Silica-based Nano-coating on Zirconia Surfaces Using Reactive Magnetron Sputtering: Effect on Chemical Adhesion of Resin Cements

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

INFLUENCE OF HVOF COATING ON THE FATIGUE STRENGTH OF 15-5 PH STAINLESS STEEL

Structural component failures due to cyclic loading are associated to surface damage of materials and its interaction with environment. Fatigue failure occurs with stresses below the yield strength of each material and is a result of crack initiation and propagation. In aeronautical components is an important parameter to be considered in project, as well as the corrosion and wear resistance. Thermally sprayed HVOF coatings have been considered to replace galvanic chromium deposits with comparable performance for wear and corrosion resistance. The aim of present research is to study the influence of WC-13Co-4Cr applied by HVOF, on the axial fatigue strength of 15-5 PH stainless steel. The shot peening treatment was used to restore fatigue performance.

Effect of Silver Nanoparticles in a Hydroxyapatite Coating applied by Atmospheric Plasma Spray

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Evaluation of tensile tetention of Y-TZP crowns after long-term aging: Effect of the core substrate and crown surface conditioning

This study evaluated the effect of the core substrate type (dentin and composite resin) on the retention of crowns made of yttrium oxide stabilized tetragonal zirconia polycrystal (Y-TZP), submitted to three inner surface conditionings. For this purpose, 72 freshly extracted molars were embedded in acrylic resin, perpendicular to the long axis, and prepared for full crowns: 36 specimens had crown preparations in dentin; the remaining 36 teeth had the crowns removed, and crown preparations were reconstructed with composite resin plus fiber posts with dimensions identical to the prepared dentin. The preparations were impressed using addition silicone, and 72 Y-TZP copings for the tensile test were produced. Cementation was performed with a dual-cured cement containing phosphate monomers. For cementation, the crown preparation (dentin or resin) was conditioned with the adhesive system, and the ceramic was subjected to one of three surface treatments: isopropyl alcohol, tribochemical silica coating, or thin low-fusing glassy porcelain layer application plus silanization. After 24 hours, all specimens were submitted to thermocycling (6000 cycles) and placed in a special tensile testing device in a universal testing machine to determine failure loads. The failure modes of all samples were analyzed under a stereomicroscope. Two-way analysis of variance showed that the surface treatment and substrate type (alpha=0.05) affected the tensile retention results. The dentin substrate presented the highest tensile retention values, regardless of the surface treatment. When the substrate was resin, the tribochemical silica coating and low-fusing glaze application plus silanization groups showed the higher retention values.

Effect of surface treatments on the shear bond strength of luting cements to Y-TZP ceramic

Statement of problem Because zirconia is a glass-free material, alternative surface treatments such as airborne-particle abrasion or silica coating should be used for long-term bonding. However, these surface treatments in combination with different bonding agents and luting cements have not yet been studied. Purpose The purpose of the study was to evaluate the effect of surface treatments on the shear bond strength (SBS) of luting cements to Y-TZP ceramic. Material and methods Zirconia disks (N=240) were airborne-particle abraded with the following particles (n=48): 50 μm Al2O3; 120 μm Al2O3; 30 μm silica-coated Al2O3 (Rocatec Soft); 120 μm Al2O3+110 μm silica-coated Al2O3 (Rocatec Plus); and Rocatec Plus. After silanization of the zirconia surface, composite resin disks were bonded with (n=12) RelyX Luting 2; RelyX ARC; RelyX U100; and Panavia F. The bonded specimens were thermocycled (10 000 cycles) and tested for SBS. Failure mode was determined with a stereomicroscope (×20). The morphology and elemental composition of airborne-particle abraded surfaces were evaluated with scanning electron microscopy (×500) and energy-dispersive x-ray spectroscopy (×50). Results Surface treatments, cements, and their interaction were significant (P<.001). For RelyX ARC, Rocatec Soft and Rocatec Plus provided the highest SBS. In general, surface treatments did not influence the SBS of RelyX U100 and Panavia F. Regardless of the cement, no significant difference was found between 50 μm and 120 μm Al2O3 particles, between Rocatec Soft and Rocatec Plus, or between Rocatec Plus and 120 μm Al2O3 particles+Rocatec Plus. All groups showed adhesive failures. Different particle sizes provided differences in morphological patterns. The elemental composition comprised Al and Al/Si for alumina and silica-abraded zirconia. Conclusions Particle size did not influence the SBS of the groups abraded exclusively with alumina or silica-coated particles. RelyX ARC was more surface-treatment dependent than RelyX U100 or Panavia F.

