The effect of sliding speed on the wear of steel-tool steel pairs

This study examines the effect of sliding speed and surface temperature on the wear behavior of an unlubricated mild steel-tool steel contact pair using the pin-on-disc test. The operating conditions and contact pair are of interest to the automotive sheet metal stamping industry and the broader metal forming community, where high contact pressures and moderate forming speeds can result in significant frictional heating and thus affect tool life. It will be shown that, while adhesive wear is dominant at the tool steel surface for all sliding speeds examined, the adhesive wear rate is very sensitive to sliding speed during slow speed conditions but relatively insensitive to sliding speed during higher speed conditions. These higher sliding speeds result in high frictional heating, however, the effect of increasing bulk temperature results in a transition from adhesive wear to material removal-dominated mechanisms. It is concluded that there is a distinct difference in the wear response for comparable surface temperature and bulk temperature conditions, at the low to moderate sliding speeds and temperatures examined in this study. The SEM and profilometry analysis show that the technique of increasing sliding speed to replicate bulk temperature conditions (or vice versa), may not result in equivalent wear rates and mechanisms.

Wear mechanisms and microstructure of pulsed plasma nitrided AISI H13 tool steel

AISI H13 tool steel discs were pulsed plasma nitrided during different times at a constant temperature of 400 °C. Wear tests were performed in order to study the acting wear mechanisms. The samples were characterized by X-ray diffraction, scanning electron microscopy and hardness measurements. The results showed that longer nitriding times reduce the wear volumes. The friction coefficient was 0.20 ± 0.05 for all tested conditions and depends strongly on the presence of debris. After wear tests, the wear tracks were characterized by optical and scanning electron microscopy and the wear mechanisms were observed to change from low cycle fatigue or plastic shakedown to long cycle fatigue. These mechanisms were correlated to the microstructure and hardness of the nitrided layer.

Frictional behaviour and wear performance of a nitrocarburised coating sliding against AISI 1019 steel

This work employed a commercial nitrocaburising process to diffuse a coating onto M2 grade high speed tool steel. Properties of the nitrocaburised coating (CN) such as thickness, roughness and hardness were characterised using a variety of techniques including Glow-Discharge Optical Emission Spectrometry (GD-OES) and Scanning Electron Microscopy (SEM). A tribological test has been developed in which two nominally identical crossed cylinders slide over each other under selected test conditions. The test has been employed to investigate the wear performance of both CN coated and uncoated M2 specimens and frictional behaviour of the sliding interface between the tool and a AISI 1019 steel workpiece under unlubricated (dry) and lubricated conditions. Fourier Transform Infrared Spectroscopy (FTIR) was used to monitor the formation of chemical species from the oxidation of lubricant during tribological testing.

Ferritic nitrocarburising of tool steels

Four different tool steel materials, P20, H13, M2 and D2, were nitrocarburised at 570°C in a fluidised bed furnace. The reactive diffusion of nitrogen and carbon into the various substrate microstructures is compared and related to the different alloy carbide distributions. The effect of carbon bearing gas (carbon dioxide, natural gas) on carbon absorption is reported, as well as its influence on compound layer growth and porosity. Partial reduction of Fe3O4 at the surface resulted in the formation of a complex, epsi-nitride containing oxide layer. In H13, carbon was deeply absorbed throughout the entire diffusion zone, affecting the growth of grain boundary cementite, nitrogen diffusivity and the sharpness of the compound layer: diffusion zone interface. When natural gas was used, carbon became highly concentrated in the compound layer, while surface decarburisation occurred with carbon dioxide. These microstructural effects are discussed in relation to hardness profiles, and compound layer hardness and ductility. The surfaces were characterised using glow discharge optical emission spectroscopy, optical and scanning electron microscopy and X-ray diffraction.

Fluidised bed nitrocarburising of tool steels

The work examines how ferritic nitrocarburising, a common heat treatment process for steels, can be adapted to the fluidised bed furnace. The effect of fluidising powder contamination on repeatability, composition of the reactive gas mixture, the development of nitrocarburised tool steel microstructure and resulting wear properties were investigated.

