Push-out bond strength of CAD/CAM-ceramic luted to dentin with self-adhesive resin cements

OBJECTIVES: This study evaluated the initial and the artificially aged push-out bond strength between ceramic and dentin produced by one of five resin cements. METHODS: Two-hundred direct ceramic restorations (IPS Empress CAD) were luted to standardized Class I cavities in extracted human molars using one of four self-adhesive cements (SpeedCEM, RelyX Unicem Aplicap, SmartCem2 and iCEM) or a reference etch-and-rinse resin cement (Syntac/Variolink II) (n=40/cement). Push-out bond strength (PBS) was measured (1) after 24h water storage (non-aged group; n=20/cement) or (2) after artificial ageing with 5000 thermal cycles followed by 6 months humid storage (aged group; n=20/cement). Nonparametrical ANOVA and pairwise Wilcoxon rank-sum tests with Bonferroni-Holm adjustment were applied for statistical analysis. The significance level was set at alpha=0.05. In addition, failure mode and fracture pattern were analyzed by stereomicroscope and scanning electron microscopy. RESULTS: Whereas no statistically significant effect of storage condition was found (p=0.441), there was a significant effect of resin cement (p<0.0001): RelyX Unicem showed significantly higher PBS than the other cements. Syntac/Variolink II showed significantly higher PBS than SmartCEM2 (p<0.001). No significant differences were found between SpeedCEM, SmartCem2, and iCEM. The predominant failure mode was adhesive failure of cements at the dentin interface except for RelyX Unicem which in most cases showed cohesive failure in ceramic. SIGNIFICANCE: The resin cements showed marked differences in push-out bond strength when used for luting ceramic restorations to dentin. Variolink II with the etch-and-rinse adhesive Syntac did not perform better than three of the four self-adhesive resin cements tested.

Teeth restored using fiber-reinforced posts: in vitro fracture tests and finite element analysis

In dentistry the restoration of decayed teeth is challenging and makes great demands on both the dentist and the materials. Hence, fiber-reinforced posts have been introduced. The effects of different variables on the ultimate load on teeth restored using fiber-reinforced posts is controversial, maybe because the results are mostly based on non-standardized in vitro tests and, therefore, give inhomogeneous results. This study combines the advantages of in vitro tests and finite element analysis (FEA) to clarify the effects of ferrule height, post length and cementation technique used for restoration. Sixty-four single rooted premolars were decoronated (ferrule height 1 or 2 mm), endodontically treated and restored using fiber posts (length 2 or 7 mm), composite fillings and metal crowns (resin bonded or cemented). After thermocycling and chewing simulation the samples were loaded until fracture, recording first damage events. Using UNIANOVA to analyze recorded fracture loads, ferrule height and cementation technique were found to be significant, i.e. increased ferrule height and resin bonding of the crown resulted in higher fracture loads. Post length had no significant effect. All conventionally cemented crowns with a 1-mm ferrule height failed during artificial ageing, in contrast to resin-bonded crowns (75% survival rate). FEA confirmed these results and provided information about stress and force distribution within the restoration. Based on the findings of in vitro tests and computations we concluded that crowns, especially those with a small ferrule height, should be resin bonded. Finally, centrally positioned fiber-reinforced posts did not contribute to load transfer as long as the bond between the tooth and composite core was intact.

The influence of toothbrushing and coffee staining on different composite surface coatings

