Electrocatalytic hydrogenation of acetophenone using a Polymer Electrolyte Membrane Electrochemical Reactor

The use of a solid polymeric electrolyte, spe, is not commonly found in organic electrosynthesis despite its inherent advantages such as the possible elimination of the electrolyte entailing simpler purification processes, a smaller sized reactor and lower energetic costs. In order to test if it were possible to use a spe in industrial organic electrosynthesis, we studied the synthesis of 1-phenylethanol through the electrochemical hydrogenation of acetophenone using Pd/C 30 wt% with different loadings as cathode and a hydrogen gas diffusion anode. A Polymer Electrolyte Membrane Electrochemical Reactor, PEMER, with a fuel cell structure was chosen to carry out electrochemical reduction with a view to simplifying an industrial scale-up of the electrochemical process. We studied the influence of current density and cathode catalyst loading on this electroorganic synthesis. Selectivity for 1-phenylethanol was around 90% with only ethylbenzene and hydrogen detected as by-products.

Electrochemical synthesis at pre-pilot scale of 1-phenylethanol by cathodic reduction of acetophenone using a solid polymer electrolyte

The pre-pilot scale synthesis of 1-phenylethanol was carried out by the cathodic hydrogenation of acetophenone in a 100 cm2 (geometric area) Polymer Electrolyte Membrane Electrochemical Reactor. The cathode was a Pd/C electrode. Hydrogen oxidation on a gas diffusion electrode was chosen as anodic reaction in order to take advantage of the hydrogen evolved during the reduction. This hydrogen oxidation provides the protons needed for the synthesis. The synthesis performed with only a solid polymer electrolyte, spe, has lower fractional conversion although a higher selectivity than that carried out using a support–electrolyte–solvent together with a spe. However, the difference between these two cases is rather small and since the work-up and purification of the final product are much easier when only a spe is used, this last process was chosen for the pre-pilot electrochemical synthesis of 1-phenylethanol.

SIGNIFICANCE OF HEAT DISSIPATION IN THE CATHODE CATALYST LAYER ON THE LIFETIME AND RELIABILITY OF POLYMER ELECTROLYTE FUEL CELLS

To study the dissipation of heat generated due to the formation of pinholes that cause local hotspots in the catalyst layer of the Polymer Electrolyte Fuel Cell, a two-phase non-isothermal model has been developed by coupling Darcy’s law with heat transport. The domain under consideration is a section of the membrane electrode assembly with a half-channel and a half-rib. Five potential locations where a pinhole might form were analyzed: at the midplane of the channel, midway between the channel midplane and the channel wall, at the channel or rib wall, midway between the rib midplane and the channel wall, at the midplane of the rib. In the first part of this work, a preliminary thermal model was developed. The model was then refined to account for the two-phase effects. A sensitivity study was done to evaluate the effect of the following properties on the maximum temperature in the domain: Catalyst layer thermal conductivity, the Microporous layer thermal conductivity, the anisotropy factor of the Catalyst layer thermal conductivity, the Porous transport layer porosity, the liquid water distribution and the thickness of the membrane and porous layers. Accounting for the two-phase effects, a slight cooling effect was observed across all hotspot locations. The thermal properties of the catalyst layer were shown to have a limited impact on the maximum temperature in the catalyst layer of new fuel cells without pinhole. However, as hotspots start to appear, thermal properties play a more significant role in mitigating the thermal runaway.

Nanocomposite Nafion-Silica membranes for direct methanol fuel cells

Commercially available proton exchange membranes such as Nafion do not meet the requirements for high power density direct methanol fuel cells, partly due to their high methanol permeability. The aim of this work is to develop a new class of high-proton conductivity membranes, with thermal and mechanical stability similar to Nafion and reduced methanol permeability. Nanocomposite membranes were produced by the in-situ sol-gel synthesis of silicon dioxide particles in preformed Nafion membranes. Microstructural modification of Nafion membranes with silica nanoparticles was shown in this work to reduce methanol crossover from 7.48x10-6 cm2s^-1 for pure Nafion® to 2.86 x10-6 cm2s^-1 for nanocomposite nafion membranes (Methanol 50% (v/v) solution, 75 degrees C). Best results were achieved with a silica composition of 2.6% (w/w). We propose that silica inhibits the conduction of methanol through Nafion by blocking sites necessary for methanol diffusion through the polymer electrolyte membrane. Effects of surface chemistry, nanoparticle formation and interactions with Nafion matrix are further addressed.

Effect of fiber alignment in gelled electrospun membranes based on poly(vinylidene fluoride) for battery applications

Battery separators based on electrospun membranes of poly(vinylidene fluoride) (PVDF) have been prepared in order to study the effect of fiber alignment on the performance and characteristics of the membrane. The prepared membranes show an average fiber diameter of 272 nm and a degree of porosity of 87 %. The gel polymer electrolytes are prepared by soaking the membranes in the electrolyte solution. The alignment of the fibers improves the mechanical properties for the electrospun membranes. Further, the microstructure of the membrane also plays an important role in the ionic conductivity, being higher for the random electrospun membrane due to the lower tortuosity value. Independently of the microstructure, both membranes show good electrochemical stability up to 5.0 V versus Li/Li+. These results show that electrospun membranes based on PVDF are appropriate for battery separators in lithium-ion battery applications, the random membranes showing a better overall performance.

