Análise microestrutural de misturas cerâmicas de grês porcelanato com adição de chamote de telhas cerâmicas

MELO, Maxymme Mendes de ; PINHEIRO, Andrea Santos ; NASCIMENTO, R. M. ; MARTINELLI, Antonio Eduardo ; DUTRA, Ricardo Peixoto Suassuna ; MELO, Marcus Antônio de Freitas . Análise microestrutural de misturas cerâmicas de grês Porcelanato com adição de chamote de telhas cerâmicas. Cerâmica (São Paulo. Impresso), v. 55, p. 356-364, 2009

Estudo do efeito da adição da escória de aciaria no processamento e propriedades finais de telhas cerâmicas

This research presents an overview of the addition steelwork dust of ceramic shingles in order to contribute to the utilization use of such residue. The ceramic industry perspective in the Brazilian State of Piauí is quite promising. Unlike other productive sectors, the ceramic industry uses basically natural raw materials. Its final products are, in short, the result of transforming clay compounds. These raw materials are composed primarily of aluminum oxide, silicon, iron, sodium, magnesium, end calcium, among others. It was verified that steelwork dust is composed primarily of these same oxides, so that its incorporation in to structural ceramics is a very reasonable idea. Both clay and steelwork powder were characterized by AG, XRF, XRD, TGA and DTA. In addition, steelwork dust samples containing (0%, 5%, 10%, 15%, 20% and 25%) were extruded and burned at 800°C, 850°C, 900°C and 950°C. Then t echnological tests of linear shrinkage, water uptake, apparent porosity, apparent density and flexural strengthwere carried at. The results showed the possibility of using steelwork powder in ceramic shingles until 15% significant improvement in physical and mechanical properties. This behavior shows the possibility of burning at temperatures lower than 850ºC, thus promoting a product final cost reduction

Estudo de rejeitos de galvanoplastia e a sua aplicação na fabricação de peças cerâmicas rústicas para fins decorativos

Pós-graduação em Geologia Regional - IGCE

Análise microestrutural de misturas cerâmicas de grês porcelanato com adição de chamote de telhas cerâmicas

MELO, Maxymme Mendes de ; PINHEIRO, Andrea Santos ; NASCIMENTO, R. M. ; MARTINELLI, Antonio Eduardo ; DUTRA, Ricardo Peixoto Suassuna ; MELO, Marcus Antônio de Freitas . Análise microestrutural de misturas cerâmicas de grês Porcelanato com adição de chamote de telhas cerâmicas. Cerâmica (São Paulo. Impresso), v. 55, p. 356-364, 2009

Análise microestrutural de misturas cerâmicas de grês porcelanato com adição de chamote de telhas cerâmicas

MELO, Maxymme Mendes de ; PINHEIRO, Andrea Santos ; NASCIMENTO, R. M. ; MARTINELLI, Antonio Eduardo ; DUTRA, Ricardo Peixoto Suassuna ; MELO, Marcus Antônio de Freitas . Análise microestrutural de misturas cerâmicas de grês Porcelanato com adição de chamote de telhas cerâmicas. Cerâmica (São Paulo. Impresso), v. 55, p. 356-364, 2009

Estudo do efeito da adição da escória de aciaria no processamento e propriedades finais de telhas cerâmicas

This research presents an overview of the addition steelwork dust of ceramic shingles in order to contribute to the utilization use of such residue. The ceramic industry perspective in the Brazilian State of Piauí is quite promising. Unlike other productive sectors, the ceramic industry uses basically natural raw materials. Its final products are, in short, the result of transforming clay compounds. These raw materials are composed primarily of aluminum oxide, silicon, iron, sodium, magnesium, end calcium, among others. It was verified that steelwork dust is composed primarily of these same oxides, so that its incorporation in to structural ceramics is a very reasonable idea. Both clay and steelwork powder were characterized by AG, XRF, XRD, TGA and DTA. In addition, steelwork dust samples containing (0%, 5%, 10%, 15%, 20% and 25%) were extruded and burned at 800°C, 850°C, 900°C and 950°C. Then t echnological tests of linear shrinkage, water uptake, apparent porosity, apparent density and flexural strengthwere carried at. The results showed the possibility of using steelwork powder in ceramic shingles until 15% significant improvement in physical and mechanical properties. This behavior shows the possibility of burning at temperatures lower than 850ºC, thus promoting a product final cost reduction

