Adhesion to Er : YAG laser-prepared dentin after long-term water storage and thermocycling

This in vitro study evaluated the microtensile bond strength of a resin composite to Er:YAG-prepared dentin after long-term storage and thermocycling. Eighty bovine incisors were selected and their roots removed. The crowns were ground to expose superficial dentin. The samples were randomly divided according to cavity preparation method (I-Er:YAG laser and II-carbide bur). Subsequently, an etch & rinse adhesive system was applied and the samples were restored with a resin composite. The samples were subdivided according to time of water storage (WS)/number of thermocycles (TC) performed: A) 24 hours WS/no TC; B) 7 days WS/500 TC; C) 1 month WS/2,000 TC; D) 6 months WS/12,000 TC. The teeth were sectioned in sticks with a cross-sectional area of 1.0-mm(2), which were loaded in tension in a universal testing machine. The data were subjected to two-way ANOVA, Scheffe and Fisher`s tests at a 5% level. In general, the bur-prepared group displayed higher microtensile bond strength values than the laser-treated group. Based on one-month water storage and 2,000 thermocycles, the performance of the tested adhesive system to Er:YAG-laser irradiated dentin was negatively affected (Group IC), while adhesion of the bur-prepared group decreased only within six months of water storage combined with 12,000 thermocycles (Group IID). It may be concluded that adhesion to the Er:YAG laser cavity preparation was more affected by the methods used for simulating degradation of the adhesive interface.

Etch and rinse versus self-etching adhesives systems: Tridimensional micromechanical analysis of dentin/adhesive interface

The purpose of this study was to evaluate stress distribution in the hybrid layer produced by two adhesive systems using three-dimensional finite element analysis (FEA). Four FEA models (M) were developed: Mc, a representation of a dentin specimen (41 x 41 x 82 mu m) restored with composite resin, exhibiting the adhesive layer, hybrid layer (HL), resin tags, peritubular dentin, and intertubular dentin to simulate the etch-and-rinse adhesive system; Mr, similar to Mc, with lateral branches of the adhesive; Ma, similar to Mc, however without resin tags and obliterated tubule orifice, to simulate the environment for the self-etching adhesive system; Mat, similar to Ma, with tags. A numerical simulation was performed to obtain the maximum principal stress (sigma(max)). The highest sigma(max) in the HL was observed for the etch-and-rinse adhesive system. The lateral branches increased the sigma(max) in the HL. The resin tags had a little influence on stress distribution with the self-etching system. (C) 2012 Elsevier Ltd. All rights reserved.

Long-term nano-mechanical properties of biomodified dentin-resin interface components

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Morphology and bacterial colonisation of tooth/ceramic restoration interface after different cement excess removal techniques

Objectives: To evaluate the influence of different protocols for resin cement removal during cementation on biofilm formation.Methods: Twenty-eight ceramic blocks, which were injected under pressure, were placed over enamel blocks obtained from freshly extracted bovine incisors. The ceramic blocks were cemented to the enamel blocks using a dual-cured resin cement and the excess resin was removed according to the experimental group: TS: Teflon spatula; BR: brush; BR+: brush and polishing; SB+: scalpel blade and polishing. After autoclaving, the samples were colonised by incubation in a sucrose broth suspension standardised with Streptococcus mutans in microaerophilic stove. Specimens were quantitatively analysed for bacterial adherence at the adhesive interface using confocal laser scanning microscopy and counting the colony forming units, and qualitatively analysed using SEM. The roughness (Ra/Rz/RSm) was also analysed. Data were analysed by 1-way ANOVA and Tukey's test (5%).Results: The roughness values ranged from 0.96 to 1.69 mu m for Ra (p > 0.05), from 11.59 to 22.80 mu m for Rz (p = 0.02 < 0.05) and from 293.2 to 534.3 mu m for RSm (p = 0.00). Bacterial adhesion varied between 1,974,000 and 2,814,000 CFU/ml (p = 0.00). Biofilm mean thickness ranged from 0.477 and 0.556 mu m (p > 0.05), whilst the biovolume values were between 0.388 and 0.547 mu m(3)/mu m(2) (p = 0.04). Lower values for roughness, bacterial adhesion, biofilm thickness and biovolume were found with BR, whilst TS presented the highest values for most of the parameters. SEM images confirmed the quantitative values.Conclusions: The restoration margin morphology and interface roughness affects bacterial accumulation. The brush technique promoted less bacterial colonisation at the adhesive interface than did the other removal methods.Clinical significance: The brush technique seems to be a good option for removing the excess resin cement after adhesive cementation in clinical practice, as indicated by its better results with lower bacterial colonisation. (C) 2012 Elsevier Ltd. All rights reserved.

