Thermogravimetric analysis of the copper silicate mineral dioptase Cu6[Si6O18]·6H2O

There have been a few studies on the thermal decomposition of dioptase Cu6[Si6O18]·6H2O. The results of these analyses are somewhat conflicting and the conclusions vary among these thermo-analytical studies. The objective of this research is to report the thermal analysis of dioptase from different origins and to show the mechanism of decomposition. Thermal decomposition occurs over a very wide temperature range from around 400 to 730 °C with the loss of water. Two additional mass loss steps are observed at around 793 and 835 °C with loss of oxygen. The infrared spectra of dioptase in the hydroxyl stretching region enables the hydrogen bond distances of water molecules in the dioptase structure to be calculated. The large variation in the hydrogen bond distances offers an explanation as to why the decomposition of dioptase with loss of water occurs over such a wide temperature range.

Thermal analysis and vibrational spectroscopic characterization of the boro silicate mineral datolite – CaBSiO4(OH)

The objective of this work is to determine the thermal stability and vibrational spectra of datolite CaBSiO4(OH) and relate these properties to the structure of the mineral. The thermal analysis of datolite shows a mass loss of 5.83% over a 700–775 °C temperature range. This mass loss corresponds to 1 water (H2O) molecules pfu. A quantitative chemical analysis using electron probe was undertaken. The Raman spectrum of datolite is characterized by bands at 917 and 1077 cm−1 assigned to the symmetric stretching modes of BO and SiO tetrahedra. A very intense Raman band is observed at 3498 cm−1 assigned to the stretching vibration of the OH units in the structure of datolite. BOH out-of-plane vibrations are characterized by the infrared band at 782 cm−1. The vibrational spectra are based upon the structure of datolite based on sheets of four- and eight-membered rings of alternating SiO4 and BO3(OH) tetrahedra with the sheets bonded together by calcium atoms.

Vibrational spectroscopy of the silicate mineral plumbotsumite Pb5(OH)10Si4O8 : an assessment of the molecular structure

We have used scanning electron microscopy with energy dispersive X-ray analysis to determine the precise formula of plumbotsumite, a rare lead silicate mineral of formula Pb5(OH)10Si4O8. This study forms the first systematic study of plumbotsumite from the Bigadic deposits, Turkey. Vibrational spectroscopy was used to assess the molecular structure of plumbotsumite as the structure is not known. The mineral is characterized by sharp Raman bands at 1047, 1055 and 1060 cm−1 assigned to SiO stretching vibrational modes and sharp Raman bands at 673, 683 and 697 cm−1 assigned to OSiO bending modes. The observation of multiple bands offers support for a layered structure with variable SiO3 structural units. Little information may be obtained from the infrared spectra because of broad spectral profiles. Intense Raman bands at 3510, 3546 and 3620 cm−1 are ascribed to OH stretching modes. Evidence for the presence of water in the plumbotsumite structure was inferred from the infrared spectra.

Infrared and Raman spectroscopic characterization of the silicate mineral olmiite CaMn2+[SiO3(OH)](OH) : implications for the molecular structure

We have studied the mineral olmiite CaMn\[SiO3(OH)](OH) which forms a series with its calcium analogue poldevaartite CaCa\[SiO3(OH)](OH) using a range of techniques including scanning electron microscopy, thermogravimetric analysis , Raman and infrared spectroscopy. Chemical analysis shows the mineral is pure and contains only calcium and manganese in the formula. Thermogravimetric analysis proves the mineral decomposes at 502°C with a mass loss of 8.8% compared with the theoretical mass loss of 8.737%. A strong Raman band at 853 cm-1 is assigned to the SiO stretching vibration of the SiO3(OH) units. Two Raman bands at 914 and 953 cm-1 are attributed to the antisymmetric vibrations.Two intense Raman bands observed at 3511 and 3550 cm-1 are assigned to the OH stretching vibration of the SiO3(OH) units. The observation of multiple OH bands supports the concept of the non-equivalence of the OH units. Vibrational spectroscopy enables a detailed assessment of the molecular structure of olmiite.

A vibrational spectroscopic study of the silicate mineral ardennite-(As)

