Synthesis and properties of novel polyimides from sulfonated binaphthalene dianhydride for proton exchange membranes

A sulfonated dianhydride monomer, 6,6-disulfonic-4,4'-binaphthyl-1,1',8,8'-tetracarboxylic dianhydride (SBTDA), was successfully synthesized by direct sulfonation of the parent dianhydride, 4,4'-binaphthyl-1,1',8,8'-tetracarboxylic dianhydride (BTDA), using fuming sulfuric acid as the sulfonating reagent. A series of sulfonated homopolyimides were prepared from SBTDA and various common nonsulfonated diamines. The resulting polymer electrolytes, which contain ion conductivity sites on the deactivated positions of the aryl backbone rings, displayed high proton conductivities of 0.25-0.31 S cm(-1) at 80 degrees C. The oxidative stability test indicated that the attachment of the -SO3H groups onto the dianhydride units did not deteriorate the oxidative stability of the SPI membranes.

Synthesis of sulfonated poly(arylene-co-naphthalimide)s as novel polymers for proton exchange membranes

A series of novel sulfonated poly(arylene-co-binaphthalimide)s (SPPIs) were successfully synthesized via Ni(0) catalytic coupling of sodium 3-(2,5-dichlorobenzoyl)benzenesulfonate and bis(chloronaphthalimide)s. Bis(chloronaphthalimide)s were conveniently prepared from 5-chloro-1,8-naphthalic anhydride and various diamines. Tough and transparent SPPI membranes were prepared and the electrolyte properties of the copolymers were intensively investigated as were the effects of different diamine structures on the copolymer characterisitics. The copolymer membrane Ia-80, with an ion exchange capacity (IEC) of 2.50 meq g(-1), displayed a higher proton conductivity, i.e. 0.135 S cm(-1) at 20 degrees C, as compared to Nafion 117 (0.09 S cm(-1), 20 degrees C).

Novel thin-film composite membranes with improved water flux from sulfonated cardo poly(arylene ether sulfone) bearing pendant amino groups

A new class of polymeric amine, namely, sulfonated cardo poly(arylene ether sulfone) (SPES-NH2) was synthesized and used for the preparation of thin-film composite membrane. The TFC membranes were prepared on a polysulfone supporting film through interfacial polymerization with trimesoyl chloride (TMC) solutions and amine solutions containing SPES-NH2 and m-phenylenediamine (MPDA). The resultant membranes were characterized with water permeation performance, chemical structure, hydrophilicity of active layer and membrane morphology including top surface and cross-section.

Sulfonated poly(arylene-co-imide)s as water stable proton exchange membrane materials for fuel cells

A novel sulfonated poly(arylene-co-imide)s were synthesized by Ni(0) catalytic copolymerization of sodium 3-(2,5-dichlorobenzoyl)benzenesulfonate and naphthalimide dichloride monomer. The synthesized copolymers with the - SO3H group on the side-chain of polymers possessed high molecular weights revealed by their high viscosity and the formation of tough and flexible membranes. Because of the introduction of electron donating phenoxy groups into naphthalimide moieties, the hydrolysis of the imide rings was depressed. The resulting copolymers exhibited excellent water stability. The copolymer membranes display no apparently change in appearance, flexibility, and toughness after a soaking treatment in pressurized water at 140 degrees C for 250 h.

Ethylene polymerization by (alpha-diimine)nickel(II) complexes bearing different substituents on para-position of imines activated with MMAO

A series of (alpha-diimine)nickel(II) complexes [ArN = C(Nap)C = NAr]NiBr2 (Nap = 1,8-naphthdiyl, Ar = 2,6-Me2C6H3, 3a; Ar = 2,4,6-Me3C6H2 3b; Ar = 2,6-Me-2-4-tBuC(6)H(2), 3c; Ar 2,6-Me-2-4-BrC6H2, 3d; Ar = 2,6-Me-2-4-ClC6H2, 3e; Ar 2,6-iPr(2)C(6)H(3), 3f; Ar = 2,4,6-iPr(3)C(6)H(2), 3g; Ar = 2,6-iPr-4-BrC6H2, 3h) have been synthesized, characterized, and investigated as precatalysts for ethylene polymerization in the presence of modified methylaluminoxane (MMAO).

Novel Sulfonated Polyimide Ionomers by Incorporating Pyridine Functional Group in the Polymer Backbone

A series of sulfonated polyimides (SPIs) containing pyridine ring in the polymer backbone were synthesized by the polycondensation of 1,4,5,8-naphthalene-tetracarboxylic dianhydride (NTDA), 5-(2,6-bis(4-arninophenyl)pyridin-4-yl)-2-methoxy benzene sulfonic acid (SDAM), and 4,4'-diaminodiphenyl ether (ODA). Flexible, transparent, and tough membranes were obtained. Property study revealed that all the membranes displayed high thermal stability with the desulfonation and decomposition temperature higher than 290 and 540 degrees C, respectively, as well as good mechanical property with Young's modulus larger than 1.0 GPa, maximum strength (MS) on a scale of 60-80 MPa, and elongation at break (EB) ranged from 41.79 to 75.17%.

