Stability against crystallization and spectroscopic properties of Tm3+ doped fluorophosphate glasses

Fluorophosphate glasses with various content of Al(PO3)(3) were prepared. With the increment of Al(PO3)(3) content, density decreases while refractive index increases, and transition temperature, crystallization peak temperature and melt temperature increase which were suggested by differential scanning calorimetry. These glasses exhibit the best stability against crystallization with 7-9 mol'Yo Al(PO3)(3) content. Normalized Raman spectra were used to analyze structure and phonon state. The increment of Al(PO3)(3) content does not affect phonon energy but results in the augment of phonon density. Absorption spectra were measured. H-3(6) -> F-3(4) transition exhibits absorption at L band of the third communication window. Compared with the energy of Tm3+ excited states in other glass system, F-3(4) energy of Tm3+ in these glasses is considerable higher and H-3(4) energy is considerable lower, and it can be predicted that emission band of H-3(4) -> F-3(4) transition is close to the amplified band of gain-shift Tm3+ doped fiber amplifier. Analyses of Judd-Ofelt theory suggest when Al(PO3)(3) content is no more than 7 mol%, Judd-Ofelt parameters Omega(t) and the lifetime of H-3(4) energy level of TM3+ vary little with the increment of Al(PO3)(3) content, and when Al(PO3)(3) content is more than 7 mol%, Omega(2) and Omega(6) increase and radiative lifetime of H-3(4) energy level of Tm3+ drops sharply with the increment of Al(PO3)(3) content. (c) 2006 Elsevier B.V. All rights reserved.

Effect of chloride ions' introduction on structural, thermal stability, and spectroscopic properties in Yb3+Er3+-codoped germanate-bismuth-lead glasses

Yb3+Er3+-codoped chloride-modified germanate-bismuth-lead glasses have been synthesized by the conventional melting and quenching method. Structural and thermal stability properties have been obtained on the basis of the Raman spectra and differential thermal analysis, which indicate that the PbCl2 addition has an important influence on the phonon density of states, maximum phonon energy, and thermal stability of host glasses. The Judd-Ofelt intensity parameters and quantum efficiencies were calculated on the basis of the Judd-Ofelt theory and lifetime measurements. For the 1.53 mu m emission band, the full widths at the half-maximum increase and peak wavelengths are blueshifted with increasing PbCl2 content. Moreover, the effect of the PbCl2 addition on the phonon density of states, OH- content, and upconversion luminescence has been discussed and evaluated. Our results reveal that, with increasing PbCl2 content, the decrease of phonon density and OH- content contributes more to the enhanced upconversion emissions than that of maximum phonon energy. (c) 2005 Optical Society of America

Efficient diode-pumped Yb : Gd2SiO5 laser

An efficient diode-pumped laser was demonstrated by using an ytterbium-doped laser crystal, Yb:Gd2SiO5 (Yb:GSO), wherein Yb3+ ions exhibit the largest ground-state splitting among all the ytterbium-doped crystals. The Yb:GSO laser can be operated at a low pumping threshold, and the most efficient laser occurs around 1088 nm since the corresponding emission band has the largest emission cross section and the lowest thermal population. A slope efficiency of 75% was demonstrated for a continuous-wave Yb:GSO laser at 1094 nm, and self-pulsed lasers were achieved within the tunable range of 1091-1105 nm, which are the longest laser wavelengths achieved for Yb3+ lasers. (c) 2006 American Institute of Physics.

Infrared (1.2-1.6 mu m) luminescence in Yb, Cr : YAG with 940 nm diode pumping

Infrared (1.2-1.6 mum) luminescence in a yttrium aluminium garnet (YAG) crystal, co-doped with Yb (10 at.%) and Cr (0.05 at.%) ions, was investigated under CW laser diode pumping (lambda = 940 nm). The Cr4+ emission band was observed with its peak at 1.35 mum and measured to be about 6% with respect to Yb3+ IR luminescence (lambda = 1.03 mum). Analysis of the crystal absorption and luminescence spectra allows one to conclude that Yb3+-Cr4+ energy transfer is a mechanism responsible for the B-3(2)(T-3(2))-B-3(1)((3)A(2)) emission of Cr4+ ions. This crystal is promising as an efficient source of the near infrared emission. (C) 2004 Elsevier B.V. All rights reserved.

