Ionic conductivity of bis(2-cyanoethyl) ether-lithium salt and poly(propylether imine)-lithium salt liquid electrolytes

We report here a multiple-nitrile based lithium-salt liquid electrolyte. The ionic conductivity of poly (propyl ether imine) (abbreviated as PETIM) lithium salt dendrimer liquid electrolyte was observed to be a function of dendrimer generation number, n=0 (monomer)-3. While the highest room temperature ionic conductivity value (similar to 10(-1) Sm-1) was recorded for the bis-2cyanoethyl ether monomer (i.e. zeroth generation; G(0)-CN), conductivity decreased progressively to lower values (similar to 10(-3) Sm-1) with increase in generation number (G(1)-CN -> G(3)-CN). The G(0)-CN and higher dendrimer generations showed high thermal stability (approximate to 150 to 200 degrees C), low moisture sensitivity and tunable viscosity (similar to 10(-2) (G(0)-CN) to 3 (G(3)-CN) Pa s). The linker ether group was found to be crucial for ion transport and also eliminated a large number of detrimental features, chiefly moisture sensitivity, chemical instability associated typically with prevalent molecular liquid solvents. Based on the combination of several beneficial physicochemical properties, we presently envisage that the PETIM dendrimers especially the G(0)-CN electrolytes hold promise as electrolytes in electrochemical devices such as lithium-ion batteries.

Effect of pressure on the ionic conductivity of Li+ and Cl- ions in water

A molecular dynamics simulation study of aqueous solution of LiCl is reported as a function of pressure. Experimental measurements of conductivity of Li+ ion as a function of pressure shows an increase in conductivity with pressure. Our simulations are able to reproduce the observed trend in conductivity. A number of relevant properties have been computed in order to understand the reasons for the increase in conductivity with pressure. These include radial distribution function, void and neck distributions, hydration or coordination numbers, diffusivity, velocity autocorrelation functions, angles between ion-oxygen and dipole of water as well as OH vector, mean residence time for water in the hydration shell, etc. These show that the increase in pressure acts as a structure breaker. The decay of the self part of the intermediate scattering function at small wave number k shows a bi-exponential decay at 1 bar which changes to single exponential decay at higher pressures. The k dependence of the ratio of the self part of the full width at half maximum of the dynamic structure factor to 2Dk(2) exhibits trends which suggest that the void structure of water is playing a role. These support the view that the changes in void and neck distributions in water can account for changes in conductivity or diffusivity of Li+ with pressure. These results can be understood in terms of the levitation effect. (C) 2012 American Institute of Physics. http://dx.doi.org/10.1063/1.4756909]

Relation Between the Diffusivity, Viscosity, and Ionic Radius of LiCl in Water, Methanol, and Ethylene Glycol: A Molecular Dynamics Simulation

A molecular dynamics (MD) investigation of LiCl in water, methanol, and ethylene glycol (EG) at 298 K is reported. Several; structural and dynamical properties of the ions as well as the solvent such as self-diffusivity, radial distribution functions, void and neck distributions, velocity autocorrelation functions, and mean residence times of solvent in the first solvation shell have been computed. The results show that the reciprocal relationship between the self-diffusivity of the ions and the viscosity is valid in almost all solvents with the exception of water. From an analysis of radial distribution functions and coordination numbers the nature of hydrogen bonding within the solvent and its influence on the void and neck distribution becomes evident. It is seen that the solvent solvent interaction is important in EG while solute solvent interactions dominate in water and methanol. From Voronoi tessellation, it is seen that the voids and necks within methanol are larger as compared to those within water or EG. On the basis of the void and neck distributions obtained from MD simulations and literature experimental data of limiting ion conductivity for various ions of different sizes we show that there is a relation between the void and neck radius on e one hand and dependence of conductivity on the ionic radius on the other. It is shown that the presence of large diameter voids and necks in methanol is responsible for maximum in limiting ion conductivity (lambda(0)) of TMA(+), while in water in EG, the maximum is seen for Rb+. In the case of monovalent anions, maximum in lambda(0) as a function ionic radius is seen for Br- in water EG but for the larger ClO4- ion in methanol. The relation between the void and neck distribution and the variation in lambda(0) with ionic radius arises via the Levitation effect which is discussed. These studies show the importance of the solvent structure and the associated void structure.

Role of Cu2+ ions substitution in magnetic and conductivity behavior of nano-CoFe2O4

Cobalt copper ferrite nanopowders with composition Co1-xCu5Fe2O4 (0.0 <= x <= 0.5) was synthesized by solution combustion method. The powder X-ray diffraction studies reveal the formation of single ferrite phase with particle size of similar to 11-35 nm. Due to increase in electron density with in a material, X-ray density increase with increase of Cu2+ ions concentration. As Cu2+ ions concentration increases, saturation magnetization decreases from 38.5 to 26.7 emu g(-1). Further, the squareness ratio was found to be similar to 0.31-0.46 which was well below the typical value 1, which indicates the existence of single domain isolated ferrimagnetic samples. The dielectric and electrical modulus was studied over a frequency range of 1 Hz to 1 MHz at room temperature using the complex impedance spectroscopy technique. Impedance plots showed only one semi-circle which corresponds to the contributions of grain boundaries. The lower values of dielectric loss at higher frequency region may be quite useful for high frequency applications such as microwave devices. (C) 2014 Elsevier B.V. All rights reserved.

