Iridium(III)-surfactant complex immobilized in mesoporous silica via templated synthesis: a new route to optical materials

In this work we report the preparation of a new blue-emitting material based on the templated synthesis of mesoporous silica (MCM-41) using micellar solutions of the newly synthesized monocationic metallosurfactant complex bis[1-benzyl-4-(2,4-difluorophenyl)-1H-1,2,3-triazole](4,4'-diheptadecyl-2,2'- bipyridine)-iridium(III) chloride in hexadecyl-trimethyl-ammonium bromide (CTAB). Under ambient conditions, significant increases in excited state lifetime and quantum yield values (up to 45%), were obtained for the solid materials in comparison to the corresponding micellar solutions. Solid state (1)H and (19)F NMR spectroscopies were successfully employed for quantifying the luminophore content in terms of Ir-surfactant to CTAB and Ir-surfactant to silica ratios.

Mesoporous silica-immobilized aluminium chloride as a new catalyst system for the isopropylation of naphthalene

Mesoporous MCM-41 silica immobilized aluminium chloride shows high catalytic activity and selectivity in the Friedel-Crafts alkylation of naphthalene with isopropanol.

Oxidation of toluene in waste gas streams using mesoporous Ti-hexagonal mesoporous silica

Various mesoporous catalysts with titanium loadings between 0.5 and 4 Ti wt. % and surface areas between 600 and 1,600 m(2)/g were synthesized using the molecular designed dispersion technique. These catalysts were tested using toluene oxidation in a fixed bed reactor at temperatures between 300 and 550degreesC. The reaction products were found to be CO2 and CO with selectivity towards CO2 above 80% for all catalysts. The catalytic activity of the catalysts increases with titanium loading. The total conversion at 550degreesC was not affected by the textural porosity, but increased textural porosity did significantly reduce the ignition temperature by up to 50degreesC. The Thiele modulus was calculated to be much less than one for all these materials indicating that the reaction rate is not diffusion, limited.

Superior electric double layer capacitors using ordered mesoporous carbons

This paper reports for the first time superior electric double layer capacitive properties of ordered mesoporous carbon (OMCs) with varying ordered pore symmetries and mesopore structure. Compared to commercially used activated carbon electrode, Maxsorb, these OMC carbons have superior capacitive behavior, power output and high-frequency performance in EDLCs due to the unique structure of their mesopore network, which is more favorable for fast ionic transport than the pore networks in disordered microporous carbons. As evidenced by N-2 sorption, cyclic voltammetry and frequency response measurements, OMC carbons with large mesopores, and especially with 2-D pore symmetry, show superior capacitive behaviors (exhibiting a high capacitance of over 180 F/g even at very high sweep rate of 50 mV/s, as compared to much reduced capacitance of 73 F/g for Maxsorb at the same sweep rate). OMC carbons can provide much higher power density while still maintaining good energy density. OMC carbons demonstrate excellent high-frequency performances due to its higher surface area in pores larger than 3 nm. Such ordered mesoporous carbons (OMCs) offer a great potential in EDLC capacitors, particularly for applications where high power output and good high-frequency capacitive performances are required. (C) 2005 Elsevier Ltd. All rights reserved.

Tailored Jeffamine molecular tools for ordering mesoporous Silica

Herein, we report the formation of organized mesoporous silica materials prepared from a novel nonionic gemini surfactant, myristoyl-end capped Jeffamine, synthesized from a polyoxyalkyleneamine (ED900). The behavior of the modified Jeffamine in water was first investigated. A direct micellar phase (L1) and a hexagonal (H1) liquid crystal were found. The structure of the micelles was investigated from the SAXS and the analysis by Generalized Indirect Fourier Transformation (GIFT), which show that the particles are globular of coreshell type. The myristoyl chains, located at the ends of the amphiphile molecule are assembled to form the core of the micelles and, as a consequence, the molecules are folded over on themselves. Mesoporous materials were then synthesized from the self-assembly mechanism. The recovered materials were characterized by SAXS measurements, nitrogen adsorptiondesorption analysis, transmission and scanning electron microscopy. The results clearly evidence that by modifying the synthesis parameters, such as the surfactant/silica precursor molar ratio and the hydrothermal conditions, one can control the size and the nanostructuring of the resulting material. It was observed that, the lower the temperature of the hydrothermal treatment, the better the mesopore ordering.

