Microstructure and electromagnetic characteristics of Ni nanoparticle film coated carbon microcoils

Carbon microcoils (CMCs) have been coated with a Ni nanoparticle film using an electroless plating process. The morphology, the elemental composition and the phases in the coating layer, complex permittivity and permeability of the CMCs and Ni-coated CMCs were, respectively, investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and microwave vector network analysis at room temperature. A homogeneous dispersion of Ni nanoparticles on the outer surface of the CMCs was obtained, with a mean particle size of ∼34.4 nm and the phosphorus content of about 8.5 wt%. When comparing the coated and uncoated CMC samples, the real (ε′) and imaginary (ε″) part of the complex permittivity as well as dielectric dissipation factor (tgδε = ε″/ε′) of the Ni-coated CMCs were much smaller, while the real (μ′) and imaginary (μ″) part of the complex permeability and the magnetic dissipation factor (t g σμ = μ″ / μ′) were larger. The enhanced microwave absorption of Ni-coated CMCs resulted from stronger dielectric and magnetic losses. In contrast, the microwave absorption of uncoated CMCs was mainly attributed to the dielectric rather than magnetic losses.

Carbon saturation of arrays of Ni catalyst nanoparticles of different size and pattern uniformity on a silicon substrate

The kinetics of saturation of Ni catalyst nanoparticle patterns of the three different degrees of order, used as a model for the growth of carbon nanotips on Si, is investigated numerically using a complex model that involves surface diffusion and ion motion equations. It is revealed that Ni catalyst patterns of different degrees of order, with Ni nanoparticle sizes up to 12.5 nm, exhibit different kinetics of saturation with carbon on the Si surface. It is shown that in the cases examined (surface coverage in the range of 1-50%, highly disordered Ni patterns) the relative pattern saturation factor calculated as the ratio of average incubation times for the processes conducted in the neutral and ionized gas environments reaches 14 and 3.4 for Ni nanoparticles of 2.5 and 12.5 nm, respectively. In the highly ordered Ni patterns, the relative pattern saturation factor reaches 3 for nanoparticles of 2.5 nm and 2.1 for nanoparticles of 12.5 nm. Thus, more simultaneous saturation of Ni catalyst nanoparticles of sizes in the range up to 12.5 nm, deposited on the Si substrate, can be achieved in the low-temperature plasma environment than with the neutral gas-based process.

Size-selected Ni catalyst islands for single-walled carbon nanotube arrays

Many properties of single-walled carbon nanotube (SWCNT) arrays are determined by the size and surface coverage of the metal catalyst islands from which they are nucleated. Methods using thermal fragmentation of continuous metal films frequently fail to produce size-uniform islands. Hybrid numerical simulations are used to propose a new approach to controlled self-assembly of Ni islands of the required size and surface coverage using tailored gas-phase generated nanocluster fluxes and adjusted surface temperatures. It is shown that a maximum surface coverage of 0.359 by 0.96-1.02 nm Ni catalyst islands can be achieved at a low surface temperature of 500 K. Optimized growth of Ni catalyst islands can lead to fabrication of size-uniform SWCNT arrays, suitable for numerous nanoelectronic applications. This approach is deterministic and is applicable to a range of nanoassemblies where high surface coverage and island size uniformity are required.

Amino group positions dependent morphology and coverage of electropolymerized metallophthalocyanine (M = Ni and Co) films on electrode surfaces

