Structural characterisation of reaction zone for friction stir welded aluminium-stainless steel joint

In the present investigation, commercially pure Al has been joined with 304 stainless steel (SS) by friction stir welding. The assembly finds widespread application in the field of cryogenics, nuclear, structural industries and domestic appliances. Microstructural characterisation was carried out using scanning and transmission electron microscopes. It has been found that diffusion of Fe, Cr and Ni is substantial within Al; however, diffusion of Al within 304SS is limited. Owing to interdiffusion of chemical species across the bondline, discrete islands of Fe3Al intermetallic form within the reaction zone. The rubbing action of tool over the butting edge of 304SS removed fine particles from 304SS, which were embedded in the stirring zone of Al matrix. Subsequently, austenite underwent phase transformation to ferrite due to large strain within this grain. Fracture path mainly moves through stirring zone of Al alloy under tensile loading; however, in some places, presence of Fe3Al compound has been also found.

Sensitisation identification of stainless steel to intergranular stress corrosion cracking by atomic force microscopy

A new technique was developed for characterisation of stainless steel to intergramilar stress corrosion cracking by atomic force microscopy. The technique proved to be effective in sensitisation identification of AISI 304 stainless steel and might be promising in sensitisation identification of other stainless steels. (c) 2007 Elsevier B.V. All rights reserved.

Effect of twinning on microstructural evolution during dynamic recrystallisation of hot deformed as-cast austenitic stainless steel

An as-cast austenitic stainless steel was hot deformed at 1173 K, 1223 K, and 1373 K (900 °C, 950 °C, and 1100 °C) to a strain of 1 with a strain rate of 0.5 or 5 s⁻¹. The recrystallised fraction is observed to be dependent on dynamic recrystallisation (DRX). DRX grains nucleated at the initial stages of recrystallization have similar orientation to that of the deformed grains. With increasing deformation, Cube texture dominates, mainly due to multiple twinning and grain rotation during deformation.

Influence of cast versus wrought microstructure on the processing map for hot working of stainless steel type AISI 304

Processing maps for hot working of as-cast and wrought stainless steels of type AISI 304 have been developed in the temperature range 600 to 1250°C and strain rate range 0.001 to 100 s−1. The domain of dynamic recrystallization (DRX) in as-cast material occurs at higher temperatures (1250°C) and lower strain rates (0.001 s−1) than in the wrought steel (1100°C and 0.01 s−1). The effect is explained in terms of enhanced nucleation rate of DRX due to the carbide, ferrite particles, stable oxides/nitrides and second-phase intermetallics in the as-cast microstructure. The DRX domain is wider in the wrought material although the peak efficiency is less (32%) than in the as-cast case (40%). The flow instability regime is not significantly affected by the initial microstructure

Influence of strain rate and state-of-stress on the formation of ferrite in stainless steel type AISI 304 during hot working

The influence of strain rate and state-of-stress on the formation of ferrite in stainless steel type AISI 304L, 304 and 304 as-cast, during hot working has been studied. Compression and torsion tests were conducted in the temperature range 1100 to 1250 degrees C and strain rate range 0.001 to 100 s(-1) on these materials, Ferrite formation occurs during deformation at temperatures above 1150 degrees C and strain rates above 10 s(-1), in stainless steel type AISI 304L and 304. The tendency for the formation of ferrite is more in as-cast 304 than in wrought 304, In as-cast 304 the ferrite forms at lower temperatures and strain rates, The tendency for the ferrite formation is more in torsion than in compression.

Grain-Size Effects on the High-Temperature Oxidation of Modified 304 Austenitic Stainless Steel

The high-temperature oxidation behavior of modified 304 austenitic stainless steels in a water vapor atmosphere was investigated. Samples were prepared by various thermo mechanical treatments to result in different grain sizes in the range 8-30 mu m. Similar I 3 pound grain boundary fraction was achieved to eliminate any grain-boundary characteristics effect. Samples were oxidized in an air furnace at 700 A degrees C with 20 % water vapor atmosphere. On the fine-grained sample, a uniform Cr2O3 layer was formed, which increased the overall oxidation resistance. Whereas on the coarse-grained sample, an additional Fe2O3 layer formed on the Cr-rich oxide layer, which resulted in a relatively high oxidation rate. In the fine-grained sample, grain boundaries act as rapid diffusion paths for Cr and provided enough Cr to form Cr2O3 oxide on the entire sample surface.