Sol-Gel Mesoporous Silica Aerogels and Bio Hybrids for Functional Applications

The thesis covers a systematic investigation on the synthesis of silica aerogels and microspheres with tailored porosity, at ambient conditions by varying the experimental parameters as well as using organic templates. Organically modified silica-gelatin and silica-chitosan hybrids were developed for the first time using alkylalkoxysilanes such as MTMS and VTMS. Application of novel silica-biopolymer antiwetting coatings on different substrates such as glass, leather and textile is also demonstrated in the thesis.

Studies on Catalysis by Ordered Mesoporous SBA-15 Materials Modified with Transition Metals

To meet the challenges related to the chemical industry,development of efficient catalysts is necessary.The mesoporous materials like SBA-15 are considered as good catalyst candidates of 21st century.SBA-15 mesoporous materials are catalytically inactive,but allow the dispersion of catalytically active phases into the framework.So these materials can be considered as an interesting alternative for preparing catalytically active metal nanoparticles in-situ into it.In the present work various transition metals are incorporated to improve the catalytic activity of SBA-15 material.The fundamental aspects of the preparation,characterization and the activity studies are briefly viewed in this thesis. Systematic investigation of the physico-chemical properties and catalytic activity studies of the prepared materials were carried out and presented in this Study.

Factorial design to optimize microwave-assisted synthesis of FDU-1 silica with a new triblock copolymer

The synthesis of FDU-1 silica with large cage-like mesopores prepared with a new triblock copolymer Vorasurf 504 (R) (Eo)(38)(BO)(46)(EO)(38) was developed. The hydrothermal treatment temperature, the dissolution of the copolymer in ethanol, the HCl concentration, the solution stirring time and the hydrothermal treatment time in a microwave oven were evaluated with factorial design procedures. The dissolution in ethanol is important to produce a material with better porous morphology. Increases in the hydrothermal temperature (100 degrees C) and HCl concentration (2 M) improved structural, textural and chemical properties of the cubic ordered mesoporous silica. Also, longer times induced better physical and chemical property characteristics. (C) 2010 Elsevier Inc. All rights reserved.

Adsorption of Pb(2+), Cu(2+) and Cd(2+) in FDU-1 silica and FDU-1 silica modified with humic acid

Ordered mesoporous silica with cubic structure, type FDU-1, was synthesized under strong acid media using B-50-6600 poly(ethylene oxide)-poly(butilene oxide)-poly(ethylene oxide) triblock copolymer (EO(39)BO(47)EO(39)) and tetraethyl orthosilicate (TEOS). Humic acid (HA) was modified to the synthesis process at a concentration of 1.5 mmol per gram of SiO(2). Thermogravimetry, small angle X-ray diffraction, nitrogen adsorption and high resolution transmission electron microscopy were used to characterize the samples. The pristine FDU-1 and FDU-1 with incorporated 1.5 mmol of HA were tested for adsorption of Pb(2+), Cu(2+) and Cd(2+) in aqueous solution. Incorporation of humic acid into the FDU-1 silica afforded an adsorbent with strong affinity for Cd(2+), Cu(2+) and Pb(2+) from single ion solutions. Adsorption of Cu(2+) was significantly enhanced after incorporation of humic acid, a fact that can be explained by the formation of complexes with carboxylic and phenolic groups at low concentrations of the metal cation. The results demonstrated the potential applicability of FDU-1 with incorporated HA in the removal of low concentrations of heavy metal cations from aqueous solution, such as wastewaters, after usual precipitation of metal hydroxides in alkaline medium and proper pH conditioning in the range between 6 and 7. (C) 2007 Elsevier Inc. All rights reserved.

Rhodamine 6G encapsuled mesoporous silica channels

We report the effect of solvent on the rhodamine 6G encapsuled into channels of mesoporous silica, synthesized by two-step process that gives intermediary stable hybrid micelles. Mesoporous materials have been obtained by the method that involves surfactant micelles (mainly cationic) and inorganic precursor of the structure to be obtained. MSU-X type mesoporous silica has been synthesized with polyethylene oxide surfactant as the directing-structure agent and tetraethyl orthosilicate Si(OEt)(4) as the silica source. The influence of the solvent on the encapsulation of rhodamine dye was systematically explored, specially its influence on the luminescence properties. Rhodamine 6G encapsuled into mesoporous silica channel was characterized by UV-Vis and luminescence spectroscopies, scanning electron microscopy, small angle x ray scattering and N(2) sorption-desorption. The pore size and the solvent effects into luminescence dye encapsuled into mesoporous silica channels are observed in the visible absorption and emission spectra of rhodamine 6G. The intense photo luminescence band of rhodamine 6G dye is in 500 to 600 nm region. The observed shift of the absorption and emission bands can be assigned to the effect of the solvents dielectric constant and pore size of mesoporous silica.

