Microstructure and compression behavior of chip consolidated magnesium

Chips produced by turning a commercial purity magnesium billet were cold compacted and then hot extruded at four different temperatures: 250, 300, 350, and 400 degrees C. Cast billets, of identical composition, were also extruded as reference material. Chip boundaries, visible even after 49: 1 extrusion at 400 degrees C, were observed to suppress grain coarsening. Although 250 degrees C extruded chip-consolidated product showed early onset of yielding and lower ductility, fully dense material (extruded at 400 degrees C) had nearly 40% reduction in grain size with 22% higher yield strength and comparable ductility as that of the reference. The study highlights the role of densification and grain refinement on the compression behavior of chip consolidated specimens.

Microstructure and tensile properties of consolidated magnesium chips

In this study tensile properties of consolidated magnesium chips obtained from solid state re-cycling (SSR) has been examined and correlated with the microstructure. Chips machined from as-cast billet of pure magnesium were consolidated through SSR technique, comprising of compaction at ambient conditions followed by hot extrusion at four different temperatures viz., 250, 300, 350 and 400 degrees C. The extruded rods were characterized for microstructure and their room temperature tensile properties. Both ultimate tensile strength and 0.2% proof stress of these consolidated materials are higher by 15-35% compared to reference material (as cast and extruded). Further these materials obey Hall-Petch relation with respect to strength dependence of grain size. Strain hardening behavior, measured in terms of hardening exponent, hardening capacity and hardening rate was found to be distinctly different in chip consolidated material compared to reference material. Strength asymmetry, measured as a ratio of compressive proof stress to tensile proof stress was higher in chip consolidated material. (C) 2012 Elsevier B.V. All rights reserved.

Effect of nanoscale boron carbide particle addition on the microstructural evolution and mechanical response of pure magnesium

In this study, the effect of nano-B4C addition on the microstructural and the mechanical behavior of pure Mg are investigated. Pure Mg-metal reinforced with different amounts of nano-size B4C particulates were synthesized using the disintegrated melt deposition technique followed by hot extrusion. Microstructural characterization of the developed Mg/x-B4C composites revealed uniform distribution of nano-B4C particulates and significant grain refinement. Electron back scattered diffraction (EBSD) analyses showed presence of relatively more recrystallized grains and absence of fiber texture in Mg/B4C nanocomposites when compared to pure Mg. The evaluation of mechanical properties indicated a significant improvement in tensile properties of the composites. The significant improvement in tensile ductility (similar to 180% increase with respect to pure Mg) is among the highest observed when compared to the pure Mg based nanocomposites existing in the current literature. The superior mechanical properties of the Mg/B4C nanocomposites are attributed to the uniform distribution of the nanoparticles and the tendency for texture randomization (absence of fiber texture) achieved due to the nano-B4C addition. (C) 2013 Elsevier Ltd. All rights reserved.

Superplasticity and cavitation of recycled AZ31 magnesium alloy fabricated by solid recycling process

Superplastic behaviour of Mg-alloy AZ31 was investigated to clarify the possibility of its use for superplastic forming (SPF) and to accurately evaluate material characteristics under a biaxial stress by utilizing a multi-dome test. The material characteristics were evaluated under three different superplastic temperatures , 643, 673, and 703 K in order to determine the most suitable superplastic temperature. Finite Element Method (FEM) simulation of rectangular pan forming was carried out to predict the formability of the material into a complex shape. The superplastic material properties are used for the simulation of a rectangular pan. Finally, the simulation results are compared with the experimental results to determine the accuracy of the superplastic material characteristics. The experimental results revealed that the m values are greater than 0.3 under the three superplastic temperatures, which is indicative of superplasticity. The optimum superplastic temperature is 673 K, at which a maximum m value and no grain growth were observed. The results of the FEM simulation revealed that certain localized thinning occurred at the die entrance of the deformed rectangular pan due to the insufficient ductility of the material. The simulation results also showed that the optimum superplastic temperature of AZ31 is 673 K.

Effect of microalloying with rare-earth elements on the texture of extruded magnesium-based alloys

A series of alloys have been produced with microalloying additions of rare-earth (RE) elements in the range of 0.1–0.4 wt.%. The alloys have been extruded to produce grain sizes of 23 ± 5 μm. The texture of the extruded alloys was measured, and it was found that the extrusion texture was weakened by the addition of RE elements. The samples with weakened extrusion textures exhibited an increase in the tensile elongation.

Influence of alloying additions on the extrudability of magnesium

The extrusion behaviour of a series of magnesium alloys was investigated and compared to a common aluminium alloy using limit diagrams. The variation in the limits was related to the different flow stress and solidus temperature of each alloy. The findings of this work have enabled predictions of the relative extrudability of new prototype alloys.