Application of Mossbauer spectroscopy to the study of corrosion resistance in NaCl solution of plasma nitrided AISI 316L stainless steel

Corrosion research in steels is one of the areas in which Mossbauer spectroscopy has become a required analytical technique, since it is a powerful tool for both identifying and quantifying distinctive phases (which contain Fe) with accuracy. In this manuscript, this technique was used to the study of corrosion resistance of plasma nitrided AISI 316L samples in the presence of chloride anions. Plasma nitriding has been carried out using dc glow-discharge, nitriding treatments, in medium of 80 vol.% H-2 and 20 vol.% N-2, at 673 K, and at different time intervals: 2, 4, and 7 h. Treated samples were characterized by means of phase composition and morphological analysis, and electrochemical tests in NaCl aerated solution in order to investigate the influence of treatment time on the microstructure and the corrosion resistance, proved by conversion electron Mossbauer spectroscopy (CEMS), glancing angle X-ray diffraction (GAXRD), scanning electron microscopy (SEM) and potentiodynamic polarization. A modified layer of about 8 gin was observed for all the nitrided samples, independently of the nitriding time. A metastable phase, S phase or gamma(N), was produced. It seems to be correlated with gamma`-Fe-4 N phase. If the gamma(N) fraction decreases, the gamma` fraction increases. The gamma(N) magnetic nature was analyzed. When the nitriding time increases, the results indicate that there is a significant reduction in the relative fraction of the magnetic gamma(N) (in) phase. In contrast, the paramagnetic gamma(N) (p) phase increases. The GAXRD analysis confirms the Mossbauer results, and it also indicates CrN traces for the sample nitrided for 7 h. Corrosion results demonstrate that time in the plasma nitriding treatment plays an important role for the corrosion resistance. The sample treated for 4 h showed the best result of corrosion resistance. It seems that the epsilon/gamma` fraction ratio plays an important role in thin corrosion resistance since this sample shows the maximum value for this ratio. (c) 2008 Published by Elsevier B.V.

Directory of steel foundries in the United States, Canada, and Mexico, 1961-62.

"Producerh [i.e. Producers] of carbon, low and high alloy, heat and corrosion steel castings, high manganese castings, investment mold castings, shell mold castings, and tool steel castings are included."

High speed steel /

Mode of access: Internet.

Sintering of freeformed maraging steel with boron additions

This paper describes the sintering of an 18Ni(350) maraging steel with additions of boron, with the aim of producing high hardness rapid tooling. Reaction of the boron with the alloying elements in the maraging steel resulted in the formation of a Mo- and Ti-rich borides. The former melted at similar to1220degreesC, providing a liquid phase for enhanced sintering. Although densification could occur regardless of the boron content, especially at high temperature, 0.4% B was required to produce a near full density component. The formation of the various borides depleted the matrix of critical age hardening elements. However, by altering the starting powder composition to compensate for this, hardness close to the wrought alloy has been achieved. This hardness was comparable to a common die casting tool steel. Examples of dies produced using selective laser sintering (SLS) are also shown. (C) 2003 Elsevier B.V. All rights reserved.

Morphological features of interfacial intermetallics and interfacial reaction rate in Al-11Si-2.5Cu-(0.15/0.60)Fe cast alloy/die steel couples

Soldering reactions are commonly observed during high pressure die casting of aluminium alloys, and involve the formation and growth of interfacial intermetallics between the die and the cast alloy. It is generally believed that close to 1% Fe is necessary in the aluminium alloy to reduce soldering. However, the role of iron in the interfacial reaction has not been studied in detail. In this investigation, reaction couples were formed between H13 tool steel substrates and an Al-11Si-2.5Cu melt containing either 0.15 or 0.60% Fe. Examination revealed distinctly different intermetallic layer morphology. The overall growth and chemistry of the reaction layer and the reaction rate measured by the consumption of the substrate were compared for the two alloy melts. It was demonstrated that a higher iron content reduces the rate of interfacial reaction, consistent with an observed thicker compact ( solid) intermetallic layer. Hence, the difference in reaction rate can be explained by a significant reduction in the diffusion flux due to a thicker compact layer. Finally, the mechanism of the growth of a thicker compact layer in the higher iron melt is proposed, based on the phase relations and diffusion both within and near the interfacial reaction zone. (C) 2004 Kluwer Academic Publishers.

