A comparison of the film thickness of two adhesive luting agents and the effect of thermocycling on their microTBs to feldspathic ceramic.

The aim of the present study was to evaluate the effect of thermocycling (TC) on the microtensile bond strength (microTBS) of two luting agents to feldspathic ceramic and to measure their film thickness (FT). For the microTBS test, sixteen blocks (6.4 x 6.4 x 4.8 mm) were fabricated using a feldspathic ceramic, etched with 10% hydrofluoric acid, rinsed and treated with the silane agent. The ceramic blocks were divided into two groups (n= 8): Gr1: dual-cured resin cement and Gr2: flowable resin. The luting agents were applied on the treated surfaces. Microsticks (1 +/-0. 1mm2) were prepared and stored under two conditions: dry, specimens immediately submitted to the microTBS test, and TC (6,000 cycles; 5 degrees C-55 degrees C). The microTBS was evaluated using a universal testing machine (1 mm/min). The microTBS data (MPa) were submitted to two-way ANOVA and Tukey' test (5%). For the FT test (ISO 4049), 0.05 ml of each luting agent (n=8) was pressed between two Mylar-covered glass plates (150 N) for 180 seconds and light polymerized. FT was measured using a digital paquimeter (Model 727-2001). The data (mm) were submitted to one-way ANOVA. The luting cement did not influence the microTBS results (p= 0.4467). Higher microtensile bond values were found after TC (20.5 +/- 8.6 MPa) compared to the dry condition (13.9 +/- 4. 7MPa), for both luting agents. The luting agents presented similar film thicknesses: Gr1- 0.052 +/- 0.016 mm; Gr2-0.041 +/- 0.003 mm. The luting agents presented similar film thickness and microTBS values, in dry and TC conditions and TC increased the bond strength regardless of the luting agent.

Bonding all-ceramic restorations with two resins cement techniques: A clinical report of three-year follow-up

Ceramics have been widely used for esthetic and functional improvements. The resin cement is the material of choice for bonding ceramics to dental substrate and it can also dictate the final esthetic appearance and strength of the restoration. The correct use of the wide spectrum of resin luting agents available depends on the dental tooth substrate. This article presents three-year clinical results of a 41 years old female patient B.H.C complaining about her unattractive smile. Two all-ceramic crowns and two laminates veneers were placed in the maxillary incisors and cemented with a self-adhesive resin luting cement and conventional resin luting cement, respectively. After a three-year follow-up, the restorations and cement/teeth interface were clinically perfect with no chipping, fractures or discoloration. Proper use of different resin luting cements shows clinical appropriate behavior after a three-year follow-up. Self-adhesive resin luting cement may be used for cementing all-ceramic crowns with high predictability of success, mainly if there is a large dentin surface available for bonding and no enamel at the finish line. Otherwise, conventional resin luting agent should be used for achieving an adequate bonding strength to enamel.

Cytotoxicity of resin-based luting cements to pulp cells

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Transdentinal cytotoxicity of resin-based luting cements to pulp cells

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

The effect of curing light and chemical catalyst on the degree of conversion of two dual cured resin luting cements

The aim of this study was to evaluate the influence of different curing lights and chemical catalysts on the degree of conversion of resin luting cements. A total of 60 disk-shaped specimens of RelyX ARC or Panavia F of diameter 5 mm and thickness 0.5 mm were prepared and the respective chemical catalyst (Scotchbond Multi-Purpose Plus or ED Primer) was added. The specimens were light-cured using different curing units (an argon ion laser, an LED or a quartz-tungsten-halogen light) through shade A2 composite disks of diameter 10 mm and thickness 2 mm. After 24 h of dry storage at 37A degrees C, the degree of conversion of the resin luting cements was measured by Fourier-transformed infrared spectroscopy. For statistical analysis, ANOVA and the Tukey test were used, with p a parts per thousand currency signaEuro parts per thousand 0.05. Panavia F when used without catalyst and cured using the LED or the argon ion laser showed degree of conversion values significantly lower than RelyX ARC, with and without catalyst, and cured with any of the light sources. Therefore, the degree of conversion of Panavia F with ED Primer cured with the quartz-tungsten-halogen light was significantly different from that of RelyX ARC regardless of the use of the chemical catalyst and light curing source. In conclusion, RelyX ARC can be cured satisfactorily with the argon ion laser, LED or quartz-tungsten-halogen light with or without a chemical catalyst. To obtain a satisfactory degree of conversion, Panavia F luting cement should be used with ED Primer and cured with halogen light.

