Thermal study of the solid-state reactions on Pt-15%Rh/Hg system

Thermogravimetry (TG), energy dispersive X-ray microanalysis (EDX), scanning electron microscopy (SEM), mapping surface and X-ray diffraction (XRD) were used for the study of solid-state reaction on Pt-15%Rh with electrodeposited mercury. The results suggest when heated the mercury film react with the Pt-15%Rh alloy to form intermetallics having different thermal stabilities indicated by three mass loss steps. The first mass loss step occurs between room temperature and 184 degrees C only the bulk Hg is removed and PtHg4, PtHg2 and RhHg2 were characterized by XRD. The second step, between 184 and 271 degrees C, was attributed to PtHg4 decomposition with formation of PtHg2 stabilized by RhHg2. The third step, between 271 and 340 degrees C, was attributed to decomposition of a solid-solution of PtHg2/RhHg2. The fourth step, between 340 and 600 degrees C, was ascribed to: (1) a thermal decomposition of PtHg2, formed by a PtHg eutectoid reaction (similar to 340 degrees C) on the surface and (2) Hg removal from a solid solution of Pt-15%Rh(Hg). (C) 2013 Elsevier B.V. All rights reserved.

Highly selective sulfur transfer reaction in the solid state

Benzyltriethylammonium tetrathiomolybdate 1 reacts readily with benzyl halides, alkyl iodides and acyl halides in the solid state to give the corresponding disulfides in good yields and with remarkable selectivity.

Reaction of La2CuO4 with binary metal oxides in the solid state: Metathesis, addition, and redox metathesis pathways

Investigation of the reaction of La2CuO4 with several binary metal oxides in the solid state at elevated temperatures has revealed three different reaction pathways. Reaction of La2CuO4 with strongly acidic oxides such as Re2O7, MoO3, and V2O5 follows a metathesis route, yielding a mixture of products: La3ReO8/La2MoO6/LaVO4 and CuO. Oxides such as TiO2, MnO2, and RuO2 which are not so acidic yield addition products: La2CuMO6 (M = Ti, Mn, Ru). SnO2 is a special case which appears to follow a metathesis route, giving La2Sn2O7 pyrochlore and CuO, which on prolonged reaction transform to the layered perovskite La2CuSnO6. The reaction of La2CuO4 with lower valence oxides VO2 and MoO2, on the other hand, follows a novel redox metathesis route, yielding a mixture of LaVO4/LaCuO2 and La2MoO6/Cu, respectively. This result indicates that it is the redox reactivity involving V-IV + Cu-II --> V-V + Cu-I and Mo-IV + Cu-II --> Mo-VI + Cu-0, and not the acidity of the binary oxide, that controls the nature of the products formed in these cases. The general significance of these results toward the synthesis of complex metal oxides containing several metal atoms is discussed.

Crystal chemistry and photomechanical behavior of 3,4-dimethoxycinnamic acid: correlation between maximum yield in the solid-state topochemical reaction and cooperative molecular motion

A new monoclinic polymorph, form II (P2(1)/c, Z = 4), has been isolated for 3,4-dimethoxycinnamic acid (DMCA). Its solid-state 2 + 2 photoreaction to the corresponding alpha-truxillic acid is different from that of the first polymorph, the triclinic form I (P (1) over bar, Z = 4) that was reported in 1984. The crystal structures of the two forms are rather different. The two polymorphs also exhibit different photomechanical properties. Form I exhibits photosalient behavior but this effect is absent in form II. These properties can be explained on the basis of the crystal packing in the two forms. The nanoindentation technique is used to shed further insights into these structure-property relationships. A faster photoreaction in form I and a higher yield in form II are rationalized on the basis of the mechanical properties of the individual crystal forms. It is suggested that both Schmidt-type and Kaupp-type topochemistry are applicable for the solid-state trans-cinnamic acid photodimerization reaction. Form I of DMCA is more plastic and seems to react under Kaupp-type conditions with maximum molecular movements. Form II is more brittle, and its interlocked structure seems to favor Schmidt-type topochemistry with minimum molecular movement.