Electropolymerized films of teraaminometallophthalocyanines (MTAPc; M = Ni and Co) with amino groups at α- (4α-MTAPc) and β- (4β-MTAPc) positions were prepared on glassy carbon (GC) and indium tin oxide (ITO) electrodes. It was found that the electropolymerization growth rate of 4α-MTAPc was less than that of 4β-MTAPc prepared under identical conditions. Further, the surface coverage of the polymerized 4β-MTAPc film was greater than that of 4α-MTAPc polymerized film. Atomic force microscopy (AFM), X-ray diffraction (XRD) and UV–visible spectroscopic studies were carried out for the polymerized films of 4α-NiIITAPc (p-4α-NiIITAPc) and 4β-NiIITAPc (p-4β-NiIITAPc) alone because both Ni(II) and Co(II) polymerized films show similar trend in electropolymerization and surface coverage values. AFM images show that p-4α-NiIITAPc film contains islands and the thickness of this film was nearly three times less than that of p-4β-NiIITAPc. XRD patterns for the two polymerized films reveal that p-4β-NiIITAPc film was relatively more crystalline than p-4α-NiIITAPc film. Further, the compactness of these films was scrutinized from their barrier properties toward [Fe(CN)6]3−/4− redox couple. The differences in the polymerization growth rate of 4α-MTAPc and 4β-MTAPc, and the thicknesses of the resultant polymerized films suggest that unlike 4β-MTAPc one or two amino groups might have not involved in electropolymerization in the case of 4α-MTAPc. Further, the influence of surface coverage on the electrocatalytic properties of the polymerized films was studied by taking p-4β-CoIITAPc and p-4α-CoIITAPc films as examples. The electrocatalytic oxygen reduction current was almost same at both the electrodes suggesting that only the surface species were involved in the electrocatalytic reduction of oxygen.

Pentacene on Ni(111): room-temperature molecular packing and temperature-activated conversion to graphene

We investigate, using scanning tunnelling microscopy, the adsorption of pentacene on Ni(111) at room temperature and the behaviour of these monolayer films with annealing up to 700 °C. We observe the conversion of pentacene into graphene, which begins from as low as 220 °C with the coalescence of pentacene molecules into large planar aggregates. Then, by annealing at 350 °C for 20 minutes, these aggregates expand into irregular domains of graphene tens of nanometers in size. On surfaces where graphene and nickel carbide coexist, pentacene shows preferential adsorption on the nickel carbide phase. The same pentacene to graphene transformation was also achieved on Cu(111), but at a higher activation temperature, producing large graphene domains that exhibit a range of moiré superlattice periodicities.

Unprecedented transformation of tetrathienoanthracene into pentacene on Ni(111)

The imaging and characterization of single-molecule reaction events is essential to both extending our basic understanding of chemistry and applying this understanding to challenges at the frontiers of technology, for example, in nanoelectronics. Specifically, understanding the behavior of individual molecules can elucidate processes critical to the controlled synthesis of materials for applications in multiple nanoscale technologies. Here, we report the synthesis of an important semiconducting organic molecule through an unprecedented reaction observed with submolecular resolution by scanning tunneling microscopy (STM) under ultrahigh vacuum (UHV) conditions. Our images reveal a sulfur abstraction and cyclization reaction that converts tetrathienoanthracene precursors into pentacene on the Ni(111) surface. The identity of the final reaction product was confirmed by time-of-flight secondary ion mass spectrometry (TOF-SIMS). This reaction has no known literature analogue, and highlights the power of local-probe techniques for exploring new chemical pathways.

Dynamic strain ageing in Ni-base superalloy 720Li

An experimental investigation into the dynamic strain ageing (DSA) of a wrought Ni-base superalloy 720Li was conducted. Characteristics of jerky, flow have been studied at intermediate temperatures of 350, 400 and 450 degrees C at strain-rates between 10(-3) and 10(-5) s(-1). Serrations of Type C are predominant within the temperature/strain-rate range explored. The major characteristics of the serrations-i.e. (a) critical plastic strain for onset of serrations, epsilon(c); (b) average stress decrement, Delta sigma(avg); and (c) strain increment between serrations. Delta epsilon(BS)-have been examined at selected temperatures and strain-rates. Negative strain-rate sensitivity was observed in the DSA regime. However. temperature did not influence tensile properties such as yield strength, ultimate strength. elongation, reduction in area, and work hardening rate or fracture features in DSA regime. Analysis of the results Suggests that locking of the mobile dislocations by substitutional alloying elements is responsible for the DSA in alloy 720Li.

