Analysis of microstructure and texture evolution in pure magnesium during symmetric and asymmetric rolling

Asymmetric rolling of commercially pure magnesium was carried out at three different temperatures: room temperature, 200 degrees C and 350 degrees C. Systematic analysis of microstructures, grain size distributions, texture and misorientation distributions were performed using electron backscattered diffraction in a field emission gun scanning electron microscope. The results were compared with conventional (symmetric) rolling carried out under the same conditions of temperature and strain rate. Simulations of deformation texture evolution were performed using the viscoplastic self-consistent polycrystal plasticity model. The main trends of texture evolution are faithfully reproduced by the simulations for the tests at room temperature. The deviations that appear for the textures obtained at high temperature can be explained by the occurrence of dynamic recrystallization. Finally, the mechanisms of texture evolution in magnesium during asymmetric and symmetric rolling are explained with the help of ideal orientations, grain velocity fields and divergence maps displayed in orientation space.

Development of novel grain morphology during hot extrusion of magnesium AZ21 alloy

Microstructure and microtexture evolution during static annealing of a hot-extruded AZ21 magnesium alloy was studied. Apart from fine recrystallized equiaxed grains and large elongated deformed grains, a new third kind of abnormal grains that are stacked one after the other in a row parallel to the extrusion direction were observed. The crystallographic misorientation inside these grains was similar to that of the fine recrystallized grains. The large elongated grains exhibited significant in-grain misorientation. A self-consistent mechanistic model was developed to describe the formation of these grain morphologies during dynamic recrystallization (DRX). The texture of pre-extruded material, although lost in DRX, leaves a unique signature which manifests itself in the form of these grain morphologies. The origin of abnormal stacked grains was associated with slow nucleation in pre-extruded grains of a certain orientation. Further annealing resulted in large secondary recrystallized grains with occasional extension twins. (c) 2009 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Deformation behaviour of Titanium in torsion

The evolution of microstructure and texture in Hexagonal Close Pack commercially pure titanium has been studied in torsion in a strain rate regime of 0.001 to 1 s(-1). Free end torsion tests carried out on titanium rods indicated higher stress levels at higher strain rate but negligible change in the strain-hardening behaviour. There was a decrease in the intra-granular misorientation while a negligible change in the amount of contraction and extension twins was observed with increase in strain rate. The deformed samples showed a C-1 fibre (c-axis is first rotated 90 degrees in shear direction and then +30 degrees in shear plane direction) at all the strain rates. With the increase in strain rate, there was an increase in the intensity of the C-1 fibre and it became more heterogeneous with a strong {11(2)over-bar6}< 2(8)over-bar)63 > component. In the absence of extensive twinning, pyramidal < c+a > slip system is attributed for the observed deformation texture. The present investigation, therefore, substantiates the theoretical prediction of increase in strength of texture with strain rate in torsion.

Evolution of Texture and Microstructure in Commercially Pure Titanium with Change in Strain Path During Rolling

The evolution of microstructure and texture in commercially pure titanium has been studied as a function of strain path during rolling using experimental techniques and viscoplastic self-consistent simulations. Four different strain paths, namely unidirectional rolling, two-step cross rolling, multistep cross rolling, and reverse rolling, have been employed to decipher the effect of strain path change on the evolution of deformation texture and microstructure. The cross-rolled samples show higher hardness with lower microstrain and intragranular misorientation compared to the unidirectional rolled sample as determined from X-ray diffraction and electron backscatter diffraction, respectively. The higher hardness of the cross-rolled samples is attributed to orientation hardening due to the near basal texture. Viscoplastic self-consistent simulations are able to successfully predict the texture evolution of the differently rolled samples. Simulation results indicate the higher contribution of basal slip in the formation of near basal texture and as well as lower intragranular misorientation in the cross-rolled samples.

Deformation behaviour at macro- and nano-length scales: The development of orientation gradients

The deformation behaviour of macrocrystalline and nanocrystalline nickel shows a striking similarity in terms of higher intragranular misorientation and a texture with dominant Brass component on rolling. This is in contrast to microcrystalline nickel, with lower intragranular misorientation and typical Copper type texture. This has been attributed to the free surfaces in macrocrystalline sample and grain boundaries in nanocrystalline sample. Experimental evidence of `Grain Boundary Affected Zone' (GBAZ) showing multi-slip in contrast to limited slip in the grain interiors has been provided. The similarity in evolution of texture and intragranular misorientation is explained on the basis of reduced contribution from the GBAZ at the two extreme length scales.

