nth-order kinetics was used, nbeing determined via non-linear regression, using the Levenberg-Marquardt method. Zeta potential measurements indicated that electrostatic interactions were important for the sorption process. Regarding equilibrium experiments, data were well fitted to a hybrid Langmuir-Freundlich isotherm, and estimated Gibbs free energy of adsorption as a function of mass of dye per area of chitosan showed that the process of adsorption becomes more homogeneous as the pH of the continuous phase decreased. Considering the kinetics of sorption, although a pseudo-nth-order description yielded good fits, a kinetic equation involving diffusion adsorption phenomena was found to be more consistent in terms of a physicochemical description of the sorption process

Hydrochemical evaluation of different spring waters for bottling

This investigation was carried out within the Parana sedimentary basin in São Paulo and Mato Grosso do Sul States, Brazil, and involved the sampling of different spring water samples with the purpose of evaluating their quality for bottling Several methods were utilized for acquiring the hydrochemical data, such as methyl orange end-point titration, potentiometry, ion selective electrodes, spectrophotometry, atomic absorption spectrophotometry and inductively coupled plasma spectrometry The results obtained for the analyzed samples were compared with the guideline values established by the São Paulo State and Brazilian Health Ministry legislations for defining the potable water standards The Brazilian Code for Mineral Waters that was established by Register 7841 published on 8 August 1945 was also taken into account for verifying if the spring waters are mineralized The hydrochemical data allowed the identification of anthropogenic and geogenic inputs of some constituents in most of the samples, which affected the water quality and did not allow them to be utilized for commercial purposes (bottling) The waters of these springs can only become appropriate for human consumption after previous chemical treatment

Amorphous manganese polyphosphates: preparation, characterization and incorporation of azo dyes

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Hydrochemical evaluation of bottled mineral waters and spring at Corumbataí city, São Paulo State, Brazil

This investigation was carried out within São Paulo State, Brazil, and involved the sampling of well-known mineral bottled waters for performing a comparative hydrochemical study and of a spring occurring at Corumbataí city, in order to evaluate its suitability for bottling. Several methods were utilized for acquiring the hydrochemical data like the methyl orange end-point titration, potentiometry, ion selective electrode, colorimetry, flame photometry and inductively-coupled plasma spectrometry. The results obtained for the analyzed samples were compared with the guideline values established by the National Commission of Rules and Standards for Food of the Brazilian Health Ministry published in 1976. The Brazilian Code for Mineral Waters that was established by Register 7841 published on 8 August 1945 was also taken into account for verifying if the spring waters are mineralized. The hydrochemical data allowed identify some constituents impoverishing the water quality, thus, implying on its nonutilization for commercial purposes (bottling). In one specific case, the spring water only can become appropriate for human consumption after previous chemical treatment. © 201 WIT Press.