Effect of counterpressure during equal-channel angular pressing on nanoporosity formation in ultrafine-grained copper

Results of small-angle X-ray scattering and high-precision density measurements showed that the application of counterpressure during the equal-channel angular pressing (ECAP) of ultrafine-grained copper leads to a decrease in nanoporosity and an increase in mechanical properties of the ECAP-processed metal.

Equal-channel angular pressing and annealing of a twinning-induced plasticity steel : microstructure, texture, and mechanical properties

In this work, a high-manganese Fe-23Mn-1.5Al-0.3C Twinning-Induced Plasticity (TWIP) steel was subjected to plastic shear deformation using Equal-Channel Angular Pressing (ECAP) at 300 °C following route BC and additional annealing. The microstructure evolution during both deformation by ECAP and subsequent annealing was investigated and correlated with the mechanical properties. The successive grain refinement during ECAP was promoted by two parallel mechanisms, namely dislocation driven grain fragmentation and twin fragmentation, and accounted for the ultra-high strength. In addition, due to the relatively low volume fraction of deformation twins after ECAP at 300 °C, further contribution of deformation twinning during room temperature deformation allowed additional work-hardening capacity and elongation. During subsequent recovery annealing the ultra-fine grains and deformation twins were thermally stable, which supported retainment of the high yield strength along with regained uniform elongation. For the first time, the texture evolution during ECAP and during the following heat treatment was analyzed. After 1, 2, and 4 ECAP passes a transition texture with the characteristic texture components of both high- and low-SFE materials developed. During the following heat treatment the texture evolution proceeded similar to that observed in the same material after cold rolling. Retaining of the ECAP texture components due to oriented nucleation at grain boundaries and triple junctions as well as annealing twinning accounted for the formation of a weak, retained ECAP texture after recrystallization.

Evolution of nanoscale porosity during equal-channel angular pressing of titanium

Small-angle neutron scattering (SANS) analysis and transmission electron microscopy evidence suggest the occurrence of nanoscale porosity in commercial-purity titanium processed by equal-channel angular pressing (ECAP). SANS data were produced at two different facilities (GKSS, Germany; and Los Alamos, USA) and were analysed using three different methods. The results are consistent and yield a conclusive picture of the distribution of the scattering centres, which are believed to be associated with nanoporosity. Back pressure applied during ECAP tends to reduce the average pore size, which also depends on the processing route used. The results of the study strongly suggest that ECAP leaves a footprint in titanium in the form of a population of polydispersed nanovoids, which may play an important role in subsequent processing of the material.

Improving hydrogen storage properties of magnesium based alloys by equal channel angular pressing

Equal channel angular pressing was applied to a commercial magnesium alloy ZK60 in order to improve its hydrogen storage properties. The microstructure refinement and increase in the density of crystal lattice defects caused by equal channel angular pressing increase hydrogen desorption pressure, change the slope of the pressure plateau in pressure-composition isotherms, decrease the pressure hysteresis, and accelerate the hydrogen desorption kinetics. It is argued that a proper design of the defect structure of materials is a key element in the search for economically viable and environmentally acceptable solutions for mobile hydrogen storage based on metal hydrides.

Non-equal channel angular pressing of aluminum alloy

Strain history, microstructure and texture were studied in an aluminum alloy processed by the recently proposed process of non-equal channel angular pressing (NECAP). Comparison with alloy processed by equal channel angular pressing (ECAP) has been performed. A much finer microstructure was obtained in NECAP, showing that in this modified ECAP test the grain-refinement process was more efficient. The results indicate that the NECAP test has some interesting features that may be of interest for further research.

