Analysis of asymmetrical cold rolling with varying coefficients of friction

In this research, asymmetrical cold rolling was produced by the difference in the coefficient of friction between rolls and sheets rather than the difference of roll radius or rotation speeds. The influence of friction coefficient ratio on the cross shear deformation, rolling pressure and torque was investigated using slab analysis. The results showed that the shear deformation zone length increased with the increase of the friction coefficient ratio. The rolling force decreased only under the condition that the friction coefficient ratio increased while the sum of the friction coefficients was held constant. As the reduction per pass was increased, the shear deformation zone length increased and the rolling force also increased. An increase of the front tension resulted in a decrease of the shear deformation zone length. An increase of back tension, however, led to an increase of the shear deformation zone length. The reduction of rolling torque for the work roll with higher surface roughness was greater than that for the work roll with lower surface roughness. (C) 2002 Elsevier Science B.V. All rights reserved.

On post-instability processes in adiabatic shear in hot rolled steel

EXPERIMENTS carried out using a split Hopkinson torsional bar have shown that only one shear band develops in specimens of hot rolled steel which break during testing. We observed, however, that in specimens which were not deformed to failure, several fine shear bands appeared. We believe that these formed during the loading cycle before the appearance of the final shear band and were not due to the effect of unloading. So we developed a numerical model to study the evolution of shear banding from several finite amplitude disturbances (FADs) in both temperature and strain rate. This numerical model reveals the detailed processes by which the FADs evolve into a fully developed shear band and suggests that beyond instability, the so-called shear banding process consists of two stages: inhomogeneous shearing and true shear-banding. The latter is characterized by the collapse of the stress and an abrupt increase of the local shear strain rate.