Imobilização do íon cromo oriundo de cinzas da incineração de serragem de couro em corpos cerâmicos vitrificados

Este trabalho teve como objetivo principal investigar o processo de imobilização do íon cromo, oriundo da cinza de incineração da serragem de couro curtido ao cromo (CSC), em corpos cerâmicos vitrificados. Para tanto, foram desenvolvidas formulações com adição de vidro sodocálcico a CSC, que foram submetidas a diferentes temperaturas de queima. Para o aprofundamento da investigação dos fenômenos atuantes no processo de imobilização do íon cromo, foram formuladas massas cerâmicas com a adição de óxidos puros de Na2O, TiO2, MgO e CaO, à composição CSC e vidro sodo-cálcido. As massas cerâmicas foram conformadas por prensagem uni-axial de duplo efeito e queimadas em forno elétrico tipo mufla, nas temperaturas de 750, 800, 950 e 1000ºC. Posteriormente, foram caracterizadas quanto às propriedades físicas e composição mineralógica, bem como, avaliadas quanto à imobilização do cromo através de ensaios de lixiviação, segundo a Norma NBR 10.005. O controle de fases formadas resultante do processamento cerâmico foi investigado com o auxílio de difração de raios X e mapeamento por microssonda EDS. Os resultados obtidos indicam que é possível obter a imobilização do íon cromo da CSC, de acordo com o limite máximo estabelecido pela NBR 10.004 (5mg/L), utilizando vidro e agentes de vitrificação/densificação, como o óxido de titânio e óxido de magnésio. Quanto mais elevada a temperatura de queima, mais efetiva foi a imobilização de cromo nos corpos cerâmicos investigados. O aumento da temperatura de queima diminui a porosidade aberta, via formação de fase vítrea, levando desse modo a uma diminuição da lixiviação do cromo. No entanto, a adição somente de vidro a CSC aumentou a lixiviação do cromo dos corpos cerâmicos, embora sempre menor para temperaturas de queima crescentes. Deve-se isso, ao aumento de fases lixiviáveis, como cromatos de sódio, a partir da reação do sódio, do vidro sodo-cálcico e do cromo da CSC. Os corpos cerâmicos que apresentaram a fase cromato de sódio, apresentaram deficiente imobilização do íon cromo, em todas as formulações investigadas.

Reciclagem de pó de aciaria elétrica como matéria-prima na fabricação de materiais cerâmicos argilosos : controle das emissões atmosféricas de zinco

O pó de aciaria é um dos resíduos sólidos gerados pela indústria siderúrgica durante a produção de aço em forno elétrico a arco. Este trabalho tem por objetivo investigar a evolução de Zn na produção de materiais cerâmicos ao utilizar-se pó de aciaria como matéria-prima no processamento de massas cerâmicas à base de argilas vermelhas. Para tanto, foram preparadas massas cerâmicas contendo 0, 1, 5, 10, 20 e 30% em peso de pó de aciaria. Os corpos-de-prova, medindo cerca de 20x60x8 mm3, foram prensados e queimados em fornos elétricos tipo mufla, em laboratório. As temperaturas de queima foram de 850oC a 1050oC, taxa de aquecimento de 150°C/h e 300°C/h, em patamar de queima de 2 horas. Com o objetivo de avaliar as possíveis emissões atmosféricas geradas durante a queima, os corpos-de-prova foram dispostos em um reator de quartzo, com pressão abaixo da pressão atmosférica. As emissões gasosas assim coletadas eram lavadas e a água de lavagem foi analisada. Os resultados mostraram que Zn foi coletado nas águas de lavagens dos gases, não ficando totalmente imobilizado na estrutura cerâmica. De acordo com os resultados obtidos, observou-se que quanto maior a taxa de aquecimento, maior a emissão de zinco nas águas de lavagem dos gases. O pó de aciaria é um dos resíduos sólidos gerados pela indústria siderúrgica durante a produção de aço em forno elétrico a arco. Este trabalho tem por objetivo investigar a evolução de Zn na produção de materiais cerâmicos ao utilizar-se pó de aciaria como matéria-prima no processamento de massas cerâmicas à base de argilas vermelhas. Para tanto, foram preparadas massas cerâmicas contendo 0, 1, 5, 10, 20 e 30% em peso de pó de aciaria. Os corpos-de-prova, medindo cerca de 20x60x8 mm3, foram prensados e queimados em fornos elétricos tipo mufla, em laboratório. As temperaturas de queima foram de 850oC a 1050oC, taxa de aquecimento de 150°C/h e 300°C/h, em patamar de queima de 2 horas. Com o objetivo de avaliar as possíveis emissões atmosféricas geradas durante a queima, os corpos-de-prova foram dispostos em um reator de quartzo, com pressão abaixo da pressão atmosférica. As emissões gasosas assim coletadas eram lavadas e a água de lavagem foi analisada. Os resultados mostraram que Zn foi coletado nas águas de lavagens dos gases, não ficando totalmente imobilizado na estrutura cerâmica. De acordo com os resultados obtidos, observou-se que quanto maior a taxa de aquecimento, maior a emissão de zinco nas águas de lavagem dos gases.

