Toughening mechanism of polymer blends: Influence of voiding ability of dispersed-phase particles

The parameters which effect the cavitation strain of polymer blends toughened with a shear yield mechanism have been studied by analysis of the stress acted on the equatorial plane of dispersed-phase particles. As a result, the cavitation strain of polymer blends depends on the Young's modulus and the Poisson's ratio of the dispersed-phase particles and the matrix and also on the break stress of dispersed-phase particles. We tried to provide a criterion for selecting the materials used as dispersed-phase particles which can effectively enhance the toughness of polymer blends. (C) 1996 John Wiley & Sons, Inc.

EFFECT OF PARTICLE-SIZE ON IMPACT STRENGTH OF POLYMER BLENDS

The effect of particle size on impact strength of polymer blends with ductile fracture was studied. The results are in agreement with the experiments. (C) 1995 John Wiley & Sons, Inc.

IN-SITU COMPOSITE - PHENOLPHTHALEIN POLYETHERSULFONE-THERMOTROPIC LIQUID-CRYSTALLINE POLYMER BLENDS

Phase behavior, thermal, theological and mechanical properties plus morphology have been studied for a binary polymer blend. The blend is phenolphthalein polyethersulfone (PES-C) with a thermotropic liquid crystalline polymer (LCP), a condensation copolymer of p-hydroxybenzoic acid with ethylene terephthalate (PHB-PET). It was found that these two polymers form optically isotropic and homogeneous blends by means of a solvent casting method. The homogeneous blends undergo phase separation during heat treatment. However, melt mixed PES-C/PHB-PET blends were heterogeneous based upon DSC and DMA analysis and SEM examination. Addition of LCP in PES-C resulted in a marked reduction of melt viscosity and thus improved processability. Compared to pure PES-C, the charpy impact strength of the blend containing 2.5% LCP increased 2.5 times. Synergistic effects were also observed for the mechanical properties of blends containing < 10% LCP. Particulates, ribbons, and fibrils were found to be the typical morphological units of PHB-PET in the PES-C matrix, which depended upon the concentration of LCP and the processing conditions.

FRACTURE-TOUGHNESS AND MORPHOLOGY OF PHENOLPHTHALEIN POLY(ETHER SULFONE) THERMOTROPIC LIQUID-CRYSTALLINE POLYMER BLENDS

Blends of a new phenolphthalein poly (ether sulfone) (PES-C) and a thermotropic liquid crystalline polymer (LCP) were prepared by melt-blending in a twin-screw extruder. Rheological properties, fracture toughness, K(IC), and morphology of the blends were

INTERFACIAL BEHAVIOR OF COMPATIBILIZERS IN POLYMER BLENDS

From an analysis of the literature and our experimental results, we have established that interfacial tension is a function of the concentration of a compatibilizer, and put forward a 'three-stage' physical model to account for the compatibilizing behavio

ENTANGLEMENT FLUCTUATION DURING PHASE-SEPARATION IN POLYMER BLENDS

For perhaps the first time, the dynamics of liquid-liquid phase separation was studied by time-resolved mechanical spectrometry in order to establish the relationship between blends' properties and the phase structures during spinodal decomposition (SD). The selected system was chlorinated polyethylene (CPE)/ethylene-vinyl acetate copolymer (EVA). It was found that in the early and intermediate stage of SD, the storage modulus (G') and the loss modulus (G'') increase with time after the initiation of the isothermal phase separation; in the later stage, G' and G'' decrease as phase separation proceeds. An entanglement fluctuation model was presented to manifest this phenomenon; it was found that the rheological behavior agrees well with the expections of the model in the early stage. For the later stage, the reduction of G' and G'' can be attributed to the increment of phase-domain size. (C) 1993 John Wiley & Sons, Inc.

STATISTICAL THERMODYNAMICS OF POLYDISPERSE POLYMER BLENDS WITH STRONG INTERACTION

A statistical thermodynamics theory of polydisperse polymer mixtures with strong interaction between dissimilar components based on a lattice fluid model is formulated. Expressions for the free energy, equation of state, phase stability and spinodal for a polydisperse, binary polymer mixture with strong interaction are derived.

FACTOR-ANALYSIS APPLIED TO X-RAY-DIFFRACTION DIAGRAMS OF POLYMER BLENDS

The feasibility of applying the method of factor analysis to X-ray diffraction diagrams of binary blends of polypropylene and ethylene-propylene-diene terpolymer (PP/EPDM) was examined. The result of mathematical treatment was satisfactory. The number of scattering species and their concentrations in six kinds of PP/EPDM blends were determined. The separation of the spectral peaks of each species in the blends, contributing spectral intensities, was carried out.

FRACTAL BEHAVIOR OF SPINODAL DECOMPOSITION IN POLYMER BLENDS

Fractal behaviour of ramified domains in the late stage of spinodal phase separation in a binary polymer blend of poly(vinyl acetate) with poly(methyl methacrylate) was investigated by optical microscopic method. In the late stage of the spinodal decomposition, the fractal dimension D is about 1.64. It implies that some anomalous properties of irregular structure probably may be explained by fractal concepts.

