Investigation of the corrosion behaviour of AA 2024-T3 in low concentrated chloride media

Aluminium alloy (AA) 2024-T3 is an important engineering material due to its widespread use in the aerospace industry. However, it is very prone to localized corrosion attack in chloride containing media, which has been mainly associated to the presence of coarse intermetallics (IMs) in its microstructure. In this work the corrosion behaviour of AA 2024-T3 in low concentrated chloride media was investigated using microscopy and electrochemical methods. TEM/EDS observations on non-corroded samples evidenced the heterogeneous composition within the IMs. In addition, SEM observations showed that intermetallics with the same nominal composition present different reactivity, and that both types of coarse IMs normally found in the alloy microstructure are prone to corrosion. Moreover, EDS analyses showed important compositional changes in corroded IMs, evidencing a selective dissolution of their more active constituents, and the onset of an intense oxygen peak, irrespective to the IM nature, indicating the formation of corrosion products. On the other hand, the results of the electrochemical investigations, in accordance with the SEM/EDS observations, evidenced that IMs corrosion dominates the electrochemical response of the alloy during the first hours of immersion in the test electrolyte. (c) 2008 Elsevier Ltd. All rights reserved.

Social behaviour of collared peccaries (Pecari tajacu) under three space allowances

Captive breeding of peccaries is on the increase in neotropical countries. Few studies, however, have reported behavioural responses of wild animals under farmed conditions. Therefore, the aim of this study was to evaluate the effects of space allowance on the occurrence of social behaviour patterns on farmed collared peccary (Pecan tajacu). We observed three herds of collared peccaries each containing eight acquainted individuals. Using a 3 x 3 Latin square design, herds were allocated, in a random order, to one of the three experimental enclosures, each with a different size. 375, 750 and 1,500 m(2) of total available area, each with three wooden shelters. We recorded all the occurrences of selected positive and agonistic behavioural patterns that occurred 90 min before and during feeding Enclosure size had a significant effect on agonistic patterns of peccaries during feeding, in that more agonistic behaviour was observed in smaller spaces We also found that shelter usage increased as space decreased Differing space allowances, however, did not have an effect on the occurrence of positive interactions that were more frequent before compared to during feeding. We concluded that enclosure size had an effect on the expression of agonistic be and the use of shelters by collared peccaries Thus, animal welfare can be improved by adopting at least 187 5 m(2) per peccary. In addition, our study also confirmed the importance of shelter areas in collared peccary husbandry.

Evaluation of the role of environmental factors in the human gastrointestinal tract on the behaviour of probiotic cultures of Lactobacillus casei Shirota and Lactobacillus casei LC01 by the use of a semi-dynamic in vitro model

This study evaluated the influence of gastrointestinal environmental factors (pH, digestive enzymes, food components, medicaments) on the survival of Lactobacillus casei Shirota and Lactobacillus casei LC01, using a semi-dynamic in vitro model that simulates the transit of microorganisms through the human GIT. The strains were first exposed to different simulated gastric juices for different periods of time (0, 30, 60 and 120 min), and then to simulated intestinal fluids for zero, 120, 180 and 240 min, in a step-wise format. The number of viable cells was determined after each step. The influence of food residues (skim milk) in the fluids and resistance to medicaments commonly used for varied therapeutic purposes (analgesics, antiarrhythmics, antibiotics, antihistaminics, proton pump inhibitors, etc.) were also evaluated. Results indicated that survival of both cultures was pH and time dependent, and digestive enzymes had little influence. Milk components presented a protective effect, and medicaments, especially anti-inflammatory drugs, influenced markedly the viability of the probiotic cultures, indicating that the beneficial effects of the two probiotic cultures to health are dependent of environmental factors encountered in the human gastrointestinal tract.

Exploring Change in Neanderthal Behavioural Complexity: An Innovative Approach to the Study of Neanderthal Behaviour

Diachronic approaches provide potential for a more sophisticated framework within which to examine change in Neanderthal behavioural complexity using archaeological proxies such as symbolic artefacts, faunal assemblages and technology. Analysis of the temporal appearance and distribution of such artefacts and assemblages provide the basis for identifying changes in Neanderthal behavioural complexity in terms of symbolism, faunal extraction and technology respectively. Although changes in technology and faunal extraction were examined in the wider study, only the results of the symbolic study are presented below to illustrate the potential of the approach.

Organizational behaviour: An emotions perspective

This opening chapter provides an overview of organizational behavior theory and research and the paradigms that have dominated the field to date. Running through a discussion of rational notions of organizational behavior, to concepts of bounded rationality and most recently the call for bounded emotionality perspectives, we identify for the reader what a bounded emotionality perspective adds to the understanding of organizations. We then provide an overview of the remaining chapters in the book and how they contribute to the book's objectives.

