Pt-RuO(2) electrodes prepared by thermal decomposition of polymeric precursors as catalysts for direct methanol fuel cell applications

The electrocatalytic activity of Pt and RuO(2) mixed electrodes of different compositions towards methanol oxidation was investigated. The catalysts were prepared by thermal decomposition of polymeric precursors and characterized by energy dispersive X-ray, scanning electronic microscopy, X-ray diffraction and cyclic voltammetry. This preparation method allowed obtaining uniform films with controlled stoichiometry and high surface area. Cyclic voltammetry experiments in the presence of methanol showed that mixed electrodes decreased the potential peak of methanol oxidation by approximately 100 mV (RHE) when compared to the electrode containing only Pt. In addition, voltammetric experiments indicated that the Pt(0.6)Ru(0.4)O(y) electrode led to higher oxidation current densities at lower potentials. Chronoamperometry experiments confirmed the contribution of RuO(2) to the catalytic activity as well as the better performance of the Pt(0.6)Ru(0.4)O(y) electrode composition. Formic acid and CO(2) were identified as being the reaction products formed in the electrolysis performed at 400 and 600 mV. The relative formation of CO(2) was favored in the electrolysis performed at 400 mV (RHE) with the Pt(0.6)Ru(0.4)O(y) electrode. The presence of RuO(2) in Pt-Ru-based electrodes is important for improving the catalytic activity towards methanol electrooxidation. Moreover, the thermal decomposition of polymeric precursors seems to be a promising route for the production of catalysts applicable to DMFC. (C) 2009 International Association for Hydrogen Energy. Published by Elsevier Ltd. All rights reserved.

Luminescent and morphological study of Sr(2)CeO(4) blue phosphor prepared from oxalate precursors

Luminescent and morphological studies of Sr(2)CeO(4) blue phosphor prepared from cerium-doped strontium oxalate precursor are reported Powder samples were prepared from 5 and 25 mol% Ce(3+)-doped strontium oxalate as well as from a mechanical mixture of strontium oxalate and cerium oxalate at a 4 1 ratio respectively All the samples were characterized by XRD IR PLS and SEM The luminescent and structural properties of the Sr(2)CeO(4) material are little affected by the SrCO(3) remaining from precursors The Sr(2)CeO(4) material consists in one-dimensional chains of edge-sharing CeO(6) octahedra that are linked together by Sr(2+) ions The carbonate ion might be associated with oxygen ions of the linear chain and also with the oxygen atoms located in the equatorial position which consequently affects the charge transfer bands between O(2-) and Ce(4+). As observed by SEM, the morphological changes are related to each kind of precursor and thermal treatment along with irregular powder particles within the size range 05-2 mu m (c) 2010 Elsevier B V All rights reserved

One-pot synthesis of mixed (Z)-1,2-bis(organylchalcogene)-1-alkenes precursors of the novel beta-organylthio vinyllithium intermediates

One-pot hydrochalcogenation of 1-phenylthioacetylenes using organylselenolate and organyltellurolate anions generated by the insertions of selenium and tellurium in n-organyl lithium produced (Z)-1,2-bis(organylchalcogene)-1-alkenes. The chemical reactivity of these mixed 1,2-bis(organylchalcogene)-1-alkenes was studied by Te/Li and Se/Li stereoretentive exchanges carried out with n-butyl lithium, furnishing the new intermediate species (Z)-beta-organylthio vinyllithium anions, which were trapped with aldehydes, to give the (Z)-3-hydroxy vinyl thioethers with total control of the regio- and stereochemistry. (c) 2010 Elsevier Ltd. All rights reserved.

Characterization and voltammetric behavior of Pt(y)Mo(z)O(x)/C electrodes prepared by the thermal decomposition of polymeric precursors

Carbon-supported catalysts containing platinum and molybdenum oxide are prepared by thermal decomposition of polymeric precursors. The Pt(y)Mo(z)O(x)/C materials are characterized by energy dispersive X-ray spectroscopy, transmission electron microscopy, and X-ray diffraction. The catalysts present a well-controlled stoichiometry and nanometric particles. Molybdenum is present mainly as the MoO(3) orthorhombic structure, and no Pt alloys are detected. The voltammetric behavior of the electrodes is investigated; a correlation with literature results for PtMo/C catalysts prepared by other methods is established. The formation of soluble species and the aging effect are discussed. (C) 2009 Elsevier B.V. All rights reserved.

