Single-step chemical synthesis of ferrite hollow nanospheres

We report a single-step chemical synthesis of iron oxide hollow nanospheres with 9.3 nm in diameter. The sample presents a narrow particle diameter distribution and chemical homogeneity. The hollow nature of the particles is confirmed by HRTEM and HAADF STEM analysis. Electron and x-ray diffraction show that the outer material component is constituted by 2 nm ferrite crystals. Mossbauer data provide further evidence for the formation of iron oxide with high structural disorder, magnetically ordered at 4.2 K and superparamagnetism at room temperature. An unusual magnetic behavior under an applied field is reported, which can be explained by the large fraction of atoms existing at both inner and outer surfaces.

Structural Investigation of MFe(2)O(4) (M = Fe, Co) Magnetic Fluids

Ferrites of the type M(II)Fe(2)O(4) (M = Fe and Co) have been prepared by the traditional coprecipitation method. These ferrites were modified by the adsorption of fatty acids derived from soybean and castor oil and were then dispersed in cyclohexane, providing very stable magnetic fluids, readily usable in nonpolar media. The structural properties of the ferrites and modified ferrites as well as the magnetic fluids were characterized by XRD (X-ray powder diffraction), TEM (transmission electron microscopy), DRIFTS (diffusion reflectance infrared Fourier transform spectroscopy), FTMR (Fourier transform near-infrared), UV-vis, normal Raman spectroscopy, and surface-enhanced Raman scattering (SERS). XRD and TEM analysis have shown that the magnetic nanoparticles (nonmodified and modified) present diameters in the range of 10-15 nm. DRIFTS measurements have shown that the carboxylate groups of soybean and castor oil fatty acids adsorb on the ferrite surface, forming three different structures: a bridging bidentate, a bridging monodentate, and a bidentate chelate structure. The FTIR and Raman spectra of nonmodified Fe(3)O(4) and CoFe(2)O(4) nanoparticles have shown that the number of observed phonons is not compatible with the expected O(h)(7) symmetry, since IR-only active phonons were observed. in the Raman spectra and vice versa. SERS measurements of a CoFe(2)O(4) thin film on a SERS-active gold electrode at different applied potentials made possible the assignment of the signals near 550 and 630 cm(-1) to Co-O motions and the signals near 470 and 680 cm(-1) to Fe-O motions.

Catalytic properties of thioredoxin immobilized on superparamagnetic nanoparticles

Thioredoxin (Trx1), a very important protein for regulating intracellular redox reactions, was immobilized on iron oxide superparamagnetic nanoparticles previously coated with 3-aminopropyltriethoxysilane (APTS) via covalent coupling using the EDC (1-ethyl-3-{3-dimethylaminopropyl}carbodiimide) method. The system was extensively characterized by atomic force microscopy, vibrational and magnetic techniques. In addition, gold nanoparticles were also employed to probe the exposed groups in the immobilized enzyme based on the SERS (surface enhanced Raman scattering) effect, confirming the accessibility of the cysteines residues at the catalytic site. For the single coated superparamagnetic nanoparticle, by monitoring the enzyme activity with the Ellman reagent, DTNB=5,5`-dithio-bis(2-15 nitrobenzoic acid), an inhibitory effect was observed after the first catalytic cycle. The inhibiting effect disappeared after the application of an additional silicate coating before the AFTS treatment, reflecting a possible influence of unprotected iron-oxide sites in the redox kinetics. In contrast, the doubly coated system exhibited a normal in-vitro kinetic activity, allowing a good enzyme recovery and recyclability. (C) 2011 Elsevier Inc. All rights reserved.