Infrared (1.2-1.6 mu m) luminescence in Cr4+: Yb3Al5O12 single crystal with 940 nm diode pumping

Infrared (1.2-1.6 mu m) luminescence in a ytterbium aluminium garnet (YbAG) crystal, doped with Cr (0.05 at.%) ions, was investigated under CW laser diode pumping (lambda = 940 nm). The Cr4+ emission band was observed with its peak at 1.34 mu m and measured to be about 1.3 times with respect to Yb3+ IR luminescence (lambda = 1.03 mu m). We demonstrate that for the excitation wavelength of 940 nm Yb3+ ions act as sensitizers of the B-3(2)(T-3(2))-B-3(1)((3)A(2)) emission of Cr4+ ions. This crystal is promising as a high-efficient system for tunable laser (1.2-1.6 mu m) output. (c) 2004 Elsevier B.V. All rights reserved.

Low-threshold and continuously tunable Yb : Gd2SiO5 laser

Yb:Gd2SiO5 (Yb:GSO) exhibits a large fundamental manifold splitting. Its long-wavelength emission band around 1088 nm, which has the largest emission cross section, encounters the lowest reabsorption losses caused by thermal population of the terminal laser level. As a result, low-threshold and tunable continuous-wave Yb:GSO lasers were demonstrated. A slope efficiency up to 86% and a pumping threshold as low as 127 mW were achieved for a continuous-wave Yb:GSO laser at 1092.5 nm under the pump of a high-brightness laser diode. A continuous tunability between 1000 and 1120 nm was realized with an SF14 prism as the intracavity tuning element. (c) 2006 American Institute of Physics.

Effect of air annealing on the spectral properties of Ce : Y3Al5O12 single crystals grown by the temperature gradient technique

Five absorption hands, at 227, 300 340, 370 and 457nm, were observed in the optical absorption spectrum of Ce:Y3Al5O12 (Ce:YAG) crystals grown by the temperature gradient technique (TGT). The absorption bands at 227, 340, and 457 nm were identified Lis belonging to the Ce3+ -ion in the YAG crystal. A near UV optical emission band at 398nm was observed. with an excitation spectrum containing two bands, at 235 and 370nm. No fluorescence was detected under 300 nm excitation. The pair of absorption bands at 235 and 370 nm and the absorption band at 300 nm were attributed to the F- and F+-type color centers, respectively. The color centers model was also applied to explain the spectral changes in the Ce:YAG (TGT) crystal, including the reduction in the Ce 31 -ion absorption intensity, after annealing in an oxidizing atmosphere (air). (C) 2004 Elsevier B.V. All rights reserved.

Cooperative and charge transfer luminescence in Yb3+ -doped yttrium aluminum perovskite (YAlO3)

YAlO3 (YAP) crystals with different Yb3+ concentration have been grown by Czochralski method and cooperative fluorescence of Yb3+ ions in YAP crystal was studied under 940-nm infrared (IR) LD excitation at room temperature. The Yb concentration dependence of absorption intensity of IR and charge transfer bands exhibit different features. The green emission band in the region of 480-520nm was assigned to the cooperative deexcitation of two Yb3+ ions. The remaining upconverted emission bands containing various sharp peaks associated with impurity ions were observed and discussed. Charge transfer luminescence of heavily doped 20at% Yb:YAP is strongly temperature dependent and no concentration quenching of the charge transfer luminescence was found through the investigation of different Yb levels samples. (c) 2006 Elsevier B.V. All rights reserved.

Cr4+在Al2O3多晶体中的光谱性能研究

Transparent polycrystalline Cr:Al2O3 ceramics were synthesized by conventional pressureless synthesis processing. The absorption and emission spectra of Cr:Al2O3 ceramics specimens before and after annealing were measured at room temperature. It was discovered that the emission spectra of Cr4+ in Al2O3 octahedral coordination site is in infrared wavelength range of 1100-1600 nm. The emission peak of Cr4+ is centered at 1223 nm, which is similar to that of Cr4+ in tetrahedral site. Al2O3 has smaller lattice constant, resulting in the larger crystal field strength, so there is a blue shift in the peak of Cr4+:Al2O3 ceramics compared to those of other Cr4+-doped crystals. And the emission band is much narrower with full width at half maximum Delta lambda 37 nm.

Spectral properties of Ho : GdVO4 single crystal

Absorption and emission spectral properties of GdVO4 single crystal doped with Ho3+ ions were investigated at room temperature. Polarized absorption cross section is calculated in the range of 400-2200nm. Results were analyzed and parameters were calculated based on Judd-Ofelt theory, the emission spectrum shows that the emission intensity around the wavelength of 546 nm associated with transition S-5(2) -> I-5(8) is much stronger than other bands in the observed range and potentially enable the green light output around this emission band in this crystal. (c) 2006 Elsevier B.V. All rights reserved.