On the specific filtration mechanism of a mesoporous silica membrane, prepared with non-connecting parallel pores

We report the singular filtration properties of an ultrafiltration membrane made with mesoporous silica that exhibits cylindrical pores aligned mostly normal to the support. This membrane supported on tubular commercial macroporous alumina supports was prepared by the interfacial growth mechanism between stable silica-surfactant hybrid micelles made of the association of silica oligomers with polyethyleneoxide-based (PEO) surfactants and sodium fluoride, a well-known silica condensation catalyst [Boissière et al., An ultrafiltration membrane made with mesoporous MSU-X silica, Chem. Mater. 15 (2003) 460-463]. It appears that the combined effect of the silica nature of the membrane, whose surface charge can be easily adjusted by changing the pH and the non-connected cylindrical shape of the pores provides a new behavior in the retention properties, as proved by the filtration of polyoxyethylene polymers (PEO) with different molecular weights. Depending on the filtration conditions, a rejection rate of 80% and a steep cut-off at 2000 Da can be obtained or, on the reverse, polymers three times bigger than the pore diameter can diffuse through the membrane. This new filtration mechanism, which opens up new modes of separation modes, is explained in the light of both topology of the porous network and pH-dependent interactions between PEO polymers and silica porous media. © 2004 Elsevier B.V. All rights reserved.

An ultrafiltration membrane, prepared with MSU-type mesoporous silica: Preparation and specific filtration behavior

We report preparation and the singular filtration properties of an ultrafiltration membrane made with MSU-type mesoporous silica that exhibits cylindrical pores aligned mostly normal to the support. This membrane supported on tubular commercial macroporous alumina supports was prepared by the interfacial growth mechanism between stable silica-surfactant hybrid micelles made of the association of silica oligomers with polyethyleneoxide-based (PEO) surfactants and sodium fluoride, a well-known silica condensation catalyst. It appears that the combined effect of the silica nature of the membrane, whose surface charge can be easily adjusted by changing the pH and the non-connected cylindrical shape of the pores provides a new behavior in the retention properties, as proved by the filtration of polyoxyethylene polymers (PEO) with different molecular weights. Depending on the filtration conditions, a rejection rate of 80 % and a steep cut-off at 2,000 Da can be obtained or, on the reverse, polymers three times bigger than the pore diameter can diffuse through the membrane. This new filtration mechanism, which opens up new modes of separation modes, is explained in the light of both topology of the porous network and pH-dependent interactions between PEO polymers and silica porous media. © 2005 Elsevier B.V. All rights reserved.

Nanostructured materials based on mesoporous silica and mesoporous silica/apatite as osteogenic growth peptide carriers

The aim of this work was the preparation of inorganic mesoporous materials from silica, calcium phosphate and a nonionic surfactant and to evaluate the incorporation and release of different concentrations of osteogenic growth peptide (OGP) for application in bone regeneration. The adsorption and release of the labeled peptide with 5,6-carboxyfluorescein (OGP-CF) from the mesoporous matrix was monitored by fluorescence spectroscopy. The specific surface area was 880 and 484 m2 g- 1 for pure silica (SiO) and silica/apatite (SiCaP), respectively; the area influenced the percentage of incorporation of the peptide. The release of OGP-CF from the materials in simulated body fluid (SBF) was dependent on the composition of the particles, the amount of incorporated peptide and the degradation of the material. The release of 50% of the peptide content occurred at around 4 and 30 h for SiCaP and SiO, respectively. In conclusion, the materials based on SiO and SiCaP showed in vitro bioactivity and degradation; thus, these materials should be considered as alternative biomaterials for bone regeneration. © 2013 Elsevier B.V.

Sol-gel thin-film based mesoporous silica and carbon nanotubes for the determination of dopamine, uric acid and paracetamol in urine

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Comparison among different pH values of Rhodamine B solution impregnated into mesoporous silica