Magnetic coupled electrochemistry: Exploring the use of superparamagnetic nanoparticles for capturing, transporting and concentrating trace amounts of analytes

We propose the use of functionalized superparamagnetic nanoparticles for capturing, and transporting analytes, in association with an external miniature magnet to deposit such nanocarrier species at the electrode surface. This approach can be employed for the electroanalytical determination of chemical species capable of interacting with the nanoparticles, or in the opposite case, to block their response at the electrode surface. The concept was successfully demonstrated by using aminofunctionalized nanoparticles to block the discharge of hexacyanoferrate(II) ions, and to enhance the signals of aquapentacyanoferrate(II) ions via coordination to the surface amino groups. Selective analysis was also performed for silver ions, surpassing the stripping methods in terms of versatility and usefulness. (C) 2010 Elsevier B.V. All rights reserved.

An investigation of the activation process of high temperature shift catalyst

The aim of this work is to address the activation process of a high temperature shift (HTS) catalyst, composed of Fe2O3/Cr2O3/CuO, by analyzing it before activation (HTS-V) and after activation (HTS-A) using complementary characterization techniques. The textural and morphological characterizations were done by transmission electron rnicroscopy (TEM) and nitrogen physisorption at 77 K; crystallographic structure was confirmed by X-ray diffraction (XRD); electronic structure was analyzed by X-ray absorption spectroscopy (XAS) and the chemical composition of the catalyst`s surface was obtained by X-ray photoelectron spectroscopy (XPS). The investigation pointed out that the HTS-V catalyst presents good textural and morphological properties, which are not deeply affected by the activation process (sample HTS-A). The iron oxide phase in the HTS-V catalyst is hematite whereas in HTS-A catalyst is magnetite with Fe2+/Fe3+ ratio close to the expected value (0.5). For both samples, the Cr ions seem to be incorporated in the iron oxide lattice with higher concentration at particle surface. In the HTS-V catalyst, the Cu ions have oxidation number II and occupy in average distorted octahedral sites; after the activation, the Cu ions are partially reduced, suggesting that the reduction of the Cu species is complex. (C) 2007 Elsevier B.V. All rights reserved.

Perpendicularly self-oriented and shape-controlled L1(0)-FePt nanorods directly synthesized by a temperature-modulated process

The synthesis and self-assembly of tetragonal phase-containing L1(0)-Fe(55)Pt(45) nanorods with high coercive field is described. The experimental procedure resulted in a tetragonal/cubic phase ratio close to 1:1 for the as-synthesized nanoparticles. Using different surfactant/solvent proportions in the process allowed control of particle morphology from nanospheres to nanowires. Monodisperse nanorods with lengths of 60 +/- 5 nm and diameters of 2-3 nm were self-assembled in a perpendicular oriented array onto a substrate surface using hexadecylamine as organic spacer. Magnetic alignment and properties assigned, respectively, to the shape anisotropy and the tetragonal phase suggest that the self-assembled materials are a strong candidate to solve the problem of random magnetic alignment observed in FePt nanospheres leading to applications in ultrahigh magnetic recording (UHMR) systems capable of achieving a performance of the order of terabits/in(2).

