Hydrothermal phase equilibria in Ln2O3-H2O-CO2 systems : I. The lighter lanthanides

Phase diagrams for Nd2O3-H2O-CO2 and Gd2O3-H2O-CO2 systems at 1500 atm are given along with the results of selected runs in La, Sm and Eu systems. The stable phases in systems of La and Nd, are Ln(OH)CO3-B, Ln2O2CO3-II and LnOOH, in addition to the Ln(OH)3 phase at extremely low partial pressures of CO2 in the system. The systems become more and more complex with decreasing ionic radi and the number of stable carbonate phases increases. Ln2(CO3)3 · 3H2O orthorhombic (tengerate-like phase) is stable from Sm to Gd in addition to the other phases. The Gd(OH)CO3-A (ancylite-like phase) is hydrothermally stable at XCO2 greater-or-equal, slanted 0.5 while its hexagonal polymorph, Gd(OH)CO3-B is stable at low partial pressures of CO2 in the system.

Thermodynamic properties of Pb2PtO4 and PbPt2O4 and phase equilibria in the system Pb–Pt–O

The compounds Pb2PtO4 and PbPt2O4 were synthesized from an intimate mixture of yellow PbO and Pt metal powders by heating under pure oxygen gas at 973 K for periods up to 600 ks with intermediate grinding and recompacting. Both compounds were found to decompose on heating in pure oxygen to PbO and Pt, apparently in conflict with the requirements for equilibrium phase relations in the ternary system Pb–Pt–O. The oxygen chemical potential corresponding to the three-phase mixtures, Pb2PtO4 + PbO + Pt and PbPt2O4 + PbO + Pt were measured as a function of temperature using solid-state electrochemical cells incorporating yttria-stabilized zirconia as the solid electrolyte and pure oxygen gas at 0.1 MPa pressure as the reference electrode. The standard Gibbs free energies of formation of the ternary oxides were derived from the measurements. Analysis of the results indicated that the equilibrium involving three condensed phases Pb2PtO4 + PbO + Pt is metastable. Under equilibrium conditions, Pb2PtO4 should have decomposed to a mixture of PbO and PbPt2O4. Measurement of the oxygen potential corresponding to this equilibrium decomposition as a function of temperature indicated that decomposition temperature in pure oxygen is 1014(±2) K. This was further confirmed by direct determination of phase relations in the ternary Pb–Pt–O by equilibrating several compositions at 1023 K for periods up to 850 ks and phase identification of quenched samples using X-ray diffraction (XRD), scanning electron microscopy (SEM) and energy dispersive X-ray spectroscopy (EDS). Only one ternary oxide PbPt2O4 was stable at 1023 K under equilibrium conditions. Alloys and intermetallic compounds along the Pb–Pt binary were in equilibrium with PbO.

Hydrothermal phase equilibria in Ln2O3-H2O-CO2 systems for Tm, Yb and Lu

Phase diagrams for Tm2O3-H2O-CO2. Yb2O3-H2O-CO2 and Lu2O3-H2O-CO2 systems at 650 and 1300 bars have been investigated in the temperature range of 100–800°C. The phase diagrams are far more complex than those for the lighter lanthanides. The stable phases are Ln(OH)3, Ln2(CO3)3.3H2O (tengerite phase), orthorhombic-LnOHCO3, hexagonal-Ln2O2CO3. LnOOH and cubic-Ln2O3. Ln(OH)3 is stable only at very low partial pressures of CO2. Additional phases stabilised are Ln2O(OH)2CO3and Ln6(OH)4(CO3)7 which are absent in lighter lanthanide systems. Other phases, isolated in the presence of minor alkali impurities, are Ln6O2(OH)8(CO3)3. Ln4(OH)6(CO3)3 and Ln12O7(OH)10,(CO3)6. The chemical equilibria prevailing in these hydrothermal systems may be best explained on the basis of the four-fold classification of lanthanides.

Thermodynamics and phase equilibria in the system Ga---In using multi-parameter functions

A four and a five-parameter functions are used to analyse and interpret the high and low temperature thermodynamic data and phase equilibria in the Ga-In system.

Phase equilibria in the system CaO-CoO-SiO2 and Gibbs energies of formation of the quaternary oxides CaCoSi2O6, Ca2CoSi2O7, and CaCoSiO4