Strain localisation patterns under equal-channel angular pressing

Instabilities of plastic flow in the form of localised shear bands were experimentally observed to result from equal-channel angular pressing (ECAP) of magnesium alloy AZ31. The appearance of shear bands and their spacing were dependent on velocity of the pressing and applied back-pressure. A generic gradient plasticity theory involving second-order strain gradient terms in a constitutive model was applied to the case of AZ31 deformed by ECAP. Linear stability analysis was applied to the set of equations describing the deformation behaviour in the process zone idealised as a planar shear zone. A full analytical solution providing a dispersion relation between the rate of growth of a perturbation and the wave number was obtained. It was shown that the pattern of incipient localised shear bands exhibits a spectrum of characteristic lengths corresponding to admissible wave numbers. The interval of the spectrum of wave numbers of viable, i.e. growing, perturbations predicted by linear stability analysis was shown to be in good agreement with the experimentally observed spectrum. The effect of back-pressure applied during ECAP was also considered. The predicted displacement of the shear band spectrum towards lower wave numbers, shown to be a result of the decreased shear strain rate in the shear zone, was consistent with the experimentally observed increase of the band spacing with increased back-pressure. A good predictive capability of the general modelling frame used in conjunction with linear stability analysis was thus demonstrated in the instance of the particular alloy system and the specific processing conditions considered.

Effect of processing parameters on the magnetic properties and macrotexture of a Nd13.5Fe73.8Co6.7B5.6Ga0.4 alloy processed by equal channel angular pressing with back pressure

Equal channel angular pressing (ECAP) is a well-established thermo-mechanical processing technique, which could induce the c-axis texture of Nd2Fe14B in a melt-spun Nd13.5Fe73.8Co6.7B5.6Ga0.4 alloy. However, the effects of ECAP processing parameters, such as temperature, back pressure (BP), and multiple-pass ECAP routes, remain unknown for this alloy. In this paper, we have investigated the effects of these processing parameters on the c-axis texture formation. It is found by X-ray diffraction macrotexture analysis that the maximum intensity of (001) pole figures for the tetragonal-Nd2Fe14B phase (Imax) shows an increase from 2.7 to 4.1 m.r.d. (multiples of random distribution) by increasing the ECAP temperature from 723 to 823 K, while the difference in remanent magnetization between easy and hard directions (Δ Mr) rises from 24.0 to 41.5 Am2/kg. When the BP was increased from 0.25 to 0.5 GPa at 823 K, Imax showed an increase from 2.8 to 4.1 m.r.d. However, Imax saturated for BPs above 0.5 GPa, suggesting that BP has limited effect on the texture formation, although it is necessary for the compaction of the alloy powders. Two multiple-pass ECAP routes conventionally known as routes A and C were employed for two-pass ECAP at 823 K. It is found that route A processing is effective in enhancing the texture formation, while the texture is lost by a subsequent pressing when adopting route C. Therefore, the compaction of Nd13.5Fe73.8Co6.7B5.6Ga0.4 alloy powder using route A ECAP passes with 0.5 GPa BP at 823 K results in pronounced texture, which is beneficial for anisotropic hard magnetic properties.

Microstructure evolution and hardness variation during annealing of equal channel angular pressed ultra-fine grained nickel subjected to 12 passes

The microstructure, thermal stability and hardness of ultra-fine grained (UFG) Ni produced by 12 passes of equal channel angular pressing (ECAP) through the route Bc were studied. Comparing the microstructure and hardness of the as-ECAPed samples with the published data on UFG Ni obtained after 8 passes of ECAP through the route Bc reveals a smaller average grain size (230 nm in the present case compared with 270 nm in 8-pass Ni), significantly lower dislocation density (1.08 x 10(14) m(-2) compared with 9 x 10(14) m(-2) in 8-pass Ni) and lower hardness (2 GPa compared with 2.45 GPa for 8-pass Ni). Study of the thermal stability of the 12-pass UFG Ni revealed that recovery is dominant in the temperature range 150-250A degrees C and recrystallisation occurred at temperatures > 250 A degrees C. The UFG microstructure is relatively stable up to about 400 A degrees C. Due to the lower dislocation density and consequently a lower stored energy, the recrystallisation of 12-pass ECAP Ni occurred at a higher temperature (similar to 250 A degrees C) compared with the 8-pass Ni (similar to 200 A degrees C). In the 12-pass Nickel, hardness variation shows that its dependence on grain size is inversely linear rather than the common grain size(-0.5) dependence.