Optical and photocatalytic properties of nanocrystalline TiO2 synthesised by solid-state chemical reaction

Nanoparticulate TiO₂ is of interest for a variety of technological applications, including optically transparent UV-filters and photocatalysts for the destruction of chemical waste. The successful use of nanoparticulate TiO₂ in such applications requires an understanding of how the synthesis conditions effect the optical and photocatalytic properties. In this study, we have investigated the effect of heat treatment temperature on the properties of nanoparticulate TiO₂ powders that were synthesised by solid-state chemical reaction of anhydrous TiOSO₄ with Na₂CO₃. It was found that the photocatalytic activity increased with the heat treatment temperature up to a maximum at 600 °C and thereafter declined. In contrast, the optical transparency decreased monotonically with the heat treatment temperature. These results indicate that solid-state chemical reaction can be used to prepare powders of nanoparticulate TiO₂ with properties that are optimised for use as either optically transparent UV-filters or photocatalysts.

In situ solid state oxidation reaction for La1-xSrxMnO3 (x=0, 0.1, 0.2 and 0.3) formation

In situ solid state oxidation reaction for an alternative La1-xSrxMnO3 (x = 0, 0.1, 0.2 and 0.3) formation is reported. Samples have been obtained by using strontium peroxide, lanthanum and manganese (III) oxide reagents. Strontium peroxide has induced the oxidation of Mn+3 to Mn+4. Lanthanum strontium-doped manganite was obtained without secondary phase formation. La0.825Sr0.175MnO3 showed two structural transitions. The first from 88 to 373 K and the second at 1073 K. which are explained by Jahn-Teller effect at low temperature and cation displacement at high temperature. (C) 2001 Elsevier B.V. B.V. All rights reserved.

Thermal and crystalographic studies of mixture La2O3-SrO prepared via reaction in the solid state

The compound obtained via state solid reaction of the La2O3 and SrO oxides and expose the room atmosphere shows the crystallographic data of the compound reported as La2SrOx. However, thermogravimetric, differential thermal analysis and XRD with controlled temperature indicated that the stoichiometry of the compound is 2La(OH)(3)-SrCO3, which structural parameters were determined by using the Rietveld method. It was verified that when the compound exposed at room atmosphere, the mixture oxide absorbs H2O and CO2 producing hydroxide and carbonate of lanthanum and strontium, respectively, which thermal decomposition occurs by the same steps, producing the La2O3-SrO.

Reaction pathways in the solid state synthesis of multiferroic BiFeO 3

The obtaining of multiferroicBiFeO3 as a pure single-phase product is particularly complex since the formation of secondary phases seems to be unavoidable. The process by which these secondary impurities are formed is studied by analyzing the diffusion and solidstate reactivity of the Bi2O3–Fe2O3 system. Experimental evidence is reported which indicates that the progressive diffusion of Bi3+ ions into the Fe2O3 particles governs the solidstatesynthesis of the perovskite BiFeO3 phase. However a competition is established between the diffusion process which tends to complete the formation of BiFeO3, and the crystallization of stable Bi2Fe4O9 mullite crystals, which tend to block that formation reaction.

Reaction pathways in the solid state synthesis of multiferroic BiFeO3

The obtaining of multiferroic BiFeO3 as a pure single-phase product is particularly complex since the formation of secondary phases seems to be unavoidable. The process by which these secondary impurities are formed is studied by analyzing the diffusion and solid state reactivity of the Bi2O3?Fe2O3 system. Experimental evidence is reported which indicates that the progressive diffusion of Bi3+ ions into the Fe2O3 particles governs the solid state synthesis of the perovskite BiFeO3 phase. However a competition is established between the diffusion process which tends to complete the formation of BiFeO3, and the crystallization of stable Bi2Fe4O9 mullite crystals, which tend to block that formation reaction.