Phase relations in the pseudoternary system CaO-CoO-SiO2 have been established at 1323 K. Three quaternary oxides were found to be stable: CaCoSi2O6 with clinopyroxene (Cpx), Ca2CoSi2O7 with melilite (Mel), and CaCoSiO4 with olivine (Ol) structures. The Gibbs energies of formation of the quaternary oxides from their component binary oxides were measured using solid-state galvanic cells incorporating yttria-stabilized zirconia as the solid electrolyte in the temperature range of 1000-1324 K. The results can be summarized as follows: CoO (rs) + CaO (rs) + 2SiO(2) (Qtz) --> CaCoSi2O6 (Cpx), Delta G(f)(0) = -117920 + 11.26T (+/-150) J/mol CoO (rs) + 2CaO (rs) + 2SiO(2) (Qtz) --> Ca2CoSi2O7 (Mel), Delta G(f)(0) = -192690 + 2.38T (+/-130) J/mol CoO (rs) + CaO (rs) + SiO2 (Qtz) --> CaCoSiO2 (Ol), Delta G(f)(0) = -100325 + 2.55T (+/-100) J/mol where rs = rock salt (NaCl) structure and Qtz = quartz. The uncertainty limits correspond to twice the standard error estimate. The experimentally observed miscibility gaps along the joins CaO-CoO and CaCoSiO4-Co2SiO4 were used to calculate the excess free energies of mixing for the solid solutions CaxCo1-xO and (CayCo1-y)CoSiO4:Delta G(E) = X(1 - X)[31975X + 26736 (1 - X)] J/mol and Delta G(E) = 23100 (+/-250) Y(1 - Y) J/mol. A T-X phase diagram for the binary CaO-CoO was computed from the thermodynamic information; the diagram agrees with information available in the literature. The computed miscibility gap along the CaCoSiO4-Co2SiO4 join is associated with a critical temperature of 1389 (+/-15) K. Stability fields for the various solid solutions and the quaternary compounds are depicted on chemical-potential diagrams for SiO2, CaO, and CoO at 1323 K.

Growth of Nanometric Gold Particles in Solution Phase

The time evolution of colloidal gold particles in the nanometric regime has been investigated by employing electron microscopy and electronic absorption spectroscopy. The particle size distributions are essentially Gaussian and show the same time dependence for both the mean and the standard deviation, enabling us to obtain a time-independent universal curve for the particle size. Temperature dependent studies show the growth to be an activated process with a barrier of about 18 kJ mol(-1). We present a phenomenological equation for the evolution of particle size and suggest that the growth process is stochastic.

Thermodynamic constraints along isograms in ternary systems: application to three-phase equilibria

Thermodynamic constraints on component chemical potentials in three-phase fields introduced by the various isograms suggested in the literature are derived for a ternary system containing compounds. When compositions of two compounds lie on an isogram, it is associated with specific characteristics which can be used to obtain further understanding of the interplay of thermodynamic factors that determine phase equilibria. When two compounds are shared by adjacent three-phase fields, the constraints are dictated by binary compositions generated by the intersection of a line passing through the shared compounds with the sides of the ternary triangle. Generalized expressions for an arbitrary line through the triangle are presented. These are consistent with special relations obtained along Kohler, Colinet and Jacob isograms. Five axioms are introduced and proved. They provide valuable tools for checking consistency of thermodynamic measurements and for deriving thermodynamic properties from phase diagrams. (C) 1997 Elsevier Science S.A.

Thermodynamics of CuAlO2 and CuAl2O4 and phase equilibria in the system Cu2O CuO-Al2O3

The standard Gibbs free energies of formation of CuAlO2 and CuAl2O4 were determined in the range 700° to 1100°C, using emf measurements on the galvanic cells (1) Pt,CuO +] Cu2O/CaO-ZrO2/O2,Pt; (2) Pt,Cu +] CuAlO2+] Al2O3/CaO-ZrO2/ Cu +] Cu2O,Pt; and (3) Pt,CuAl2O4+] CuAlO2+]Al2O3/CaO-ZrO2/O2,Pt. The results are compared with published information on the stability of these compounds. The entropy of transformation of CuO from tenorite to the rock-salt structure is evaluated from the present results and from earlier studies on the entropy of formation of spinels from oxides of the rock-salt and corundum structures. The temperatures corresponding to 3-phase equilibria in the system Cu2O-CuO-Al2O3 at specified O2 pressures calculated from the present results are discussed in reference to available phase diagrams.

Thermodynamics and phase equilibria in the system Cu2O CuO ()Ga2O3

The standard Gibbs free energies of formation of CuAlO2 and CuAl2O4 were determined in the range 700° to 1100°C, using emf measurements on the galvanic cells (1) Pt,CuO +] Cu2O/CaO-ZrO2/O2,Pt; (2) Pt,Cu +] CuAlO2+] Al2O3/CaO-ZrO2/ Cu +] Cu2O,Pt; and (3) Pt,CuAl2O4+] CuAlO2+]Al2O3/CaO-ZrO2/O2,Pt. The results are compared with published information on the stability of these compounds. The entropy of transformation of CuO from tenorite to the rock-salt structure is evaluated from the present results and from earlier studies on the entropy of formation of spinels from oxides of the rock-salt and corundum structures. The temperatures corresponding to 3-phase equilibria in the system Cu2O-CuO-Al2O3 at specified O2 pressures calculated from the present results are discussed in reference to available phase diagrams.

Three phase equilibria for activity determinations: system Co Mn

A solid state e.m.f. cell with yttria-doped thoria as the electrolyte and a mixture of Cr + Cr sub 2 O sub 3 as the reference electrode, was employed for the measurement of the activity of manganese in the Co--Mn system at 1760 deg K, for 0.3 > X sub Mn > 0.05. The liquid alloy was contained in an alumina crucible and saturated with MnAl sub 2+2x O sub 4+3x . The cell can be represented by Pt, W, (Co--Mn) + MnAl sub 2+2x O sub 4+3x + Al sub 2 O sub 3 /ThO sub 2 --Y sub 2 O sub 3 /Cr + Cr sub 2 O sub 3 , Pt. The activity of manganese shows negative deviations from Raoult's law. The activities in the Co--Mn system are intermediate between those in the Fe--Mn and Ni--Mn systems. The Gibbs' energies of mixing in these systems follow the trends given by Miedema's model. 14 ref.--AA.