Efeito no processo ECAP (EQUAL CHANNEL ANGULAR) na microestrutura e nas propriedades mecânicas de uma liga comercial de alumínio AA3104

Pós-graduação em Engenharia Mecânica - FEG

Deformation field variations in equal channel angular extrusion due to back pressure

Flow lines were analysed in aluminium alloy 6061 during equal channel angular extrusion (ECAE) in a 90° die with and without the application of back pressure during pressing. The lines appeared much more rounded when a back pressure was applied compared to the case of conventional ECAE testing. With the help of an analytic flow function, the deformation field was obtained. It is shown that back pressure slightly lowers the total strain, strongly increases the size of the plastic zone and significantly reduces the plastic strain rate.

Evolution of texture during equal channel angular extrusion of commercially pure aluminum: Experiments and simulations

The evolution of crystallographic texture has been comprehensively studied for commercially pure Al as a function of amount of ECAE deformation for the three major routes of ECAE processing. It has been observed that processing through different routes leads to different type of texture, in both qualitative as well as quantitative sense. The results have been analyzed on the basis of existing concepts on ECAE deformation and simulations have been carried out using the simple shear model of ECAE implemented into the Viscoplastic Self Consistent model of polycrystal plasticity. The simulations revealed that non-octahedral slip is needed to reproduce the experimental texture development.

Evolution of Grain-Boundary Microstructure and Texture in Interstitial-Free Steel Processed by Equal-Channel Angular Extrusion

The equal-channel angular extrusion (ECAE) of Ti-bearing interstitial-free (IF) steel was performed following two different routes, up to four passes, at a temperature of 300 degrees C. The ECAE led to a grain refinement to submicron size. After the second pass, the grain size attained saturation thereafter. The microstructural analysis indicated the presence of coincident-site lattice (CSL) boundaries in significant fraction, in addition to a high volume fraction of high-angle random boundaries and some low-angle boundaries after the deformation. Among the special boundaries, Sigma 3 and Sigma 13 were the most prominent ones and their fraction depended on the processing route followed. A deviation in the misorientation angle distribution from the Mackenzie distribution was noticed. The crystallographic texture after the first pass resembled that of simple shear, with the {112}, {110}, and {123} aligned to the macroscopic shear plane.

Room-temperature equal channel angular extrusion of pure magnesium

In this paper, we demonstrate a way to impart severe plastic deformation to magnesium at room temperature to produce ultrafine grain size of similar to 250 nm through equal channel angular extrusion (ECAE). The strategy to deform magnesium at lower temperature or to achieve such grain sizes has been proposed as: (i) to obtain a suitable initial orientation with high Schmid factor for basal slip and low Schmid factor for pyramidal/prismatic slip; (ii) to take advantage of low stacking fault energy of basal and high stacking fault energies of prismatic/pyramidal planes in order to relatively work-harden the basal plane with respect to the pyramidal/prismatic plane; and (iii) to lower the temperature of deformation in steps, leading to continual refinement of grains, resulting in finer grain size. The experimental as well as simulated texture of ECAE-processed samples indicate that the deformation mechanism leading to ultrafine grain size is slip-dominated. The recrystallization mechanism during ECAE has been found to be orientation-dependent. (C) 2010 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Local texture and microstructure in cube-oriented nickel single crystal deformed by equal channel angular extrusion

Local texture and microstructure was investigated to study the deformation mechanisms during equal channel angular extrusion of a high purity nickel single crystal of initial cube orientation. A detailed texture and microstructure analysis by various diffraction techniques revealed the complexity of the deformation patterns in different locations of the billet. A modeling approach, taking into account slip system activity, was used to interpret the development of this heterogeneous deformation.

Texture evolution in commercially pure titanium after warm equal channel angular extrusion

Texture development in commercially pure titanium during equal channel angular extrusion (ECAE) through Routes A, Be and C has been studied up to three passes at 400 C. Textures were measured using X-ray diffraction, while the microstructural analyses were performed using electron back-scattered diffraction as well as transmission electron microscopy. Occurrences of dynamic restoration processes (recovery and recrystallization) were clearly noticed at all levels of deformations. Finally, the textures were simulated using a viscoplastic polycrystal self-consistent (VPSC) model. Simulations were performed incorporating basal, prismatic and pyramidal slip systems as well as tensile and compressive twinning. The simulated textures corroborate well with experimental textures in spite of the occurrence of dynamic restoration processes. (C) 2010 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.