Crosslinking of poly[(3-hydroxybutyrate)-co-(3-hydroxyvalerate)] using dicumyl peroxide as initiator

In order to modify poly [(3-hydroxybutyrate)-co-(3-hydroxyvalerate)] (PHBV), the crosslinking of this copolymer was carried out at 160degreesC using dicumyl peroxide (DCP) as the initiator. The torque of the PHBV melt showed an abrupt upturn when DCP was added. Appropriate values for the gel fraction and crosslink density were obtained when the DCP content was up to 1 wt% of the PHBV. According to the NMR spectroscopic data, the location of the free radical reaction was determined to be at the tertiary carbons in the PHBV chains. The melting point, crystallization temperature and crystallinity of PHBV decreased significantly with increasing DCP content. The effect of crosslinking on the melt viscosity of PHBV was confirmed as being positive. Moreover, the mechanical properties of PHBV were improved by curing with DCP. When 1 wt% DCP was used, the ultimate elongation of PHBV increased from 4 to 11 %. A preliminary biodegradation study confirmed the total biodegradability of crosslinked PHBV.

Stabilization of polymer bilayers by introducing crosslinking at the interface

Bisphenol A solid epoxy serves as an effective reaction compatibilizer to the bisphenol A polycarbonate (PC)/PMMA bilayer systems. Addition of epoxy to the bottom PMMA layer can retard or even prevent the dewetting of PC films by introducing crosslinking between both components at the interface. This is the first investigation of polymer bilayers stabilized by chemical reactions.

LDPE/carbon black conductive composites: Influence of radiation crosslinking on PTC and NTC properties

The electrical resistivity of low-density polyethylene/carbon black composites irradiated by Co-60 gamma-rays was investigated as a function of temperature. The experimental results obtained by scanning electron microscopy, solvent extraction techniques, and pressure-specific volume-temperature analysis techniques showed that the positive temperature coefficient (PTC) and negative temperature coefficient (NTC) effects of the composites were influenced by the irradiation dose, network forming (gel), and soluble fractions (Sol). The NTC effect was effectively eliminated when the radiation dose reached 400 kGy. The results showed that the elimination of the NTC effect was related to the difference in the thermal expansion of the gel and Sol regions. The thermal expansion of the sol played an important role in both increasing the PTC intensity and decreasing the NTC intensity at 400 kGy.

Crystallization and Crosslinking of polyamide-1010 under elevated pressure

The structure and thermal properties of polyamide-1010 (PA1010), treated at 250degreesC for 30 min under pressures of 0.7-2.5 GPa, were studied with wide-angle X-ray diffraction (WAXD), infrared (IR), differential scanning calorimetry (DSC), and thermogravimetric analysis (TGA). Crystals were formed when the pressures were less than 1.0 GPa or greater than 1.2 GPa. With increasing pressure, the intensity of the diffraction peak at approximately 24degrees was enhanced, whereas the peak at approximately 20degrees was depressed. The triclinic crystal structure of PA1010 was preserved. The highest melting temperature of the crystals obtained in this work was 208degreesC for PA1010 treated at 1.5 GPa. Crosslinking occurred under pressures of 1.0-1.2 GPa. Only a broad diffraction peak centered at approximately 20degrees was observed on WAXD patterns, and no melting and crystallization peaks were found on DSC curves. IR spectra of crosslinked PA1010 showed a remarkable absorption band at 1370 cm(-1). The N-H stretching vibration band at 3305 cm(-1) was weakened. Crystallized PA1010 had a higher thermal stability than crosslinked PA1010, as indicated on TGA curves by a higher onset temperature of decomposition.

Hydrogel of biodegradable cellulose derivatives. I. Radiation-induced crosslinking of CMC

Radiation crosslinking of carboxymethylcellulose (CMC) with a degree of substitution (DS) from 0.7 to 2.2 was the subject of the current investigation. CMC was irradiated in solid-state and aqueous solutions at various irradiation doses. The DS and the concentration of the aqueous solution had a remarkable affect on the crosslinking of CMC. Irradiation of CMC, even with a high DS, 2.2 in solid state, and a low DS, 0.7 in 10% aqueous solution, resulted in degradation. However, it was found that irradiation of CMC with a relatively high DS, 1.32, led to crosslinking in a 5% aqueous solution, and 20% CMC gave the highest gel fraction. CMC with a DS of 2.2 induced higher crosslinking than that with a DS of 1.32 at lower doses with the same concentration. Hence, it was apparent that a high DS and a high concentration in an aqueous solution were favorable for high crosslinking of CMC. It is assumed that; high radiation crosslinking of CMC was induced by the increased mobility of its molecules in water and by the formation of CMC radicals from the abstraction of H atoms from macromolecules in the intermediate products of water radiolysis. A preliminary biodegradation study confirmed that crosslinked CMC hydrogel can be digested by a cellulase enzyme. (C) 2000 John Wiley & Sons, Inc.