We have used a combination of scanning electron microscopy with EDX and vibrational spectroscopy to study the mineral ardennite-(As). The mineral ardennite-(As) of accepted formula Mn2þ 4 (Al,Mg)6(Si3O10)(SiO4)2(AsO4,VO4)(OH)6 is a silicate mineral which may contain arsenate and/or vanadates anions. Because of the oxyanions present, the mineral lends itself to analysis by Raman and infrared spectroscopy. Qualitative chemical analysis shows a homogeneous phase, composed by Si, Mn, Al and As. Ca and V were also observed in partial substitution for Mn and As. Raman bands at 1197, 1225, 1287 and 1394 cm-1 are assigned to SiO stretching vibrations. The strong Raman bands at 779 and 877 cm-1 are assigned to the AsO3- 4 antisymmetric and symmetric stretching vibrations. The Raman band at 352 cm-1 is assigned to the m2 symmetric bending vibration. The series of Raman bands between 414 and 471 cm-1 are assigned to the m4 out of plane bending modes of the AsO3-4 units. Intense Raman bands observed at 301 and 314 cm-1 are attributed to the MnO stretching and bending vibrations. Raman bands at 3041, 3149, 3211 and 3298 cm-1 are attributed to the stretching vibrations of OH units. There is vibrational spectroscopic evidence for the presence of water adsorbed on the ardennite-(As) surfaces.

A vibrational spectroscopic study of the silicate mineral inesite Ca2(Mn,Fe)₇Si10O28(OH)⋅5H2O

We have studied the hydrated hydroxyl silicate mineral inesite of formula Ca2(Mn,Fe)7Si10O28(OH)⋅5H2O using a combination of scanning electron microscopy with EDX and Raman and infrared spectroscopy. SEM analysis shows the mineral to be a pure monomineral with no impurities. Semiquantitative analysis shows a homogeneous phase, composed by Ca, Mn2+, Si and P, with minor amounts of Mg and Fe. Raman spectrum shows well resolved component bands at 997, 1031, 1051, and 1067 cm-1 attributed to a range of SiO symmetric stretching vibrations of [Si10O28] units. Infrared bands found at 896, 928, 959 and 985 cm-1 are attributed to the OSiO antisymmetric stretching vibrations. An intense broad band at 653 cm-1 with shoulder bands at 608, 631 and 684 cm-1 are associated with the bending modes of the OSiO units of the 6- and 8-membered rings of the [Si10O28] units. The sharp band at 3642 cm-1 with shoulder bands at 3612 and 3662 cm-1 are assigned to the OH stretching vibrations of the hydroxyl units. The broad Raman band at 3420 cm-1 with shoulder bands at 3362 and 3496 cm-1 are assigned to the water stretching vibrations. The application of vibrational spectroscopy has enabled an assessment of the molecular structure of inesite to be undertaken.

Silicate-based bioceramics for periodontal regeneration

Periodontal disease is characterized by the destruction of the tissues that attach the tooth to the alveolar bone. Various methods for regenerative periodontal therapy including the use of barrier membranes, bone replacement grafts, and growth factor delivery have been investigated; however, true regeneration of periodontal tissue is still a significant challenge to scientists and clinicians. The focus on periodontal tissue engineering has shifted from attempting to recreate tissue replacements/constructs to the development of biomaterials that incorporate and release regulatory signals to achieve in situ periodontal regeneration. The release of ions and molecular cues from biomaterials may help to unlock latent regenerative potential in the body by regulating cell proliferation and differentiation towards different lineages (e.g. osteoblasts and cementoblasts). Silicate-based bioactive materials, including bioactive silicate glasses and ceramics, have become the materials of choice for periodontal regeneration, due to their favourable osteoconductivity and bioactivity. This article will focus on the most recent advances in the in vitro and in vivo biological application of silicate-based ceramics, specifically as it relates to periodontal tissue engineering.

A vibrational spectroscopic study of the silicate mineral analcime – Na2(Al4SiO4O12)·2H2O : a natural zeolite

We have studied the mineral analcime using a combination of scanning electron microscopy with energy dispersive spectroscopy and vibrational spectroscopy. The mineral analcime Na2(Al4SiO4O12)·2H2O is a crystalline sodium silicate. Chemical analysis shows the mineral contains a range of elements including Na, Al, Fe2+ and Si. The mineral is characterized by intense Raman bands observed at 1052, 1096 and 1125 cm−1. The infrared bands are broad; nevertheless bands may be resolved at 1006 and 1119 cm−1. These bands are assigned to SiO stretching vibrational modes. Intense Raman band at 484 cm−1 is attributed to OSiO bending modes. Raman bands observed at 2501, 3542, 3558 and 3600 cm−1 are assigned to the stretching vibrations of water. Low intensity infrared bands are noted at 3373, 3529 and 3608 cm−1. The observation of multiple water bands indicate that water is involved in the structure of analcime with differing hydrogen bond strengths. This concept is supported by the number of bands in the water bending region. Vibrational spectroscopy assists with the characterization of the mineral analcime.