Desenvolvimento de cerâmica vermelha utilizando rejeitos da construção civil

The Industry of the Civil Construction has been one of the sectors that most contribute to the pollution of the environment, due to the great amount of residues generated by the construction, demolition and the extraction of raw material. As a way of minimizing the environmental impacts generated by this industry, some governmental organizations have elaborated laws and measures about the disposal of residues from the building construction (CONAMA - resolution 307). This work has as objective the reutilization of residues compound of sand, concrete, cement, red bricks and blocks of cement and mortar for the production of red ceramic, with the objective of minimizing costs and environmental impacts. The investigated samples contained 0% to 50% of residues in weight, and they were sintered at temperatures of 950°C, 1000°C, 1050°C, 1100°C and 1150°C. After the sinterization, the samples were submitted to tests of absorption of water, linear retraction, resistance to bending, apparent porosity, specific density, XRD and SEM. Satisfactory results were obtained in all studied compositions, with the possible incorporation of up to 50% of residues in ceramic mass without great losses in the mechanical strength, giving better results to the incorporation of 30% of residues in the fabrication of ceramic parts, such as roofing tiles, bricks masonry and pierced bricks

Efeito da adição de carbonatos em formulação de massa para revestimento cerâmico utilizando matérias-primas do Piauí

Piauí state is a major producer of traditional red ceramic burning as bricks, tiles and ceramic tiles, with its main production center located in the city of Teresina. The state has large reserves of raw materials that can be used in the ceramic coating as clays, quartz, talc and carbonates. However, in the preparation of ceramic bodies using only a mixture of clays with different characteristics. The study aims to evaluate the effect of adding two types of carbonates in the ceramic semiporous mass coating produced in Piauí and then to verify the potential use of these carbonates as supplementary raw material product manufactured or the feasibility of obtaining a ceramic plate that meets the specifications for the porous coating. For this, were characterized the ceramic Piauí coating mass, a calcitic carbonate and a dolomitic, were made in the levels of 2, 4, 8, 16, and 32%. The masses were formed by pressing and burneds in two environments: a laboratory furnace (1080°C, 1120°C, 1140°C, and 1160°C) and an industrial furnace (1140°C). Then, following tests of linear shrinkage water absorption, apparent porosity, bulk density and flexural strength. Furthermore, the fired specimens were tested for their macrostructure and microstructure. The results showed the possibility of using the carbonate in ceramic mass flooring produced in Piauí, as added in small proportions improved dimensional stability and increased mechanical strength of ceramics pieces. It also proved itself possible to produce porous coating when added in higher levels

Uso de resíduo e de minerais de pegmatito da região do seridó RN e de argilas portuguesas em formulações de grês porcelanato