The aim of our study is to evaluate the performance of surface sealants and conventional polishing after ageing procedures. Eighty circular composite restorations were performed on extracted human molars. After standardised roughening, the restorations were either sealed with one of three surface sealants (Lasting Touch (LT), BisCover LV (BC), G-Coat Plus (GP) or a dentin adhesive Heliobond (HB)) or were manually polished with silicon polishers (MP) (n = 16). The average roughness (Ra) and colourimetric parameters (CP) (L*a*b*) were evaluated. The specimens underwent an artificial ageing process by thermocycling, staining (coffee) and abrasive (toothbrushing) procedures. After each ageing step, Ra and CP measurements were repeated. A qualitative surface analysis was performed with SEM. The differences between the test groups regarding Ra and CP values were analysed with nonparametric ANOVA analysis (α = 0.05). The lowest Ra values were achieved with HB. BC and GP resulted in Ra values below 0.2 μm (clinically relevant threshold), whereas LT and MP sometimes led to higher Ra values. LT showed a significantly higher discolouration after the first coffee staining, but this was normalised to the other groups after toothbrushing. The differences between the measurements and test groups for Ra and CP were statistically significant. However, the final colour difference showed no statistical difference among the five groups. SEM evaluation showed clear alterations after ageing in all coating groups. Surface sealants and dentin adhesives have the potential to reduce surface roughness but tend to debond over time. Surface sealants can only be recommended for polishing provisional restorations.

Age hardening of a sintered Al-Cu-Mg-Si-(Sn) alloy

The age hardening response of a sintered Al-3.8 wt% Cu-1.0 wt% Mg-0.70 wt% Si alloy with and without 0.1 wt% Sn was investigated. The sequence of precipitation was characterised using transmission electron microscopy. The ageing response of the sintered Al-Cu-Mg-Si-(Sn) alloy is similar to that of cognate wrought 2xxx series alloys. Peak hardness was associated with a fine, uniform dispersion of lath shaped precipitates, believed to be either the betaor Q phase, oriented along < 010 >. directions and theta' plates lying on {001}(alpha). planes. Natural ageing also resulted in comparable behaviour to that observed in wrought alloys. Porosity in the powder metallurgy alloys did not significantly affect the kinetics of precipitation during artificial ageing. Trace levels of tin, used to aid sintering, slightly reduced the hardening response of the alloy. However, this was compensated for by significant improvements in density and hardness. (c) 2005 Elsevier B.V. All rights reserved.

Corrosion protection of PVD and paint coatings for selective solar absorber surfaces

The selective solar absorber surface is a fundamental part of a solar thermal collector, as it is responsible for the solar radiation absorption and for reduction of radiation heat losses. The surface’s optical properties, the solar absorption (á) and the emittance (å), have great impact on the solar thermal collector efficiency. In this work, two coatings types were studied: coatings obtained by physical vapor deposition (PVDs) and coatings obtained by projection with different paints (PCs) on aluminum substrates. The most common industrial high performing solar selective absorbers are nowadays produced by vacuum deposition methods, showing some disadvantages, such as lower durability, lower resistance to corrosion, adhesion and scratch, higher cost and complex production techniques. Currently, spectrally selective paints are a potential alternative for absorbing surfaces in low temperature applications, with attractive features such as ease of processing, durability and commercial availability with low cost. Solar absorber surfaces were submitted to accelerated ageing tests, specified in ISO 22975-3. This standard is applicable to the evaluation of the long term behavior and service life of selective solar absorbers for solar collectors working under typical domestic hot water system conditions. The studied coatings have, in the case of PVDs solar absorptions between 0.93 and 0.96 and emittance between 0.07 and 0.10, and in the case of PCs, solar absorptions between 0.91 and 0.93 and emittance between 0.40 and 0.60. In addition to evaluating long term behavior based on artificial ageing tests, it is also important to know the degradation mechanism of different coatings that are currently in the market. Electrochemical impedance spectroscopy (EIS) allows for the assessment of mechanistic information concerning the degradation processes, providing quantitative data as output, which can easily relate to the kinetic parameters of the system. EIS measures were carried out on Gamry FAS2 Femostat coupled with a PCL4 Controller. Two electrolytes were used, 0.5 M NaCl and 0.5 M Na2SO4, and the surfaces were tested at different immersion times up to 4 weeks. The following types of specimens have been tested: Aluminium with/without surface treatment, 3 selective paint coatings (one with a poly(urethane) binder and two with silicone binders) and 2 PVD coatings. Based on the behaviour of the specimens throughout the 4 weeks of immersion, it is possible to conclude that the coating showing the best protective properties corresponds to the selective paint coating with a polyurethane resin followed by the other paint coatings, whereas both the PVD coatings do not confer any protection to the substrate, having a deleterious effect as compared to the untreated aluminium reference.