Investigação da Interface Metal-Porcelana da Liga Ni-Cr-Mo Soldada a LASER

The interface formed between the metal and the porcelain of a LASER welded Ni-Cr-Mo alloy was studied. The characterization was carried out through optical microscopy, scanning electron microscopy, X-ray dispersive spectroscopy-EDS and mechanical testing by three-point flexion test-TPE in the region LASER welded with and without the porcelain. The porcelain adhesion with the alloy alone is possible after the oxidation of the metallic surface and subsequent application of an adhesive called opaco. The applied porcelain, on the base metal and fusion zone presented some distinct behaviors. After the TPF test the base metal presented fractures while that in the fusion zone was completely gone. One noticed that the region submitted to the LASER welding showed less porcelain adhesion than the region of the base metal due to the microestructural refinement of the fusion zone. These results can be evidenced by the EDS of the studied regions. The TPF had demonstrated that the Ni-Cr-Mo alloy submitted to the LASER welding, undergone significant alterations in its mechanical properties after the application of the porcelain.

Micromechanics of dentin/adhesive interface in function of dentin depth: 3d finite element analysis

Objectives: The aim of this study was to analyze the stress distribution on dentin/adhesive interface (d/a) through a 3-D finite element analysis (FEA) varying the number and diameter of the dentin tubules orifice according to dentin depth, keeping hybrid layer (HL) thickness and TAǴs length constant. Materials and Methods: 3 models were built through the SolidWorks software: SD - specimen simulating superficial dentin (41 x 41 x 82 μm), with a 3 μm thick HL, a 17 μm length Tag, and 8 tubules with a 0.9 μm diameter restored with composite resin. MD - similar to M1 with 12 tubules with a 1.2 μm diameter, simulating medium dentin. DD - similar to M1 with 16 tubules with a 2.5 μm diameter, simulating deep dentin. Other two models were built in order to keep the diameter constant in 2.5 μm: MS - similar to SD with 8 tubules; and MM - similar to MD with 12 tubules. The boundary condition was applied to the base surface of each specimen. Tensile load (0.03N) was performed on the composite resin top surface. Stress field (maximum principal stress in tension - σMAX) was performed using Ansys Wokbench 10.0. Results: The peak of σMAX (MPa) were similar between SD (110) and MD (106), and higher for DD (134). The stress distribution pathway was similar for all models, starting from peritubular dentin to adhesive layer, intertubular dentin and hybrid layer. The peak of σMAX (MPa) for those structures was, respectively: 134 (DD), 56.9 (SD), 45.5 (DD), and 36.7 (MD). Conclusions: The number of dentin tubules had no influence in the σMAX at the dentin/adhesive interface. Peritubular and intertubular dentin showed higher stress with the bigger dentin tubules orifice condition. The σMAX in the hybrid layer and adhesive layer were going down from superficial dentin to deeper dentin. In a failure scenario, the hybrid layer in contact with peritubular dentin and adhesive layer is the first region for breaking the adhesion. © 2011 Nova Science Publishers, Inc.

Investigação de compósitos cimentícios para preenchimento de juntas da interface e de nichos em ligações de estruturas pré- moldadas

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Evaluation of metallic brackets adhesion after the use of bleaching gels with and without amorphous calcium phosphate (ACP): in vitro study

OBJETIVO: avaliar, in vitro, a influência do clareamento dentário com gel contendo fosfato de cálcio amorfo (ACP) na resistência da união adesiva de braquetes metálicos. MÉTODOS: trinta e seis dentes incisivos bovinos foram seccionados no limite coronorradicular e tiveram suas coroas incluídas em cilindros de PVC. Os corpos de prova foram divididos em três grupos (n = 12), de acordo com a realização do tratamento clareador e tipo de gel utilizado, sendo: G1 (controle) - sem clareamento; G2 - clareamento com gel sem ACP (Whiteness Perfect, FGM); G3 - clareamento com gel contendo ACP (Nite White ACP, Discus Dental). Os grupos G2 e G3 foram submetidos a 14 ciclos de clareamento, seguidos de intervalo de espera de 15 dias para a fixação adesiva dos braquetes metálicos. O ensaio mecânico de cisalhamento foi realizado em máquina universal Kratos, com velocidade de 0,5mm/min. Após o teste mecânico, os corpos de prova foram avaliados quanto ao índice de remanescente adesivo (ARI). Os resultados foram submetidos à ANOVA, ao teste de Tukey e ao de Kruskall-Wallis (α = 5%). RESULTADOS: diferenças significativas foram observadas entre os grupos testados. O grupo controle G1 (11,1MPa) mostrou uma resistência ao cisalhamento estatisticamente superior aos grupos submetidos ao clareamento (G2 = 5,40MPa; G3 = 3,73MPa), os quais não diferiram entre si. Não se observou diferença significativa para o ARI entre os grupos estudados. CONCLUSÃO: o clareamento dentário reduz a resistência da união adesiva de braquetes metálicos, enquanto a presença de ACP no gel clareador não influencia os resultados encontrados.

