Lateral field emitters fabricated using carbon nanotubes

We report on the fabrication of lateral emitters using carbon nanotubes (CNTs) grown via plasma enhanced chemical vapour deposition (PECVD). Carbon nanotubes are dispersed randomly onto a substrate, mapped, contacted with metal, and by etching the substrate, a suspended lateral emitter structure is formed. Field emission measurements from the lateral emitters show a turn-on voltage as low as 12 V. The emission characteristics showed good fits to the Fowler-Nordheim (FN) theory indicating that conventional field emission was indeed observed from these devices. © 2003 Elsevier Science B.V. All rights reserved.

Self-aligned split gate electrodes fabricated on suspended carbon nanotubes

We describe the fabrication of self-aligned split gate electrodes on suspended multiwalled carbon nanotube structures. A suspended multiwalled carbon nanotube structure was used as an evaporation mask for the deposition of metal electrodes resulting in the formation of discontinuous wire deposition. The metal deposits on the nanotubes are removed with lift-off due to the poor adhesion of metal to the nanotube surface. Using Al sacrificial layers, it was possible to fabricate self-aligned contact electrodes and control electrodes nanometers from the suspended carbon nanotubes with a single lithography step. It was also shown that the fabrication technique may also be used to form nano-gaped contact electrodes. The technique should prove useful for the fabrication of nano-electromechanical systems.

Study of multi-walled carbon nanotube structures fabricated by PMMA suspended dispersion

We report on the electrical characteristics of plasma enhanced chemical vapour deposition (PECVD)-grown, multi-walled carbon nanotube (MWCNT) devices made by a new fabrication method, PMMA suspended dispersion. This method makes it possible to suspend nanotubes between metal electrodes and to remove unwanted nanotubes from the substrate. The measurements show that the MWCNTs are metallic and able to maintain a current density ∼2×106 A/cm2 for more than 15 days with a maximum current density of ∼1.8×107 A/cm2. This high current density and reliability will make PECVD-grown MWCNTs applicable to field emission cathodes. © 2002 Elsevier Science B.V. All rights reserved.

Self-aligned split gate electrodes fabricated on suspended carbon nanotubes

We describe the fabrication of self-aligned split gate electrodes on suspended multiwalled carbon nanotube structures. A suspended multiwalled carbon nanotube structure was used as an evaporation mask for the deposition of metal electrodes resulting in the formation of discontinuous wire deposition. The metal deposits on the nanotubes are removed with lift-off due to the poor adhesion of metal to the nanotube surface. Using Al sacrificial layers, it was possible to fabricate self-aligned contact electrodes and control electrodes nanometers from the suspended carbon nanotubes with a single lithography step. It was also shown that the fabrication technique may also be used to form nano-gaped contact electrodes. The technique should prove useful for the fabrication of nano-electromechanical systems. © 2003 Materials Research Society.

Structure and mechanical properties of ceramic coatings fabricated by plasma electrolytic oxidation on aluminized steel

Ceramic coatings were formed by plasma electrolytic oxidation (PEO) on aluminized steel. Characteristics of the average anodic voltages versus treatment time were observed during the PEO process. The micrographs, compositions and mechanical properties of ceramic coatings were investigated. The results show that the anodic voltage profile for processing of aluminized steel is similar to that for processing bulk Al alloy during early PEO stages and that the thickness of ceramic coating increases approximately linearly with the Al layer consumption. Once the Al layer is completely transformed, the FeAl intermetallic layer begins to participate in the PEO process. At this point, the anodic voltage of aluminized steel descends, and the thickness of ceramic coating grows more slowly. At the same time, some micro-cracks are observed at the Al2O3/FeAl interface. The final ceramic coating mainly consists of gamma-Al2O3, mullite, and alpha-Al2O3 phases. PEO ceramic coatings have excellent elastic recovery and high load supporting performance. Nanohardness of ceramic coating reaches about 19.6 GPa. (c) 2007 Elsevier B. V. All rights reserved.