Spectroscopic properties of Ce : YAP scintillation crystal grown by temperature gradient technique

Spectroscopic properties of Ce-doped yttrium orthoaluminate (Ce:YAlO3 or Ce:YAP) crystals grown by temperature gradient technique (TGT) were investigated, and the effects of the growth conditions on the properties were analyzed.. Methods of optical absorption (OA), photoluminescence (PL), photoluminescence decay (PLD), X-ray excited luminescence (XL) and cathodeluminescence (CL) were used in these investigations. The results showed that the absorption band peak at 202, 394 and 532 nm originated from F and F+ color center induced by the weak reducing growth atmosphere, green emission band near 500 ran derived from Ce3+ -Ce3+ pairs and band at 650 similar to 850 run from some unintentional impurity in crystals.

Infrared to visible upconversion fluorescence in Yb,Tm : YAG single crystal

Absorption spectrum from 400 to 2000 run and upconversion fluorescence spectra under 940 nm pumping of YAG single crystal codoped with 5 at.% Yb3+ and 4 at.% Tm3+ were studied at room temperature. The blue upconversion emission centered at 483 nm corresponds to the transition (1)G(4) -> H-3(6), the emission band around 646 nm corresponds to the transition (1)G(4) -> F-3(4) of Tm3+. Energy transfer from Yb3+ to Tm3+ is mainly nonradiative and the transfer efficiency was experimentally assessed. The line strengths, transition probabilities and radiative lifetimes of (1)G(4) level were calculated by using Judd-Ofelt theory. Gain coefficient calculated from spectra shows that the upconversion corresponding with transitions (1)G(4) -> H-3(6) in YAG doped with Yb3+ and Tm3+ is potentially useful for blue light Output. (c) 2006 Elsevier B.V. All rights reserved.

Edge-defined, film-fed growth (EFG) technique for the preparation of alpha-Al2O3 : C crystal with highly sensitive thermoluminescence response

In this work, alpha-Al2O3:C, a highly sensitive thermoluminescence dosimetry crystal, was grown by the EFG method in which a graphite heating unit and shield acted as the carbon source during the growth process. The optical, luminescent properties and dosimetric characteristics of the crystal were investigated. The as-grown crystal shows a single glow peak at 536 K, which is associated with Cr3+ ions. After annealing in H-2 at 1673 K for 80 h, the crystal shows a single glow peak at 460 K and a blue emission band at 415 nm. The thermoluminescent response of the annealed crystal shows linear-sublinear-saturation characteristics in the dose range from 5 x 10(-6) to 100 Gy.

New observations on the pressure dependence of luminescence from Eu2+-doped MF2 (M = Ca, Sr, Ba) fluorides

The luminescence from Eu2+ ions in MF2 (M = Ca, Sr, Ba) fluorides has been investigated under the pressure range of 0-8 GPa. The emission band originating from the 4f(6)5d(1) -> 4f(7) transition of Eu2+ ions in CaF2 and SrF2 shows the red-shift as increasing pressure with pressure coefficients of -17 meV/GPa for CaF2 and -18 meV/GPa for SrF2. At atmospheric pressure, the emission spectrum of BaF2:Eu2+ comprises two peaks at 2.20 and 2.75 eV from the impurity trapped exciton (ITE) and the self-trapped exciton (STE), respectively. As the pressure is increased, both emission peaks shift to higher energies, and the shifting rate is slowed by the phase transition from the cubic to orthorhombic phase at 4 GPa. Due to the phase transition at 4-5 GPa pressure, the ITE emission disappears gradually, and the STE emission is gradually replaced by the 4f(6)5d(1) -> 4f(7) transition of Eu2+. Above 5 GPa, the pressure behavior of the 4f(6)5d(1) -> 4f(7) transition of EU2+ in BaF2: EU2+ is the same as the normal emission of Eu2+ in CaF2 and SrF2 phosphors.

The growth temperatures dependence of optical and electrical properties of InN films

InN films grown on sapphire at different substrate temperatures from 550 degrees C to 700 degrees C by metalorganic chemical vapor deposition were investigated. The low-temperature GaN nucleation layer with high-temperature annealing (1100 degrees C) was used as a buffer for main InN layer growth. X-ray diffraction and Raman scattering measurements reveal that the quality of InN films can be improved by increasing the growth temperature to 600 degrees C. Further high substrate temperatures may promote the thermal decomposition of InN films and result in poor crystallinity and surface morphology. The photoluminescence and Hall measurements were employed to characterize the optical and electrical properties of InN films, which also indicates strong growth temperature dependence. The InN films grown at temperature of 600 degrees C show not only a high mobility with low carrier concentration, but also a strong infrared emission band located around 0.7 eV. For a 600 nm thick InN film grown at 600 degrees C, the Hall mobility achieves up to 938 cm(2)/Vs with electron concentration of 3.9 x 10(18) cm(-3).