Major histocompatibility complex (MHC) class II-positive dendritic cells in the rat iris - In situ development from MHC class II-negative precursors

Purpose. To examine the postnatal development of major histocompatibility complex (MHC) class II-positive dendritic cells (DC) in the iris of the normal rat eye. Methods. Single-and double-color immunomorphologic studies were performed on whole mounts prepared from rat iris taken at selected postnatal ages (2 to 3 days to 78 weeks). Immunopositive cells were enumerated, using a quantitative light microscope, and MHC class II expression on individual cells was assessed by microdensitometric analysis. Results. Major histocompatibility class II-positive DCs in the iris developed in an age-dependent manner and reached adult-equivalent density and structure at approximately 10 weeks of age, considerably later than previously described in other DC populations in the rat. In contrast, the anti-rat DC monoclonal antibody OX62 revealed a population of cells present at adult-equivalent levels as early as 3 weeks after birth. Dual-color immunostaining and microdensitometric analysis demonstrated that during postnatal growth, development of the network of MHC class II-positive DCs was a consequence of the progressive increase in expression of MHC class II antigen by OX62-positive cells. Conclusions. During postnatal growth, the DC population of the iris develops initially as an OX62-positive-MHC class II-negative population, which then develops increasing MHC class II expression in situ and finally resembles classic DC populations in other tissue sites. Maturation of the iris DC population is temporally delayed compared with time to maturation in other tissue sites in the rat.

Classical and non-classical HLA molecules and p16(INK4a) expression in precursors lesions and invasive cervical cancer

Objectives: Viruses and turnout cells may regulate the expression of HLA molecules on the cell surface to escape immune system surveillance. Absence of classical HLA class I molecules may impair the action of specific cytotoxic cells, whereas non-classical HLA class I molecules may regulate innate and adaptive immune cells. We assess here the possible associations between classical/non-classical class I HLA and p16(INK4a) molecule expression in cervical biopsies of women infected with HPV, stratified according to grade of the lesion and HPV type. Study design: Cervical biopsies (N = 74) presenting cervical intraepithelial neoplasia grade 1 (CIN1) (n = 31), CIN2-3 (n = 19), and invasive cancer (n = 14) were evaluated alongside 10 normal cervical specimens. Results: HLA-A/B/C/G staining was observed in the early stages of HPV infection. A significant association was detected between HLA-A/B/C staining and HPV16/18 infection (OR = 0.12, 95%CI: 0.0163-0.7899; p = 0.04). HLA-E expression increased with the progression of the lesion (chi(2)-test for trend = 4.01; p = 0.05), and a significant association was found between HLA-E staining and HPV16/18 infection (OR = 11.25, 95%CI: 2.324-54.465; p = 0.003). Irrespective of the grade of the lesion, HLA-A/B/C staining and p16(INK4a) presented a good concordance (Kappa: 0.67). Conclusions: HLA-E overexpression seemed to be associated with invasive cancer and HPV16/18 infection. (C) 2008 Elsevier Ireland Ltd. All rights reserved.

Advanced precursors in marine biosynthetic study. Part 2: The biosynthesis of isocyanides and isothiocyanates in the tropical marine sponge Axinyssa n.sp.

The biosynthetic origins of the isocyanide and isothiocyanate groups in 9-isocyanop upukeanane (2) and 9-isothiocyanato-pupukeanane (3) are investigated by incorporation of [C-14]-labelled advanced precursors into the sponge Axinyssa n.sp. (C) 2001 Elsevier Science Ltd. All rights reserved.

