La0.8Sr0.2Mn1.1O3 (LSM1.1)-10 mol% Sc2O3-Stabilized ZrO2 co-doped with CeO2 (ScSZ) composite cathodes were investigated for anode-supported solid oxide fuel cells (SOFCs) with thin 8 mol% Y2O3-stabilized ZrO2 (YSZ) electrolyte. X-ray diffraction (XRD) results indicated that the ScSZ electrolytes displayed good chemical compatibility with the nonstoichiometric LSM1.1 against co-firing at 1300 degrees C. Increasing the CeO2 content in the ScSZ electrolytes dramatically suppressed the electrode polarization resistance, which may be related to the improved surface oxygen exchange or the enlarged active area of cathode. The 5Ce10ScZr was the best electrolyte for the composite cathodes, which caused a small ohmic resistance decrease and the reduced polarization resistance and brought about the highest cell performance. The cell performances at lower temperatures seemed to rely on the electrode polarization resistance more seriously, than the ohmic resistance. Compared with the cell impedance at higher temperatures, the higher the 5Ce10ScZr proportion in the composite cathodes, the smaller the increment of the charge transfer resistance at lower temperatures. The anode-supported SOFC with the LSM1.1-5Ce10ScZr (60:40) composite cathode achieved the maximum power densities of 0.82 W/cm(2) at 650 degrees C and 2.24 W/cm(2) at 800 degrees C, respectively. (c) 2005 Elsevier B.V. All rights reserved.

Co-tape casting fabrication, field assistant sintering and evaluation of a coke resistant La0.2Sr0.7TiO3-Ni/YSZ functional gradient anode supported solid oxide fuel cell

The ability to directly utilize hydrocarbons and other renewable liquid fuels is one of the most important issues affecting the large scale deployment of solid oxide fuel cells (SOFCs). Herein we designed La_0.2Sr_0.7TiO₃-Ni/YSZ functional gradient anode (FGA) supported SOFCs, prepared with a co-tape casting method and sintered using the field assisted sintering technique (FAST). Through SEM observations, it was confirmed that the FGA structure was achieved and well maintained after the FAST process. Distortion and delamination which usually results after conventional sintering was successfully avoided. The La_0.2Sr_0.7TiO₃-Ni/YSZ FGA supported SOFCs showed a maximum power density of 600mWcm^-2 at 750°C, and was stable for 70h in CH₄. No carbon deposition was detected using Raman spectroscopy. These results confirm the potential coke resistance of La_0.2Sr_0.7TiO₃-Ni/YSZ FGA supported SOFCs.

Understanding the Flash Sintering of Rare-Earth-Doped Ceria for Solid Oxide Fuel Cell

A novel electrical current applied technique known as flash sintering has been applied to rapidly (within 10 min) densify electrolytes including Ce_0.8Gd_0.2O_1.9 (GDC20), Ce_0.9Gd_0.1O_1.95 (GDC10), and Ce_0.8Sm_0.2O_1.9 (SDC20) for application in Solid Oxide Fuel Cells (SOFCs). The densification temperature for the three electrolytes was 554°C, 635°C, and 667°C, respectively, which is far below conventional sintering temperatures. All specimens after flash sintering maintained the pure fluorite structure and exhibited a well-densified microstructure. To investigate the flash-sintering mechanism, we have applied Joule heating effect with blackbody radiation theory, and found that this theory could reasonably interpret the flash-sintering phenomenon by matching theoretically calculated temperature with the real temperature. More importantly, one of the materials inherent properties, the electronic conductivity, has been found correlated with the onset of flash sintering, which indicates that the electrons and holes are the primary current carriers during the start of flash-sintering process. As a result, potential densification mechanisms have been discussed in terms of spark plasma discharge.

Investigation into the effect of molybdenum-site substitution on the performance of Sr2Fe1.5Mo0.5O6-δ for intermediate temperature solid oxide fuel cells

In this paper, niobium doping is evaluated as a means of enhancing the electrochemical performance of a Sr₂Fe_1.5Mo_0.5O_6-δ (SFM) perovskite structure cathode material for intermediate temperature solid oxide fuel cells (IT-SOFCs) applications. As the radius of Nb approximates that of Mo and exhibits +4/+5 mixed valences, its substitution is expected to improve material performance. A series of Sr₂Fe_1.5Mo_0.5-xNb_xO_6-δ (x = 0.05, 0.10, 0.15, 0.20) cathode materials are prepared and the phase structure, chemical compatibility, microstructure, electrical conductivity, polarization resistance and power generation are systematically characterized. Among the series of samples, Sr₂Fe_1.5Mo_0.4Nb_0.10O_6-δ (SFMNb_0.10) exhibits the highest conductivity value of 30 S cm^-1 at 550°C, and the lowest area specific resistance of 0.068 Ω cm² at 800°C. Furthermore, an anode-supported single cell incorporating a SFMNb_0.10 cathode presents a maximum power density of 1102 mW cm^-2 at 800°C. Furthermore no obvious performance degradation is observed over 15 h at 750°C with wet H₂(3% H₂O) as fuel and ambient air as the oxidant. These results demonstrate that SFMNb shows great promise as a novel cathode material for IT-SOFCs.

