Double-layer and solvation forces measured in a molten salt and its mixtures with water

Measurements have been made of the force between molecularly smooth mica surfaces immersed in ethylammonium nitrate, which is a molten salt at room temperature, and in mixtures of this salt with water across the concentration range from 10 -4 M to that of the pure salt, which is 11.2 M. At low concentrations the salt behaves as a typical 1:1 electrolyte, and we measure an electrical double-layer force whose range decreases with increasing salt concentration. At high concentrations, above about 1 M, the double-layer force becomes so weak and short-ranged that it is completely dominated by a solvation force extending up to 5 nm. In the pure molten salt the solvation force is an oscillatory function of surface separation comparable to that measured in simple nonpolar liquids. No monotonic component of solvation force is found.

Syntheses of bismuth titanate templates obtained by the molten salt method

Bismuth titanate templates (Bi4Ti3O12) were synthesized by the molten salt method in Na2SO4 and K2SO4 fluxes, using an amorphous Bi4Ti 3O12 precursor and a mechanically mixed Bi 2O3+TiO2 mixture as the starting materials. The templates were characterized by means of X-Ray Diffraction, FT-IR, FT-Raman, FEG-SEM and TEM. The templates are free of secondary phases and present orthorhombic structure with orientation in the c-plane. FT-IR suggests no traces of sulfate groups revealing that the molten salt synthesis was beneficial for elimination of inorganic species and for the arrangement of individual nanocrystals into ordered lattices. FEG-SEM analyses of BIT templates revealed that most of the grains were homogeneous with a length of 3.1 μm and a width of 0.3 μm and had plate-like morphology. TEM investigations show that the c-axis of the perovskite units is parallel to the thickness direction of the grains and no liquid-phase was formed during BIT phase formation. © 2013 Elsevier Ltd and Techna Group S.r.l.

Electrochemical Properties of Li3N Dissolved in Molten LiCl at 900 K

Thermodynamic properties of Li3N dissolved in the molten LiCl salt at 900 K were explored using electrochemical methods. It was difficult to determine precisely the decomposition voltage of Li3N dissolved in the molten salt by cyclic voltammetry. The oxidation wave of N3– ion could not be located with high accuracy. However, the lithium activity of the Pb-Li alloy in equilibrium with the molten salt containing dissolved Li3N under nitrogen atmosphere could be measured electrochemically with high accuracy using the Li/Li + reference electrode. Under the conditions used in this study, the potential of the Li-Pb electrode is equal to the decomposition voltage of Li3N. The activity of Li3N in molten LiCl was determined for anionic fractions of N3– ranging from xN3– = 10–4 to 0.028. The nitride ion concentration in the salt was determined by chemical titration. The activity coefficient of the Li3N at high dilution was found to be very low, around 10–4. The activity coefficient increases sharply with composition and has a value of 0.25 at xN3– = 0.028. ©2001 The Electrochemical Society. All rights reserved.

Synthesis of protective Mo-Si-B coatings in molten salts and their oxidation behavior in an air-water mixture

The formation of various phases during boronizing of silicided molybdenum substrates (MoSi2/Mo) was investigated. Boronizing treatments were conducted in molten salts under an inert gas atmosphere in the 700-1000 degrees C temperature range for 3-7 h. Depending on the process type (non-current or electrochemical) and molten salt temperature, the formation of different boride phases (MoB, Mo2B5, MoB2, MoB4) was observed. At the same time, substantial oxidation of the bulk molybdenum disilicide phase (MoSi2) to the Mo5Si3 phase was observed in non-current boronizing. The oxidation resistance of the coatings was investigated by the weight change in an air-water (2.3 vol.%) mixture at a temperature of 500 degrees C for a period up to 700 h. Results indicated that a two-phase microstructure consisting of the MoSi2, matrix phase with 12-15 wt.% of the MoB4 phase greatly improved the oxidation resistance of the molybdenum substrates. The weight gain rate observed was 6.5 center dot 10(-4) mg/cm(2) h. (c) 2006 Elsevier B.V. All rights reserved.

Novel high salt content polymer electrolytes based on high Tg polymers

Conductivities greater than or equal to 10⁻⁸ S cm⁻¹ at T_g are reported in polymer electrolytes based on lithium triflate salt and a series of polymers whose T_g is greater than 90°C. The highest conductivities were observed for poly(acrylonitrile) based systems with salt concentrations greater than 60 wt.%. The conductivity in all cases investigated increases with increasing salt concentration. ¹H-NMR T₂ relaxation measurements suggest that T_g decreases with increasing salt content and confirms that these materials are glassy at room temperature and hence that the conductivity is significantly decoupled from the structural relaxations. It appears that the nature of the polymer is important in determining the level of ionic conductivity, possibly due to differences in polymer coordinating ability or differences in T_g. Polymer-in-salt mixtures based on a tetra-alkyl ammonium imide molten salt and several high T_g polymers are also reported. The conductivities of these mixtures appear to be independent of the polymer type.