In the State Rio Grande do Norte, Brazil, the most significant deposits of minerals in the production of granite and pegmatite are Seridó region. Municipalities of Parelhas and Equador are the main responsible for the production of feldspar, quartz, kaolin and granite. The ceramic industries are always in search of competitiveness by investing in new products or improving existing techniques. The stoneware is a type of pottery that stands in the market because it presents technical and aesthetic characteristics superior to other existing products. Characteristics of the raw materials initially obtained with chemical analysis and mineralogical analysis are crucial in getting a product that satisfies the conditions in a manufacturing process and is, in principle, directly related to the firing cycle. This research aimed at developing new formulations for the mass production of ceramic stoneware. The raw materials initially characterized were feldspar, quartz, kaolin and granite. As part of the research was developed at the University of Aveiro, in Portugal, we used two clays used in the production of Portuguese ceramics. The raw material Brazilian and Portuguese and the final product, both in Portugal and Brazil, were analyzed for X-ray fluorescence, X-ray diffraction, granulometric analysis, dilatometric analysis, thermal analysis and analysis of scanning electron microscopy (MEV). The specimens prepared at the University of Aveiro (DECV) were sintered at 10000C and 12000C and the specimens prepared in UFRN were sintered at 10000C, 10500C, 11000C, 11500C, 12000C, 12500C and 13000C, but the best results and demonstrating the presence of the mineral mullite were at temperatures of 12000C, 12500C and 13000C. The results showed that the granite waste used may be considered raw material of excellent quality for use in the ceramic industry and coating floors and more accurately by the industry of stoneware. Physical and mechanical tests conducted on samples of the formulations F01 and F02 developed in UFRN showed a water absorption and mechanical strength suitable for the stoneware

Desenvolvimento de membranas porosas de alumina para fins de tratamento de efluente industrial têxtil

Textile production has been considered as an activity of high environmental impact due to the generation of large volumes of waste water with high load of organic compounds and strongly colored effluents, toxic and difficult biodegradability. This thesis deals with obtaining porous alumina ceramic membranes for filtration of textile effluent in the removal of contaminants, mainly color and turbidity. Two types of alumina with different particle sizes as a basis for the preparation of formulation for mass production of ceramic samples and membranes. The technological properties of the samples were evaluated after using sintering conditions: 1,350ºC-2H, 1,450ºC-30M, 1,450ºC-2H, 1,475ºC-30M and 1,475ºC-2H. The sintered samples were characterized by XRD, XRF, AG, TG, DSC, DL, AA, MEA, RL, MRF-3P, SEM and Intrusion Porosimetry by Mercury. After the characterization, a standard membrane was selected with their respective sintering condition for the filterability tests. The effluent was provided by a local Textile Industry and characterized at the entry and exit of the treatment plant. A statistical analysis was used to study the effluent using the following parameters: pH, temperature, EC, SS, SD, oil and grease, turbidity, COD, DO, total phosphorus, chlorides, phenols, metals and fecal coliform. The filtered effluent was evaluated by using the same parameters. These results demonstrate that the feasibility of the use of porous alumina ceramic membranes for removing contaminants from textile effluent with improved average pore size of 0.4 micrometre (distribution range varying from 0,025 to 2.0 micrometre), with total porosity of 29.66%, and average percentages of color removal efficiency of 89.02%, 92.49% of SS, turbidity of 94.55%, metals 2.70% (manganese) to 71.52% (iron) according to each metal and COD removal of 72.80%

Estudo de Matérias-Primas do Rio Grande do Norte para Uso em Revestimento Poroso: Influência do teor de dolomita e temperatura de calcinação nas propriedades físico-mecânicas