Reduction kinetics of NiO-YSZ composite for application in solid oxide fuel cell

A porous nickel-8 mol% yttria stabilized zirconia (Ni-8YSZ) composite, used as anode for solid oxide fuel cell, was obtained by reduction of NiO-8YSZ cermet. The first goal was the evaluation of the temperature effect of powder processing by thermogravimetry. In addition, the influence of porosity in the reduction kinetic of the sample sintered at 1450 A degrees C was evaluated. The final porosity produced in NiO-8YSZ composite by pore former was 30.4 and 37.9 vol.%, respectively, for 10 and 15 mass% of corn starch. The sample with 15 mass% of corn starch promotes a reduction rate almost twice higher than sample with 10 mass% of corn starch. The porosity introduced by the reduction of NiO was 23 vol.%.

High performance cobalt-free perovskite cathode for intermediate temperature solid oxide fuel cells

Bi doping of SrFeO3d results in the formation of a structure with high symmetry and extraordinary electrochemical performance for Bi0.5Sr0.5FeO3-d, which is capable of competing effectively with the current Co-based cathode benchmark with additional advantages of lower thermal expansion and cost.

Characterization and evaluation of BaCo0.7Fe0.2Nb0.1O3−δ as a cathode for proton-conducting solid oxide fuel cells

This study characterizes BaCo0.7Fe0.2Nb0.1O3−δ (BCFN) perovskite oxide and evaluates it as a potential cathode material for proton-conducting SOFCs with a BaZr0.1Ce0.7Y0.2O3-δ (BZCY) electrolyte. A four-probe DC conductivity measurement demonstrated that BCFN has a modest electrical conductivity of 2–15 S cm−1 in air with p-type semiconducting behavior. An electrical conductivity relaxation test showed that BCFN has higher Dchem and Kchem than the well-known Ba0.5Sr0.5Co0.8Fe0.2O3−δ oxide. In addition, it has relatively low thermal expansion coefficients (TECs) with values of 18.2 × 10−6 K−1 and 14.4 × 10−6 K−1 at temperature ranges of 30–900 °C and 30–500 °C, respectively. The phase reaction between BCFN and BZCY was investigated using powder and pellet reactions. EDX and XRD characterizations demonstrated that BCFN had lower reactivity with the BZCY electrolyte than strontium-containing perovskite oxides such as SrCo0.9Nb0.1O3-δ and Ba0.6Sr0.4Co0.9Nb0.1O3−δ. The impedance of BCFN was oxygen partial pressure dependent. Introducing water into the cathode atmosphere reduced the size of both the high-frequency and low-frequency arcs of the impedance spectra due to facilitated proton hopping. The cathode polarization resistance and overpotential at a current density of 100 mA cm−2 were 0.85 Ω cm−2 and 110 mV in dry air, which decreased to 0.43 Ω cm−2 and 52 mV, respectively, in wet air (∼3% H2O) at 650 °C. A decrease in impedance was also observed with polarization time; this was possibly caused by polarization-induced microstructure optimization. A promising peak power density of ∼585 mW cm−2 was demonstrated by an anode-supported cell with a BCFN cathode at 700 °C.

Deactivation and regeneration of oxygen reduction reactivity on double perovskite Ba2Bi0.1Sc0.2Co1.7O6−x cathode for intermediate-temperature solid oxide fuel cells

in situ high-temperature X-ray diffraction and thermal gravimetric- differential thermal analysis on room-temperature powder, as well as X-ray diffraction, Raman spectroscopy, and transmission electron microscopy on quenched powder, were applied to study crystal structure and phase transformations in Ba₂Bi_0.1Sc_0.2Co _1.7O_6-x (BBSC). Heating BBSC in air to over 800 °C produces a pure cubic phase with space group Fm3m (no. 225), and cooling down below 800 °C leads to a mixture of three noncubic phases including an unknown phase between 200 and 650 °C, a 2H hexagonal BaCoO3 with space group P63/mmc (no. 194) between 600 and 800 °C, and an intermediate phase at 800 °C. These three phases exist concurrently with the major cubic phase. The weight gain and loss between 300 and 900 °C suggest the occurrence of cobalt reduction, oxidation, and disproportion reactions with dominant reduction reaction at above 600 °C. The thermal expansion of BBSC was also examined by dilatometry. BBSC has a highly temperature-dependent thermal expansion coefficient which relates well with its structure evolution. Furthermore, the oxygen reduction reaction (ORR) of BBSC was probed by symmetrical cell and three-electrode configurations. The presence of hexagonal phase at 700 °C rarely affects the ORR performance of BBSC as evidenced by a slight increase of its area-specific resistance (ASR) value following 48 h of testing in this three-electrode configuration. This observation is in contrast to the commonly held point of view that noncubic phase deteriorates performance of perovskite compounds (especially in oxygen transport applications). Moreover, cathodic polarization treatment, for example, current discharge from BBSC (tested in three-electrode configuration), can be utilized to recover the original ORR performance. The cubic structure seems to be retained on the cathodic polarization - the normal cathode operating mode in fuel cells. Stable 72-h performance of BBSC in cathodic polarization mode further confirms that despite the presence of phase impurities, BBSC still demonstrates good performance between 500 and 700 °C, the desired intermediate operating temperature in solid oxide fuel cells.