O aroma ambiental e sua relação com as avaliações e intenções do consumidor no varejo

A atmosfera de uma loja é capaz de provocar emoções e comportamentos que estimulam a compra. Entre as suas dimensões, está o aroma ambiental, adicionado artificialmente ao ambiente. Este artigo investiga a relação entre a presença de aroma ambiental no varejo e as avaliações de loja, ambiente de loja e produtos, além das intenções comportamentais relativas ao retorno e ao tempo gasto na loja. A pesquisa teve uma etapa exploratória, exame de publicações em fisiologia, psicologia e comportamento do consumidor, para construção do referencial teórico e formulação das hipóteses, e outra causal, quase experimento, para identificar as relações de causa e efeito na presença de aroma. O estudo foi conduzido em uma butique de frutos do mar, e os instrumentos de coleta de dados, escalas de diferencial semântico, basearam-se em pesquisas similares. As análises incluíram técnicas de estatística descritiva e teste de hipóteses. Os resultados revelaram que a presença de aroma ambiental não aumentou as avaliações nem a intenção de retorno, mas reteve o consumidor por mais tempo na loja.

Hexanuclear and undecanuclear iron(III) carboxylates as catalyst precursors for cyclohexane oxidation

Two multinuclear complexes [Fe-6(mu(3)-O)(2)(mu(4)-O-2)L-10(OAc)(2)(H2O)(2)]center dot 2.625Et(2)O center dot 2.375H(2)O (1) and [(Fe11Cl)-Cl-III-(mu(4)-O)(3)(mu(3)-O)(5)L-16(dmf)(2.5)(H2O)(0.5)]center dot Et2O center dot 1.25dmf center dot 3.8H(2)O (2), where HL = 3,4,5-trimethoxybenzoic acid and dmf = dimethylformamide, have been prepared from trinuclear iron(III) carboxylates via their structural rearrangement in dimethylformamide or diethyl ether-dimethylformamide 9:1, respectively, and slow vapor diffusion of diethyl ether into the reaction mixture. Both compounds have been characterized by X-ray diffraction, optical, Mossbauer spectroscopy, and magnetic measurements. Complex 1 possesses a hexanuclear ferric peroxido-dioxido {Fe-6(O-2)(O)(2)}(12+) core unit, which adopts a recliner conformation, while complex 2 contains an unprecedented {Fe11O8Cl}(16+) core, in which 9 ferric ions are six-coordinate and the remaining two are five-coordinate. Another structural feature of note of the undecanuclear core is the presence of a deformed cubane entity {Fe-4(mu(3)-O)(mu(4)-O)(3)}(4+). Both complexes act as catalyst precursors for the oxidation of cyclohexane to cyclohexanol and cyclohexanone with aqueous H2O2, in the presence of pyrazinecarboxylic acid. Remarkable TONs and TOFs (the latter mainly for 1) with concomitant quite good yields have been achieved under mild conditions. Moreover, 1 exhibits remarkably high activity in an exceptionally short reaction time (45 min), being unprecedented for any metal catalyzed alkane oxidation by H2O2. The catalytic reactions proceed via Fenton type chemistry.

Thermodynamic pathway for the formation of SnSe and SnSe2 polycrystalline thin films by selenization of metal precursors

In this work, tin selenide thin films (SnSex) were grown on soda lime glass substrates by selenization of dc magnetron sputtered Sn metallic precursors. Selenization was performed at maximum temperatures in the range 300 °C to 570 °C. The thickness and the composition of the films were analysed using step profilometry and energy dispersive spectroscopy, respectively. The films were structurally and optically investigated by X-ray diffraction, Raman spectroscopy and optical transmittance and reflectance measurements. X-Ray diffraction patterns suggest that for temperatures between 300 °C and 470 °C, the films are composed of the hexagonal-SnSe2 phase. By increasing the temperature, the films selenized at maximum temperatures of 530 °C and 570 °C show orthorhombic-SnSe as the dominant phase with a preferential crystal orientation along the (400) crystallographic plane. Raman scattering analysis allowed the assignment of peaks at 119 cm−1 and 185 cm−1 to the hexagonal-SnSe2 phase and those at 108 cm−1, 130 cm−1 and 150 cm−1 to the orthorhombic-SnSe phase. All samples presented traces of condensed amorphous Se with a characteristic Raman peak located at 255 cm−1. From optical measurements, the estimated band gap energies for hexagonal-SnSe2 were close to 0.9 eV and 1.7 eV for indirect forbidden and direct transitions, respectively. The samples with the dominant orthorhombic-SnSe phase presented estimated band gap energies of 0.95 eV and 1.15 eV for indirect allowed and direct allowed transitions, respectively.