Pyrrolidinium imides : a new family of molten salts and conductive plastic crystal phases

A new family of molten salts is reported, based on the N-alkyl, N-alkyl pyrrolidinium cation and the bis(trifluoromethane sulfonyl)imide anion. Some of the members of the family are molten at room temperature, while the smaller and more symmetrical members have melting points around 100 °C. Of the room-temperature molten salt examples, the methyl butyl derivative exhibits the highest conductivity; at 2 × 10^-3 S/cm this is the highest molten salt conductivity observed to date at room temperature among the ammonium salts. This highly conductive behavior is rationalized in terms of the role of cation planarity. The salts also exhibit multiple crystalline phase behavior below their melting points and exhibit significant conductivity in at least their higher temperature crystal phase. For example, the methyl propyl derivative (mp = 12 °C) shows ion conductivity of 1 × 10^-6 S/cm at 0 °C in its higher temperature crystalline phase.

An investigation into the thermophysical and rheological properties of nanofluids for solar thermal applications

Considered to be the next generation of heat transfer fluids, nanofluids have been receiving a growing amount of attention in the past decade despite the controversy and inconsistencies that have been reported. Nanofluids have great potential in a wide range of fields, particularly for solar thermal applications. This paper presents a comprehensive review of the literature on the enhancements in thermophysical and rheological properties resulting from experimental works conducted on molten salt nanofluids that are used in solar thermal energy systems. It was found that an increase in specific heat of 10–30% was achieved for most nanofluids and appeared independent of particle size and to an extent mass concentration. The specific heat increase was attributed to the formation of nanostructures at the solid–liquid interface and it was also noted that the aggregation of nanoparticles has detrimental effects on the specific heat increase. Thermal conductivity was also found to increase, though less consistently, ranging from 3% to 35%. Viscosity was seen to increase with the addition of nanoparticles and is dependent on the amount of aggregation of the particles. An in-depth micro level analysis of the mechanisms behind the thermophysical property changes is presented in this paper. In addition, possible trends are discussed relating to current theorised mechanisms in an attempt to explain the behaviour of molten salt nanofluids.

Electrochemical deoxidation of RE–O (RE=Gd, Tb, Dy, Er) solid solutions

The removal of oxygen from rare-earth metals (RE, RE=Gd, Tb, Dy, Er) by an electrochemical deoxidation method was investigated. A titanium basket containing the rare-earth metal sample, submerged in molten CaCl2 electrolyte, formed the cathode of an electrolysis cell. A high-purity graphite anode was used. The calcium metal produced at the cathode effectively deoxidized the rare-earth metal. Carbon monoxide and dioxide were generated at the graphite anode. Rare-earth metals containing more than 2000 mass ppm oxygen were deoxidized to 10–50 mass ppm level by electrolysis at 1189 K for 36 ks (10 h). Cyclic voltammetry was used to characterize the molten salt at different stages of the process. The effectiveness of the process is discussed with the aid of a chemical potential diagram for RE–O solid solutions. The new electrochemical technique is compared with the conventional deoxidation methods reported in the literature. The possibility of nitrogen removal from the rare-earth metals by the electrochemical method is outlined.

Production of niobium powder by electronically mediated reaction (EMR) using calcium as a reductant

Explored in this study is an electronically mediated reaction (EMR) route for the production of niobium powder using calcium as a reductant for niobium oxide (Nb2O5). Feed material, Nb2O5, and reductant calcium alloy containing aluminum and nickel were charged into electronically isolated locations in a molten salt (e.g. CaCl2) at 1173 K. The current flow through an external path between the feed and reductant locations was monitored. A current approximately 0.4 A was measured during the reaction in the external circuit connecting cathode and anode location. Niobium powder with low aluminum and nickel content was obtained although liquid Ca–Al–Ni alloy was used as the reductant. This clearly demonstrates that niobium metal powder can be produced by an electronically mediated reaction (EMR), without direct physical contact between feed (Nb2O5) and reductant (calcium). Mechanism of calciothermic reduction of Nb2O5 in the molten salt is discussed using an isothermal chemical potential diagram.

High Temperature Phase Transition Studies and Dielectric Properties of Sr2SbMnO6

Sr2SbMnO6 (SSMO) ceramics were, fabricated using the nanocrystalline powders obtained via molten salt synthesis (MSS) method. High temperature X-ray diffraction studies confirmed the structural phase transition (room temperature tetragonal (I4/mcm) to the cubic phase (Pm-3m)) temperature to be around 736K. The discontinuity in the phase transition indicated its first order nature reflecting the presence of ferroelectric-like distortions in SSMO prepared from MSS which seemed to be unique as it was not observed so far in the case of SSMO prepared using solid-state reaction method. The dielectric behavior of SSMO was studied in the 300-950 K temperature range at high frequencies (MHz range) in order to suppress the of space charge and related effects that dominate at such higher temperatures and mask the real phase transition.