Lacunae Infills for in Situ Treatment of Historic Glazed Tiles

Knowledge of current conservation materials and methods together with those adopted in the past is essential to aid research and improve or develop better conservation options. The infill and painting of tile lacunae are subjected to special requirements mainly when used in outdoor settings. A selection of the most commonly used materials was undertaken and performed based on inquiries to practitioners working in the field. The infill pastes comprised organic (epoxy, polyester), inorganic (slaked lime,hydraulic lime and zinc hydroxychloride) and mixed organic–inorganic (slaked lime mixed with a vinylic resin)binders. The selected aggregates were those most commonly used or those already present in the commercially formulated products. The infill pastes were characterised by SEM, MIP, open porosity, water absorption by capillarity, water vapour permeability, thermal and hydric expansibilities and adhesion to the ceramic body. Their performance was assessed after curing, artificial ageing (salt ageing and UV–Temp–RH cycles) and natural ageing. The results were interpreted in terms of their significance as indicators of effectiveness, compatibility and durability

Forensic aspects of the weathering and ageing of spray paints

This paper presents a preliminary study on the degradation of spray paint samples, illustrated by Optical, FTIR and Raman measurements. As opposed to automotive paints which are specifically designed for improved outdoor exposure and protected using hindered amine light absorbers (HALS) and ultra-violet absorbers (UVA), the spray paints on their side are much simpler in composition and very likely to suffer more from joint effects of solar radiation, temperature and humidity. Six different spray paint were exposed to outdoor UV-radiation for a total period of three months and both FTIR and Raman measurements were taken systematically during this time. These results were later compared to an artificial degradation using a climate chamber. For infrared spectroscopy, degradation curves were plotted using the photo-oxidation index (POI), and could be successfully approximated with a logarithmic fitting (R2 > 0.8). The degradation can appear after the first few days of exposure and be important until 2 months, where it stabilizes and follow a more linear trend afterwards. One advantage is that the degradation products appeared almost exclusively at the far end (∼3000 cm−1) of mid-infrared spectra, and that the fingerprint region of the spectra remained stable over the studied period of time. Raman results suggest that the pigments on the other side, are much more stable and have not shown any sign of degradation over the time of this study. Considering the forensic implications of this environmental degradation, care should be taken when comparing samples if weathering is an option (e.g. an exposed graffiti compared to the paint from a fresh spray paint can). Degradation issues should be kept in mind as they may induce significant differences between paint samples of common origin.

The effect of the ocean water immersion and UV ageing on the dynamic mechanical properties of the PPS/glass fiber composites

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Evaluation of hardness and colour change of soft liners after accelerated ageing.

INTRODUCTION: Soft liners have been developed to offer comfort to denture wearers. However, this comfort is compromised when there is a change in the properties of the material, causing colour change, solubility, absorption and hardening. These characteristics can compromise the longevity of soft liners. AIM: The aim of this in vitro study was to investigate the effect of ageing on both the hardness and colour change of two soft liners following accelerated ageing. METHODS: Two denture liners, one resin based (Trusoft, Bosworth, Illinois, USA) and one silicone based (Ufi Gel P, Voco GMBH, Cuxhaven, Germany), were tested in this study for both hardness (using the Shore A scale) and colour change (using the CIE L*a*b* colour scale), initially and after 1008 hours (6 weeks) of accelerated ageing. Statistical analysis was performed using the unpaired t-test with the Welch correction. RESULTS: These indicated that both materials increased in hardness and underwent colour change after accelerated ageing. The initial hardness of Trusoft was far lower than that of Ufi Gel P (18.2 Shore A units vs 34.8 Shore A units). However, for Trusoft the changes for both hardness (from 18.2 to 52.1 Shore A units) and colour change (16.85 on the CIE L*a*b* colour scale) were greater than those for Ufi Gel P, for which hardness changed from 34.8 to 36.5 Shore A units and the colour change was 5.19 on the CIE L*a*b* colour scale. CONCLUSIONS: Ufi Gel P underwent less hardness and colour change after accelerated ageing than Trusoft. On the other hand, the use of Trusoft may be preferable in cases where initial softness is a major consideration, such as when relining an immediate denture after implant surgery.