The state of Rio Grande do Norte presents a great potentiality for the production of ceramic tiles because of having natural raw material in quantity and quality making its economical exploration possible, beyond the great energetic differential of the state, the natural gás. This works aims to study the influence of the dolomite and granulometry concentration and calcinations temperature in the obtaining of formulations for porous coverings which have to be coherent to the project,s specifications. The experiments have involved the physical-chemical and mineralogical characterizations of raw materials and mechanical tests in the dry and burnt proof bodies preceding a mixture experiment planning with the use of the response surface methodology, in order to get the best raw materials combinations to produce a ceramic mass with specific properties. The twelve ceramic masses studied in this work were prepared by the via dry process, characterized, shaped by uniaxial pressing and sinterized in the temperatures of 940ºC, 1000ºC, 1060ºC, 1120ºC and 1180ºC, using a fast burning cycle. The crystalline phases formed during the sintering in the temperatures in study have revealed the presence of anorthite and diopside beyond quartz with a remaining phase. These phases were the main responsible ones by the physical- mechanical properties of the sinterized proof bodies. The proof bodies after the sintering stage have presented water absorption higher than 10% and a good dimensional stability in all studied temperatures. However, the flexural breaking strength results in the temperatures of 940ºC, 1000ºC and 1060ºC, under the temperature zone of the vitrification of ceramic whiteware do not reach the flexural breaking strength specific for the porous wall tile (15 MPa), but in the temperature of 1120ºC next to the vitrification temperature zone, some whiteware ceramic (formulations) has reached the specified value for the porous wall tile. The results of this work have showed that the studied raw materials have great importance for used in the production of porous wall tiles (BIII)

Aproveitamento de resíduo de beneficiamento do caulim na produção de porcelanato cerâmico

Nowadays, industries from all sectors have great concerns over the disposition of the residues generated along the productive process. This is not different in the mineral sector, as this generates great volumes of residues. It was verified that the kaolin improvement industry generates great volumes of residue basically constituted of kaolinite, muscovite mica and quartz, which are basic constitution elements to formularisations of ceramics masses to the production of covering of stoneware tiles type. This happens because the methodology applied to the improvement process is still very rudimentary, what causes a very low yield, only ¼ from all the material volume that enters the improvement process, in the end, is marketable. The disposal of this residue, in a general way, causes a very big negative environmental impact, what has justified the researches efforts aiming to find a rational solution to this problem. In this way, the intention of this present work is the utilization of this residue in the manufacture of products to high quality ceramics covering, stoneware tiles in an industrial scale. For this purpose, the influence of the addition of the residue to a standard ceramics mass used by a ceramics sector company, already established in the market, with the intention of verifying the possibility of use of this residue as the mass complementary raw material and even the possible partial or total substitution of one of the components of the mass for the raw material in evidence will be studied. To the accomplishment of this work, the kaolin improvement residue generated by an industry of exploitation and improvement of kaolin, located in the region of Equador-RN, in the levels 1,2,4,8, 16 and 32% will be added to the standard mass already used for the production of stoneware tiles. The raw materials used, kaolin residue and the standard mass, were characterized through DRX, FRX, DTA, TGA and dilatometry. After the sintering of the bodies of test, tests of water absorption, apparent porosity, post burning linear retraction, apparent specific mass and flexural strength (3 point bending) were realized to determinate the technological properties of these materials. The results show the studied residue can be considered raw material of great potential to the industry of floor and ceramics covering of the stoneware tiles type

Aproveitamento de resíduo de caulim em cerâmica branca

The world market of Kaolin has been growing as new investments for better quality of materials have been applied. This market produces amounts of dross that are put in the environment in a wrong way, causing damages to it. Trying to reduce these damages, researches have been done in an attempt to use kaolin dross in ceramic. The disposal of kaolin dross in the environment by the industries of the states of Rio Grande do Norte and Paraiba have great impact in society. Usually this dross is disposed clandestinely in places like roads, river banks and lands of small cities. The present work shows the characteristics of the kaolin produced by the mining company in Junco do Seridó, Paraiba state, western Seridó, 300 km from Natal, in the border of both states. After that, researches were done to study its physical and the chemistry characteristics, trying to see if it can be used in white ceramic. The samples got were bolted in fabric of 325# . The technological characteristics tried to use it as a product in white ceramic. For that, it was made a haracterization of the subject matter through enlargement analyses, ATG and ATD, elaborating three formulations that were burned in four different temperatures, 1175, 1200, 1250 and 1300 degrees centigrade up to 30 minutes. After the burning, the subjects were submitted to water absorbing tests, linear retreating, apparent porosity, apparent specific mass, resistance to flexibility and MEV. For one of the mixtures it was obtained demanded properties for a semi porous material