Ethanol is inefficient to remove endodontic sealer residues of dentinal surface

Endodontic sealer residues on dentinal surface have negative effects on adhesion of adhesives system and/or can cause discoloration of the dental crown. Objective: To evaluate the efficacy of 95% ethanol in removal of residues of epoxy-based (AH Plus), methacrylate-based (Epiphany SE) or calcium-based (Sealapex) sealers on dentinal surface. Material and methods: Thirty-two bovine incisor dental crown fragments (0.5 mm x 0.5 mm) were treated with 17% EDTA and 2.5% NaOCl. The specimens were divided into three experimental groups (n = 10): G1 (AH Plus), G2 (Epiphany SE) and G3 (Sealapex). In each group was applied a coating of one endodontic sealer type and were left undisturbed for 5 minutes. After this period, the specimens were cleaned with 95% ethanol. The control group was composed by two specimens that did not receive any sealer or cleaning treatment. The sealer residues persistence after cleaning with 95% ethanol was evaluated by scanning electron microscopy (x500) and a score system was applied. Data obtained were analyzed by Kruskal-Wallis and Dunn tests (α = 5%). Results: Moderate amount of endodontic sealer residues were observed in all groups, regardless of the endodontic sealer compositions. G1, G2 and G3 presented similar amount of sealer residues on dentinal surface after cleaning with 95% ethanol (p > 0.05). Conclusion: 95% ethanol was inefficiency to remove completely AH Plus, Epiphany SE and Sealapex residues of sealer-contaminated dentin.

Ethanol is inneficient to remove endodontic sealer residues of dentinal surface

Introduction: Endodontic sealer residues on dentinal surface have negative effects on adhesion of adhesives system and/or can cause discoloration of the dental crown. Objective: To evaluate the efficacy of 95% ethanol in removal of residues of epoxy-based (AH Plus), methacrylate-based (Epiphany SE) or calcium-based (Sealapex) sealers on dentinal surface. Material and methods: Thirty-two bovine incisor dental crown fragments (0.5 mm x 0.5 mm) were treated with 17% EDTA and 2.5% NaOCl. The specimens were divided into three experimental groups (n = 10): G1 (AH Plus), G2 (Epiphany SE) and G3 (Sealapex). In each group was applied a coating of one endodontic sealer type and were left undisturbed for 5 minutes. After this period, the specimens were cleaned with 95% ethanol. The control group was composed by two specimens that did not receive any sealer or cleaning treatment. The sealer residues persistence after cleaning with 95% ethanol was evaluated by scanning electron microscopy (x500) and a score system was applied. Data obtained were analyzed by Kruskal-Wallis and Dunn tests (α = 5%). Results: Moderate amount of endodontic sealer residues were observed in all groups, regardless of the endodontic sealer compositions. G1, G2 and G3 presented similar amount of sealer residues on dentinal surface after cleaning with 95% ethanol (p > 0.05). Conclusion: 95% ethanol was inefficiency to remove completely AH Plus, Epiphany SE and Sealapex residues of sealercontaminated dentin.

