The diffusion of Co⠶溩 Zrâ â Tiâ â alloy /|nS. Kumar. -- 260 St Catharines [Ont.] : Dept. of Physics, Brock University,

The diffusion of Co60 in the body centered cubic beta phase of a ZrSOTi SO alloy has been studied at 900°, 1200°, and 1440°C. The results confirm earlier unpublished data obtained by Kidson17 • The temperature dependence of the diffusion coefficient is unusual and suggests that at least two and possibly three mechanisms may be operative Annealing of the specimen in the high B.C.C. region prior to the deposition of the tracer results in a large reduction in the diffusion coefficient. The possible significance of this effect is discussed in terms of rapid transport along dislocation network.

Retention at room temperature of the tetragonal t ``-form in Sc(2)O(3)-doped ZrO(2) nanopowders

Synchrotron X-ray powder diffraction was applied to the study of the effect of crystallite size on the crystal structure of ZrO(2)-10 mol% Sc(2)O(3) nanopowders synthesized by a nitrate-lysine gel-combustion route Nanopowders with different average crystallite sizes were obtained by calcination at several temperatures, ranging from 650 to 1200 degrees C The metastable t""-form of the tetragonal phase, exhibiting a cubic unit cell and tetragonal P4(2)/nmc spatial symmetry, was retained at room temperature in fine nanocrystalline powders, completely avoiding the presence of the stable rhombohedral beta phase. Differently, this phase was identified in samples calcined at high temperatures and its content increased with increasing crystallite size The critical maximum crystallite size for the retention of the mestastable t""-form resulted of about 35 nm (C) 2009 Elsevier B.V All rights reserved

The effects of temperature on the molecular orientation of zinc phthalocyanine films

Phthalocyanine compounds have been widely investigated as candidate materials for technological applications, which is mainly due to their thermal stability and possibility of processing in the form of thin films. In most applications, the controlled growth of thin films with high crystalline quality is essential. In this study, zinc phthalocyanine (ZnPc) thin films were prepared by evaporation on glass and Au-coated glass substrates with subsequent annealing at different temperatures in ambient atmosphere. The morphological and structural features of 80 nm thick zinc phthalocyanine films were investigated, evidencing an alpha -> beta phase transformation after annealing the films at 200 A degrees C, as indicated by UV-Vis spectroscopy and FTIR analyses. A better uniformity of the annealed films was also evidenced via AFM analysis, which may be of importance for applications where film homogeneity and excellent optical quality are required.

Corrosion behavior of Ti-13Nb-13Zr alloy used as a biomaterial

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Effect of 4 mass% Ag addition on the thermal behavior of the Cu-9 mass% Al alloy

The effect of 4 mass% Ag addition on the thermal behavior of the Cu-9 mass% Al alloy was studied using differential scanning calorimetry (DSC), optical microscopy (OM), scanning electron microscopy (SEM), energy dispersive X-ray analysis (EDX) and X-ray diffractometry (XRD). The results showed that the presence of silver causes (Cu)-alpha+(alpha+gamma1)-->(Cu)-alpha+beta transformation to occur in two stages. In the first one, part of the produced beta phase combines with the precipitated Ag to give a silver-rich phase and in the second one the transformation is completed. The formation of this silver-rich phase seems to be enhanced at very low cooling rates.

Isothermal decomposition kinetics in the Cu-9%Al-4%Ag alloy

The influence of 4 wt.%Ag addition on the isothermal decomposition kinetics of the beta' phase in the Cu-9wt.%Al alloy was studied by microhardness measurements, optical and scanning electron microscopy (SEM), energy dispersive X-ray (EDX) analysis, and X-ray diffractometry. The results showed that the presence of Ag decreases the beta' --> (alpha + gamma(1)) decomposition reaction rate in the Cu-9%Al-4%Ag alloy, an effect that may be associated to the gamma(1) phase which catalyses the Ag precipitation, making it faster than the decomposition reaction, and thus, stabilizing the martensitic phase. (C) 2003 Elsevier B.V. All rights reserved.

