164 resultados para Solvothermal


Relevância:

20.00% 20.00%

Publicador:

Resumo:

A kind of carbon nanotube bundle has been synthesized by a simple one-step solvothermal reaction between Na and hexachlorobenzene (HCB) using NiCl2 as catalyst precursor. Before the reaction, NiCl2 was initially dispersed ultrasonically in cyclohexane then prereduced by Na at 230degreesC to produce small Ni particles in reduced state. The tubes thus-produced have a uniform outer diameter of about 20 nm, an inner diameter of 4 nm, and are highly ordered assembled as bundles which have a 2D hexagonal arrangement as proven by SAXS and TEM experiments.

Relevância:

20.00% 20.00%

Publicador:

Resumo:

Luminescent Ln (Eu3+, Tb3+) doped hydroxyapatite (Eu:HAp, Tb:HAp) phosphors were successfully fabricated via the cetyltrimethylammonium bromide (CTAB)/n-octane/n-butanol/water microemulsion-mediated solvothermal process. The structure, morphology, and optical properties were systematically characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray photoelectron spectra (XPS), Fourier transform infrared spectroscopy (FT-IR), and photoluminescence (PL) spectra as well as the kinetic decays, respectively.

Relevância:

20.00% 20.00%

Publicador:

Resumo:

Novel three-dimensional (3D) flowerlike MnWO4 micro/nanocomposite structure has been successfully synthesized for the first time. The synthesized products were systematically studied by X-ray powder diffraction (XRD), field-emission scanning electron microscopy (FESEM) and transmission electron microscopy (TEM) and photoluminescence (PL) spectra. It is found that both reaction time and temperature have significant effects on the morphology of the products.

Relevância:

20.00% 20.00%

Publicador:

Resumo:

One-dimensional hexagonal Ba2CIF3 microrods with highly uniform morphology and size have been successfully synthesized via a facile solvothermal method at a low temperature (160 degrees C). X-ray diffraction (XRD), scanning electron microscopy (SEM), and transmission electron microscopy (TEM) were used to characterize the samples. The synthesis process, based on a phase-transfer and separation mechanism, allows the control of properties such as particle size and shape in low dispersity by bonding the surfactant oleic acid to the crystal surface.

Relevância:

20.00% 20.00%

Publicador:

Resumo:

Highly crystalline and nearly monodisperse In2O3 nanocrystals with both cube and flower shapes were successfully synthesized in one step through a facile aqueous solvothermal method for the first time, free of any surfactant or template. X-ray diffraction (XRD), transmission electron microscopy (TEM), selective area electron diffraction (SAED), and high-resolution transmission electron microscopy (HRTEM) were used to characterize the samples. In our work, the use of diethylene glycol (DEG) is a crucial factor for the formation of the In2O3 phase.

Relevância:

20.00% 20.00%

Publicador:

Resumo:

MF2 (M = Ca, Sr, Ba) nanocrystals (NCs) were synthesized via a solvothermal process in the presence of oleic acid and characterized by x-ray diffraction (XRD), transmission electron microscopy (TEM), Fourier transform infrared (FT-IR) spectra, UV/vis absorption spectra, photoluminescence (PL) excitation and emission spectra, and lifetimes, respectively. In the synthetic process, oleic acid as a surfactant played a crucial role in confining the growth and solubility of the MF2 NCs. The as-prepared CaF2, SrF2 and BaF2 NCs present morphologies of truncated octahedron, cube and sheet in a narrow distribution, respectively.

Relevância:

20.00% 20.00%

Publicador:

Resumo:

By using ethylenediamine as both an alkali and ligand, quantum size SnO2, nanocrystallites were synthesized with a solvothermal route. The transmission electron micrographs (TEM) were employed to characterize the morphologies of the products. The crystal sizes of the as-synthesized SnO2 were ranged form 2.5 to 3.6 nm. The crystal structure and optical properties of the products were investigated by X-ray diffraction, Fourier transform infrared spectroscopy, optical absorption spectra, photoluminescence and Raman spectra.

Relevância:

20.00% 20.00%

Publicador:

Resumo:

Submicrometer zinc oxide (ZnO) with different morphologies including spindle-like, pencil-like, branch rod-like and frizzy flower-like shapes, have been hydrothermally synthesized in mixed solvents of ethanol and water at 140 degrees C. It was found that the volumes of added ammonia, surfactant (cetyltrimethylammonium bromide, CTAB), and mixed solvent play crucial roles in morphological control of ZnO nanostructures. Increasing the volume of ammonia added to the reaction system, the shape of ZnO evolves from spindle into branch rod-like. Synergetic influence between CTAB and ammonia can only be observed at high concentration of ammonia.