Radiation crosslinking of biodegradable poly(butylene succinate) and its heat distortion behavior

Poly(butylene succinate), (PBS1) was irradiated with Co-60-gamma radiation at various temperatures. The gel fraction of PBS I irradiated at molten state (100 degreesC) is higher than that of the samples irradiated at lower temperatures with the same dose. Two-step irradiation ( irradiation at room temperature and then irradiation at 100 degreesC) yielded the highest gel content as compared with other treatment conditions. It is due to the network structure formed by preirradiation at room temperature and further irradiation at molten state reduce degradation of PBS1. PBS1 prepared by the two-step irradiation was improved in heat distortion resistance because of its higher gel content. Unirradiated PBS1 sheets broke immediately at 110 degreesC. On the other hand, for samples (gel fraction 50%) irradiated by asing the two-step method, they did not break even at 130 degreesC for 200 min.

Radiation crosslinking of biodegradable poly(butylene succinate) at high temperature

Poly(butylene succinate), (PBS) with different molecular weight was gamma -irradiated at different temperatures and various doses. PBS with high molecular weight and smaller peak area of crystal melting gave the highest gel content at the same temperatures and dose. A two-step irradiation (irradiation in molten state after irradiation at room temperature) gave the highest gel content in different conditions. This is due to the formation of network structure by pre-irradiation at room temperature that leads to less degradation. PBS prepared by two step irradiation was effective for improvement of heat stability because of high gel content formation. Unirradiated PBS sheets broke immediately at 110 degrees, while the irradiated sample (gel fraction, 50%) by a two step-method did not break even up to 200 minutes at 130 degreesC. The PBS sheets are biodegradable even after crosslinking.

The effect of chain flexibility and chain mobility on radiation crosslinking of polymers

Radiation crosslinking of polymers mainly depends on the structure of polymer chain. The flexibility and mobility of chain directly influence the possibility of the reactive radicals recombination. Flexible chain is easier to crosslink than rigid-chain polymer. The latter must be crosslinked at high temperature, as most polymers can only crosslink above their melting point. Structural effect also influences the mechanism of radiation crosslinking of polymers. We find from the results in literature and in our laboratory that, the flexibility chain polymer mainly crosslinked with H type, but the rigid chain polymer mainly crosslinked with Y type. (C) 2001 Published by Elsevier Science Ltd.

Efforts to decrease crosslinking extent of polyethylene in a reactive extrusion grafting process

Grafting of acrylic acid and glycidyl methacrylate onto low density polyethylene (LDPE) was performed by using a corotating twin-screw extruder. The effects of residence time and concentration of initiator and monomers on degree of grafting and gel content of grafting LDPE were studied systematically. Paraffin, styrene, p-benzoquinone, triphenyl phosphite, tetrachloromethane, and oleic acid were added to try to decrease the extent of crosslinking of LDPE. 4-hydroxyl-2,2,6,6-tetramethyl-1-piperidinyloxy (4-hydroxyl-TEMPO) and dipentamethylenethiuram tetrasulfide were also tried to inhibit crosslinking reaction of LDPE during its extruding grafting process. It was found that p-benzoquinone, triphenyl phosphite and tetrachloromethane were good inhibitors for crosslinking of LDPE. (C) 2000 John Wiley & Sons, Inc.

Crosslinking of polyimides via spirodilactone unit in polymer backbone

A new approach for the crosslinking of polyimides via the lactamization of spirodilactone unit in polyimide backbone was studied by two means: model reaction and the comparison of the properties of the polyimide precursors to those of the crosslinking polymers. Polyimides 4 and 5 were soluble in N,N'dimethylacetamide (DMAc), dimethylformamide (DMF), dimethylsulfoxide (DMSO), N'-methylpyrrolidone (NMP), and other common organic solvents, whereas their corresponding crosslinking polymers were insoluble in these solvents. The glass transition temperatures for polyimide 5 and its crosslinking polymer were 262 degrees C and 291 degrees C, whereas those for polyimide 4 and its crosslinking polymer were 265 degrees C and 360 degrees C. The weight-loss rate of the crosslinling polymers was apparently slower than that of the precursors when the temperature was >400 degrees C. The 10% weight-loss temperature for the polyimides 4 and 5 was <500 degrees C, whereas that for the crosslinking polymers was close to or above 600 degrees C. The results indicate that this type of crosslinking polymer has good thermal properties. The temperature for the formation of lactam was above 180 degrees C. (C) 1999 John Wiley & Sons, Inc.

Effect of crosslinking distribution on gas permeability and permselectivity of crosslinked polyimides

Crosslinking modification of polyimide, prepared from 3,3'4,4'-benzophenone tetracarboxyl dianhydride (BTDA) and 2,3,5,6-tetramethyl-1,4-diphenylenediamine (4MPDA), was performed by two methods, putting the polyimide in ambient environment for 4 months, and under UV irradiation for 2 or 8 h. The gas permeation properties of the crosslinked polyimides were investigated. The crosslinked polyimides induced by UV irradiation, in which crosslinking occurs in the surface layer, are of much higher gas permselectivity of hydrogen to nitrogen than that induced by the ambient environment, in which crosslinking takes place in the whole matrix, but their gas permeabilities for hydrogen are similar. (C) 1999 Elsevier Science Ltd. All rights reserved.