X-Ray Spectroscopic Studies of the Surface Species in Co-Mo-Al2O3 Hydrodesulphurization Catalysts

Octahedrally coordinated CoII and MoIV species are present on the surfaces of sulfided Co-Mo-Al2O3 catalysts used for hydrodesulfurization. They were characterized by XPE, EXAFS and XANES data. An excess of sulfur in the surface species can be explained in terms of the presence of S[stack 22 ] ions. Disulfide bridges could play a role in the hydrodesulfurization.

Dry sliding wear behavior of Al2O3 fiber reinforced aluminum composites

Dry sliding wear behavior of die-cast ADC12 aluminum alloy composites reinforced with short alumina fibers were investigated by using a pin-on-disk wear tester. The Al2O3 fibers were 4 mu m in diameter and were present in volume fractions (T-f)ranging from 0.03 to 0.26, The length of the fiber varied from 40 to 200 mu m. Disks of aluminum-alumina composites were rubbed against a pin of nitrided stainless steel SUS440B with a load of 10 N at a sliding velocity of 0.1 m/s. The unreinforced ADC 12 aluminum alloy and their composites containing low volume fractions of alumina (V-f approximate to 0.05) showed a sliding-distance-dependent transition from severe to mild wear. However, composites containing high volume fractions of alumina ( V-f > 0.05) exhibited only mild wear for all sliding distances. The duration of occurrence of the severe wear regime and the wear rate both decrease with increasing volume fraction. In MMCs the wear rate in the mild wear regime decreases with increase in volume fraction: reaching a minimum value at V-f = 0.09 Beyond V-f = 0.09 the wear rate increasesmarginally. On the other hand, the wear rate of the counterface (steel pin) was found to increase moderately with increase in V-f. From the analysis of wear data and detailed examination of (a) worn surfaces, (b) their cross-sections and (c) wear debris, two modes of wear mechanisms have been identified to be operative, in these materials and these are: (i) adhesive wear in the case of unreinforced matrix material and in MMCs with low Vf and (ii) abrasive wear in the case of MMCs with high V-f. (C) 2000 Elsevier Science Ltd. All rights reserved.

Laser Surface Alloying of a Creep Resistant Magnesium Alloy MRI 230D with Al and Al2O3

A creep resistant permanent mould cast Mg alloy MRI 230D was laser surface alloyed with Al and a mixture of Al and Al2O3 using pulsed Nd:YAG laser irradiation at four different scan speeds in order to improve the corrosion and wear resistance. The microstructure, corrosion and wear behavior of the laser surface alloyed material is reported in this manuscript. The coating comprised of a featureless microstructure with cellular-dendritic microstructure near the interface and exhibited good interfacial bonding. A few solidification cracks reaching down to substrate were also observed. The two step coating with Al followed by a mixture of Al and Al2O3 exhibited a slightly better corrosion resistance than the single step coating with Al. In the long run, however, corrosion resistance of both the coatings became comparable to the as-cast alloy. The corroded surface of the laser surface alloyed specimens revealed a highly localized corrosion. The laser surface alloyed specimens exhibited an improvement in wear resistance. The laser scan speed did not exhibit a monotonic trend either in corrosion or wear resistance.

Dielectric Properties of Epoxy-Al2O3 Nanocomposite System for Packaging Applications

In recent times, there has been an ever-growing need for polymer-based multifunctional materials for electronic packaging applications. In this direction, epoxy-Al2O3 nanocomposites at low filler loadings can provide an excellent material option, especially from the point of view of their dielectric properties. This paper reports the dielectric characteristics for such a system, results of which are observed to be interesting, unique, and advantageous as compared to traditionally used microcomposite systems. Nanocomposites are found to display lower values of permittivity/tan delta over a wide frequency range as compared to that of unfilled epoxy. This surprising observation has been attributed to the interaction between the epoxy chains and the nanoparticles, and in this paper this phenomenon is analyzed using a dual layer interface model reported for polymer nanocomposites. As for the other dielectric properties associated with the nanocomposites, the nano-filler loading seems to have a significant effect. The dc resistivity and ac dielectric strength of the nanocomposites were observed to be lower than that of the unfilled epoxy system at the investigated filler loadings, whereas the electrical discharge resistant properties showed a significant enhancement. Further analysis of the results obtained in this paper shows that the morphology of the interface region and its characteristics decide the observed interesting dielectric behaviors.

An in situ EXAFS investigation of bimetallic Cu---Ni/γ-Al2O3 catalysts

In situ EXAFS investigations have been carried out on Ni/γ-Al2O3 and Cu---Ni/γ-Al2O3 catalysts with different metal loadings, and prepared by different procedures. As-prepared Ni/γ-Al2O3 on calcination gives NiO and NiAl2O4-like phases on the surface, the proportion of the latter increasing with the increase in calcination temperature; the proportion of the NiO-like phase, on the other hand, increases with the metal loading. The reducibility of Ni/γ-Al2O3 to give metallic Ni on the surface directly depends on the proportion of the NiO-like phase present before reduction. Co-impregnating with Cu suppresses the formation of the surface aluminate and thereby favours the reduction to metallic Ni. This conclusion is clearly substantiated by our studies of bimetallic catalysts containing varying Cu/Ni ratios and also those prepared by the two-stage impregnation procedure.