Performance of wrought aluminium and magnesium alloy tubes in three-point bending

This present work examines the load carrying capacity, energy absorption and fracture characteristics of wrought magnesium and aluminium alloy tubes in three-point bending. Magnesium alloy AZ31, and aluminium alloys 6063 and 7075, were extruded into cylindrical tubes of both equivalent thickness and mass. A strong thickness effect was present meaning that the AZ31 tube had significantly higher load and energy absorption performance than an equivalent mass 6063 tube, albeit not as high as the 7075 tube. Hinge formation and maximum load was delayed for the magnesium alloy, meaning that a high energy absorption rate persisted to higher deformation displacements than the aluminium alloys. It was also found that fracture during deformation was dependent on the indenter diameter, tube thickness and lower support separation.

The Challenge of inhomogeneous deformation in magnesium and its alloys

It is shown that wrought magnesium alloys display a number of significant types of deformation inhomogeneities. These are influenced by the variation in the ease of basal slip amongst grains, micro-textures, shear banding, twinning and grain boundary sliding. Key features of each of these effects are examined and their engineering consequences and challenges are identified.

Effect of grain size on the performance of extruded magnesium alloy tubes in three-point bending

The performance of extruded AZ31, AZ61 and AM-EX1 tubes was examined in three-point bending. Different extrusion temperatures were used to investigate the effect of grain size on the load-carrying capacity, energy absorption and fracture propensity of the tubes. Results showed that while the peak load increased with a smaller average recrystallised grain size, the retention of large elongated un-recrystallised grains in the microstructure reduced the load. The presence of the large elongated grains also appeared detrimental to the ability of the tube to deform before fracture.

Solute segregation and texture modification in an extruded magnesium alloy containing gadolinium

The alloy Mg-1.5Gd has been extruded at different temperatures to produce two significantly different textures. At lower extrusion temperatures there was significant solute clustering in the matrix, coupled with segregation of solute to the grain boundaries. At higher temperatures these two phenomena were both less pronounced. It is suggested here that segregation of solute to the grain boundaries plays a significant role in the texture modification effect that rare earth elements have in magnesium alloys.

Texture selection mechanisms in uniaxially extruded magnesium alloys

Extrusion textures in magnesium alloys are of high interest due to their influence on yield asymmetry. This data supports work describing three mechanisms of texture selection that may play a role during extrusion. These mechanisms involve localized differences in deformation at the grain level, the change in local environment experienced by grain boundary bulges and shear banding. The work employs visco-plastic crystal plasticity and electron backscattering diffraction.

Influence of orientation on twin nucleation and growth at low strains in a magnesium alloy

The resolved shear stress is believed to play an important role in twin formation. The present study tests this idea for an extruded magnesium alloy by examining "tension" twinning in different grain orientations. Electron backscatter diffraction analysis is employed for alloy AZ31 tested in compression along the extrusion axis to strains between 0.008 and 0.015. For heavily twinned grains, it is seen that twinning occurs on 2.3 twin systems per grain on average. The active systems are also most commonly those with, or very near to, the highest Schmid factor. The most active system in multiply twinned grains accounts on average for ∼0.6 of the twinning events. In addition, it is found that the twin habit plane falls within 6° of the K1 plane. Orientations with the highest Schmid factors (0.45-0.5) for twinning display twin aspect ratios greater by ∼40% and twin number densities greater by ∼10 times than orientations with maximum Schmid factors for twinning of 0.15-0.2. Thus the Schmid factor for twinning is seen to affect nucleation more than thickening in the present material. Viscoplastic crystal plasticity simulations are employed to obtain approximations for the resolved shear stress. Both the twin aspect ratio and number density correlate quite well with this term. The effect of the former can be assumed to be linear and that of the latter follows a power law with exponent ∼13. Increased aspect ratios and number densities are seen at low Schmid factors and this may relate to stress fluctuations, caused most probably in the present material by the stress fields at the tips of blocked twins. Overall, it is evident that the dominance of twinning on high Schmid factor systems is preserved at the low strains examined in the present work, despite the stress fluctuations known to be present. © 2014 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Effect of alloying and extrusion temperature on the microstructure and mechanical properties of Mg-Zn and Mg-Zn-RE alloys

Extruded Mg-Zn-RE alloys have been shown to exhibit excellent combinations of yield strength and ductility, but it is not completely clear how adding rare earth metals to Mg-Zn alters the microstructure and affects the mechanical properties. Microstructural changes and the resulting mechanical properties from changes in composition and extrusion temperature have been investigated for Mg-. x Zn-. y RE (. x=2.5 and 5. wt.%, y=0 and 1. wt. %, and RE=Gd and Y) alloys. Adding RE to Mg-Zn increased the strength and reduced the ductility, while increasing the zinc concentration in the Mg-Zn-RE alloys had the reverse effect.