Relevância:

20.00% 20.00%

Publicador:

Resumo:

Well-dispersed YVO4:Ln(3+) (Ln = Eu, Dy, and Sm) nanocrystals with uniform morphology and size have been synthesized via a facile solvothermal route. XRD results demonstrate that all of the three samples can be well indexed to the pure tetragonal phase Of YVO4, indicating that the Eu3+, Dy3+, and Sm3+ have been effectively doped into the host lattices of YVO4. TEM images show that the YVO4 nanocrystals exhibit ellipsoid shape and a mean size of about 20 nm, which is in good agreement with the estimation of XRD results.

Relevância:

20.00% 20.00%

Publicador:

Resumo:

Strontium hydroxyapatite (Sr-5(PO4)(3)OH, SrHAp) microspheres with 3D architectures have been successfully prepared through a efficient and facile solvothermal process. The experimental results indicate that the SrHAP microspheres are composed of a large amount of nanosheets, which are assembled in a radial form from the center to the surface of the microspheres. The as-obtained SrHAp samples show an intense and bright blue emission from 350 to 570 nm centered at 427 nm (CIE coordinates: x = 0.153, y = 0.081; lifetime: 9.2 ns; quantum efficiency: 31%) under long-wavelength UV light excitation (344 nm). This blue emission might result from the CO2 center dot- radical impurities in the crystal lattice. Furthermore, the surfactants CTAB and trisodium citrate have an obvious impact on the morphologies and the luminescence properties of the products, respectively.

Relevância:

20.00% 20.00%

Publicador:

Resumo:

Complex metal fluoride NaMgF3 nanocrystals were successfully synthesized via a solvothermal method at a relatively low temperature with the presence of oleic acid, and characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), Fourier transform infrared (FT-IR) spectra, photoluminescence (PL) excitation and emission spectra, respectively. fit the synthetic process, oleic acid as a Surfactant played a Crucial role in confining the growth and solubility of the NaMgF3 nanocrystals. The as-prepared NaMgF3 nanocrystals have quasi-spherical shape with a narrow distribution. A possible formation mechanism of the nanocrystals was proposed based on the effect of oleic acid. The as-prepared NaMgF3 nanocrystals are highly crystalline and well-dispersed in cyclohexane to form stable and clear colloidal Solutions, which demonstrate a strong emission band centered at 400 nm in photoluminescence (PL) spectra compared with the cyclohexane solvent.

Relevância:

20.00% 20.00%

Publicador:

Resumo:

Rare-earth ions (Eu3+, Tb3+) doped AMoO(4) (A = Sr, Ba) particles with uniform morphologies were successfully prepared through a facile solvothermal process using ethylene glycol (EG) as protecting agent. X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray photoelectron spectra (XPS), Fourier transform infrared spectroscopy (FT-IR), photoluminescence (PL) spectra and the kinetic decays were performed to characterize these samples. The XRD results reveal that all the doped samples are of high purity and crystallinity and assigned to the tetragonal scheelite-type structure of the AMoO(4) phase. It has been shown that the as-synthesized SrMoO4:Ln and BaMoO4:Ln samples show respective uniform pea nut-like and oval morphologies with narrowsize distribution. The possible growth process of the AMoO(4):Ln has been investigated in detail. The EG/H2O volume ratio, reaction temperature and time have obvious effect on themorphologies and sizes of the as-synthesized products.

Relevância:

20.00% 20.00%

Publicador:

Resumo:

Monodisperse rare-earth ion (Eu3+, Ce3+, Tb3+) doped LaPO4 particles with oval morphology were successfully prepared through a facile solvothermal process without further hear treatment. X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray photoelectron spectra (XPS), Fourier transform infrared spectroscopy (FT-IR), photoluminescence (PL) spectra and the kinetic decays were performed to characterize these samples. The XRD results reveal that all the doped samples are well crystalline at 180 degrees C and assigned to the monoclinic monazite-type structure of the LaPO4 phase. It has been shown that all the as-synthesized samples show perfectly oval morphology with narrow size distribution. The possible growth mechanism of the LapO(4):Ln has been investigated as well.

Relevância:

20.00% 20.00%

Publicador:

Resumo:

Through a facile solvothermal route using zinc chloride and thiourea as reactants, wurtzite ZnS and its precursor ZnS center dot (en)(0.5) (en = ethylenediamine) with various morphologies and sizes were grown, which were characterized by XRD, SEM, TEM and N-2 adsorption and so on. The phase evolution, composition and morphologies of the products are highly dependent on the concentration of en. By keeping the en-water volume ratio at 1/2 to 1, the nanostripes-flower or nanorod-spheric wurtzite ZnS were easily obtained under 120 degrees C for 6-24 h, which possess relatively higher specific surface area and larger total pore volume.