Dynamic mechanical analysis of binary and ternary polymer blends based on nylon copolymer/EPDM rubber and EPM grafted maleic anhydride compatibilizer

The dynamic mechanical properties such as storage modulus, loss modulus and damping properties of blends of nylon copolymer (PA6,66) with ethylene propylene diene (EPDM) rubber was investigated with special reference to the effect of blend ratio and compatibilisation over a temperature range –100°C to 150°C at different frequencies. The effect of change in the composition of the polymer blends on tanδ was studied to understand the extent of polymer miscibility and damping characteristics. The loss tangent curve of the blends exhibited two transition peaks, corresponding to the glass transition temperature (Tg) of individual components indicating incompatibility of the blend systems. The morphology of the blends has been examined by using scanning electron microscopy. The Arrhenius relationship was used to calculate the activation energy for the glass transition of the blends. Finally, attempts have been made to compare the experimental data with theoretical models.

Weld line behaviour of polymer blends with special reference to PP/HDPE, PP/PS and HDPE/LDPE blends

Department of Polymer Science and Rubber Technology, Cochin University of Science and Technology

Studies on the fracture behaviour of polymer blends with special reference to PP/HDPE and PS/HIPS blends

Investigations on the fracture behaviour of polymer blends is the topic of this thesis. The blends selected are PP/HDPE and PS/HIPS. PP/HDPE blend is chosen due to its commercial importance and PS/HIPS blend is selected to study the transition from brittle fracture to ductile fracture.PP/HDPE blends were prepared at different compositions by melt blending at 180°C and fracture failure process was investigated by conducting notch sensitivity test and tensile test at different strain rates. The effects of two types of modifiers (particulate and elastomer) on the fracture behaviour and notch sensitivity of PP/HDPE blends were studied. The modifiers used are calcium carbonate, a hard particulate filler commonly used in plastics and Ethylene Propylene Diene Monomer (EPDM). They were added in 2%, 4% and 6% by weight of the blends.The study shows that the mechanical properties of PP/HDPE blends can be optimized by selecting proper blend compositions. The selected modifiers are found to alter and improve the fracture behaviour and notch sensitivity of the blends. Particulate fillers like calcium carbonate can be used for making the mechanical behaviour more stable at the various blend compositions. The resistance to notch sensitivity of the blends is found to be marginally lower in the presence of calcium carbonate. The elastomeric modifier EPDM produces a better stability of the mechanical behaviour. A low concentration of EPDM is sufficient to effect such a change. EPDM significantly improves the resistance to notch sensitivity of the blends. The study shows that judicious selection of modifiers can improve the fracture behaviour and notch sensitivity of PP/HDPE blends and help these materials to be used for critical applications.For investigating the transition in fracture behaviour and failure modes, PS/HIPS blends were selected. The blends were prepared by melt mixing followed by injection moulding to prepare the specimens for conducting tensile, impact and flexure tests. These tests were used to simulate the various conditions which promote failure.The tensile behaviour of unnotched and notched PS/HIPS blend samples were evaluated at slow speeds. Tensile strengths and moduli were found to increase at the higher testing speed for all the blend combinations whereas maximum strain at break was found to decrease. For a particular speed of testing, the tensile strength and modulus show only a very slight decrease as HIPS content is increased up to about 40%. However, there is a drastic decrease on increasing the HIPS content thereafter.The maximum strain at break shows only a very slight change up to about 40% HIPS content and thereafter shows a remarkable increase. The notched specimens also follow a comparable trend even though the notch sensitivity is seen high for PS rich blends containing up to 40% HIPS. The notch sensitivity marginally decreases with increase in HIPS content. At the same time, it is found to increase with the increase in strain rate. It is observed that blends containing more than 40% HIPS fail in ductile mode.The impact characteristics of PSIHIPS blends studied were impact strength, the energy absorbed by the test specimen and impact toughness. Remarkable increase in impact strength is observed as HIPS content in the blend exceeds 40%. The energy absorbed by the test specimens and the impact toughness also show a comparable trend.Flexural testing which helps to characterize the load bearing capacity was conducted on PS/HIPS blend samples at the two different testing speeds of 5mmlmin and 10 mm/min. The flexural strength increases with increase in testing speed for all the blend compositions. At both the speeds, remarkable reduction in flexural strength is observed as HIPS content in the blend exceeds 40%. The flexural strain and flexural energy absorbed by the specimens are found to increase with increase in HIPS content. At both the testing speeds, brittle fracture is observed for PS rich blends whereas HIPS rich blends show ductile mode of failure.Photoelastic investigations were conducted on PS/HIPS blend samples to analyze their failure modes. A plane polariscope with a broad source of light was utilized for the study. The coloured isochromatic fringes formed indicate the presence of residual stress concentration in the blend samples. The coverage made by the fringes on the test specimens varies with the blend composition and it shows a reducing trend with the increase in HIPS content. This indicates that the presence of residual stress is a contributing factor leading to brittle fracture in PS rich blends and this tendency gradually falls with increase in HIPS content and leads to their ductile mode of failure.