High structural and optical quality 1.3 mu m GaInNAs/GaAs quantum wells with higher indium content grown by molecular-beam expitaxy

High structural and optical quality 1.3 mu m GaInNAs/GaAs quantum well (QW) samples with higher (42.5%) indium content were successfully grown by molecular-beam epitaxy. The cross-sectional transmission electron microscopy measurements reveal that there are no structural defects in such high indium content QWs. The room-temperature photoluminescence peak intensity of the GaIn0.425NAs/GaAs (6 nm/20 nm) 3QW is higher than, and the full width at half maximum is comparable to, that of In0.425GaAs/GaAs 3QW, indicating improved optical quality caused by strain compensation effect of introducing N to the high indium content InGaAs epilayer. (C) 2005 American Institute of Physics.

1.55 mu m GaInNAs resonant-cavity-enhanced photodetector grown on GaAs

We report the design, growth, fabrication, and characterization of a GaAs-based resonant-cavity-enhanced (RCE) GaInNAs photodetector operating at 1.55 mu m. The structure of the device was designed using a transfer-matrix method (TMM). By optimizing the molecular-beam epitaxy growth conditions, six GaInNAs quantum wells were used as the absorption layers. Twenty-five (25)- and 9-pair GaAs/AlAs-distributed Bragg reflectors were grown as the bottom and top mirrors. At 1.55 mu m, a quantum efficiency of 33% with a full width at half maximum of 10 nm was obtained. The dark current density was 3x10(-7) A/cm(2) at a bias of 0 V and 4.3x10(-5) A/cm(2) at a reverse bias of 5 V. The primary time response measurement shows that the device has a rise time of less than 800 ps. (c) 2005 American Institute of Physics.

Optimization of GaInNAs(Sb)/GaAs quantum wells at 1.3-1.55 mu m grown by molecular beam epitaxy

The InGaNAs(Sb)/(GaNAs)/GaAs quantum wells (QWs) emitting at 1.3-1.55 mu m have been grown by molecular beam epitaxy (MBE). The parameters of the radio frequency (RF) such as RF power and flow rate are optimized to reduce the damages from the ions or energetic species. The growth temperature is carefully controlled to prevent the phase segregation and strain relaxation. The effects of Sb on the wavelength and quality are investigated. The GaNAs barrier is used to extend the wavelength and reduce the strain. A 1.5865 mu m InGaNAs(Sb)/GaNAs SQW edge emitting laser lasing at room temperature at continuous wave operation mode is demonstrated. (c) 2006 Elsevier B.V. All rights reserved.

Application of rapid thermal annealing on 1.3-1.55 mu m GaInNAs(Sb) lasers grown by molecular beam epitaxy

Rapid thermal annealing (RTA) has been demonstrated as an effective way to improve the crystal quality of GaInNAs(Sb) quantum wells (QWs). However, few investigations have been made into its application in laser growth and fabrication. We have fabricated 1.3 mu m GaInNAs lasers, both as -grown and with post-growth RTA. Enhanced photoluminescence (PL) intensity and decreased threshold current are obtained with RTA, but the characteristic temperature T-o and slope efficiency deteriorate. Furthermore, T-o has an abnormal dependence on the cavity length. We attribute these problems to the deterioration of the wafer's surface. RTA with deposition Of SiO2 was performed to avoid this deterioration, T-o was improved over the samples that underwent RTA without SiO2. Post-growth and in situ annealing were also investigated in a 1.55 mu m GaInNAsSb system. Finally, continuous operation at room temperature of a GaAs-based dilute nitride laser with a wavelength over 1.55 mu m was realized by introducing an in situ annealing process. (c) 2007 Elsevier B.V. All rights reserved.

Rapid photoluminescence quenching in GaInNAs quantum wells at low temperature

Temperature dependence of optical properties of GaInNAs/GaAs quantum wells (QWs) has been studied by photoluminescence (PL) and time-resolved PL. A rapid PL quenching is observed even at very low temperature and is of the excitation power dependence. These results strongly suggest that the non-radiative recombination process plays a very important role at low temperature. In the TRPL measurement the shape of the PL decay curve shows significant difference under different excitation powers. It is attributed to the different involvement of non-radiative recombination in the overall recombination process. The TRPL data are well fitted with the rate equation involving both the radiative and non-radiative recombination. (c) 2006 Elsevier B.V. All rights reserved.