Effect of thermal and thermo-mechanical cycling on the microstructure of Ni-rich NiTi shape memory alloys

Microstructural changes of Ni-rich NiTi shape memory alloy during thermal and thermo-mechanical cycling have been investigated using Electron Back Scattered Diffraction. A strong dependence of the orientation of the prior austenite grain on the misorientation development has been observed during thermal cycling and thermo-mechanical cycling. This effect is more pronounced at the grain boundaries compared to grain interior. At a larger applied strain, the volume fraction of stabilized martensite phase increases with increase in the number of cycling. Deformation within the martensite leads to stabilization of martensitic phase even at temperatures slightly above the austenite finish temperature. Modulus variation with respect to temperature has been explained on the basis of martensitic transformation.

Orientation dependent mechanical properties of commercially pure (cp) titanium

The present investigation is an attempt at correlating the crystallographic orientation and mechanical properties of hexagonal commercially pure titanium (cp-titanium). Annealed cp-titanium sheets are subjected to tensile deformation along the rolling direction, along 45 degrees to the rolling direction and along 90 degrees to the rolling direction respectively. Crystallographic textures and mechanical properties of these cp-titanium samples are investigated in the present study. The hardness of different grains/orientations is estimated through nanoindentation, grain average misorientation, orientation estimated elastic stiffness and Taylor factor measurements. It is observed that the hardness of the grains close to basal orientation is higher compared to non-basal orientations. It is further observed that the estimated bulk mechanical properties of cp-titanium have a direct relationship with the volume fraction of basal grains/orientations. (C) 2014 Elsevier Inc All rights reserved.

Response of shock wave deformation in AA5086 aluminum alloy

The AA5086 aluminum alloy sheets with different starting textures were subjected to shock wave deformation with an input impulse of similar to 0.2 Ns. Microstructural examination indicate no significant change in grain size; however, the evolution of substructure manifesting intra-granular misorientation was evident. The improvement in hardness indicates the absence of recovery and strain hardening during shock deformation. Shock deformed samples show characteristic texture evolution with high Brass {110}< 112 > component. The study demonstrates the viability of high velocity forming of AA5086 aluminum alloy sheet using shock wave. (C) 2014 Elsevier B.V. All rights reserved.

Microstructure dependent elastic modulus variation in NiTi shape memory alloy

Modulus variation of NiTi shape memory alloy has been investigated at microstructural level through nano dynamical mechanical analysis and compared with bulk experimental measurements. The differences between the modulus values at the macro and micro level as well as within the micro level are discussed and the corresponding variations have been explained based on the crystal structure, orientation and misorientation. The experimental results confirm a higher modulus value for the martensite phase that is in agreement with the theoretical predictions. (C) 2015 Elsevier B. V. All rights reserved.

Texture evolution during hot deformation of Moly-TZM

Moly-TZM was deformed at constant strain rate of 1.0 s(-1) to investigate the high strain rate deformation behaviour by microstructural and stress response change within a temperature range of 1400-1700 degrees C. To correlate the deformation behaviour with orientational change, recrystallization and recovery of the material, the microstructural investigation was undertaken using scanning electron microscopy (SEM) of electron back scattered diffraction (EBSD). Depending on the grain size and orientation spread recrystallized grains were identified and texture was calculated. Change in grain boundary characteristics with increasing temperature was determined by the misorientation angle distribution for the deformed and recrystallized grains. Subgrain coalescence and increase in subgrain size with increasing temperature was observed, indicating recrystallization not only occurred from the nucleation of the dislocation free grains in grain boundaries but also from the subgrain rotation and merging of the subgrains by annihilation of the low angle grain boundaries. Detailed studies on the evolution of texture of recrystallized grains showed continuous increase in <001> fiber texture in recrystallised grains, in contrast to a mixed fiber <001> +<111> for the deformed grains.

Influence of mode of deformation on microstructural heterogeneities in Ni subjected to large strain deformation

In the present work, the effect of deformation mode (uniaxial compression, rolling and torsion) on the microstructural heterogeneities in a commercial purity Ni is reported. For a given equivalent von Mises strain, samples subjected to torsion have shown higher fraction of high-angle boundaries, kernel average misorientation and recrystallization nuclei when compared to uniaxially compressed and rolled samples. This is attributed to the differences in the slip system activity under different modes of deformation.