Phase equilibria in the system NiO-CaO-SiO2 and Gibbs energy of formation of CaNiSi2O6

Phase relations in the pseudoternary system NiO-CaO-SiO2 at 1373 K are established. The coexisting phases are identified by X-ray diffraction and energy-dispersive X-ray analysis of equilibrated samples. There is only one quaternary oxide CaNiSi2O6 with clinopyroxene structure. The Gibbs energy of formation of CaNiSi2O6 is measured using a solid state galvanic cell incorporating stabilized zirconia as the solid electrolyte in the temperature range of 1000 to 1400 K:Pt, Ni + SiO2 + CaSiO3 + CaNiSi2O6 \ (Y2O3)ZrO2 \ Ni + NiO, Pt From the electromotive force (emf) of the cell, the Gibbs energy of formation of CaNiSi2O6 from NiO, SiO2, and CaSiO3 is obtained. To derive the Gibbs energy of formation of the quaternary oxide from component binary oxides, the free energy of formation of CaSiO, is determined separately using a solid state cell based on single crystal CaF2 as the electrolyte: Pt, O-2, CaO + CaF2 \ CaF2 \ CaSiO3 + SiO2 + CaF2, O-2, Pt The results can be expressed by the following equations: NiO (r.s) + CaO (r.s) + 2SiO(2) (qz) --> CaNiSi2O6 (pyr) Delta G degrees = -115,700 + 10.63T (+/-100) J mol(-1) CaO (r.s) + SiO2 (qz) --> CaSiO3 (wol) Delta G degrees = -90,030 -0.61T (+/-60) J mol(-1).

Phase equilibria and thermodynamics of the system Dy-Mg-Cl at 1073 K

The phase relations in the system Dy–Mg–Cl at 1073 K have been established by isothermal equilibration and chemical analysis of quenched samples. Liquid Mg-rich alloy was found to be in equilibrium with molten DyCl2. Therefore, DyCl2 can be synthesized by reduction of MgCl2 with excess of metallic Dy at 1073 K. The Gibbs energy of formation of DyCl2 at 1073 K was evaluated by two different methods. From voltammetric determination of decomposition voltage, the upper limit for the standard Gibbs energy of formation of DyCl2 was estimated to be −505(±20) kJ mol−1. A value of −543(±10) kJ mol−1 was deduced from phase relations using Gibbs–Duhem integration. The value for the standard Gibbs energy of DyCl2 indicates that the Dy2+ ion has a potential capability for reducing TiCl4 to metal titanium. At the same time, Mg is a reductant for Dy3+ produced during the reduction of TiCl4. Thus, it is thermodynamically confirmed that reduction of TiCl4 by magnesium using a reaction mediator in the salt phase is feasible.

Phase Equilibria in the System Al2O3-CaO-CoO and Gibbs Energy of Formation of Ca3CoAl4O10

An isothermal section of the system Al2O3-CaO-CoO at 1500 K has been established by equilibrating 22 samples of different compositions at high temperature and phase identification by optical and scanning electron microscopy, X-ray diffraction, and energy dispersive spectroscopy after quenching to room temperature. Only one quaternary oxide, Ca3CoAl4O10, was identified inside the ternary triangle. Based on the phase relations, a solid-state electrochemical cell was designed to measure the Gibbs energy of formation of Ca3CoAl4O10 in the temperature range from 1150 to 1500 K. Calcia-stabilized zirconia was used as the solid electrolyte and a mixture of Co + CoO as the reference electrode. The cell can be represented as: ( - )\textPt,\textCaAl 2 \textO 4 + \textCa 1 2 \textAl 1 4 \textO 3 3 + \textCa 3 \textCoAl 4 \textO 10 + \textCo//(CaO)ZrO 2 \text// \textCoO + \textCo,\text Pt ( + ). (−)PtCaAl2O4+Ca12Al14O33+Ca3CoAl4O10+Co//(CaO)ZrO2//CoO+Co Pt (+) From the emf of the cell, the standard Gibbs energy change for the Ca3CoAl4O10 formation reaction, CoO + 3/5CaAl2O4 + 1/5Ca12Al14O33 → Ca3CoAl4O10, is obtained as a function of temperature: \Updelta Gr\texto Unknown control sequence '\Updelta'/J mol−1 (±50) = −2673 + 0.289 (T/K). The standard Gibbs energy of formation of Ca3CoAl4O10 from its component binary oxides, Al2O3, CaO, and CoO is derived as a function of temperature. The standard entropy and enthalpy of formation of Ca3CoAl4O10 at 298.15 K are evaluated. Chemical potential diagrams for the system Al2O3-CaO-CoO at 1500 K are presented based on the results of this study and auxiliary information from the literature.