Size-Dependent Interface Phonon Transmission And Thermal Conductivity Of Nanolaminates

An analytical model for size-dependent interface phonon transmission and thermal conductivity of nanolaminates is derived based on the improved acoustic mismatch theory and the Lindemann melting theory by considering the size effect of phonon velocity and the interface lattice mismatch effect. The model suggests that the interface phonon transmission is dominant for the cross-plane thermal conductivity of nanolaminates and superlattices, and the intrinsic variety of size effect of thermal conductivity for different systems is proposed based on the competition mechanism of size effect of phonon transport between two materials constituting the interfaces. The model's prediction for thermal conductivity of nanolaminates agrees with the experimental results. (C) 2008 American Institute of Physics.

A dual mode SOI CMOS MEMS based thermal conductivity and IR absorption gas sensor

Design, FEM modelling and characterization of a novel dual mode thermal conductivity and infrared absorption sensor using SOI CMOS technology is reported. The dual mode sensing capability is based on the temperature sensitivity and wideband infrared radiation emission of the resistive heating element. The sensor was fabricated at a commercial foundry using a 1 μm process and measures only 1×1 mm2. Infrared detectors usually use thermopiles in addition to a separate IR source. A single highly responsive dual mode source and sensing element targeting not only low molecular mass gases but also greenhouse gases, while consuming 40 mW power at 700°C in synthetic air, thus makes this sensor particularly viable for battery powered handheld devices. © 2013 IEEE.

Investigation on the structural origin of n-type conductivity in InN films

This work presents a study of the correlation between the electrical properties and the structural defects in nominally undoped InN films. It is found that the density of edge-type threading dislocations (TDs) considerably affects the electron concentration and mobility in InN films. The Hall-effect measured electron concentration increases, while the Hall mobility decreases with the increase in the edge-type TD density. With the combination of secondary ion mass spectrometry and positron annihilation analysis, we suggest that donor-type point defects at the edge-type TD lines may serve as dominant donors in InN films and affect the carrier mobility.

Growth and characterization of InGaAs/InAlAs/InP high-electron-mobility transistor structures towards high channel conductivity

High-quality InGaAs/InAlAs/InP high-electron-mobility transistor (HEMT) structures with lattice-matched or pseudomorphic channels have been grown by molecular-beam epitaxy (MBE). The purpose of this work is to enhance the channel conductivity by changing the epitaxial structure and growth process. With the use of pseudomorphic step quantum-well channel, the highest channel conductivity is achieved at x = 0.7, the corresponding electron mobilities are as high as 12300 (300 K) and 61000 cm(2)/V.s (77 K) with two-dimensional electron gas (2DEG) density of 3.3 x 10(12) cm(-2). These structures are comprehensively characterized by Hall measurements, photoluminescence, double crystal X-ray diffraction and transmission electron microscopy. Strong room-temperature luminescence is observed, demonstrating the high optical quality of the samples. We also show that decreasing the In composition in the InyAl1-yAs spacer is very effective to increase the 2DEG density of PHEMT structures. (C) 1998 Published by Elsevier Science B.V. All rights reserved.

Scaling and the thermal conductivity of the Frenkel-Kontorova model

We have studied the dependence of the thermal conductivity kappa on the strength of the interparticle potential lambda and the strength of the external potential beta in the Frenkel-Kontorova model. We found that the functional relation can be expressed in a scaling form, kappa(proportional to) lambda 3/2/beta(2 center dot). This result is first obtained by nonequilibrium molecular dynamics. It is then confirmed by two analytical methods, the self-consistent phonon theory and the self-consistent stochastic reservoirs method. The thermal conductivity kappa is therefore a decreasing functon of beta and an increasing function of lambda.

Novel hydrophilic-hydrophobic multiblock copolyimides as proton exchange membranes: Enhancing the proton conductivity

A series of novel multiblock copolymers based on sulfonated copolyimides were developed and evaluated for use as proton exchange membranes (PEMs). In these multiblock copolyimides, the hydrophilic blocks were composed of the sulfonated dianhydride and the sulfonated diamine, with sulfonic acid groups on every aromatic ring (i.e., fully sulfonated). This molecular design was implemented to effectively enhance the proton conductivity. The properties of the multiblock copolyimides with varying IEC values or block lengths were investigated to obtain a better understanding of the relationship between molecular structure and properties of proton exchange membranes. The water uptake and proton conductivity were found to be highly dependent upon their structure. The block copolymers displayed significantly higher proton conductivities, especially at low relative humidity than the random copolymers with a similar IEC.