Contribuição ao beneficiamento de finos de fosfatos

Foram estudadas as características de floculação da hidro-xiapatita, calcita e quartzo com poliacrilamidas aniônicas. Tanto as suspensões de hidroxiapatita como a calcita foram completamente floculadas enquanto que o quartzo foi refratário a floculação com esses polimeros. Entretanto, observou-se que a floculação da calcita foi impedida com a utilização de um poliacrilato de sódio, enquanto que a hidroxiapatita continuou a ser floculada pela poliacrilamida num intervalo de concentração de O a 1000 g/ton de poliacrilato. Estes resultados permitiram estabelecer condições para a floculação seletiva de hidroxiapatita em misturas sintéticas com quartzo e calcita. Nestes sistemas foram estudados diversos parâmetros operacionais, tais como tipo de separação, efeito do teor da alimentação, e influência da moagem. Onde a separação estagiada apresentou melhor resultado, uma moagem adicional no sistema não favoreceu a seletividade. Por outro lado, o teor de P205 no concentrado é proporcional ao teor presente na alimentação. A hidroxiapatita, em estudo, de alta pureza (de acordo com técnicas de análise química, espectrofotometria de infravermelho e difração de raios X) apresentou um parto de carga zero em pH 6,77 na presença de diversos eletrólitos. A aplicação do sistema de floculação seletiva a fraçoes ultrafinas industriais foi estudada em detalhe e comparada com processos de flotação e floco-flatação. 0s resultados obtidos mostraram que a floculação seletiva somente foi eficiente nos sistemas sintéticos. A flotação, embora o minério apresente uma granulometria muito fina, foi mais eficiente que a floculação seletiva e a floco-flotação nos sistemas reais, em termos de taxa de enriquecimento e percentual de rejeição de massa. Entretanto com a floco-flotação foi possivel obter altas recuperações(-90%) para os minérios de Araxá e Itataia. Para o minério de Tapira, um aumento do teor de P2O5 foi obtido com a flotação da fração seletivamente floculada. As taxas de enriquecimento obtidas foram baixas (entre 1,35 e 2,101 em função das associações entre a apatita do minério com óxido de ferro e argila, o que revelou a caracterização mineralógica. Conclue-se que a concentração de minerios fosfatados de baixo teor é uma operação onerosa, onde o fator predominante é a absorção seletiva de reagentes e atransferência não específica de material de ganga nos respectivos concentrados.

Caracterização do concentrado de ilmenita produzido na Mina do Guaju, Paraíba, visando identificar inclusões de monazita e outros contaminantes

O presente estudo tem como proposta, identificar o modo como o mineral monazita se encontra no concentrado final de ilmenita. Este concentrado é o produto resultante do beneficiamento do minério extraído de depósitos do tipo pláceres, conhecidos como depósitos de areias pretas. Estes depósitos são formados por dunas litorâneas pertencentes à jazida do Guaju, no município de Mataraca-PB. Todo o processo de lavra e beneficiamento deste minério ocorre na Mina do Guaju, a qual é operada pela empresa Millennium Inorganic Chemicals do Brasil S/A, pertencente a Lyondell Chemical Company. A ilmenita é um mineral composto por óxido de ferro e titânio, FeTiO3. Quase toda a ilmenita produzida na mina é transferida para o processo de fabricação de pigmento. A exigência para o uso na fabricação de pigmento é de que o concentrado final de ilmenita tenha um teor mínimo de 53% de TiO2 e um teor máximo de 0,1% de P2O5, entre outras substâncias. A monazita é o principal mineral fonte de óxido de tório, que é radioativo. No processo de fabricação de pigmento, a monazita é um contaminante indesejado. De acordo com a proposta de trabalho, foi feito um estudo de caracterização mineralógica de amostras do concentrado final de ilmenita fornecidas pela empresa. Inicialmente foram feitas análises em lupa, onde muitos grãos de leucoxeno foram identificados. O leucoxeno é uma alteração da ilmenita que permanece com as mesmas características magnéticas e eletrostáticas, tornando impossível, assim, a sua separação no processo de concentração. Também foi verificada a existência de grãos de monazita liberados em pequenas quantidades neste concentrado, indicando uma provável ineficiência no processo de separação. Numa segunda etapa foram realizadas análises dos grãos de ilmenita com o uso de um Microscópio Eletrônico de Varredura (MEV) acoplado a um Espectrômetro de Dispersão de Energia (EDS), para permitir a determinação de elementos químicos na amostra. Esta análise teve como objetivo verificar a existência de inclusões de monazita nos grãos de ilmenita. Porém, o que se observou foi a existência de algumas inclusões de quartzo e de alguns vazios deixados, provavelmente, por inclusões arrancadas durante o processo de preparação das amostras. Alguns destes vazios apresentaram formas semelhantes a de cristais de monazita, indicando a possibilidade da existência de inclusões deste mineral. Entretanto, a quantidade de grãos com possíveis inclusões de monazita é muito pequena, sendo insignificante como contaminante do concentrado final. Embora alguns vazios se assemelhem à forma da monazita, nenhum dos resultados do EDS identificou vestígios de sua presença. Ao final deste estudo ficou evidente que a principal fonte de contaminação do concentrado final de ilmenita corresponde à monazita, a qual se encontra liberada neste concentrado. Desta forma, há a necessidade de se melhorar o processo de separação dos minerais, de modo que a quantidade de monazita no concentrado final seja a menor possível, não prejudicando o rendimento da recuperação de ilmenita.