Gilded bronze conservation: assessment of protective treatments by accelerated ageing and of treatment removal procedures by laser cleaning

In the current study, we analyze the effectiveness of an organosilane compound, 3-mercapto-propyl-tri-methoxy-silane (abbreviated PropS-SH), in the corrosion protection of fire-gilded bronzes. Firstly, the coating was applied on as-gilded bronze. Subsequently, it was also applied on pre-patinated bronze, because the substrate on which protective coatings are applied in real conservation interventions are corroded artifacts (cleaning procedures never remove all the corrosion products). Aiming to obtain results that simulate the situation of real artifacts, a dropping test that simulates outdoor exposure in runoff conditions (unsheltered areas of monuments) was employed in order to prepatinate the gilded bronze samples, which are the substrate for applying the protective coating. The preparation of the samples by applying the protective coating was performed in collaboration with the Corrosion Studies Centre “Aldo Daccò” from Ferrara University. After the artificial exposure cycles the samples underwent investigations through a variety of spectroscopic methods including SEM, Raman, FIB, AAS and color measurements. In order to evaluate the possible removal of the organosilane coating, protected samples were subjected to laser cleaning tests and characterized by SEM/EDS so as to assess the changes in composition and morphology of the treated surfaces. The laser cleaning treatment was performed at the Institute of Applied Physics “Nello Carrara” (CNR Sesto Fiorentino (FI)). The morphology and chemical composition of the samples was observed before and after the operation in order to obtain information about the fluence and type of laser which are best suited to the removal of this type of coating.

Do we need to rethink our waterways? Values of ageing waterways in current and future society

In the past canals were developed, and some rivers were heavily altered, driven by the need for good transportation infrastructure. Major investments were made in navigation locks, weirs and artificial embankments, and many of these assets are now reaching the end of their technical lifetime. Since then the concept of integrated water resource management (IWRM) emerged as a concept to manage and develop water-bodies in general. Two pressing problems arise from these developments: (1) major reinvestment is needed in order to maintain the transportation function of these waterways, and (2), it is not clear how the implementation of the concept of IWRM can be brought into harmony with such reinvestment. This paper aims to illustrate the problems in capital-intensive parts of waterway systems, and argues for exploring value-driven solutions that rely on the inclusion of multiple values, thus solving both funding problems and stakeholder conflicts. The focus on value in cooperative strategies is key to defining viable implementation strategies for waterway projects.

Historic and modern alloys: atmospheric corrosion and development of accelerated ageing methodologies