Effects of sulphurization time on Cu2ZnSnS4 absorbers and thin films solar cells obtained from metallic precursors

We report the results of a study of the sulphurization time effects on Cu2ZnSnS4 absorbers and thin film solar cells prepared from dc-sputtered tackedmetallic precursors. Three different time intervals, 10 min, 30min and 60 min, at maximum sulphurization temperature were considered. The effects of this parameter' change were studied both on the absorber layer properties and on the final solar cell performance. The composition, structure, morphology and thicknesses of the CZTS layers were analyzed. The electrical characterization of the absorber layer was carried out by measuring the transversal electrical resistance of the samples as a function of temperature. This study shows an increase of the conductivity activation energy from 10 meV to 54meV for increasing sulphurization time from 10min to 60min. The solar cells were built with the following structure: SLG/Mo/CZTS/CdS/i-ZnO/ZnO:Al/Ni:Al grid. Several ac response equivalent circuit models were tested to fit impedance measurements. The best results were used to extract the device series and shunt resistances and capacitances. Absorber layer's electronic properties were also determined using the Mott–Schottky method. The results show a decrease of the average acceptor doping density and built-in voltage, from 2.0 1017 cm−3 to 6.5 1015 cm−3 and from 0.71 V to 0.51 V, respectively, with increasing sulphurization time. These results also show an increase of the depletion region width from approximately 90 nm–250 nm.

Cu2ZnSnS4 absorber layers obtained through sulphurization of metallic precursors: Graphite box versus sulphur flux

In this work we employed a hybrid method, combining RF-magnetron sputtering with evaporation, for the deposition of tailor made metallic precursors, with varying number of Zn/Sn/Cu (ZTC) periods and compared two approaches to sulphurization. Two series of samples with 1×, 2× and 4× ZTC periods have been prepared. One series of precursors was sulphurized in a tubular furnace directly exposed to a sulphur vapour and N2+5% H2 flux at a pressure of 5.0×10+4 Pa. A second series of identical precursors was sulphurized in the same furnace but inside a graphite box where sulphur pellets have been evaporated again in the presence of N2+5% H2 and at the same pressure as for the sulphur flux experiments. The morphological and chemical analyses revealed a small grain structure but good average composition for all three films sulphurized in the graphite box. As for the three films sulphurized in sulphur flux grain growth was seen with the increase of the number of ZTC periods whilst, in terms of composition, they were slightly Zn poor. The films' crystal structure showed that Cu2ZnSnS4 is the dominant phase. However, in the case of the sulphur flux films SnS2 was also detected. Photoluminescence spectroscopy studies showed an asymmetric broad band emission whichoccurs in the range of 1–1.5 eV. Clearly the radiative recombination efficiency is higher in the series of samples sulphurized in sulphur flux. We have found that sulphurization in sulphur flux leads to better film morphology than when the process is carried out in a graphite box in similar thermodynamic conditions. Solar cells have been prepared and characterized showing a correlation between improved film morphology and cell performance. The best cells achieved an efficiency of 2.4%.

Precursors’ order effect on the properties of sulfurized Cu2ZnSnS4 thin films

A dc magnetron sputtering-based method to grow high-quality Cu2ZnSnS4 (CZTS) thin films, to be used as an absorber layer in solar cells, is being developed. This method combines dc sputtering of metallic precursors with sulfurization in S vapour and with post-growth KCN treatment for removal of possible undesired Cu2−xS phases. In this work, we report the results of a study of the effects of changing the precursors’ deposition order on the final CZTS films’ morphological and structural properties. The effect of KCN treatment on the optical properties was also analysed through diffuse reflectance measurements. Morphological, compositional and structural analyses of the various stages of the growth have been performed using stylus profilometry, SEM/EDS analysis, XRD and Raman Spectroscopy. Diffuse reflectance studies have been done in order to estimate the band gap energy of the CZTS films. We tested two different deposition orders for the copper precursor, namely Mo/Zn/Cu/Sn and Mo/Zn/Sn/Cu. The stylus profilometry analysis shows high average surface roughness in the ranges 300–550 nm and 230–250 nm before and after KCN treatment, respectively. All XRD spectra show preferential growth orientation along (1 1 2) at 28.45◦. Raman spectroscopy shows main peaks at 338 cm−1 and 287 cm−1 which are attributed to Cu2ZnSnS4. These measurements also confirm the effectiveness of KCN treatment in removing Cu2−xS phases. From the analysis of the diffuse reflectance measurements the band gap energy for both precursors’ sequences is estimated to be close to 1.43 eV. The KCN-treated films show a better defined absorption edge; however, the band gap values are not significantly affected. Hot point probe measurements confirmed that CZTS had p-type semiconductor behaviour and C–V analysis was used to estimate the majority carrier density giving a value of 3.3 × 1018 cm−3.