Activation energy for the reverse eutectoid reaction in hypo-eutectoid Cu-Al alloys

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of low contents of a polyaniline derivative on the crystallization and electrical properties of blends with PVDF

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of commercial mouthwashes on the corrosion resistance of Ti-10Mo experimental alloy

The purpose of this work was to evaluate the effect of three commercial mouthwashes on the corrosion resistance of Ti-10Mo experimental alloy. Experiments were made at 37.0 +/- 0.5 degrees C in a conventional three-compartment double wall glass cell containing commercial mouthwashes. Three mouthwashes with different active ingredients were tested: ( I) 0.05% sodium fluoride + 0.03% triclosan; (II) 0.5 g/l cetylpyridinium chloride + 0.05% sodium fluoride; (III) 0.12% chlorohexidine digluconate. The assessment of the individual effect of active ingredients was studied by using 0.05% sodium fluoride. Commercially pure titanium (CP Ti) was used as control. Microstructures from Ti-10Mo experimental alloy and CP Ti were also evaluated using optical microscopy. Ti-10Mo as-cast alloy shows the typical rapidly cooled dendrites microstructure (beta phase) while CP Ti has exhibited a metastable martensitic microstructure. Electrochemical behavior of dental materials here studied was more affected by mouthwash type than by Ti alloy composition or microstructure. In both alloys passivation phenomenon was observed. This process may be mainly related to Ti oxides or other Ti species present in spontaneously formed film. Small differences in passive current densities values may be connected with changes in film porosity and thickness. Protective characteristics of this passive film are lower in 0.05% sodium fluoride + 0.03% triclosan mouthwash than in the other two mouthwashes tested.

Morphology of poly(vinylidene fluoride) and poly(o-metoxyaniline) blends

Blends of poly(o-methoxyaniline) - POMA - and poly(vinylidene fluoride) - PVDF - of various compositions were prepared from organic solvent solutions. Flexible, free-standing and stretchable films were obtained by casting, which were characterized by conductivity measurements, electron microscopy and differential scanning calorimetry. As expected, the blends conductivity increases with increasing contents of the conducting polymer. The onset of the conductivity at low contents of conducting polymer indicates a low percolation threshold for the blends. Despite the presence of the conductive host, the blends displayed the crystalline spherulitic morphology and the beta-phase characteristic of pure PVDF. This morphology appears to be destroyed, however, if the film is stretched by zone-drawing.

Development of Ti-Mo alloys for biomedical applications: Microstructure and electrochemical characterization

Ti-Mo alloys from 4 to 20 Mo wt.% were arc-melted. Their compositions and surfaces were analyzed by EDX, XRF and SEM. The Mo mapping shows a homogeneous distribution for all alloys. The XRD analysis showed that the crystal structure of the alloys is sensitive to the Mo concentration; a mixture of the hexagonal alpha' and orthorhombic alpha '' phases was observed for the Ti-4Mo alloy, and the alpha '' phase is observed almost exclusively when the concentration of Mo added to the Ti reaches 6%. A significant retention of the beta phase is observed for the alloy containing 10% Mo, while at higher Mo concentrations (15% and 20%), retention of phase beta is only verified. Preliminary electrochemical studies have indicated a valve-metal behavior and good corrosion resistance in aerated Ringer solution for all alloys. (c) 2006 Published by Elsevier B.V.

Thermal behavior of the Cu-22.55 at.%Al alloy with small Ag additions

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Low-frequency high-temperature internal friction in Ti-13Nb-13Zr alloy

Recent studies have been done to achieve biomedical alloys containing non-toxic elements and presenting low elastic moduli. It has been reported that Ti-Nb-Zr alloys rich in beta phase, especially Ti-13Nb-13Zr, have potential characteristics for substituting conventional materials such as Ti-6Al-4V, stainless steel and Co alloys. The aim of this work is to study the internal friction (IF) of Ti-13Nb-13Zr (TNZ) alloy due to the importance of the absorption impacts in orthopedic applications. The internal friction of this alloy produced by arc melting was measured using an inverted torsion pendulum with the free decay method. The measurements were performed from 77 to 700 K with heating rate of 1 K/min, in a vacuum better than 10-5 mBar. The results show a relaxation structure at high temperature strongly dependent on microstructure of the material. Qualitative discussions are presented for the experimental results, and the possibility of using the TNZ as a high damping material is briefly mentioned.

Efeito do oxigênio nas propriedades anelásticas e biocompatibilidade das ligas de Ti-8%pTa e Ti-16%pTa utilizadas como biomaterial

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Ti-Mo alloys employed as biomaterials: Effects of composition and aging heat treatment on microstructure and mechanical behavior

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)