Effect of nonradiative recombination on carrier dynamics in GaInNAs/GaAs quantum wells

The nonradiative recombination effect on carrier dynamics in GaInNAs/GaAs quantum wells is studied by time-resolved photoluminescence (TRPL) and polarization-dependent TRPL at various excitation intensities. It is found that both recombination dynamics and spin relaxation dynamics strongly depend on the excitation intensity. Under moderate excitation intensities the PL decay curves exhibit unusual non-exponential behaviour. This result is well stimulated by a rate equation involving both the radiative and non-radiative recombinations via the introduction of a new parameter of the effective concentration of nonradiative recombination centres in the rate equation. In the spin dynamics study, the spin relaxation also shows strong excitation power dependence. Under the high excitation power an increase of spin polarization degree with time is observed. This new finding provides a useful hint that the spin process can be controlled by excitation power in GaInNAs systems.

Enhancement of photoluminescence intensity of GaInNAs/GaAs quantum wells by two-step rapid thermal annealing

We investigate the effect of rapid thermal annealing on InGaNAs/GaAs quantum wells. At optimized annealing temperatures and times, the greatest enhancement of the photoluminescence intensity is obtained by a special two-step annealing process. To identify the mechanism affecting the material quality during the rapid thermal annealing, differential temperature analysis is applied, and temperature- and power-dependent photoluminescence is carried out on the samples annealed under different conditions. Our experiment reveals that some composition redistribution or other related ordering process may occur in the quantum-well layer during annealing. Annealing at a lower temperature for a long time primarily can remove defects and dislocations while annealing at a higher temperature for a short time primarily homogenizes the composition in the quantum wells.

The role of Sb in the molecular beam epitaxy growth of 1.30-1.55 mu m wavelength GaInNAs/GaAs quantum well with high indium content

Sb-assisted GaInNAs/GaAs quantum wells (QWs) with high (42.5%) indium content were investigated systematically. Transmission electron microscopy, reflection high-energy electron diffraction and photoluminescence (PL) measurements reveal that Sb acts as a surfactant to suppress three-dimensional growth. The improvement in the 1.55 mu m range is much more apparent than that in the 1.3 mu m range.. which can be attributed to the difference in N composition. The PL intensity and the full-width at half maximum of the 1.55 mu m single-QW were comparable with that of the 1.3 Am QWs. (c) 2006 Elsevier B.V. All rights reserved.

Influence of growth parameters of frequency-radio plasma nitrogen source on extending emission wavelengths from 1.31 mu m to 1.55 mu m GaInNAs/GaAs quantum wells grown by molecular-beam epitaxy

High (42.5%) indium content GaInNAs/GaAs quantum wells with room temperature emission wavelength from 1.3 mu m to 1.5 mu m range were successfully grown by Radio Frequency Plasma Nitrogen source assisted Molecular Beam Epitaxy. The growth parameters of plasma power and N-2 How rate were optimized systematically to improve the material quality. Photoluminescence and transmission electron microscopy measurements showed that the optical and crystal quality of the 1.54 mu m GaInNAs/GaAs QWs was kept as comparable as that in 1.31 mu m.

Post-growth and in situ annealing on GaInNAs(Sb) and their application in 1.55 mu m lasers

Rapid thermal annealing (RTA) has been demonstrated as an important way to improve the crystal quality of GaInNAs(Sb)/GaAs quantum wells. However little investigation has been made into their application in laser growth, especially at a wavelength of 1.55 mu m. When a GaAs-based laser is grown, AlGaAs is usually used for cladding layers. The growth of the p-cladding layer usually takes 30-45 min at a growth temperature higher than that of the GaInNAs(Sb) active region, which affects the material quality. To investigate this effect, various post-growth annealing processes were performed to simulate this process. Great enhancement of the PL intensity was obtained by a two-step process which consisted of annealing first at 700 degrees C for 60 s and then at 600 degrees C for 45 min. We transferred this post-growth annealing to in situ annealing. Finally, a GaInNAsSb laser was grown with a 700 degrees C in situ annealing process. Continuous operation at room temperature of a GaAs-based dilute nitride laser with a wavelength beyond 1.55 mu m was realized for the first time.