A study of ternary Cu2SnS3 and Cu3SnS4 thin films prepared by sulfurizing stacked metal precursors

Thin films of Cu2SnS3 and Cu3SnS4 were grown by sulfurization of dc magnetron sputtered Sn–Cu metallic precursors in a S2 atmosphere. Different maximum sulfurization temperatures were tested which allowed the study of the Cu2SnS3 phase changes. For a temperature of 350 ◦C the films were composed of tetragonal (I -42m) Cu2SnS3. The films sulfurized at a maximum temperature of 400 ◦C presented a cubic (F-43m) Cu2SnS3 phase. On increasing the temperature up to 520 ◦C, the Sn content of the layer decreased and orthorhombic (Pmn21) Cu3SnS4 was formed. The phase identification and structural analysis were performed using x-ray diffraction (XRD) and electron backscattered diffraction (EBSD) analysis. Raman scattering analysis was also performed and a comparison with XRD and EBSD data allowed the assignment of peaks at 336 and 351 cm−1 for tetragonal Cu2SnS3, 303 and 355 cm−1 for cubic Cu2SnS3, and 318, 348 and 295 cm−1 for the Cu3SnS4 phase. Compositional analysis was done using energy dispersive spectroscopy and induced coupled plasma analysis. Scanning electron microscopy was used to study the morphology of the layers. Transmittance and reflectance measurements permitted the estimation of absorbance and band gap. These ternary compounds present a high absorbance value close to 104 cm−1. The estimated band gap energy was 1.35 eV for tetragonal (I -42m) Cu2SnS3, 0.96 eV for cubic (F-43m) Cu2SnS3 and 1.60 eV for orthorhombic (Pmn21) Cu3SnS4. A hot point probe was used for the determination of semiconductor conductivity type. The results show that all the samples are p-type semiconductors. A four-point probe was used to obtain the resistivity of these samples. The resistivities for tetragonal Cu2SnS3, cubic Cu2SnS3 and orthorhombic (Pmn21) Cu3SnS4 are 4.59 × 10−2 cm, 1.26 × 10−2 cm, 7.40 × 10−4 cm, respectively.

CuxSnSx+1 (x = 2, 3) thin films grown by sulfurization of metallic precursors deposited by dc magnetron sputtering

We report the results of the growth of Cu-Sn-S ternary chalcogenide compounds by sulfurization of dc magnetron sputtered metallic precursors. Tetragonal Cu2SnS3 forms for a maximum sulfurization temperature of 350 ºC. Cubic Cu2SnS3 is obtained at sulfurization temperatures above 400 ºC. These results are supported by XRD analysis and Raman spectroscopy measurements. The latter analysis shows peaks at 336 cm-1, 351 cm-1 for tetragonal Cu2SnS3, and 303 cm-1, 355 cm-1 for cubic Cu2SnS3. Optical analysis shows that this phase change lowers the band gap from 1.35 eV to 0.98 eV. At higher sulfurization temperatures increased loss of Sn is expected in the sulphide form. As a consequence, higher Cu content ternary compounds like Cu3SnS4 grow. In these conditions, XRD and Raman analysis only detected orthorhombic (Pmn21) phase (petrukite). This compound has Raman peaks at 318 cm-1, 348 cm-1 and 295 cm-1. For a sulfurization temperature of 450 ºC the samples present a multi-phase structure mainly composed by cubic Cu2SnS3 and orthorhombic (Pmn21) Cu3SnS4. For higher temperatures, the samples are single phase and constituted by orthorhombic (Pmn21) Cu3SnS4. Transmittance and reflectance measurements were used to estimate a band gap of 1.60 eV. For comparison we also include the results for Cu2ZnSnS4 obtained using similar growth conditions.