The atmospheric corrosion of modern and historic alloys used in cultural heritage has been investigated by applying specific accelerated ageing methods. Three main research lines were carried out, involving different materials. In the first part, the atmospheric corrosion of a modern Cu-3Si-1Mn bronze was investigated through accelerated ageing tests simulating outdoor runoff conditions. The corrosion processes were evaluated through different analyses, and the results obtained were compared to those of a traditional quaternary bronze. The second line was carried out to characterise historic aluminium alloys used in aeronautics to develop and apply innovative protection strategies for their conservation. Historic wrecks were identified and characterised through micro and macroscale observations. Moreover, accelerated ageing tests were performed on both historic and modern alloys to compare their behaviour and select the best modern substrate to be used for the development of effective coatings. The third research line aimed to develop accelerate sampling and ageing methods to investigate the role of particulate matter (PM) in the atmospheric corrosion of bronzes and metals in general. The first approach consisted in the fine-tuning of an efficient accelerated method for ambient PM sampling on bronze specimens followed by their accelerated ageing, in order to establish a correlation between the PM and the substrate’s corrosion. After the accelerated ageing of the specimens, the corrosion was evaluated by surface characterisation and correlated to the PM features. The second approach consisted in the development of a synthetic PM formulation and of an artificial deposition method, which was performed by spraying mixtures containing the main PM inorganic fractions on a G-85 bronze with an airbrush. The deposition efficiency was assessed, and the effect of synthetic PM on the bronze corrosion was evaluated. The results were compared to those obtained by ambient PM deposition.

Update On Ultraviolet A And B Radiation Generated By The Sun And Artificial Lamps And Their Effects On Skin.

Solar radiation, especially ultraviolet A (UVA) and ultraviolet B (UVB), can cause damage to the human body, and exposure to the radiation may vary according to the geographical location, time of year and other factors. The effects of UVA and UVB radiation on organisms range from erythema formation, through tanning and reduced synthesis of macromolecules such as collagen and elastin, to carcinogenic DNA mutations. Some studies suggest that, in addition to the radiation emitted by the sun, artificial sources of radiation, such as commercial lamps, can also generate small amounts of UVA and UVB radiation. Depending on the source intensity and on the distance from the source, this radiation can be harmful to photosensitive individuals. In healthy subjects, the evidence on the danger of this radiation is still far from conclusive.

Artificial Gait In Complete Spinal Cord Injured Subjects: How To Assess Clinical Performance.

Objective Adapt the 6 minutes walking test (6MWT) to artificial gait in complete spinal cord injured (SCI) patients aided by neuromuscular electrical stimulation. Method Nine male individuals with paraplegia (AIS A) participated in this study. Lesion levels varied between T4 and T12 and time post injured from 4 to 13 years. Patients performed 6MWT 1 and 6MWT 2. They used neuromuscular electrical stimulation, and were aided by a walker. The differences between two 6MWT were assessed by using a paired t test. Multiple r-squared was also calculated. Results The 6MWT 1 and 6MWT 2 were not statistically different for heart rate, distance, mean speed and blood pressure. Multiple r-squared (r2 = 0.96) explained 96% of the variation in the distance walked. Conclusion The use of 6MWT in artificial gait towards assessing exercise walking capacity is reproducible and easy to apply. It can be used to assess SCI artificial gait clinical performance.

The need for artificial tears in glaucoma patients: a comparative, retrospective study

PURPOSE: To evaluate the need for artificial tears by glaucoma patients under topical hypotensive treatment and to identify risk factors associated with it. METHODS: The charts of 175 glaucoma patients under medical treatment and 175 age-matched controls were reviewed. Age, gender, use of artificial tears, number of glaucoma medications used, and duration of treatment were recorded. RESULTS: Significantly more glaucoma patients (n=92; 52.6%) used artificial tears compared to age-matched controls (n=31; 17.7%) (p<0.001). Significantly more females (n=81; 39%) than males (n=42; 28.9%) used artificial tears (p=0.036). When the whole population was analyzed, female gender (OR=1.63) and the presence of glaucoma (OR= 5.14) were risk factors for the use of artificial tears (p<0.05). When the glaucoma population was analyzed, female gender (OR=2.57), number of medications >2 (OR=1.92), and duration of treatment >5 years (OR=2.93) were risk factors for the use of artificial tears (p<0.05). CONCLUSIONS: Topical treatment with antiglaucoma medication is a risk factor for the use of artificial tears. Female gender and long-term treatment of glaucoma with two or more medications were aggravating factors for the need for artificial tears.