Effect of the degree of porosity on the performance of poly(vinylidene fluoride-trifluoroethylene)/poly(ethylene oxide) blend membranes for lithium-ion battery separators

Porous polymer membranes based on poly(vinylidene fluoride-trifluoroethylene)/poly(ethylene oxide) copolymers, P(VDF-TrFE)/PEO, are prepared through the, from partial to total, elimination of PEO, leading to interconnected micropores in the polymer blends. Electrolyte uptake, thermal and mechanical properties depend on the amount of PEO present in the polymer blend. Further, the degree of crystallinity of PEO and the elastic modulus (E´) of the polymer blend decrease with increasing PEO removal. Electrical properties of the polymer blend membranes are influenced by the porosity and are dominated by diffusion. The temperature dependence of ionic conductivity follows the Arrhenius behavior. It is the highest for the membranes with a volume fraction of pores of 44% (i.e, 90% PEO removal), reaching a value of 0.54 mS.cm-1 at room temperature. Battery performance was determined by assembling Li/C-LiFePO4 swagelok cells. The polymer blends with 90% PEO removal exhibit rate (124 mAhg-1 at C/5 and 47 mAhg-1 at 2C) and cycling capabilities suitable for lithium ion battery applications.

Poly(2,5-bibenzimidazole) Membranes: Physico-Chemical Characterization Focused on Fuel Cell Applications

Membranes of Poly(2,5-benzimidazole) (ABPBI), prepared by polycondensation in polyphosphoric acid, were characterized from the fuel cell application point of view: mechanical properties of the membranes for different acid doping levels, thermal stability, permeability for the different gases/vapors susceptible of use in the cell (hydrogen, oxygen, methanol and ethanol), electro-osmotic water drag coefficient, oxidation stability to hydroxyl radicals, phosphoric acid leaching rate and, finally, in-plane membrane conductivity. ABPBI membranes presented an excellent thermal stability, above 500 degrees C in oxygen, suitable mechanical properties for high phosphoric acid doping levels, a low methanol and ethanol limiting permeation currents, and oxygen permeability compared to Nafion membranes, and a low phosphoric acid leaching rate when exposed to water vapor. On the contrary, hydrogen permeation current was higher than that of Nafion, and the chemical stability was very limited. Membrane conductivity achieved 0.07 S cm(-1) after equilibration with a humid environment. Fuel cell tests showed reasonable good performances, with a maximum power peak of 170 mW cm(-2) for H-2/air at 170 degrees C operating under a humidified hydrogen stream, 39.9 mW cm(-2) for CH3OH/O-2 at 200 degrees C for a methanol/water weight ratio of 1: 2, and 31.5 mW cm(-2) for CH3CH2OH/O-2 at the same conditions than for methanol. (C) 2012 The Electrochemical Society. [DOI: 10.1149/2.014207jes] All rights reserved.

Enhancement of Electrical Conductivity in Plasticized Chitosan Based Membranes

Plasticized natural macromolecules-based polymer electrolyte samples were prepared and characterized. The plasticization of chitosonium acetate with glycerol increased the ionic conductivity value from 3.0 x 10(-7) S/cm to 1.1 x 10(-5) S/cm. The conductivity temperature relationship of the samples exhibits either VTF or Arrhenius type depending on the glycerol concentration in the sample. The dielectric studies evidencing the relaxation process in the plasticized sample at low frequency region are due to the electric polarization effect. Moreover, the samples were transparent in the Vis region, showed thermal stability up to 160 degrees C and good surface uniformity.

Sodium Alginate-Based Ionic Conducting Membranes

The present study investigates gel polymer electrolytes (GPEs) based on sodium alginate plasticized with glycerol containing either CH3COOH or LiClO4. The membranes showed ionic conductivity results of 3.1 x 10(-4) S/cm for the samples with LiClO4 and 8.7x10(-5) S/cm for the samples with CH3COOH at room temperature. The samples also showed thermal stability up to 160 degrees C, transparency of up to 90%, surface uniformity and adhesion to glass and steel. Moreover, Dynamic Mechanical Analysis revealed two relaxations for both samples and the Ea values were between 18 and 36 kJ/mol. All the results obtained indicate that alginate-based GPEs can be used as electrolytes in electrochemical devices.

Gellan Gum-LiI Gel Polymer Electrolytes

Gellan-based polymer electrolytes (PEs), doped with lithium iodide (LiI), were prepared and their electrical properties were characterized. The samples are thermally stable up to 234 degrees C and exhibit ionic conductivity of 3.8 x 10(-4) S/cm at room temperature for the sample doped with 40 wt% of LiI. Addition of 10 wt% of glycerol promotes an increase of the ionic conductivity to 1.5 x 10(-3) S/cm, which remains stable up to 100 degrees C. The activation energies of 2.4 to 12.4 kJ/mol were derived from the Arrhenius model. The repeated ionic conductivity measurements as a function of temperature show that these membranes can be reversibly used between the room temperature and 100 degrees C.