Nonradiative recombination effect on photoluminescence decay dynamics in GaInNAs/GaAs quantum wells

The influence of nonradiative recombination on the photoluminescence (PL) decay dynamics in GaInNAs/GaAs quantum wells is studied by time-resolved photoluminescence under various excitation intensities. It is found that the PL decay process strongly depends on the excitation intensity. In particular, under the moderate excitation levels the PL decay curves exhibit unusual nonexponential behavior and show a convex shape. By introducing a new parameter of the effective concentration of nonradiative recombination centers into a rate equation, the observed results are well simulated. The cw PL data further demonstrate the nonradiative recombination effect on the optical properties of GaInNAs/GaAs quantum wells. (c) 2006 American Institute of Physics.

The effect of inserting strain-compensated GaNAs layers on the luminescence properties of GaInNAs/GaAs quantum well

Photoluminescence (PL) properties of GaInNAs/GaAs quantum wells (QWs) with strain-compensated GaNAs layers grown by molecular beam epitaxy are investigated. The temperature-dependent PL spectra of GaInNAs/GaAs QW with and without GaNAs layers are compared and carefully studied. It is shown that the introduction of GaNAs layers between well and barrier can effectively extend the emission wavelength, mainly due to the reduction of the barrier potential. The PL peak position up to 1.41 mum is observed at the room temperature. After adding the GaNAs layers into QW structures, there is no essential deterioration of luminescence efficiency. N-induced localization states are also not remarkably influenced. It implies that with optimized growth condition, high-quality GaInNAs/GaAs QWs with strain-compensated GaNAs layers can be achieved. (C) 2003 Elsevier Science B.V. All rights reserved.

The effects of concomitant In and N incorporation on the photoluminescence of GaInNAs

We investigated the effects of concomitant In- and N-incorporation on the photoluminescence (PL) of GaInNAs grown by molecular beam epitaxy. In comparison with the N-free GaInAs epilayer, the PL spectra of the GaInNAs epilayer exhibit an anomalous S-shape temperature dependence of dominant luminescence peak. Through further careful inspection, two PL peaks are clearly discerned and are associated with the interband excitonic recombinations and excitons bound to N-induced isoelectronic impurity states, respectively. By comparing the PL spectra of GaInNAs/ GaAs quantum wells (QWs) with those of In-free GaNAs/GaAs QWs grown under similar conditions, it is found that the concomitant In- and N-incorporation reduces the density of impurities and has an effect to improve the intrinsic optical transition of GaInNAs, but also enhance the N-induced clustering effects. At last, we found that rapid thermal annealing can significantly reduce the density of N-induced impurities. (C) 2002 Elsevier Science B.V. All rights reserved.

Anomalous temperature dependence of photoluminescence in GaInNAs/GaAs multiple quantum wells

Photoluminescence (PL) spectra of GaInNAs/GaAs multiple quantum wells grown on a GaAs substrate by molecular beam epitaxy are measured in a range of temperatures and excitation power densities. The energy position of the dominant PL peak shows an anomalous S-shape temperature dependence instead of the Varshni relation. By careful inspection, especially for the PL under lower excitation power density, two near bandedge peaks are well identified. These are assigned to carriers localized in nitrogen-induced bound states and interband excitonic recombinations, respectively. It is suggested that the temperature-induced switch of such two luminescence peaks in relative intensity causes a significant mechanism responsible for the S-shape shift observed in GaInNAs. A quantitative model based on the thermal depopulation of carriers is used to explain the temperature dependence of the PL peak related to N-induced bound states.

Angular dependent characteristics of a 1.3-mu m GaInNAs/GaAs quantum-well resonant cavity enhanced photodetect

Characteristics of a 1.3-mum GaInNAs RCE PD with respect to the incident light angle were analyzed both in theoretical simulation and experiments. The results show the influence can be neglected when the light incidence angle is less than 3degrees. This is a requirement for the PD to be applied in WDM networks. (C) 2002 Wiley Periodicals, Inc.