Effects of egg load on the host-selection behaviour of Helicoverpa armigera (Hubner) (Lepidoptera : Noctuidae)

We examined the effect of age-specific fecundity, mated status, and egg load on host-plant selection, by Helicoverpa armigera under laboratory conditions. The physiological state of a female moth (number of mature eggs produced) greatly influences her host-plant specificity and propensity to oviposit (oviposition motivation). Female moths were less discriminating against cowpea (a low-ranked host) relative to maize (a high-ranked host) as egg load increased. Similarly, increased egg load led to a greater propensity to oviposit on both cowpea and maize. Distribution of oviposition with age of mated females peaked shortly after mating and declined steadily thereafter until death. Most mated females (88%) carried only a single spermatophore, a few females (12%) contained two. The significance of these findings in relation to host-plant selection by H. armigera, and its management, are discussed.

Corrosion behaviour of AZ21, AZ501 and AZ91 in sodium chloride

The corrosion behaviour of AZ21, AZ501 and AZ91 was studied in 1 N NaCl at pH 11 by measuring electrochemical polarization curves, electrochemical AC impedance spectroscopy (EIS) and simultaneously measuring the hydrogen evolution rate and the: magnesium dissolution rate. The corrosion rates increased in the following order: AZ501 < AZ21 < AZ91. The: corrosion behaviour was related to alloy microstructure as revealed by optical and electron microscopy. The beta phase was very stable in the test solution and was an effective cathode. The beta phase served two roles, as a barrier and as a galvanic cathode. If the beta phase is present in the alpha matrix as intergranular precipitates with a small volume fraction, then the beta phase mainly serves as a galvanic cathode, and accelerates the corrosion of the alpha matrix. If the beta Fraction is high, then the beta phase may mainly act as an anodic barrier to inhibit the overall corrosion of the alloy. The composition and compositional distribution in the alpha phase is also crucial to the overall corrosion performance of dual phase alloys. Increasing the aluminum concentration in the alpha phase increases the anodic dissolution rate and also increases the cathodic hydrogen evolution rate. Increasing the zinc concentration in the alpha phase may have the opposite effect. (C) 1998 Elsevier Science Ltd. All rights reserved.

Modelling dispersal behaviour on a fractal landscape

We use a spatially explicit population model to explore the population consequences of different habitat selection mechanisms on landscapes with fractal variation in habitat quality. We consider dispersal strategies ranging from random walks to perfect habitat selectors for two species of arboreal marsupial, the greater glider (Petauroides volans) and the mountain brushtail possum (Trichosurus caninus). In this model increasing habitat selection means individuals obtain higher quality territories, but experience increased mortality during dispersal. The net effect is that population sizes are smaller when individuals actively select habitat. We find positive relationships between habitat quality and population size can occur when individuals do not use information about the entire landscape when habitat quality is spatially autocorrelated. We also find that individual behaviour can mitigate the negative effects of spatial variation on population average survival and fecundity. (C) 1998 Elsevier Science Ltd. All rights reserved.

Rheological behaviour of the mushy zone and its effect on the formation of casting defects during solidification

A new conceptual framework has been developed which explains the formation of shear-related casting defects such as porosity, segregation and tears. The theory relates defect formation to the mechanical behaviour of the partially solidified microstructure when shear stresses are developed during the filling of a casting and by the subsequent feeding processes during solidification. Two transition points, the dendrite coherency point and the maximum packing solid fraction, divide the mushy zone into three regions of different mechanical and feeding behaviours. The response of the mush to shear is related to the presence of these zones during solidification of a casting. The resulting defects are rationalized by considering the governing local shear stress and shear rate, local strength and time available for fluid flow. The design of the casting, the casting process used and the alloy composition all influence the relative importance of shearing on defect formation. (C) 1998 Acta Metallurgica Inc. Published by Elsevier Science Ltd. All rights reserved.

HIV risk behaviour and prevention in prison: a bleach programme for inmates in NSW

One hundred and eighty-one inmates in AIDS education courses were surveyed about their risk behaviour and access to disinfectants for syringe cleaning in 1993, Overall, 40% of respondents reported HIV risk behaviour in prison. One-quarter of respondents reported injecting, of whom three-quarters reported sharing syringes in prison. Most respondents who shared syringes reported cleaning them with disinfectants (96%), even though only one-third reported having easy access to disinfectants. One-sixth of respondents reported sharing tattooing equipment, of whom two-thirds reported using a disinfectant to clean the tattoo needle. Few respondents reported fellatio (8%) or anal intercourse (4%) in prison. Although some respondents faced difficulty in obtaining disinfectants, almost all respondents cleaned syringes with bleach when sharing. High levels of risk behaviour in prison might be reduced by methadone maintenance and condom programmes. A trial of strict one-for-one syringe exchange warrants consideration.