Influência da deposição de filmes de carbono tipo diamante na infiltração bacteriana pela interface entre implantes e pilares protéticos

Pós-graduação em Odontologia Restauradora - ICT

Estudo da modificação superficial de fibras de carbono por meio de tratamentos a plasma para o aumento da adesão na interface de compósitos fibra de carbono/PPS

Pós-graduação em Engenharia Mecânica - FEG

Effect of time between adhesive application and photoactivation on adhesion and collagen exposure

Fundacao de Amparo a Pesquisa do Estado de sao Paulo (FAPESP)

Effect of partially demineralized dentin beneath the hybrid layer on dentin-adhesive interface micromechanics

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Influência do agente de união na resistência ao cisalhamento da interface titânio/polímero de vidro

There is little information regarding bond strengths of polyglass to metal alloys. This study evaluated the influence of bonding system on shear bond strength of a composite resin (Artglass/Heraeus Kulzer) to cast titanium (Ti). Twenty metallic structures (4mm in diameter, 5mm thick) of titanium grade I were cast shaped and abraded with 250mm aluminum oxide and separated into two groups. For each group was applied one bonding system (Siloc or Retention Flow) before opaque and dentin polymer superposition. This procedure was managed using teflon matrices. They were manipulated and polymerized according to the manufacturer's recommendations. The samples were stored in distilled water for 24 hours at 37º and thermocycled (5º and 55ºC/500 cycles). Shear bond strength tests were performed by using an Instron Universal testing machine at a crosshead speed of 5mm/min. Results were analyzed statistically with one-way ANOVA (a=0,5) and they indicated that the Retention Flow system was statistically better than Siloc (20.74 MPa and 11.65 MPa , respectively). It was possible to conclude that the bonding agent influenced the adhesion between polymer and cast titanium.

Impact of bleaching pine fibre on the fibre/cement interface

The goal of this article was to evaluate the surface characteristics of the pine fibres and its impact on the performance of fibre-cement composites. Lower polar contribution of the surface energy indicates that unbleached fibres have less hydrophilic nature than the bleached fibres. Bleaching the pulp makes the fibres less stronger, more fibrillated and permeable to liquids due to removal the amorphous lignin and its extraction from the fibre surface. Atomic force microscopy reveals these changes occurring on the fibre surface and contributes to understanding the mechanism of adhesion of the resulting fibre to cement interface. Scanning electron microscopy shows that pulp bleaching increased fibre/cement interfacial bonding, whilst unbleached fibres were less susceptible to cement precipitation into the fibre cavities (lumens) in the prepared composites. Consequently, bleached fibre-reinforced composites had lower ductility due to the high interfacial adhesion between the fibre and the cement and elevated rates of fibre mineralization.

Influence of the vitreomacular interface on the efficacy of intravitreal therapy for uveitis-associated cystoid macular oedema.

PURPOSE To evaluate the effect of the vitreomacular interface (VMI) on treatment efficacy of intravitreal therapy in uveitic cystoid macular oedema (CME). METHODS Retrospective analysis of CME resolution, CME recurrence rate and monthly course of central retinal thickness (CRT), retinal volume (RV) and best corrected visual acuity (BCVA) after intravitreal injection with respect to the VMI configuration on spectral-domain OCT using chi-squared test and repeated measures anova adjusted for confounding covariates epiretinal membrane, administered drug and subretinal fluid. RESULTS Fifty-nine eyes of 53 patients (mean age: 47.4 ± 16.9 years) were included. VMI status had no effect on complete CME resolution rate (p = 0.16, corrected p-value: 0.32), time until resolution (p = 0.09, corrected p-value: 0.27) or CME relapse rate (p = 0.29, corrected p-value: 0.29). Change over time did not differ among the VMI configuration groups for BVCA (p = 0.82) and RV (p = 0.18), but CRT decrease was greater and faster in the posterior vitreous detachment (PVD) group compared to the posterior vitreous attachment (PVA) and vitreous macular adhesion (VMA) groups (p = 0.04). Also, the percentage of patients experiencing a ≥ 20% CRT thickness decrease after intravitreal injection was greater in the PVD group (83%) compared to the VMA (64%) and the PVA (16%) group (p = 0.027), however, not after correction for multiple testing (corrected p-value: 0.11). CONCLUSION The VMI configuration seems to be a factor contributing to treatment efficacy in uveitic CME in terms of CRT decrease, although BCVA outcome did not differ according to VMI status.