Dispersions of carbon nanotubes in sulfonated poly[bis(benzimidazobenzisoquinolinones)] and their proton-conducting composite membranes

A sulfonated poly[bis(benzimidazobenzisoquinolinones)] (SPBIBI) possessing a conjugated pyridinone ring was shown to be effective for dispersing multiwalled carbon nanotubes (MWCNTs) in DMSO. The dispersions in which the SPBIBI to MWCNTs mass ratio was 4:1 demonstrated the highest MWCNTs concentrations, i.e., 1.5-2.0 mg mL(-1), and were found to be stable for more than six months at room temperature. Through casting of these dispersions, MWCNTs/SPBIBI composite membranes were successfully fabricated on substrates as proton exchange membranes for fuel cell applications and showed no signs of macroscopic aggregation. The properties of composite membranes were investigated, and it was found that the homogeneous dispersion of the MWCNTs in the SPBIBI matrix altered the morphology structures of the composite membranes, which lead to the formation of more regular and smaller cluster-like ion domains.

Synthesis and properties of novel sulfonated poly(phenylquinoxaline)s as proton exchange membranes

Two series of sulfonated poly(phenylquinoxaline)s (SPPQ-x and SPPQ(O)-x, x refers to molar percentage of sulfonated tetraamine monomer) were first synthesized from a sulfonated tetraamine (4,4'-bis(3,4-diaminophenoxy)biphenyl-3.3'-disulfonic acid) and two aromatic bisbenzils (4-phenylglyoxalylbenzil and p,p'-oxydibenzil) in a mild condition. The structures of SPPQ-x and SPPQ(0)-x were characterized by IR and H-1 NMR spectra. The properties of these polymer films, such as water uptake, water swelling ratio, proton conductivity, thermal properties, methanol permeability, hydrolytic and oxidative stability were also investigated. The resulting polymers generally showed good solubility in DMAc and DMSO. Flexible and tough membranes with high mechanical strength were prepared. They show very high thermal, thermooxidative, hydrolytic stabilities and low methanol permeability. SPPQ-100 with the IEC value (2.41 mmol/g) displays the conductivity of 0.1 S/cm and a swelling ratio of 7.3% at 100 degrees C.

Blends based on sulfonated poly[bis(benzimidazobenzisoquinolinones)] and poly(vinylidene fluoride) for polymer electrolyte membrane fuel cell

A new blend system consisting of an amorphous sulfonated poly[bis(benzimidazobenzisoquinolinones)] (SPBIBI) and the semi-crystalline poly(vinylidene fluoride) (PVDF) was prepared for proton exchange membranes. The miscibility behavior of a series of blends of SPBIBI with PVDF at various weight ratios was studied by WXRD, DSC and FTIR. The properties of the blend membranes were investigated, and it was found that the introduction of PVDF in the SPBIBI matrix altered the morphological structure of the blend membranes, which led to the formation of improved connectivity channels. For instance, the conductivity of the blend membrane containing 10 wt% PVDF displayed the highest proton conductivity (i.e., 0.086 S cm(-1)) at room temperature, a value almost twofold that of the pristine SPBIBI membranes (i.e., 0.054S cm(-1)) under identical conditions.

Novel proton exchange membranes based on water resistant sulfonated poly[bis(benzimidazobenzisoquinolinones)]

Novel water resistant sulfonated poly[bis(benzimidazobenzisoquinolinones)] (SPBIBIs) were synthesized from 6,6'-disulfonic-4,4'-binaphthy]-1,1',8,8'-tetracarboxylic dianhydride (SBTDA) and various aromatic ether tetraamines. The resulting polymers with IEC in the range of 2.17-2.87 mequiv g(-1) have a combination of desired properties such as high solubility in common organic solvents, film-forming ability, and excellent thermal and mechanical properties. Flexible and tough membranes, obtained by casting from m-cresol solution, had tensile strength, elongation at break, and tensile modulus values in the range of 87.6-98.4 MPa, 35.8-52.8%, and 0.94-1.07 GPa. SPBIBI membranes with a high degree of sulfonation displayed high proton conductivity and a good resistance to water swelling as well. SPBIBI-b with IEC of 2.80 mequiv g(-1) displayed the conductivity of 1.74 x 10(-1) S cm(-1) at 100 degrees C, which was comparable to that of Nafion (R) 117 (1.78 x 10(-1) S cm(-1), at 100 degrees C).

