Experimental formulation of an anti fouling paint with tributyl tin oxide as toxic pigment

Results of the experimental formulation of an antifouling paint incorporating TBTO as toxic pigment are presented in this paper. Of the various resins tested, namely, phenolic, cashew nut shell liquid (CNSL), epoxy linseed oil with rosin and limed rosin, the paint composition with limed rosin gave the critical leaching rate of TBTO. Acid alkali test showed dissolution of matrix and visible migration of toxin to the surface. Accelerated corrosion tests had not recorded any signs of corrosion in panels painted with or without barrier coat. Raft exposure studies indicated that the new formulation could resist fouling accumulation on painted panels for 9 months.

Comparative study of Cr3C2-NiCr coatings obtained by HVOF and hard chromium coatings

In the present work the corrosion resistance of micro-cracked hard chromium and Cr3C2-NiCr (HVOF) coatings applied on a steel substrate have been compared using open-circuit potential (E-OC) measurements, electrochemical impedance spectroscopy (EIS) and polarization curves. The coatings surfaces and cross-section were characterized before and after corrosion tests using optical microscopy (OM) and scanning electron microscopy (SEM). After 18 h of immersion, the open-circuit potential values were around -0.50 and -0.25V/(Ag vertical bar AgCl vertical bar KClsat) for hard chromium and Cr3C2- NiCr, respectively. The surface analysis done after 12 h of immersion showed iron on the hard chromium surface inside/near surface cracks, while iron was not detected on the Cr3C2-NiCr surface even after 18 h. For longer immersion time hard chromium was more degraded than thermal sprayed coating. For hard chromium coating a total resistance values between 50 and 80 k Omega cm(2) were measured and two well-defined time constants were observed, without significant change with the immersion time. For Cr3C2-NiCr coating the total impedance diminished from around 750 to 25 k Omega cm(2) as the immersion time increased from 17 up to 132 h and two overlapped time constants were also observed. Polarization curves recorded after 18 h of immersion showed a lower current and higher corrosion potential for Cr3C2-NiCr coating than other samples studied. (c) 2005 Elsevier Ltd. All rights reserved.

WC-CoCr coatings sprayed by high velocity oxygen-fuel (HVOF) flame on AA7050 aluminum alloy: electrochemical behavior in 3.5% NaCl solution

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Análise morfológica da corrosão por pites em aço inoxidável austenítico AISI 310S submetido à exposição em névoa salina

O artigo teve como objetivo estudar a evolução do crescimento, distribuição e classificação dos pites em aços inoxidáveis austeníticos AISI 310S no estado como recebida e tratado termicamente, submetidos a diferentes tempos de exposição em meio salino. A aplicabilidade deste trabalho baseou-se no desenvolvimento de uma técnica para caracterização morfológica da corrosão localizada, associado com os aspectos de descrição de formas, tamanho, parâmetros específicos e populacionais. A metodologia consistiu nas seguintes etapas: preparação dos corpos de prova, testes de corrosão via névoa salina em diferentes condições, análise microestrutural, análise dos perfis dos pites, processamento digital e análise de imagens, visando caracterizar a distribuição, morfologia e o tamanho dos pites. Os resultados obtidos no processamento digital e análise de imagens dos perfis foram submetidos á análise estatística, utilizando à mediana como parâmetro de avaliação na liga como recebido e tratada. A liga como recebido, exibe a seguinte morfologia: pites hemisféricos> região de transição A> região de transição B> irregulares> cônicos. A quantidade de pites na liga tratada a cada tempo de exposição é: região de transição B> hemisféricos> região de transição A> cônicos> irregulares.

On the development of the electrochemical potentiokinetic method

The development of electrochemical potentiokinetic methods as applied to the testing of metals and alloys is followed from its early phases up to its latest advances relating to intergranular corrosion, SCC and pitting corrosion tests of stainless steels and special alloys and to the examination of their structure and properties. In assessing the susceptibility to intergranular and pitting corrosion by potentiokinetic polarization tests, the polarization curves which apply to the bulk of the alloy grains (the matrix) must be distinguished from those pertaining to grain boundaries. Cyclic polarization measurements such as the electrochemical potentiokinetic reactivation (EPR) test make it possible to derive the alloy's susceptibility to intergranular, pitting and crevice corrosion from characteristic potentials and other quantities determined in the 'double loop' test. EPR is rapid and responds to the combined effects of a number of factors that influence the properties of materials. The electrochemical p otentiokinetic tests are sensitive enough to detect structural changes in heat treated materials ranging far beyond the stainless steels alone, and can be used for non-destructive testing aimed at elucidating the properties and behavior of materials. © 2001 Elsevier Science Ltd. All rights reserved.

Influence of chromate, molybdate and tungstate on pit formation in chloride medium

It has been characterized and evaluated the 2024-T351 and 7050-T7451 aluminum alloys pitting corrosion in naturally aerated chloride aqueous solutions containing chromate, molybdate and tungstate. It has been carried out electrochemical and non-electrochemical immersion corrosion tests accompanied by surface metallography analysis using an optical microscopy. Chromate for the two alloys and in molybdate for 7050 has corrosion inhibiting effects, whereas tungstate promotes the pitting corrosion for these alloys. Quantitative surface analysis upon the alloys after immersion has indicated that pits are predominantly conical or quasi-conical and irregular. In general, pits have been wider than deep and the widest have been also the deepest. Despite inhibitor presence, when pits have been nucleated, they grow with the same intensity. © 2005 Elsevier B.V. All rights reserved.