Synthesis and characterization of lanthanum- and yttrium-doped Fe2O3 pigments

MELO, D. M. A. et al. Synthesis and charactezarion of lanthanum and yttrium doped Fe2O3 pigments. Cerâmica, São Paulo, v. 53, p. 79-82, 2007.

Síntese de nanopartículas de magnetita via decomposição térmica em meio não-aquoso

This work aims at obtaining nanoparticles of iron oxide, the magnetite one (Fe3O4), via synthesis by thermal decomposition through polyol. Thus, two routes were evaluated: a simple decomposition route assisted by reflux and a hydrothermal route both without synthetic air atmosphere using a synthesis temperature of 260ºC. In this work observed the influence of the observe of surfactants which are generally applied in the synthesis of iron oxide nanoparticles decreasing cluster areas. Further, was observed pure magnetite phase without secondary phases generally found in the iron oxide synthesis, a better control of crystallite size, morphology, crystal structure and magnetic behavior. Finally, the introduction of hydroxyl groups on the nanoparticles surface was analyzed besides its employment in the polymer production with OH radicals. The obtained materials were characterized by XRD, DLS, VSM, TEM, TG and DSC analyses. The results for the magnetite obtainment with a particle size greater than 5 nm and smaller than 11 nm, well defined morphology and good magnetic properties with superparamagnetic behavior. The reflux synthesis was more efficient in the deposition of the hydroxyl groups on the nanoparticles surface

Avaliação da corrosão em dutos por técnica gravimétrica e de resistência elétrica

With the increasing of demand for natural gas and the consequent growth of the pipeline networks, besides the importance of transport and transfer of oil products by pipeline, and when it comes to product quality and integrity of the pipeline there is an important role regarding to the monitoring internal corrosion of the pipe. This study aims to assess corrosion in three pipeline that operate with different products, using gravimetric techniques and electrical resistance. Chemical analysis of residues originated in the pipeline helps to identify the mechanism corrosive process. The internal monitoring of the corrosion in the pipelines was carried out between 2009 and 2010 using coupon weight loss and electrical resistance probe. Physico-chemical techniques of diffraction and fluorescence X-rays were used to characterize the products of corrosion of the pipelines. The corrosion rate by weight loss was analyzed for every pipeline, only those ones that has revealed corrosive attack were analyzed located corrosion rate. The corrosion potential was classified as low to pipeline gas and ranged from low to severe for oil pipelines and the pipeline derivatives. Corrosion products were identified as iron carbonate, iron oxide and iron sulfide

Evolução diagenética e caracterização dos reservatórios da seção devoniana na Bacia do Rio do Peixe-Nordeste do Brasil