Recrystallization in 304 austenitic stainless steel

A 304 austenitic stainless steel was deformed using hot torsion to study the evolution of dynamic recrystallization (DRX). The initial nucleation of dynamically recrystallization occurred by the bulging of pre-existing high angle grain boundaries at a strain much lower than the peak strain. At the
peak stress, only a low fraction of the prior grain boundaries were covered with new DRX grains. Beyond the peak stress, new DRX grains formed layers near the initial DRX and a necklace structure was developed. Several different mechanisms appeared to be operative in the formation of new high angle boundaries and grains. The recrystallization behaviour after deformation showed a classic transition from strain dependent to strain independent softening. This occurred at a strain beyond the
peak, where the fraction of dynamic recrystallization was only 50%.

Recrystallization in AISI 304 austenitic stainless steel during and after hot deformation

In order to improve the understanding of the dynamic and post-dynamic recrystallization behaviours of AISI 304 austenitic stainless steel, a series of hot torsion test have been performed under a range of deformation conditions. The mechanical and microstructural features of dynamic recrystallization (DRX) were characterized to compare and contrast them with those of the post-dynamic recrystallization. A necklace type of dynamically recrystallized microstructure was observed during hot deformation at 900 °C and at a strain rate of 0.01 s⁻¹. Following deformation, the dependency of time for 50% recrystallization, t₅₀, changed from “strain dependent” to “strain independent” at a transition strain (ε^*), which is significantly beyond the peak. This transition strain was clearly linked to the strain for 50% dynamic recrystallization during deformation. The interrelations between the fraction of dynamically recrystallized microstructure, the evolution of post-dynamically recrystallized microstructure and the final grain size have been established. The results also showed an important role of grain growth on softening of deformed austenite.

Microstructure evolution modeling during and after deformation in 304 austenitic stainless steel through cellular automaton approach

A 2D cellular automation approach was used to simulate microstructure evolution during and after hot deformation. Initial properties of the microstructure and dislocation density were used as input data to the cellular automation model. The flow curve and final grain size were the output data for the dynamic recrystallization simulation, and softening kinetics curves were the output data of static and metadynamic recrystallization simulations. The model proposed in this work considered the effect of thermomechanical parameters (e.g., temperature and strain rate) on the nucleation and growth kinetics during dynamic recrystallization. The dynamic recrystallized microstructures at different strains, temperatures, and strain rates were used as input data for static and metadynamic recrystallization simulations. It was shown that the cellular automation approach can model the final microstructure and flow curve successfully in dynamic recrystallization conditions. The postdeformation simulation results showed that the time for 50% recrystallization decreases with increasing strain for a given initial grain size and that dynamic recrystallization slows the postdeformation recrystallization kinetics compared to a model without dynamic recrystallization.

Electrochemical behavior of the cistein and diphosfonate for stainless steel in media of HCl 1 mol L(-1)

Amino acids and self assembled monolayers (SAM`s) have been studied as to their inhibiting action on the corrosion of metallic materials. The objective of work is to study the electrochemical behavior of the cisteincisteine, the diphosfonate and the mixture of both in inhibiting the action of corrosion on stainless steel 304 in HCl 1 molL(-1). As the following techniques were used: open circuit potential (OCP), potenciostatic anodic polarization (A P), chronoamperomeny (CA), electrochemical impedance spectroscopy (EIS) and optical microscopy (OM). The results of CA showed that cisteine has a double effect, catalytic and inhibiting, in function of the immersion time of the metallic part in the electrolytic solution. AP curves have shown lesser current density for the system containing cisteine diphosfonate suggesting an inhibiting synergic action. These results have been confirmed by EIS and OM.

Hot deformation and recrystallization of austenitic stainless steel: part 1. dynamic recrystallization

The hot deformation behavior of a 304 austenitic stainless steel was investigated to characterize the evolution of the dynamically recrystallized structure as a starting point for studies of the postdeformation  recrystallization behavior. The effect of different deformation parameters such as strain, strain rate, and temperature were investigated. The flow curves showed typical signs of dynamic recrystallization (DRX) over a wide range of temperatures and strain rates (i.e., different Zener–Hollomon (Z) values). However, under very high or very low Z values, the flow curves’ shapes changed toward those of the dynamic recovery and multiple peaks, respectively. The results showed that while DRX starts at a strain as low as 60 pct of the peak strain, a fully DRX microstructure needs a high strain of almost 4.5 times the initiation strain. The DRX average grain size showed power-law functions with both the Zener–Hollomon parameter and the peak stress, although power-law breakdown was observed at high Z values.