Push-out bond strengths of different dental cements used to cement glass fiber posts

Statement of problem: Since the introduction of glass fiber posts, irreversible vertical root fractures have become a rare occurrence; however, adhesive failure has become the primary failure mode. Purpose: The purpose of this study was to evaluate the push-out bond strength of glass fiber posts cemented with different luting agents on 3 segments of the root. Material and methods: Eighty human maxillary canines with similar root lengths were randomly divided into 8 groups (n=10) according to the cement assessed (Rely X luting, Luting and Lining, Ketac Cem, Rely X ARC, Biscem, Duo-link, Rely X U100, and Variolink II). After standardized post space preparation, the root dentin was pretreated for dualpolymerizing resin cements and untreated for the other cements. The mixed luting cement paste was inserted into post spaces with a spiral file and applied to the post surface that was seated into the canal. After 7 days, the teeth were sectioned perpendicular to their long axis into 1-mm-thick sections. The push-out test was performed at a speed of 0.5 mm/min until extrusion of the post occurred. The results were evaluated by 2-way ANOVA and the all pairwise multiple comparison procedures (Tukey test) (?=.05). Results: ANOVA showed that the type of interaction between cement and root location significantly influenced the push-out strength (P<.05). The highest push-out strength results with root location were obtained with Luting and Lining (S3) (19.5 ±4.9 MPa), Ketac Cem (S2) (18.6 ±5.5 MPa), and Luting and Lining (S1) (18.0 ±7.6 MPa). The lowest mean values were recorded with Variolink II (S1) (4.6 ±4.0 MPa), Variolink II (S2) (1.6 ±1.5 MPa), and Rely X ARC (S3) (0.9 ±1.1 MPa). Conclusions: Self-adhesive cements and glass ionomer cements showed significantly higher values compared to dual-polymerizing resin cements. In all root segments, dual-polymerizing resin cements provided significantly lower bond strength. Significant differences among root segments were found only for Duo-link cement.

Quantification of all-ceramic crown margin surface profile from try-in to 1-week post-cementation

To use profilometry to assess the margin surface profile of all-ceramic crowns (ACC’s) at try-in and 1-week after cementation with dual-cured resin (DC, RelyX ARC, 3 M ESPE, St. Paul, MN, USA), self-adhesive dual-cured resin (SADC, RelyX Unicem, 3 M ESPE), light-cured resin (LC, RelyX Veneer, 3 M ESPE) or chemically cured resin-modified glass ionomer (RMGI, RelyX Luting Plus, 3 M ESPE) luting cement. Methods: Forty, sound, extracted, human, premolar teeth underwent a standardised preparation for ACC’s. IPS Empress (Ivoclar-Vivadent, Liechtenstein) crowns of standard dimensions were fabricated and 10 luted with each cement and stored in water for 7 days. Three groups of serial profiles were taken, the first of the tooth preparation, the second of the crown margins at try-in and lastly of the crown margins after cementation and 7 days water storage. Results: There were no significant differences in the crown margin surface profile between the four cement groups at try-in. The change in crown margin position between try-in and post-cementation was significantly greater for DC than for LC and RMGI. SADC was not significantly different to the other cements. There were no significant differences in the crown margin extensions between the four cement groups, however most of the IPS Empress ACC’s in this study were underextended but this was not statistically significant. Conclusions: IPS Empress ACC’s seated more fully with LC and RMGI than with DC cement

In vitro cytotoxicity and in vivo-biocompatibility of contemporary resin-modified glass-ionomer cements

Objectives. To evaluate the effects of current resin-modified glass-ionomer cements (RMGICs) applied on culture of cells or implanted into subcutaneous tissue of rats.Methods. Experiment 1 - Thirty round-shaped samples of every RMGICs: Rely X Luting Cement (RL), Vitremer (VM), and Vitrebond (VB) were placed into wells with 1.1 mL of culture medium (DMEM), and incubated for 24,48 or 72 h. The extracts from every sample were applied on the MDPC-23 cells. Fresh DMEM was used as control group. The MTT assay was carried out for mitochondrial respiration. Experiment 2 - Fifty-four polyethylene tubes filled with the experimental materials were implanted into the dorsal subcutaneous tissue of rats. At 7, 30, and 90 days the animals were killed and the biopsies were processed for histological evaluation.Results. Experiment 1 - Both time of elution and material significantly influenced cell respiratory activity. in general, the extracts obtained at 24 h were less cytotoxic than 48 and 72 h incubation. The cytotoxic effect of VM and RL were not statistically different (P < 0.05) for the 24-hour period. VB showed the highest cytotoxic effect. Experiment 2 - All RMGICs elicited at 7 days a moderate to intense inflammatory reaction which decreased over time. However, connective healing occurred for most of samples at 90-day evaluation.Significance. Glass-ionomer cements may cause noticeable inflammatory response when in direct contact to connective tissue. The toxic effects of this kind of soluble material depend on the amount of components released in the aqueous environment. (C) 2005 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Human pulp response to resin cements used to bond inlay restorations