Relaxation time and conductivity of comb-like gel polymer electrolytes

Using the copolymer of acrylonitrile (AN), methyl methacrylate (MMA), and poly(ethylene glycol) methyl ether methacrylate as a backbone and poly(ethylene glycol) methyl ether (PEGME) with 1100 molecular weight as side chains, comb-like gel polymers and their Li salt complexes were synthesized. The dynamic mechanical properties and conductivities were investigated. Results showed that the gel copolymer electrolytes possess two glass transitions: alpha-transition and beta-transition. Based on the time-temperature equivalence principle, a master curve was constructed by selecting T. as reference temperature. By reference to T-0 = 50 degrees C, the relation between log c, and c was found to be linear. The master curves are displaced progressively to higher frequencies as the content of plasticizer is increased. The relation between log tau(p) and the content of plasticizer is also linear.

Study of the conductivity and side chain mobility of a comb-like polymer electrolyte using the dynamic mechanical method

Using poly(styrene-co-maleic anhydride) as a backbone and poly(ethylene glycol) methyl ether (PEGME) with different molecular weights as side chains, three comb-like polymers and their Li salt complexes were synthesized. The dynamic mechanical properties and conductivities were investigated. Results showed that the polymer electrolytes possess two glass transitions: alpha -transition and beta -transition, and the temperature dependence of the ionic conductivity shows WLF (Williams-Landel-Ferry) behavior. Based on the time-temperature equivalence principle, a master curve was constructed by selecting T-beta as reference temperature. The values of the WLF parameters (C-1 and C-2) were obtained and were found to be almost independent of the length of the PEGME side chain and the content of Li salt. By reference to T-0 = 50 degreesC. the relation between log tau (c) and c was found to be linear. The master curves are displaced progressively to higher frequencies as the molecular weight of the side chain is increased. The relation between log tau (n) and the molecular weight of the side chain is also linear. (C) 2001 Elsevier Science B.V. All rights reserved.

Transport property of polyaniline and its molecular weight dependence

The electrical conductivity of polyaniline doped with camphor sulfonic acid (PAn-CSA) was studied. The results indicate that there is a critical temperature (T-c) and the temperature dependence of PAn-CSA conductivity shows metallic and semiconductor characteristics above and below T-c, respectively. The higher the molecular weight of PAn, the lower the T-c. The conductivity was enhanced remarkably when PAn-CSA film was stretched, its room temperature conductivity is up to 750 S/cm when elogonation is 60%; however, T-c was independent of elongation.

Ionic conductivity of gel electrolyte based on polydiethylene glycol dimethacrylate and its copolymer

Gel electrolytes were prepared by thermal polymerization of diethylene glycol dimethacrylate (DIEGD) or its copolymer with methoxy polyethylene glycol monomethacrylate, molecular weight 400 (PEM(400)), at a molar ratio of 3/1 in the presence of propylene carbonate (PC) and LiClO4. Conductivity was measured by impedance spectroscopy. It was found that the conductivity data follow the Arrhenius equation in the homopolymer gel system, while the VTF equation holds true in the copolymer gel system. An increase in conductivity was observed in the copolymer gel system. However, whether in the homopolymer or in the copolymer gel system, a maximum ambient temperature conductivity was found at a salt concentration near 1.50 mol/l. Further, the activation energy values calculated from Arrhenius plots for the homopolymer gel system tended to reach a minimum value with increasing salt concentration. (C) 1996 Elsevier Science Ltd

IONIC-CONDUCTIVITY AND DYNAMIC MECHANICAL RELAXATION OF A 2-COMPONENT EPOXY NETWORK-LICLO4 ELECTROLYTE SYSTEM

The correlation between mechanical relaxation and ionic conductivity was investigated in a two-component epoxy network-LiClO4 electrolyte system. The network was composed of diglycidyl ether of polyethylene glycol (DGEPEG) and triglycidyl ether of glycerol (TGEG). The effects of salt concentration, molecular weight of PEG in DGEPEG and the proportion of DGEPEG (1000) in DGEPEG/TGEG ratio on the ionic conductivity and the mechanical relaxation of the system were studied. It was found that, among the three influential factors, the former reinforces the network chains, reduces the free volume fraction and thus increases the relaxation time of the segmental motion, which in turn lowers the ionic conductivity of the specimen. Conversely, the latter two increase the free volume and thus the chain flexibility, showing an opposite effect. From the iso-free-volume plot of the shift factor log at and reduced ionic conductivity, it is noted that the plot can be used to examine the temperature dependence of segmental mobility and seems to be useful to judge whether the incorporated salt has been dissociated completely. Besides, the ionic conductivity and relaxation time at constant reference temperature are linearly correlated with each other in all the three cases. This result gives an additional experimental confirmation of the coordinated motion model of the ionic hopping with the moving polymer chain segment, which is generally used to explain the ionic conduction in non-glassy amorphous polymer electrolytes.