Color stability of relined dentures after chemical disinfection. A randomised clinical trial

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Visual evaluation of color stability after accelerated aging of pigmented and nonpigmented silicones to be used in facial prostheses

Objectives: The objective of this study was to evaluate by a visual method of comparison the color stability of nonpigmented and pigmented facial silicones after accelerated aging. Materials and Methods: Two kinds of silicones were used in this study; one specifically formulated for facial prostheses and the other an acetic silicone for industrial use. Twenty-four trial bodies were made for each silicone. These were divided into colorless and intrinsically pigmented groups: ceramic, make-up, and iron oxide. The groups were submitted to accelerated aging for nonmetallic materials. An initial reading and subsequent readings were made at 163, 351, 692, and 1000 hours using a visual method of comparison. The values were annotated in a spreadsheet by two observers, according to scores elaborated for this study. Results: All groups presented color stability in the visual method. According to the results obtained and analyzed in this study, we can conclude that both silicones, Silastic 732 RTV and Silastic MDX 4-4210, behaved similarly, they can therefore be indicated for use in maxillofacial prosthesis. The time factor of aging influenced negatively, independently of the pigmentation, or lack of it, and of silicones and no group had visually noticeable alterations in any of the accelerated aging time, independently of the addition or not of pigments.

Evaluation of hardness and color stability in the soft lining materials after thermocycling and chemical polishing.

The aim of this study was to evaluate the Shore A hardness and color stability of two soft lining materials after thermocycling and when chemical polishing was used or omitted. Two acrylic-based soft lining materials were tested: Coe-Soft and Soft Confort, 14 specimens were made for each material. They were distributed in four groups according to the treatment performed. The specimens were thermocycled (1000 cycles) and half of the group submitted to chemical polishing (methyl methacrylate). Shore A hardness was determined and color stability was calculated by means of Commission International de l'Eclairage Lab uniform color scale using a spectrophotometer, the measurements were made immediately after deflasked, chemical polishing and thermocycling. Analysis of variance (ANOVA) and Tukey's tests were performed at p < 0.01. Color changes (deltaE) were observed after thermocycling in both soft lining materials: Soft Confort (10.60) showed significantly higher values than Coe-Soft (4.57). Coe-Soft (26.42) showed higher Shore A hardness values than Soft Confort (19.42). Chemical polishing did not influence in the color stability of both materials; however, influenced in the hardness values of Coe-Soft.

Color stability after accelerated aging of two silicones, pigmented or not, for use in facial prostheses

One of the greatest challenges faced by buccomaxillofacial prosthetists is to reproduce the patient's exact skin color and provide adequate esthetics. To reach this objective, professionals must use materials with easy characterization and that maintain color over long periods of time. The objective of this study was, thus, to evaluate the color stability of two types of silicones, Silastic 732 and Silastic MDX4-4210. Twenty-four test specimens were made from each type of silicone and were divided into a colorless group and groups intrinsically pigmented with ceramics, cosmetics or iron oxide. The specimens were submitted to an accelerated system of aging for non-metallic materials. Readings were carried out initially and after periods corresponding to 163, 351, 692 and 1,000 hours of aging, using a reflection spectrophotometer analysis, and color alterations were calculated by the CIE L*a*b* system. The data were submitted to variance analysis and Tukey's test at a 5% level of probability. The results demonstrated that, irrespective of the period of time analyzed, all the materials underwent some type of chromatic alteration (ΔE > 0). The test specimens made with Silastic 732 and MDX4-4210, without pigmentation, presented the lowest color alteration values after 1,000 hours of aging. Of the pigments, ceramic presented the lowest color alteration values and cosmetic powder presented the highest values. Thus, it may be concluded that the materials without the incorporation of pigments presented similar color alteration values, and did not differ statistically. The cosmetic powder used in this study was the pigment that most altered the color of the test specimens. © 2009 Sociedade Brasileira de Pesquisa Odontológica.

Effect of accelerated aging on the microhardness and color stability of flexible resins for dentures

Acrylic resins have been widely used due to their acceptable esthetics and desirable characteristics such as easy handling, good thermal conductivity, low permeability to oral fluids and color stability. Flexible resins were introduced on the market as an alternative to the use of conventional acrylic resins in the construction of complete and partial removable dentures. Although these resins present advantages in terms of esthetics and comfort, studies assessing chromatic and microhardness alterations of these materials are still scarce in the related literature. The aim of this study was to evaluate the chromatic and microhardness alterations of two commercial brands of flexible resins in comparison to the conventional resin Triplex when submitted to accelerated aging. The resins were manipulated according to manufacturers' instructions and inserted into a silicone matrix to obtain 21 specimens divided into 3 groups: Triplex, Ppflex and Valplast. Triplex presented the highest microhardness value (p < 0.05) for all the aging periods, which was significantly different from that of the other resins, followed by the values of Valplast and Ppflex. Comparison between the flexible resins (Ppflex and Valplast) revealed a statistically significant difference (p < 0.05) as regards color. The flexible resin Ppflex and the conventional resin Triplex presented no statistically significant difference (p < 0.05) as regards aging. The accelerated aging significantly increased the microhardness values of the resins, with the highest values being observed for Triplex. Valplast presented the greatest chromatic alteration after accelerated aging.