Photochemically induced nuclear spin polarization in reaction centers of photosystem II observed by 13C-solid-state NMR reveals a strongly asymmetric electronic structure of the P680.+ primary donor chlorophyll

We report 13C magic angle spinning NMR observation of photochemically induced dynamic nuclear spin polarization (photo- CIDNP) in the reaction center (RC) of photosystem II (PS2). The light-enhanced NMR signals of the natural abundance 13C provide information on the electronic structure of the primary electron donor P680 (chlorophyll a molecules absorbing around 680 nm) and on the pz spin density pattern in its oxidized form, P680⨥. Most centerband signals can be attributed to a single chlorophyll a (Chl a) cofactor that has little interaction with other pigments. The chemical shift anisotropy of the most intense signals is characteristic for aromatic carbon atoms. The data reveal a pronounced asymmetry of the electronic spin density distribution within the P680⨥. PS2 shows only a single broad and intense emissive signal, which is assigned to both the C-10 and C-15 methine carbon atoms. The spin density appears shifted toward ring III. This shift is remarkable, because, for monomeric Chl a radical cations in solution, the region of highest spin density is around ring II. It leads to a first hypothesis as to how the planet can provide itself with the chemical potential to split water and generate an oxygen atmosphere using the Chl a macroaromatic cycle. A local electrostatic field close to ring III can polarize the electronic charge and associated spin density and increase the redox potential of P680 by stabilizing the highest occupied molecular orbital, without a major change of color. This field could be produced, e.g., by protonation of the keto group of ring V. Finally, the radical cation electronic structure in PS2 is different from that in the bacterial RC, which shows at least four emissive centerbands, indicating a symmetric spin density distribution over the entire bacteriochlorophyll macrocycle.

Natural abundance solid-state carbon NMR studies of photosynthetic reaction centers with photoinduced polarization.

Solid-state NMR spectra of natural abundance 13C in reaction centers from photosynthetic bacteria Rhodobacter sphaeroides R-26 was measured. When the quinone acceptors were removed and continuous visible illumination of the sample was provided, exceptionally strong nuclear spin polarization was observed in NMR lines with chemical shifts resembling those of the aromatic carbons in bacteriochlorophyll and bacteriopheophytin. The observation of spin polarized 15N nuclei in bacteriochlorophyll and bacteriopheophytin was previously demonstrated with nonspecifically 15N-labeled reaction centers. Both the carbon and the nitrogen NMR studies indicate that the polarization is developed on species that carry unpaired electrons in the early electron transfer steps, including the bacteriochlorophyll dimer donor P860 and probably the bacteriopheophytin acceptor. I. Both enhanced-absorptive and emissive polarization were seen in the carbon spectrum; most lines were absorptive but the methine carbons of the porphyrin ring (alpha, beta, gamma, ) exhibited emissive polarization. The change in the sign of the hyperfine coupling at these sites indicates the existence of nodes in the spin density distribution on the tetrapyrrole cofactors flanking each methine carbon bridge.

Solid-state structure of some substituted hexahydro-1,4:5,8-diepoxy­naphthalenes

The structure of several carboxy-substituted hexahydro-1,4:5,8-diepoxynaphthalenes have been solved with X-ray crystallography, in some cases confirming previously contentious structures. The compounds of interest are constructed in efficient one-step 2 × [4+2] cycloaddition reactions from furan and acetylene carboxylate derivatives.

Unusual photodimerization of 7-fluoro-4-methylcoumarin and 6-fluoro-4-methylcoumarin in the solid state

Photodimerization of 7-fluoro-4-methylcoumarin 1 is topochemical while 6-fluoro-4-methylcoumarin 2 does not lead to the expected product based on the topochemical principles. Compound 1 yield an anti-MT photodimer with a lower dimer conversion while compound 2 results in a syn-HH photodimer. The packing features of 1, 2 and 2a (the photodimer of 2) have been unequivocally established by single crystal X-ray diffraction studies. The rationale for the significant lower dimer conversion in 1 is provided. The defect induced dimerization reaction in 2 as a function of temperature is analyzed which verifies that the reaction proceeds with an induction period. The details of the interactions involving fluorine are analyzed.