Synthesis,characterization and application studies of some polymer supported metal complexes

Polymer supports are efficient reagents,substrates and catalysts and they are extensively used for carrying out reactions at controlled rates.Tailor-made polymer supports are highly versatile which have opened an excellent area of research.Now polymer supported chemistry is being exploited at an amazing rate and it seems to join the routine world of organic synthesis.Polymer supported ligands are found to be efficient complexing agents whose high selectivity enables the analysis and removal of heavy metal ions which are toxic to all the living organisms of land and sea.polymer supported membranes function as ion selective potentiometric sensors which allow the exchange of specific ions among other ions of the same charge.In this investigation three series of polymeric schiff bases and three series of metal complexes have been prepared.An attempt is done to develop optimum conditions for the removal of heavy metal ions using polymeric schiff bases.A novel copper sensor electrode have also been prepared from polymer supported metal complex.

NMR and conductivity study of gelatin-based polymer electrolytes

Nuclear Magnetic Resonance spectroscopy (NMR) and complex impedance spectroscopy have been used to study gelatin-based polymer electrolytes plasticized with glycerol and containing lithium perchlorate. The studied samples were prepared with salt concentration of 7.9 wt% and 10.3 wt%. Ionic conductivity of about 10(-5) S/cm was obtained at room temperature for both samples. Lithium (Li-7) and proton (H-1) lineshapes and spin-lattice relaxation times were measured as a function of temperature. The Li-7 NMR relaxation results indicate that the ionic mobility in this system is comparable to those found in other plasticized polymer electrolytes.

Raman spectra of polymer electrolytes based on poly(ethylene glycol) dimethyl ether, lithium perchlorate, and the ionic liquid 1-butyl-3-methylimidazolium hexafluorophosphate

Raman spectra of polymer electrolytes based on poly(ethylene glycol) dimethyl ether (PEGdME) with LiClO(4), PEGdME/LiClO(4), and the ionic liquid 1-butyl-3-methylimidazolium hexafluorophosphate, PEGdME/[bmim]PF(6), are compared. Raman spectroscopy suggests stronger interactions in PEGdME/LiClO(4) than PEGdmE/[bmim]PF(6), thus corroborating previous results obtained by molecular dynamics simulations. Quantum Chemistry methods have been used to calculate vibrational frequencies and the equilibrium structure of segments of the polymer chain around the cation. A consistent picture has been obtained from Raman spectroscopy, density functional theory (DFT) calculations, and molecular dynamics simulations for these polymer electrolytes. (C) 2010 Elsevier B.V. All rights reserved.

Gelatin-based protonic electrolyte for electrochromic windows

Proton-conducting gel polymer electrolytes based on gelatin plasticized with glycerol and containing acetic acid were investigated, characterized, and applied to electrochromic window. For glycerol contents varying from 7% to 48%, the conductivity of the uniform and predominantly amorphous gel electrolyte was found to follow a Vogel-Tamman-Fulcher behavior with the temperature. Typically, for the electrolyte chosen to make 7 x 2 cm(2) electrochromic smart window with the configuration: glass/fluor-doped tin oxide (FTO)/WO(3)/gelatin electrolyte/CeO(2)-TiO(2)/FTO/glass and containing 28% of glycerol, the conductivities were found to be of the order of 5 x 10(-5) S/cm at room temperature and 3.6 x 10(-4) S/cm at 80 A degrees C. The device was characterized by spectroelectrochemical techniques and was tested up to 10,000 cycles showing a fast coloring/bleaching behavior, where the coloring process was achieved in 10 s and the bleaching in 2 s. The transmission variation at the wavelength of 550 nm was about 15%. The cyclic voltammograms showed a very good reversibility of the cathodic/anodic processes, and the charge density was about 3.5 mC/cm(2). The memory tests showed that the transmittance in the colored state increased by 8% in 90 min after removing the potential.

Agar-based films for application as polymer electrolytes

New types of polymer electrolytes based on agar have been prepared and characterized by impedance spectroscopy, X-ray diffraction measurements, UV-vis spectroscopy and scanning electronic microscopy (SEMI). The best ionic conductivity has been obtained for the samples containing a concentration of 50 wt.% of acetic acid. As a function of the temperature the ionic conductivity exhibits an Arrhenius behavior increasing from 1.1 x 10(-4) S/cm at room temperature to 9.6 x 10(-4) S/cm at 80 degrees C. All the samples showed more than 70% of transparency in the visible region of the electromagnetic spectrum, a very homogeneous surface and a predominantly amorphous structure. All these characteristics imply that these polymer electrolytes can be applied in electrochromic devices. (C) 2009 Elsevier Ltd. All rights reserved.