A thermogravimetric study of the oxidative growth of Al2O3/Al alloy composites

The oxidation of liquid Al–Mg–Si alloys at 900–1400 °C was studied by thermogravimetric analysis (TGA). The development of a semi-protective surface layer of MgO/MgAl2O4 allows the continuous formation of an Al2O3-matrix composite containing an interpenetrating network of metal microchannels at 1000–1350 °C. An initial incubation period precedes bulk oxidation, wherein Al2O3 grows from a near-surface alloy layer by reaction of oxygen supplied by the dissolution of the surface oxides and Al supplied from a bulk alloy reservoir through the microchannel network. The typical oxidation rate during bulk growth displays an initial acceleration followed by a parabolic deceleration in a regime apparently limited by Al transport to the near-surface layer. Both regimes may be influenced by the Si content in this layer, which rises due to preferential Al and Mg oxidation. The growth rates increase with temperature to a maximum at ~1300 °C, with a nominal activation energy of 270 kJ/mole for an Al-2.85 wt. % Mg-5.4 wt. % Si alloy in O2 at furnace temperatures of 1000–1300 °C. An oscillatory rate regime observed at 1000–1075 °C resulted in a banded structure of varying Al2O3-to-metal volume fraction.

Nucleation and growth of Al2O3/metal composites by oxidation of aluminum alloys

The nucleation and growth mechanisms during high temperature oxidation of liquid Al-3% Mg and Al-3% Mg-3% Si alloys were studied with the aim of enhancing our understanding of a new composite fabrication process. The typical oxidation sequence consists of an initial event of rapid but brief oxidation, followed by an incubation period of limited oxide growth after which bulk Al2O3/Al composite forms. A duplex oxide layer, MgO (upper) and MgAl2O4 (lower), forms on the alloy surface during initial oxidation and incubation. The spinel layer remains next to the liquid alloy during bulk oxide growth and is the eventual repository for most of the magnesium in the original alloy. Metal microchannels developed during incubation continuously supply alloy through the composite to the reaction interface. During the growth process, a layered structure exists at the upper extremity of the composite, consisting of MgO at the top surface, MgAl2O4 (probably discontinuous), Al alloy, and finally the bulk Al2O3 composite containing microchannels of the alloy. The bulk oxide growth mechanism appears to involve continuous formation and dissolution of the Mg-rich oxides at the surface, diffusion of oxygen through the underlying liquid metal, and epitaxial growth of Al2O3 on the existing composite body. The roles of Mg and Si in the composite growth process are discussed.

Potentiometric determination of activities in the two-phase fields of the system Na2O---(α)Al2O3

Three compounds have been found to be stable in the pseudobinary system Na2O---(α)Al2O3 between 825 and 1400 K; two nonstoichiometric phases, β-alumina and β″-alumina, and NaAlO2. The homogeneity of β-alumina ranges from 9.5 to 11 mol% Na2O, while that of β″-alumina from 13.3 to 15.9 mol% Na2O at 1173 K. The activity of Na2O in the two-phase fields has been determined by a solid-state potentiometric technique. Since both β- and β″-alumina are fast sodium ion conductors, biphasic solid electrolyte tubes were used in these electrochemical measurements. The open circuit emf of the following cells were measured from 790 to 980 K: [GRAPHICS] The partial molar Gibbs' energy of Na2O relative to gamma-Na2O in the two-phase regions can be represented as: DELTA-GBAR(Na2O)(alpha- + beta-alumina) = -270,900 + 24.03 T, DELTA-GBAR(Na2O)(beta- + beta"-alumina) = -232,700 + 56.19 T, and DELTA-GBAR(Na2O)(beta"-alumina + NaAlO2) = -13,100 - 4.51 T J mol-1. Similar galvanic cells using a Au-Na alloy and a mixture of Co + CoAl(2+2x)O4+3x + (alpha)Al2O3 as electrodes were used at 1400 K. Thermodynamic data obtained in these studies are used to evaluate phase relations and partial pressure of sodium in the Na2O-(alpha) Al2O3 system as a function of oxygen partial pressure, composition and temperature.