The Rio do Peixe Basin represents a main basin of northeastern Brazil and pioneering work positioned the rocks of this basin in the Early Cretaceous. However, a recent study, based on integrated pollen analysis from three wells, found an unprecedented siliciclastic sedimentary section, in the region, of early Devonian age. Therefore, the present study aims a detailed petrographic and petrological analysis of this devonian section, in the Rio do Peixe Basin and proposes a diagenetic evolution, to understand the characteristics of the porous system, identify the main reservoir petrofacies with the main factors impacting on the quality of these rocks as reservoirs and a quick study on the provenance of this section. The petrographic study was based on samples obtained from subsurface and surface. The diagenetic evolution of petrofacies and its identification were based only on subsurface samples and the study of provenance was based on surface samples. The thin sections were prepared from sandstones, pelites and sandstones intercalated with pelites. The original detrital composition for this section is arcosean and the main diagenetic processes that affected these rocks occur in various depths and different conditions, which resulted in extensive diagenetic variety. The following processes were identified: early fracture and healing of grains; albitization of K-feldspar and plagioclase; siderite; precipitation of silica and feldspar; mechanical infiltration of clay and its transformation to illite/esmectite and illite; autigenesis of analcime; dissolution; autigenesis of chlorite; dolomite/ferrous dolomite/anquerite; apatite; calcite; pyrite; titanium minerals and iron oxide-hidroxide. The occurrence of a recently discovered volcanism, in the Rio do Peixe Basin, may have influenced the diagenetic evolution of this section. Three diagenetic stages affected the Devonian section: eo, meso and telodiagenesis. This section is compositionally quite feldspathic, indicating provenance from continental blocks, between transitional continental and uplift of the basement. From this study, we observed a wide heterogeneity in the role of the studied sandstones as reservoirs. Seven petrofacies were identified, taking into account the main diagenetic constituent responsible for the reduction of porosity. It is possible that the loss of original porosity was influenced by intense diagenesis in these rocks, where the main constituent for the loss of porosity are clays minerals, oxides and carbonate cement (calcite and dolomite)

Estudo do perfil térmico de fornos do tipo "caipira" utilizados pelo setor de cerâmica vermelha em parelhas na região Seridó-RN

The present study aimed to characterize the thermal profile of wood fired oven used by the red ceramic industry in Parelhas, in the Seridó region/RN, aiming to propose structural interventions that can contribute to increasing productivity and product quality, optimize wood consumption and mitigate existing losses during the burning process. The study was conducted at Cerâmica Esperança in the city of Parelhas -RN, Brazil, during the period from August 2012 to September 2013. Four treatments were performed with three replicates, ie, with, a total of 12 experimental units (burnings). In the first stage 4 treatments were performed with three replicates, totaling 12 experimental units (firings). In the second stage 2 treatments were performed with three replications, totaling 6 experimental units (firings). The physical characteristics of the wood were analyzed using standard NBR 11941 and NBR 7190 for basic density and moisture, respectively. The clay was used as a reference parameter for distinguishing treatments. For both the analysis and characterization was carried out using techniques of fluorescence X (XRF) rays, X-ray diffraction (XRD) analysis, particle size analysis (FA). In the first and second stages were monitored: the time during the firing process, the amount of wood used at each firing, the number of parts enfornadas for subsequent determination of the percentages of losses, but also product quality. To characterize the thermal profile of the oven, we measured the temperature at 15 points scored in the surface charge put into the oven. Measurements were taken every 30 minutes from preheat until the end of burning, using a pyrometer laser sight sighting from preheating until the end of burning. In the second step 12 metal cylinders distributed on the oven walls, and the cylinder end walls 8 of the furnace 2 and rollers on each side walls are installed equidistant to 17 cm from the soil and the surface 30 of the wall are installed. The cylinders distributed on the front were placed 50 cm above the furnace, and the base of the oven 20 cm distant from the ground. 10 also thermocouples were installed, and five thermocouples distributed 1.77 cm above the combustion chambers, and one thermocouple on each side, and three thermocouples in front of the oven. We carried out the measurements of the temperatures every 1 hour during the burning two hours in cooling the cylinders with a pyrometer and thermocouples for dattaloger. These were fixed with depth of 30 cm from the wall. After statistical analysis it was found that: the thermal profile of the furnace surface and at different heights was heterogeneous; and the ranges of density and moisture content of wood are within recommended for use as an energy source standards. We conclude that even at low temperatures reached during firing there was a significant production of good quality products, this is due to high concentrations of iron oxide and potassium oxide found in clay, which lowers the melting point of the piece. The average burn time for each step varied 650-2100 minutes wood consumption was on average 20 m3, product quality was on average 16% of first quality, 70% second, third and 5% to 10% loss . The distance between the wire and the surface of the oven was a significant parameter for all treatments, but with different variations, meaning that the wire should not be so generic and unique form, used as a criterion for completion of the burn process. The central part of the furnace was the area that reached higher temperature, and in a unified manner, with the highest concentration of top quality products. The ideal temperature curve, which provided the highest quality of ceramic products was achieved in the central part of the furnace