Color stability of resins and nylon as denture base material in beverages

Purpose: Staining of prosthodontic materials may result in patient dissatisfaction and additional expense for replacement. This study aimed to determine the color stability of two heat-cured denture base acrylic (Lucitone 550, Vipi Cril) and one nylon denture base resin (Transflex) after immersion in beverages. Materials and Methods: Forty disks of each resin (20.0-mm diameter, 3.0-mm thick) were prepared and stored in distilled water for 24 hours at 37°C. During that time (T 0), the color of all specimens was spectrophotometrically measured. Each specimen was immersed in coffee, cola, red wine, and distilled water as a means of control. After 15-day (T 1) and 30-day (T 2) periods of immersion, the color of the specimens was measured again. The CIE (Commission Internationale de L' Eclairage) L*a*b* system was used to determine mean ΔE (color changes) values for each material and compared statistically with two-way ANOVA and Bonferroni intervals at 0.95. Results: In ΔET 0T 1 and ΔET 0T 2 the most severe staining was apparent with red wine (p < 0.001), followed by coffee (p < 0.01), when compared to the specimens stored in distilled water. Transflex also showed significant color change after immersion in cola (p < 0.01). In ΔET 1T 2 only red wine promoted significant staining of all resins (p < 0.0001). Conclusion: Chromatic changes were exhibited by specimens immersed in red wine, followed by coffee. For Transflex, cola also promoted color changes. The values of color changes converted to National Bureau of Standard units showed them to be perceivable to the human eye. © 2011 by the American College of Prosthodontists.

Color stability of composites: effect of immersion media.

Coloring in drinks decreases the color stability of composite restorations, reducing their longevity. The purpose of this in vitro study was to evaluate the effect of immersion media on color stability of seven different composite resins (Solidex - Shofu, Resilab-Wilcos, Signum - Heraeus, Epricord - Tokuyama, Adoro - Ivoclar Vivadent, Admira - Voco and Sinfony - 3MESPE). Seven resin-based composite specimens were prepared using a cylindrical teflon mold 2 mm thick and 10 mm in diameter Fifteen specimens of each resin were light-cured according to manufacturers' instructions and randomized into 3 groups (n= 5) according to immersion media: coffee, cola beverage and water A digital spectrophotometer Easy Shade (VITA) was used to evaluate the color changes at baseline and 7 days after immersion in each solution. Specimens were stored in the different staining media for 24 h/day during one week. The color differences were analyzed by two-way ANOVA and Tukey 's test (p< 0.05). Color change was observed after one week of immersion and there were statistical differences in staining, composite and interaction factors. The least staining was observed in Admira (deltaE= 3.934+/-0.814) and Resilab (deltaE= 3.993+/-0.735), followed by Adoro (deltaE= 4.044+/-1.001), Epri-cord (deltaE= 4.049+/-1.234), Signum (deltaE= 4.260+/-1.785), Solidex (deltaE=5,122+/-0.534) and Sinfony (deltaE=5.126+/-0.838). All of the composites tested except Adoro were susceptible to staining by substances present in coffee and cola, when stored in beverage for seven days. The lowest deltaE means were obtained with Admira.

Color Stability of Resin Used for Caries Infiltration After Exposure to Different Staining Solutions

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of intrinsic nanoparticle pigmentation on the color stability of denture base acrylic resins

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Influence of nanoparticles on color stability, microhardness, and flexural strength of acrylic resins specific for ocular prosthesis

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Color stability of a nanofilled resin: influence of polishing and finishing and fluoride solutions according to time

Aim: The aim of the study was evaluate the finishing and polishing effect of the color stability of the composite resin Filtek Supreme XT, according to different fluoride solutions and time. Material and Methods: Specimens were prepared (n=140) with half of the samples finished and polished. The experimental groups were divided according to the presence or absence of finishing and polishing and immersion solutions (artificial saliva, sodium fluoride solution at 0.05% - manipulated, Fluordent Reach, Oral B, Fluorgard). The specimens remained in artificial saliva for 24 hours and were subjected to an initial color analysis using a spectrophotometer CIELab system. Then, they were immersed in the experimental solutions for 1 minute a day. The readings of the color change were made after 24 and 48 hours, 7, 14, 21, 30 and 60 days after the first immersion. The three-way mixed Analysis of Variance (ANOVA) ("finishing/polishing", "immersion medium" and “time”) were performed. For multiple comparisons, the Sidak test for repeated measure was used, with a 5% level of significance. Results: The finishing and polishing factor showed significant variability, independently of the immersion media (p<0.001). Cconclusion: Finishing and polishing procedures yielded better color stability to composite resin over time, regardless of the immersion media.

Influence of light curing units and fluoride mouthrinse on morphological surface and color stability of a nanofilled composite resin

Composite resin is a dental material susceptible to color change over time which limits the longevity of restorations made with this material. The influence of light curing units and different fluoride mouthrinses on superficial morphology and color stability of a nanofilled composite resin was evaluated. Specimens (N = 150) were prepared and polished. The experimental groups were divided according to the type of light source (halogen and LED) and immersion media (artificial saliva, 0.05% sodium fluoride solution-manipulated, Fluordent Reach, Oral B, Fluorgard). Specimens remained in artificial saliva for 24-h baseline. For 60 days, they were immersed in solutions for 1 min. Color readout was taken at baseline and after 60 days of immersion. Surface morphology was analyzed by Scanning Electron Microscopy (SEM) after 60 days of immersion. Color change data were submitted to two-way Analysis of Variance and Tukey tests (α = 0.05). Surface morphology was qualitatively analyzed. The factor light source presented no significant variability (P = 0.281), the immersion media, significant variability (P < 0.001) and interaction between factors, no significant variability (P = 0.050). According to SEM observations, no difference was noted in the surface of the specimens polymerized by different light sources, irrespective of the immersion medium. It was concluded that the light source did not influence the color stability of composite, irrespective of the immersion media, and among the fluoride solutions analyzed, Fluorgard was the one that promoted the greatest color change, however, this was not clinically perceptible. The immersion media did not influence the morphology of the studied resin. Microsc. Res. Tech. 77:941–946, 2014. © 2014 Wiley Periodicals, Inc.