Caracterização mecânica, microestrutural e avaliação da fragilização pelo hidrogênio em tubos de aço API 5L grau X65MS PSL2

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Resistência à corrosão eletroquímica da liga TI-6AL4V prototipada para aplicações biomédicas

Pós-graduação em Engenharia Mecânica - FEIS

Efeito de oxigênio na biocompatibilidade e propriedades da liga Ti-15Mo

Pós-graduação em Ciência e Tecnologia de Materiais - FC

Estudo da corrosão das ligas Ni-Cr-Mo para próteses dentárias fixas em solução aquosa de NaF 0,05% , NaCl 0,05% e em colutórios comerciais

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Resistência à corrosão de ligas Ni-Cr-Mo em meios fluoretados para aplicações odontológicas

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Variáveis térmicas de solidificação, espaçamento dentríticos secundários e resistência à corrosão de ligas hipoeutéticas Al-Ni

No presente trabalho, é realizada uma seqüência de experimentos com ligas hipoeutéticas Al-Ni para analisar a solidificação unidirecional vertical ascendente em condições transitórias de fluxo de calor. Abordagens experimentais são desenvolvidas para a determinação quantitativa de variáveis térmicas de solidificação, tais como: tempos locais de solidificação; velocidades de deslocamento das isotermas liquidus; taxas de resfriamento à frente da isoterma liquidus e gradientes térmicos à frente da interface sólido / líquido. O trabalho analisa também a dependência dos espaçamentos dendríticos secundários em relação às variáveis térmicas de solidificação e ao teor de soluto das ligas, além de relacionar estes parâmetros com a resistência à corrosão destas ligas. Esses parâmetros dendríticos experimentais, referentes à solidificação das ligas Al - 1, 1,4 e 1,8 % Ni, não puderam ser comparados com os principais modelos teóricos de crescimento dendrítico da literatura, pois, para as ligas em estudo há uma escassez de propriedades termofísicas, impossibilitando assim esta comparação. O comportamento corrosivo é analisado pela técnica de polarização potenciodinâmica e técnica de polarização potenciodinâmica cíclica conduzidas em solução de 3,5% NaCl em temperatura ambiente, estruturas dendríticas mais grosseiras tendem a aumentar as taxas de corrosão das ligas hipoeutéticas do sistema Al-Ni. Os resultados experimentais obtidos através de ensaios de corrosão são correlacionados com a microestrutura dendrítica. Dessa forma, são determinadas tendências experimentais de crescimento dendrítico e resistência à corrosão para a solidificação unidirecional vertical ascendente.

Estudo da corrosão em ligas de alumínio utilizadas na indústria aeronáutica

A resistência e o mecanismo de corrosão das ligas de alumínio 2024, 7010, 7050 e 7475 foram estudados em solução de NaCl. Os efeitos do tratamento térmico nas ligas, concentração de oxigênio, pH, adição de oxi-ânions e temperatura do meio constituem algumas das variáveis estudadas. Primeiramente, procedeu-se à caracterização físicoquímica dos materiais através de análise química e metalográfica, mediante microscopia eletrônica de varredura e espectroscopia de energia dispersiva. As ligas 2024, 7010, 7050 e 7475 como recebidas, recozidas e envelhecidas, revelaram a existência de partículas ternárias e quaternárias, constituídas por Al:Cu:Fe e Mg ou Zn. Também foi observado um maior número de partículas pequenas de composição variável situando-se, preferencialmente, nos contornos dos grãos. Os resultados dos ensaios de corrosão em meios aerados e desaerados indicam que o cromato é efetivo como inibidor da corrosão localizada em ambas ligas e que o molibdato somente na liga 7050. O efeito inibidor do tungstato se revela em meio desaerado e é comparativamente menor daquele observado com os outros oxi-ânions. As análises quantitativas de superfície das ligas após os ensaios de imersão indicam que ainda na presença de inibidor, se pites foram nucleados, eles crescem.

Corrosão do aço-carbono: uma abordagem do cotidiano no ensino de química

In this paper, two simple ways of evaluating carbon steel sheet corrosion in a hydrochloric acid solution were presented as an experimental proposal for corrosion teaching. The first method is based on direct measurements of mass before and after corrosion tests. The second approach follows the principle of visual colorimetry by which soluble corrosion products are transformed into red complexes allowing monitoring of the products'concentration according to increases in solution color intensity. Both methods proved able to determine the corrosion rate.

Avaliação da resistência à corrosão da liga Ti-30Ta submetida a diferentes taxas de deformação visando aplicações biomédicas

This study aims to evaluate the corrosion resistance of Ti-30Ta alloy when subjected to different strain rates. Samples of the alloy Ti-30Ta were obtained from the melting of pure elements in the arc furnace in inert atmosphere (argon gas). Then, the samples were subjected to a thermal treatment and to cold worked to obtain bars. After forging, the samples were machined in accordance with ASTME9-09 standard for carried out compression tests. To microstructural characterization, samples were sectioned longitudinal and transversally and embedded in resin. After, the wet sanding and polishing were performed, followed by a chemical attack, in order to study the microstructure under an optical microscope. Microhardness was measured on the samples that were subjected to microstructural characterization by using microhardness tester. Phases were evaluated by x-rays diffraction. Corrosion tests were carried out to evaluate the influence of deformation on the corrosion resistance. Results show that microstructure was not influenced by deformation