Synthesis and property of a novel sulfonated poly(ether ether ketone) with high selectivity for direct methanol fuel cell applications

Bisphenol monomer 4-carboxylphenyl hydroquinone (4C-PH) containing carboxyl groups was synthesized by diazotization reaction of p-aminobenzoic acid and 1,4-benzoquinone and subsequent reductive reaction. Copolymerization of bisphenol A, 4C-PH, sodium 5,5'-carbonylbis(2-fluorobenzene-sulfonate) and 4,4'-difluorobenzophenone at various molar ratios through aromatic nucleophilic substitution reaction resulted in a new sulfonated poly(ether ether ketone) containing pendant carboxyl groups (C-SPEEK). The structures of the monomer 4C-PH and copolymers were confirmed by FT-IR and H-1 NMR. Flexible and transparent membranes with sulfonic and carboxylic acid groups as the proton conducting sites were prepared. The dependence of ion-exchange capacity (IEC), water uptake, proton conductivity and methanol permeability on the degree of sulfonation has been studied.

High proton conductive advanced hybrid membrane based on sulfonated Si-SBA-15

Composite membranes based on Sulfonated poly(ether ether ketone) (SPEEK) and sulfonated organically modified Si-SBA-15 (S-SBA-15) were investigated with the purpose of increasing the proton conductivity. The novelty of the composite membranes was attributed to two special structures and different ion exchange capacities (IEC) of S-SBA-15 fillers, which were embedded in membranes. The typical hexagonal channels array of S-SBA-15 was confirmed by XRD and TEM. The regular vermiculate and amorphous structures of the inorganic fillers were proved by SEM. Composite membranes were prepared through common solvent casting method. SEM images indicated that the inorganic filler with regular structure dispersed homogeneously in the composite membranes, but the amorphous filler caused an agglomeration phenomenon at the same loading content.

Novel sulfonated poly(arylene ether ketone) copolymers bearing carboxylic or benzimidazole pendant groups for proton exchange membranes

A novel strategy in which the benzimidazole group and sulfonic group are simultaneously attached to an aromatic polymer has been reported in this paper. For this purpose, sulfonated poly(arylene ether ketone) copolymers containing carboxylic acid groups (SPAEK-x-COOH, x refers to the molar percentage Of sulfonated repeating units) are prepared by the aromatic nucleophilic polycondensation of sodium 5,5'-carbonyl-bis(2-fluobenzene-sulfonate) (SDFBP), 4,4'-difluorobenzophenone (DFBP) and phenolphthalin (PPL). Then the carboxylic acid groups attached to the SPAEK-x-COOH are transformed to benzimidazole units through condensation reactions (referred to as SPAEK-x-BI). Fourier transform infrared spectroscopy and H-1 NMR measurements are used to characterize and confirm the structures of these copolymers.

Synthesis and characterization of novel sulfonated poly(arylene ether ketone) copolymers with pendant carboxylic acid groups for proton exchange membranes

A series of novel side-chain-type sulfonated poly(arylene ether ketone)s with pendant carboxylic acid groups copolymers (C-SPAEKs) were synthesized by direct copolymerization of sodium 5,5'-carbonyl-bis(2-fluorobenzenesulfonate), 4,4'-difluorobenzophenone and 4,4'-bis(4-hydroxyphenyl) valeric acid (DPA). The expected structure of the sulfonated copolymers was confirmed by FT-IR and H-1 NMR. Membranes with good thermal and mechanical stability could be obtained by solvent cast process. It should be noted that the proton conductivity of these copolymers with high sulfonation degree (DS > 0.6) was higher than 0.03 S cm(-1) and increased with increasing temperature. At 80 degrees C, the conductivity of C-SPAEK-3 (DS = 0.6) and C-SPAEK-4 (DS = 0.8) reached up to 0.12 and 0.16 S cm-1, respectively, which were higher than that of Nafion 117 (0.10 S cm(-1)).

Pore-filling membrane for direct methanol fuel cells based on sulfonated poly(styrene-ran-ethylene) and porous polyimide matrix

We have synthesized a porous co-polyimide film by coagulating a polyimide precursor in the non-solvent and thermal imidization. Factors affecting the morphology, pore size, porosity, and mechanical strength of the film were discussed. The porous polyimide matrix consists of a porous top layer and a spongy sub-structure with micropores. It is used as a porous matrix to construct sulfonated poly(styrene-ran-ethylene) (SPSE) infiltrated composite membrane for direct methanol fuel cell (DMFC) application. Due to the complete inertness to methanol and the very high mechanical strength of the polyimide matrix, the swelling of the composite membrane is greatly suppressed and the methanol crossover is also significantly reduced, while high proton conductivity is still maintained. Because of its higher proton conductivity and less methanol permeability, single fuel cell performance test demonstrated that this composite membrane outperformed Nafion membrane.