Preparation, structure, and magnetic properties of isostructural La3MAlS7 and La3MFeS7 (M = Mg, Mn, Fe, Co, Ni, or Zn)

A series of quaternary metal sulfides of the general formula La3MM′S7 (M = Mn, Fe, Co; M′ = Al and M = Mg, Mn, Fe, Co, Ni; M′ = Fe) consisting of linear chains of face shared MS6 octahedra and isolated M′S4 tetrahedra has been prepared and studied. The aluminium compounds La3MAlS7 (M = Mn, Fe, Co) exhibit linear chain antiferromagnetism. Magnetic behavior of other La3MFeS7 sulfides has been examined in detail. The magnetic susceptibility of La3MgFeS7 shows that tetrahedral site Fe3+ undergoes a transition from Image to S = 2 spin state around 150 K.

O2- and O1- types of oxygen species on Ni and barium-dosed Ni and Cu surfaces

He II UPS and XPS study of oxygen adsorption on Ni and barium-dosed Ni and Cu surfaces at 300 K show two types of oxygen species which are assigned to O2- and O1- (ad).

Ce CORE level X-ray photo electron spectroscopy of CeX2Si2 (X = Fe, Co, Ni and Cu)

Ce(3d) and (4d) core level XPS spectra of CeX = Fe, Co, Ni and Cu) suggest that the mean valence of Ce was as well as 4f hybridization strength decrease systematically from Fe to Cu. This observation is in agreement with the results of Bremstrahlung Isochromat Spectroscopy (BIS), but in disagreement with LIII-edge data reported earlier.

Low-temperature stabilization of pure Ni(IT)O

Ordinary nickel (II) oxide prepared by any of the usual methods is always contaminated with some higher valency states of nickel. Such nickel oxide however can be converted to pure nickel (II) oxide by soaking for some hours at 800–850°C in a closed system under a static inert atmosphere and in the presence of pure MnO as oxygen-getter. The resulting Ni(IT)O is highly resistant to oxidation.

A Theoretical Investigation of the Ni(II)-Catalyzed Hydrovinylation of Styrene

We report a detailed and full computational investigation on the hydrovinylation reaction of styrene with the Ni(II)-phospholane catalytic system, which was originally presumed to proceed through a cationic mechanism involving a nickel hydride intermediate. The following general features emerge from this study on a specific catalyst complex that was found to give quantitative yield and moderate selectivity: (a) the activation barrier for the initiation (18.8 kcal/mol) is higher than that for the reaction due to a low-lying square-planar pentenyl chelate intermediate originating from a Ni(II)-allyl catalyst precursor. Consequently there is an induction period for the catalysis; (b) the exit of product from the catalyst is via a β-H-transfer step instead of the usual β-H elimination pathway, which has a very high activation energy due to a trans effect of the phospholane ligand; (c) the turnover-limiting and enantio- determining transition state is also the β-H-transfer; (d) because of the absence of a hydride intermediate, the unwanted isomerization of the product is prevented; (e) since the enantio-discrimination is decided at the H-transfer stage itself, the configuration of the product in a catalytic cycle influences the enantioselectivity in the subsequent cycle; (f) the trans effect of the sole strong ligand in the d8 square-planar Ni(II), the stability of the η3-benzyl intermediate, and the availability of three coordination sites enable regioselective hydrovinylation over the possible oligomerization/polymerization of the olefin substrates and linear hydrovinylation. This work has also confirmed the previously recognized role of the hemilabile group at various stages in the mechanism.

Small nickel metal particles in Ni---Al2O3 metal-ceramic composites

Magnetic measurements have been used in combination with transmission electron microscopy to investigate small nickel metal particles in metal-ceramic composites. Estimates of the average number of atoms in the particles are given for nonmagnetic samples with low Ni content.