Deformation and structural densification in Al2O3-Y2O3 glass

In this article, we examine the unusual plastic deformation under uniaxial compression of an Al2O3-15 mol % Y2O3 (A15Y) glass synthesized by a wet chemical route At a low temperature of 650-725 degrees C, plastic deformation of this glass is largely non-viscous through shear instabilities In contrast deformation near the crystallization temperature (850 degrees C) occurs homogeneously with work hardening and with a monotonic increase in the true density of the glass by 10-12% accompanied by an increase in hardness (H) and elastic modulus (E) of up to 100% We hypothesize a phenomenon of molecular densification of the amorphous structure through a hierarchy of multiple phases, analogous to density- or entropy-driven amorphous to-amorphous phase transitions (polyamorphism) These results suggest that the present method of preparation and the unusual behavior can trigger a search for many more systems that display such behavior (C) 2010 Acta Materialia Inc Published by Elsevier Ltd All rights reserved

Microwave Irradiation Assisted Method for the Rapid Synthesis of fine Particles of alpha Al2O3 And alpha (Al1-XCrx)(2)O-3 And Their Coatings on Si(100)

Chromium substituted beta diketonate complexes of aluminium have been synthesized and employed as precursors for a novel soft chemistry process wherein microwave irradiation of a solution of the complex yields within minutes well crystallized needles of alpha (Al1 XCrx)(2)O-3 measuring 20 30 nm in diameter and 50 nm long By varying the microwave irradiation parameters and using a surfactant such as polyvinyl pyrrolidone the crystallite size and shape can be controlled and their agglomeration prevented These microstructural parameters as well as the polymorph of the Cr substituted Al2O3 formed may also be controlled by employing a different complex Samples of alpha (Al1 XCrx)(2)O-3 have been characterized by XRD FTIR and TEM The technique results in material of homogeneous metal composition, as shown by EDAX and can be adjusted as desired The technique has been extended to obtain coatings of alpha (Al1 XCrx)(2)O-3 on Si(100)

Reduction behaviour of Fe3+/Al2O3 obtained from the mixed oxalate precursor and the formation of the Fe0-Al2O3 metal-ceramic composite

Reduction behaviour of Fe3+/Al2O3 obtained by the decomposition of the oxalate precursor has been investigated by employing X-ray diffraction (XRD), Mössbauer spectroscopy and electron paramagnetic resonance (EPR) spectroscopy. Calcination of Fe3+/Al2O3 at or below 1070 K yields mainly a poorly ordered, fine particulate form of ?-Al2�xFexO3. Calcination at or above 1220 K yields ?-Al2�xFexO3. Reduction of Fe3+/Al2O3 samples calcined at or below 1070 K gives the FeAl2O4 spinel on reduction at 870 K; samples calcined at or above 1220 K give Al2-xFexO3 with a very small proportion of metallic iron. Fe3+/Al2O3 samples calcined at 1220 K or above yield metallic iron and a very small proportion of the spinel on reduction below 1270 K. In the samples reduced at or above 1270 K, the main product is metallic iron in both ferromagnetic and superparamagnetic forms. The oxalate precursor route yields more metallic iron than the sol�gel route.

A simplified kinetic model for oxidative dehydrogenation of ethylbenzene over Pd-NaBr/Al2O3 catalyst

The oxidative dehydrogenation of ethylbenzene is gaining considerable importance in recent years as a promising alternative for styrene production. This vapour phase reaction has been studied over Pd-NaBr/Al2O3 catalyst in the temperature range 623-793 K in a fixed bed reactor. Kinetic analysis of this reaction has been done using a recursion procedure developed in this work from first principles. The advantage of this method is the absence of any restriction on the conversion level as it uses an integrated rate equation. The rate of styrene formation was found to follow a linear relationship with concentration of ethylbenzene and shows a Langmuir type dependence on the concentration of oxygen.

Characteristics of superplasticity domain in the processing map for hot working of an Al alloy 2014---20vol.%Al2O3 metal matrix composite

The processing map for hot working of Al alloy 2014-20vol.%Al2O3 particulate-reinforced cast-plus-extruded composite material has been generated covering the temperature range 300-500 degrees C and the strain rate range 0.001-10 s(-1) based on the dynamic materials model. The efficiency eta of power dissipation given by 2m/(m + 1), where m is the strain rate sensitivity, is plotted as a function of temperature and strain rate to obtain a processing map. A domain of superplasticity has been identified, with a peak efficiency of 62% occurring at 500 degrees C and 0.001 s(-1). The characteristics of this domain have been studied with the help of microstructural evaluation and hot-ductility measurements. Microstructural instability is predicted at higher strain rates above (ls(-1)) and lower temperatures (less than 350 degrees C).

Fe-Cr/Al2O3 metal-ceramic composites: Nature and size of the metal particles formed during hydrogen reduction

Fe-Cr/Al2O3 metal-ceramic composites prepared by hydrogen reduction at different temperatures and for different periods have been investigated by a combined use of Mossbauer spectroscopy, x-ray diffraction, transmission electron microscopy, and energy-dispersive x-ray spectroscopy in order to obtain information on the nature of the metallic species formed. Total reduction of Fe3+ does not occur by increasing the reduction time at 1320 K from 1 to 30 h, and the amount of superparamagnetic metallic species is essentially constant (about 10%). Temperatures higher than 1470 K are needed to achieve nearly total reduction of substitutional Fe3+. Interestingly, iron favors the reduction of chromium. The composition of the Fe-Cr particles is strongly dependent on their size, the Cr content being higher in particles smaller than 10 nm.