Rapid and facile one-step synthesis of LiTaO3 nanorods

Single crystalline LiTaO3 nanorods (length of 2.5-6 mu m and diameter of 200-500 nm) were synthesized via a facile molten-salt technique. An individual single crystalline nanorod exhibited a piezoelectric coefficient of 8 pm V-1. An improved optical frequency-doubling efficiency was observed in the case of LiTaO3 nanorods as compared to that of cubic crystallites of similar size.

Effects of instabilities and coherent structures on the performance of a thermocline based thermal energy storage

We investigate the transient dynamics of disturbances inside a thermocline based molten salt thermal energy storage (TES). Numerical simulations were conducted with four inlet flow configurations. The disturbances introduced at the inlet grow via Rayleigh Taylor instability. The formed vortical motions inside the tank propagate downstream and destroy the thermocline. The vortex-thermocline interaction upsets the stratification inside the TES. The disturbance growth rate, penetration length and vortex Reynolds number are measured. The growth of penetration length prior to the vortex-thermocline interaction is quadratic. The vortex Reynolds number of the eddy which causes thermocline breakdown increases with increase in Atwood number. The impingement of vortex on thermocline is studied. (C) 2015 Elsevier Ltd. All rights reserved.

Rayleigh-Taylor instability in a thermocline based thermal storage tank

Numerical simulations are performed to study the stability characteristics of a molten salt thermocline storage unit. Perturbations are introduced into a stable flow field in such a way as to make the top-fluid heavier than the fluid at the bottom, thereby causing a possible instability in the system. The evolution pattern of the various disturbances are examined in detail. Disturbances applied for short duration get decayed before they could reach the thermocline, whereas medium and long duration disturbances evolve into a ``falling spike'' or ``stalactite-like'' structure and destabilize the thermocline. Rayleigh Taylor instability is observed inside the storage tank. The effect of the duration, velocity and temperature of the disturbance on thermocline thickness and penetration length are studied. A quadratic time dependence of penetration length was observed. New perspectives on thermocline breakdown phenomena are obtained from the numerical flow field. (C) 2015 Elsevier Masson SAS. All rights reserved.

DESIGN REQUIREMENTS FOR DIRECT SUPERCRITICAL CARBON DIOXIDE RECEIVER DEVELOPMENT AND TESTING

This paper establishes the design requirements for the development and testing of direct supercritical carbon dioxide (sCO2) solar receivers. Current design considerations are based on the ASME Boiler and Pressure Vessel Code (BPVC). Section I (BPVC) considers typical boilers/superheaters (i.e. fired pressure vessels) which work under a constant low heat flux. Section VIII (BPVC) considers pressure vessels with operating pressures above 15 psig 2 bar] (i.e. unfired pressure vessels). Section III, Division I - Subsection NH (BPVC) considers a more detailed stress calculation, compared to Section I and Section VIII, and requires a creep-fatigue analysis. The main drawback from using the BPVC exclusively is the large safety requirements developed for nuclear power applications. As a result, a new set of requirements is needed to perform detailed thermal-structural analyses of solar thermal receivers subjected to a spatially-varying, high-intensity heat flux. The last design requirements document of this kind was an interim Sandia report developed in 1979 (SAND79-8183), but it only addresses some of the technical challenges in early-stage steam and molten-salt solar receivers but not the use of sCO2 receivers. This paper presents a combination of the ASME BPVC and ASME B31.1 Code modified appropriately to achieve the reliability requirements in sCO(2) solar power systems. There are five main categories in this requirements document: Operation and Safety, Materials and Manufacturing, Instrumentation, Maintenance and Environmental, and General requirements. This paper also includes the modeling guidelines and input parameters required in computational fluid dynamics and structural analyses utilizing ANSYS Fluent, ANSYS Mechanical, and nCode Design Life. The main purpose of this document is to serve as a reference and guideline for design and testing requirements, as well as to address the technical challenges and provide initial parameters for the computational models that will be employed for the development of sCO(2) receivers.

Er3+ and Yb3+ codoped phosphate laser glass for high power flashlamp pumping

A novel Vb(3+)-Er-(3+) codoped phosphate glass for high power flashlamp pumping and high repetition rate laser at 1.54 mu m, designated EAT5-2, is developed. The weight-loss rate of is 1.3 x 10(-5) gcm(-2) h(-1) in boiling water, which is comparable to Kigre's QX-Er glass. Some spectroscopic parameters are analysed by Judd-Ofelt theory and McCumber theory The emission cross section is calculated to be 0.73 x 10(-20) cm(2). The thermo-mechanical properties of EAT5-2 are modified after an ion-exchange chemical strengthening process in a KNO3/NaNO3 molten salt bath. The thresholds for optical damage from the flashlamp pumping are tested on glass rods. A repetition rate of 15 Hz is achieved for chemically strengthened glass. The laser experimental results at. 1.54 mu m from flashlamp pumping are also reported.