A single-step synthesized cobalt-free barium ferrites-based composite cathode for intermediate temperature solid oxide fuel cells

Cobalt-free perovskite cathode with excellent oxygen reduction reaction (ORR) properties below 800 °C is a key material toward wide implementation of intermediate-temperature solid oxide fuel cells. This work reports the phase structure, microstructure and performance of such cathode based on the composite phases of triclinic Ba0.9Bi0.1FeO3-δ, cubic BaFeO3 and orthorhombic BaFe2O4 prepared by sol–gel route. The resultant barium ferrites composite cathode exhibits uniform particles, pores and elements distribution. In particular, favorable ORR properties of this cathode is demonstrated by very low interfacial resistance of only 0.036 and 0.072 Ω cm2 at 750 and 700 °C and maximum power density of 1295 and 840 mW cm−2 at 750 and 700 °C.

Development and testing of anode-supported solid oxide fuel cells with slurry-coated electrolyte and cathode

A laboratory setup was designed and put into operation for the development of solid oxide fuel cells (SOFCs). The whole project consisted of the preparation of the component materials: anode, cathode and electrolyte, and the buildup of a hydrogen leaking-free sample chamber with platinum leads and current collectors for measuring the electrochemical properties of single SOFCs. Several anode-supported single SOFCs of the type (ZrO(2):Y(2)O(3)+NiO) thick anode/(ZrO(2):Y(2)O(3)) thin electrolyte/(La(0.65)Sr(0.35)MnO(3)+ZrO(2):Y(2)O(3)) thin cathode have been prepared and tested at 700 and 800 degrees C after in situ H(2) anode reduction. The main results show that the slurry-coating method resulted in single-cells with good reproducibility and reasonable performance, suggesting that this method can be considered for fabrication of SOFCs. (c) 2005 Elsevier B.V. All rights reserved.

Study of a hybrid solid oxide fuel cell: Energetic analysis and sankey diagram

In this paper a hybrid solid oxide fuel cell (SOFC) system is analyzed. This system applies a combined cycle utilizing gas turbine associated to a SOFC for rational decentralized energy production. Initially the relative concepts about the fuel cell are presented, followed by some chemical and technical informations such as the change of Gibbs free energy in isothermal fuel oxidation (or combustion) directly into electricity. This represents a very high fraction of the lower heating value (LHV) of a hydrocarbon fuel. In the next step a methodology for the study of SOFC associated with a gas turbine system is developed, considering the electricity and steam production for a hospital, as regard to the Brazilian conditions. This methodology is applied to energetic analysis. Natural gas is considered as a fuel. In conclusion, it is shown by a Sankey Diagram that the hybrid SOFC system may be an excellent opportunity to strengthen the decentralized energy production in Brazil. It is necessary to consider that the cogeneration in this version also is a sensible alternative from the technical point of view, demanding special methods of design, equipment selection and mainly of the contractual deals associated to electricity and fuel supply.

A Model to Predict Percolation Threshold and Effective Conductivity of Infiltrated Electrodes for Solid Oxide Fuel Cells

We present a mechanistic modeling methodology to predict both the percolation threshold and effective conductivity of infiltrated Solid Oxide Fuel Cell (SOFC) electrodes. The model has been developed to mirror each step of the experimental fabrication process. The primary model output is the infiltrated electrode effective conductivity which provides results over a range of infiltrate loadings that are independent of the chosen electronically conducting material. The percolation threshold is utilized as a valuable output data point directly related to the effective conductivity to compare a wide range of input value choices. The predictive capability of the model is demonstrated by favorable comparison to two separate published experimental studies, one using strontium molybdate and one using La0.8Sr0.2FeO3-δ as infiltrate materials. Effective conductivities and percolation thresholds are shown for varied infiltrate particle size, pore size, and porosity with the infiltrate particle size having the largest impact on the results.