A vibrational spectroscopic study of the silicate mineral pectolite – NaCa2Si3O8(OH)

The mineral pectolite NaCa2Si3O8(OH) is a crystalline sodium calcium silicate which has the potential to be used in plaster boards and in other industrial applications. Raman bands at 974 and 1026 cm−1 are assigned to the SiO stretching vibrations of linked units of Si3O8 units. Raman bands at 974 and 998 cm−1 serve to identify Si3O8 units. The broad Raman band at around 936 cm−1 is attributed to hydroxyl deformation modes. Intense Raman band at 653 cm−1 is assigned to OSiO bending vibration. Intense Raman bands in the 2700–3000 cm−1 spectral range are assigned to OH stretching vibrations of the OH units in pectolite. Infrared spectra are in harmony with the Raman spectra. Raman spectroscopy with complimentary infrared spectroscopy enables the characterisation of the silicate mineral pectolite.

A vibrational spectroscopic study of the silicate mineral lomonosovite Na5Ti2(Si2O7)(PO4)O2

The mineral lomonosovite has been studied using a combination of scanning electron microscopy with energy dispersive X-ray analysis and vibrational spectroscopy. Qualitative chemical analysis gave Si, P, Na and Ti as the as major elements with small amounts of Mn, Ca, Fe and Al. The mineral lomonosovite has a formula Na5Ti2(Si2O7)(PO4)O2. Raman bands observed at 909, 925 and 939 cm−1 are associated with phosphate units. Raman bands found at 975, 999, 1070, 1080 and 1084 cm−1 are attributed to siloxane stretching vibrations. The observation of multiple bands in both the phosphate stretching and bending regions supports the concept that the symmetry of the phosphate anion in the structure of lomonosovite is significantly reduced. Infrared spectroscopy identifies bands in the water stretching and bending regions, thus suggesting that water is involved with the structure of lomonosovite either through adsorption on the surface or by bonding to the phosphate units.

A vibrational spectroscopic study of the silicate mineral harmotome – (Ba,Na,K)1-2(Si,Al)8O16⋅6H2O – A natural zeolite

The mineral harmotome (Ba,Na,K)1-2(Si,Al)8O16⋅6H2O is a crystalline sodium calcium silicate which has the potential to be used in plaster boards and other industrial applications. It is a natural zeolite with catalytic potential. Raman bands at 1020 and 1102 cm−1 are assigned to the SiO stretching vibrations of three dimensional siloxane units. Raman bands at 428, 470 and 491 cm−1 are assigned to OSiO bending modes. The broad Raman bands at around 699, 728, 768 cm−1 are attributed to water librational modes. Intense Raman bands in the 3100 to 3800 cm−1 spectral range are assigned to OH stretching vibrations of water in harmotome. Infrared spectra are in harmony with the Raman spectra. A sharp infrared band at 3731 cm−1 is assigned to the OH stretching vibration of SiOH units. Raman spectroscopy with complimentary infrared spectroscopy enables the characterization of the silicate mineral harmotome.

A vibrational spectroscopic study of the copper bearing silicate mineral luddenite

The molecular structure of the copper–lead silicate mineral luddenite has been analysed using vibrational spectroscopy. The mineral is only one of many silicate minerals containing copper. The intense Raman band at 978 cm−1 is assigned to the ν1 (A1g) symmetric stretching vibration of Si5O14 units. Raman bands at 1122, 1148 and 1160 cm−1 are attributed to the ν3 SiO4 antisymmetric stretching vibrations. The bands in the 678–799 cm−1 are assigned to OSiO bending modes of the (SiO3)n chains. Raman bands at 3317 and 3329 cm−1 are attributed to water stretching bands. Bands at 3595 and 3629 cm−1 are associated with the stretching vibrations of hydroxyl units suggesting that hydroxyl units exist in the structure of luddenite.

An enhanced procedure for the rapid digestion of high silicate archeological specimens followed by ICP-MS determination of traces of rare earth elements (REE's)

A straightforward procedure for the acid digestion of geological samples with SiO2 concentrations ranging between about 40 to 80%, is described. A powdered sample (200 mesh) of 500 mg was used and fused with 1000 mg spectroflux at about 1000 degreesC in a platinum crucible. The molten was subsequently digested in an aqueous solution of HNO3 at 100 degreesC. Several systematic digestion procedures were followed using various concentrations of HNO3. It was found that a relationship could be established between the dissolution-time and acid concentration. For an acid concentration of 15% an optimum dissolution-time of under 4 min was recorded. To verify that the dissolutions were complete, they were subjected to rigorous quality control tests. The turbidity and viscosity were examined at different intervals and the results were compared with that of deionised water. No significant change in either parameter was observed. The shelf-life of each solution lasted for several months, after which time polymeric silicic acid formed in some solutions, resulting in the presence of a gelatinous solid. The method is cost effective and is clearly well suited for routine applications on a small scale, especially in laboratories in developing countries. ICP-MS was applied to the determination of 13 Rare Earth Elements and Hf in a set of 107 archaeological samples subjected to the above digestion procedure. The distribution of these elements was examined and the possibility of using the REE's for provenance studies is discussed.