Size Effects on Strength in the Transition from Single-to-Polycrystalline Behavior

During the transition from single crystalline to polycrystalline behavior, the available data show the strength increasing or decreasing as the number of grains in a cross section is reduced. Tensile experiments were conducted on polycrystalline Ni with grain sizes (d) between 16 and 140 mu m and varying specimen thickness (t), covering a range of lambda (-t/d) between similar to 0.5 and 20. With a decrease in lambda, the data revealed a consistent trend of strength being independent of lambda at large lambda, an increase in strength, and then a decrease in strength. Microstructural studies revealed that lower constraints enabled easier rotation of the surface grains and texture evolution, independent of the specimen thickness. In specimen interiors, there was a greater ease of rotation in thinner samples. Measurements of misorientation deviations within grains revealed important differences in the specimen interiors. A simple model is developed taking into account the additional geometrically necessary dislocations due to variations in the behavior of surface and interior grains, leading to additional strengthening. A suitable combination of this strengthening and surface weakening can give rise to wide range of possibilities with a decrease in lambda, including weakening, strengthening, and strengthening and weakening.

Formation, microstructure and development of the localized shear deformation in low-carbon steels

An investigation has been made into the effect of microstructural parameters on the propensity for forming shear localization produced during high speed torsional testing by split Hopkinson bar with different average rates of 610, 650 and 1500 s(-1) in low carbon steels. These steels received the quenched, quenched and tempered as well as normalized treatments that provide wide microstructural parameters and mechanical properties. The results indicate that the occurrence of the shear localization is susceptible to the strength of the steels. In other words, the tendency of the quenched steel to form a shear band is higher than that of the other two steels. It is also found that there is a critical strain at which the shear localization occurs in the steels. The critical strain value is strongly dependent on the strength of the steels. Before arriving at this point, the material undergoes a slow work-hardening. After this point, the material suffers work-softening, corresponding to a process during which the deformation is gradually localized and eventually becomes spatially correlated to form a macroscopic shear band. Examinations by SEM reveal that the shear localization within the band involves a series of sequential crystallographic and non-crystallographic events including the change in crystal orientation, misorientation, generation and even perhaps damage in microstructures such as the initiation, growth and coalescence of the microcracks. It is expected that the sharp drop in the load-carrying capacity is associated with the growth and coalescence of the microcracks rather than the occurrence of the shear localization, but the shear localization is seen to accelerate the growth and coalescence of the microcracks. The thin foil observations by TEM reveal that the density of dislocations in the band is extremely high and the tangled arrangement and cell structure of dislocations tends to align along the shear direction. The multiplication and interaction of dislocations seems to be responsible for work-hardening of the steels. The avalanche of the dislocation cells corresponds to the sharp drop in shear stress at which the deformed specimen is broken. Double shear bands and kink bands are also observed in the present study. The principal band develops first and its width is narrower than that of the secondary band.

An analysis of the effects of symmetrical tilt grain boundaries on the plastic deformation

A numerical investigation on the simple polycrystals containing three symmetrical tilt grain boundaries (GBs) is carried out within the framework of crystal plasticity which precisely considers the finite deformation and finite lattice rotation as well as elastic anisotropy. The calculated results show that the slip geometry and the redistribution of stresses arising from the anisotropy and boundary constraint play an important role in the plastic deformation in the simple polycrystals. The stress level along GB is sensitive to the load level and misorientation, and the stresses along QB are distributed nonuniformly. The GB may exhibit a softening or strengthening feature, which depends on the misorientation angle. The localized deformation bands usually develop accompanying the GB plastic deformation, the impingement of the localized band on the GB may result in another localized deformation band. The yield stresses with different misorientation angles are favorably compared with the experimental results.

高压扭转铜试样的微观组织与压缩性能

通过高压扭转对铜试样施加不同程度的变形，研究了样品扭转面（ND面）和纵截面（TD面）上微观组织特征．对ND面，在较小的剪应变下，原始晶粒形貌模糊，晶粒内部形成等轴状的位错胞及亚晶结构；随变形量的增大，亚晶间取向差及亚晶内部的位错密度增大，最后形成亚微米尺度的等轴晶粒．对TD面，变形初期原始晶粒被拉长，晶粒内部为位错墙分割成的层状结构，层内为拉长的位错胞；随变形程度的增大，拉长晶粒的宽度减小，与剪切方向的夹角减小，晶内层状组织间距减小，并逐渐演化成拉长的亚晶组织；进一步增大变形，晶粒拉长痕迹消失，变形组织与ND面相似，为等轴状亚微米晶粒．压缩实验表明，经16圈扭转后，整个试样上的压缩性能基本均匀，σ0．2达到385MPa，应变率敏感性指数增大至0．021．