Mobilidade do sulfentrazone em Nitossolo Vermelho e em Neossolo Quartzarênico

O objetivo deste trabalho foi determinar a mobilidade do herbicida sulfentrazone em duas classes de solos (Nitossolo Vermelho e Neossolo Quartzarênico), em função de índices pluviométricos crescentes, sendo, portanto, influenciado pelas propriedades químicas e físicas dos solos com diferentes teores de ferro. em tubos de PVC de 10 cm de diâmetro por 50 cm de comprimento, preenchidos com os solos e saturados com água a 65% (p/p), foi aplicado o sulfentrazone (800 g ha-1). Na seqüência, foram simuladas chuvas diárias de 10 mm até atingir os índices pluviométricos de 30, 60 e 90 mm. Os tubos de PVC foram então desmontados - semeando-se Sorghum bicolor nas profundidades correspondentes de 2,5; 7,5; 12,5; 17,5; 22,5; e 30,0 cm da superfície do tubo - e mantidos em casa de vegetação por 15 dias, para avaliação da germinação e do crescimento inicial das plântulas. No final do experimento foram avaliadas as alterações morfofisiológicas que caracterizavam os efeitos tóxicos do produto, além de se medir o comprimento da parte aérea até a última lígula visível e a fitomassa seca das plantas. Quando sob precipitação de 90 mm no Neossolo Quartzarênico, o sulfentrazone formou uma banda de arraste de até 12,5 cm e, no Nitossolo Vermelho, até os 7,5 cm.

Mobilidade do sulfentrazone em latossolo vermelho e em chernossolo

Este trabalho objetivou determinar a mobilidade do sulfentrazone em duas classes de solos em função de índices pluviométricos, bem como possíveis influências das propriedades químicas e físicas de Latossolo Vermelho e Chernossolo com diferentes teores de ferro na ação do herbicida. Foram utilizados como recipientes 36 tubos de PVC de 10 cm de diâmetro por 50 cm de comprimento. Os recipientes foram preenchidos com os solos e umedecidos a 65% (p/p) da capacidade de saturação, quando se fez a aplicação do sulfentrazone (800 g ha-1 de i.a.) na área exposta dos solos. Na seqüência, foram simuladas chuvas diárias de 10 mm até atingir o índice pluviométrico desejado (30, 60 e 90 mm), sendo, posteriormente, desmontados seis tubos de cada solo (com e sem aplicação). Foram semeadas cinco sementes de sorgo (Sorghum bicolor) nas profundidades de 2,5; 7,5; 12,5; 17,5; 22,5; e 30,0 cm, mantidas em casa de vegetação por 15 dias para avaliação da germinação e do crescimento inicial. Decorrido esse tempo, foi realizada avaliação de possíveis alterações morfofisiológicas que pudessem ser caracterizadas como efeitos tóxicos do produto e mediu-se o comprimento da parte aérea até a última lígula visível. As partes aéreas foram secas em estufa com circulação forçada de ar (70 ºC por 96 horas), para obtenção de matéria seca. No Chernossolo ocorreu uniformidade da distribuição do produto ao longo do tubo, proporcional à precipitação, e no Latossolo Vermelho o sulfentrazone foi pouco móvel, permanecendo na camada superficial, independentemente da precipitação.