Foaming of slags under dynamic conditions

Slag foaming under dynamic conditions has been studied in laboratory scale to examine the influence of properties commonly used to describe the foaminess and foam stability of slags under steady-state conditions. Synthetically produced slags with compositions relevant to tool steel and stainless steel production were studied through X-ray equipment in measurements simulating the dynamic conditions found in real processes. It is found that the dynamic systems display a more complex behavior than systems Under steady state. Traditional theories for foaming do not seem to be valid for slag foaming under dynamic conditions. The foam displays a fluctuating behavior, which the presently available models are not able to take into account. The concept of a foaming index does not seem to be applicable, resulting in the need for alternative models.

Substrate Effects on the Micro/Nanomechanical Properties of TiN Coatings

Nanoindentation and nanoscratch tests were performed for titanium nitride (TiN) coatings on different tool steel substrates to investigate the indentation/scratch induced deformation behavior of the coatings and the adhesion of the coating–substrate interfaces and their tribological property. In this work, TiN coatings with a thickness of about 500 nm were grown on GT35, 9Cr18 and 40CrNiMo steels using vacuum magnetic-filtering arc plasma deposition. In the nanoindentation tests, the hardness and modulus curves for TiN/GT35 reduced the slowest around the film thickness 500 nm with the increase of indentation depth, followed by TiN/9Cr18 and TiN/40CrNiMo. Improving adhesion properties of coating and substrate can decrease the differences of internal stress field. The scratch tests showed that the scratch response was controlled by plastic deformation in the substrate. The substrate plays an important role in determining the mechanical properties and wear resistance of such coatings. TiN/GT35 exhibited the best load-carrying capacity and scratch/wear resistance. As a consequence, GT35 is the best substrate for TiN coatings of the substrate materials tested.

An investigation of tribological properties of CN and TiCN coatings

Today the tool industry on a worldwide basis uses hard, wear-resistant, and low-friction coatings produced by different processes such as electrochemical or electroless methods, spray technologies, thermochemical, chemical-vapor deposition (CVD), and physical vapor deposition (PVD). In the current work, two different coatings, nitrocarburized (CN) and titanium carbonitride (TiCN) on M2-grade tool steel, were prepared by commercial diffusion and PVD techniques, respectively. Properties such as thickness, roughness, and hardness were characterized using a variety of techniques, including glow-discharge optical emission spectrometry (GD-OES) and scanning electron microscopy (SEM). A crossed-cylinders wear-testing machine was used to investigate the performances of both coatings under lubrication. The effect of coatings on the performance of lubricants under a range of wear-test conditions was also examined. Degradation of lubricants during tribological testing was explored by Fourier transform infrared (FTIR) spectroscopy.

A nitrocarburising and low-temperature chromising duplex surface treatment

A duplex surface treatment has been developed involving the pre-treatment of hardened and tempered AISI H13 chromium hot-work tool steel by a ferritic nitrocarburising process, and a subsequent treatment of the nitrocarburised surface by a low-temperature chromium thermo-reactive deposition process.  The process formed a thin and hard chromium carbonitride surface layer above a hardened diffusion zone, and the low processing temperature allowed the properties of the core material to be retained. It is expected this surface treatment will find application in the treatment  of tooling used for aluminium forming operations.

Robust control applied to metal spraying for rapid tooling

The spray forming process is a novel method of rapidly manufacturing tools and dies for stamping and injection operations. The process sprays molten tool steel from a set of arc spray guns onto a ceramic former to build up a thick steel shell. The volumetric contraction that occurs as the steel cools is offset by a volumetric expansion taking place within the sprayed steel, which allows the dimensional accurate tools to be produced. To ensure that the required phase transformation takes place, the temperature of the steel is regulated during spraying. The sprayed metal acts both as a source of mass and a source of heat and by adjusting the rate at which metal is sprayed; the surface temperature profile over the surface of the steel can be controlled. The temperature profile is measured using a thermal imaging camera and regulated by adjusting the rate at which the guns spray the steel. Because the temperature is regulated by adjusting the feed rate to an actuator that is moving over the surface, this is an example of mobile control, which is a class of distributed parameter control. The dynamic system has been controlled using a PI controller before. The paper describes the application of H∞ tracking type controller as the desire was for the average temperature to follow a desired profile. A study on the controllability of the underlying system was aimed at.