Objective. The aim of this study was to evaluate the pulp response following cementation of inlays using two different resin cements.Methods. Deep Class V cavities were prepared on the buccal surface of 34 sound human premolars. impressions were taken and inlays were prepared which were cemented with the following luting materials-Group 1: Rely X(TM) Unicem. (3M ESPE); Group 2: Variolink(R) II (Ivoclar Vivadent). in Group 3 (control), after lining the cavity floor with Dycal(R) (Dentsply Caulk) the inlays were cemented with Rely X(TM) Unicem. Four additional teeth were used as an intact control group. For Variolink(R) II, the adhesive system Excite was used as part of the cementation procedure. After 7 or 60 days, the teeth were extracted and processed for histological assessment.Results. At 7 days, Rely X(TM) Unicern and Variolink(R) II system triggered in two samples a mild and moderate inflammatory response, respectively. At 60 days, the pulpal response decreased for both groups. A discrete persistent inflammatory response occurred in Group 2 in which displacement of resin components across the dentin tubules was observed. In the control group, normal histological characteristics were observed. The inflammatory response and tissue disorganization were related to the remaining dentin thickness between the cavity floor and the pulp tissue.Significance. Techniques for inlay cementation using distinct luting cements may cause specific pulpal damage. Variolink(R) II associated with the adhesive system Excite cause more aggressive effects to the pulp-dentin complex than Rely X(TM) Unicern cement when both are used to cement inlay restorations. (C) 2005 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Influence of buccal cusp reduction when using porcelain laminate veneers in premolars. A comparative study using 3-D finite element analysis

Objectives: Based on a maxillary premolar restored with laminate veneer and using the 3-D finite element analysis (FEA) and mCT data, the aim of this study was to evaluate the influence of different types of buccal cusp reduction on the stress distribution in the porcelain laminate veneer and in the resin luting cement layer. Methods: Two 3-D FEA models (M) of a maxillary premolar were built from mCT data. The buccal cusp reduction followed two configurations: Mt-buccal cusp completely covered by porcelain laminate veneer; and Mp-buccal cusp partially covered by porcelain laminate veneer. The loading (150 N in 458) was performed on the top of the buccal cusp. The finite element software (Ansys Workbench 10.0) was used to obtain the maximum shear stress (σmax) and maximum principal stress (σmax). Results: The Mp showed reduced the stress (σmax) in porcelain laminate veneer (from-2.3 to 24.5 MPa) in comparison with Mt (from-5.3 to 27.4 MPa). The difference between the peak and lower stress values of σmax in Mp (-6.8 to 26.7 MPa) and Mt (-5.3 to 27.4 MPa) was similar for the resin luting cement layer. The structures not exceeded the ultimate tensile strength or the shear bond strength. Conclusions: Cusp reduction did not affect significant increase in σmax and τmax. The Mt showed better stress distribution (τmax) than Mp. © 2011 Published by Elsevier Ireland on behalf of Japan Prosthodontic Society.

Efeitos citotóxicos de diferentes materiais dentários sobre células de linhagem odontoblástica

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Utilização de células de linhagem odontoblástica (MDPC-23) em estudos de citotoxicidade e na avaliação do efeito de fatores de crescimento sobre a expressão de genes específicos

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Avaliação de tratamentos de superfície em diferentes sistemas cerâmicos e seu efeito na resistência de união a um cimento resinoso

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Laminados cerâmicos em pré-molares: análise tridimensional pelo método dos elementos finitos

Pós-graduação em Odontologia - FOA

Citotoxidade de cimentos resinosos sobre célular obtidas da polpa de dentes humanos (HDPCs) e odontoblastóides (MDPC-23)

Pós-graduação em Reabilitação Oral - FOAR