Repair of composites: Effect of laser and different surface treatments

Objectives: This study investigated the repairs of resin composite restorations after using different surface treatments.Design: Eighty four truncated cones of Filtek Z350 were prepared and thermo-cycled (20,000 cycles). Surfaces were roughened with diamond bur and etched with 37% phosphoric acid. Those cones were divided into 7 groups (N=12): 1) Prime&Bond 2.1; 2) aluminum oxide sandblasting+Prime&Bond 2.1; 3) Er:YAG laser treatment+Prime&Bond 2.1; 4) 9.6% hydrofluoric acid for 2 min-Fsilane coupling agent.; 5) silane coupling agent; 6) auto-polymerized acrylic monomer+Prime&Bond 2.1; 7) Adper Scothbond SE. Teflon device was used to fabricate inverted truncated cones of repair composite over the surface-treated. The bonded specimens were stressed to failure under tension. The data were analyzed with oneway ANOVA and Tukey tests.Results: Mean repair strengths (SD, in MPa) were, Group-2: 18.8a; Group-1: 18.7a; Group-6: 13.4ab; Group-7: 9.5bc; Group-3: 7.5bcd; Group-4: 5.2cd; Group-5: 2.6d.Conclusions: The use of diamond bur and a conventional adhesive and the use of aluminum oxide sandblasting prior to adhesive provided a simple and cost-effective solutions to composite repair. Er:YAG laser, silane alone, 9.6% hydrofluoric acid plus silane or a self-etching adhesive results in inferior composite repair strengths. (C) 2015 Elsevier Ltd. All rights reserved.

Improved electrical transport in lightly Er-doped sol-gel spin-coating SnO2 thin films, processed by photolithography

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Characterization of calcium phosphate coating produced by biomimetic method

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Hydroxyapatite coating deposited on grade 4 titanium by plasma electrolytic oxidation

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Surface engineering of silica nanoparticles for oral insulin delivery: characterization and cell toxicity studies

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

IMPROVEMENT TO THE MARGINAL COPING FIT OF COMMERCIALLY PURE TITANIUM CAST IN PHOSPHATE-BONDED INVESTMENT BY USING A SIMPLE PATTERN COATING TECHNIQUE

Statement of problem. Coatings of zirconite, Y2O3 or ZrO2 on wax patterns before investing in phosphate-bonded investments have been recommended to reduce the reaction layer in titanium castings, but they are not easily obtainable. Spinel-based investments are relatively stable with molten titanium and could be used as coatings to improve the quality of castings made with those investments. Purpose. The purpose of this study was to evaluate the effect of pattern coating with a commercial spinel-based investment before investing in 1 of 3 phosphate-bonded investments on the marginal coping fit and surface roughness of commercially pure titanium castings. Material and methods. Ten square acrylic resin patterns (12 x 12 x 2 mm) per group were invested in the phosphate-bonded investments Rematitan Plus (RP), Rema Exakt (RE), and Castorit Super C (CA) with or without a coating of the spinel-based investment, Rematitan Ultra (RU). After casting, the specimens were cleaned and the surface roughness was measured with a profilometer. Copings for dental implants with conical abutment were invested, eliminated, and cast as previously described. The copings were cleaned and misfit was measured with a profile projector (n=10). For both tests, the difference between the mean value of RU only and each value of the phosphate-bonded investment was calculated, and the data were analyzed by 2-way ANOVA and Tukey's HSD test (alpha=.05). In addition, the investment roughness was measured in bar specimens (30 x 10 x 10 mm), and the data (n=10) were analyzed by 1-way ANOVA and Tukey's HSD post hoc test (alpha=.05). Results. Two-way ANOVA for casting surface roughness was significant because of the investment, the coating technique, and the interaction between variables. One-way ANOVA was performed to prove the interaction term, and Tukey's post hoc test showed that RP with coating had the lowest mean, while RP had the highest. CA with coating was not different from RP with coating or CA without coating. RE with coating was similar to CA, while RE was different from all groups. For coping marginal fit, the 2-way ANOVA was significant for the investment, the coating technique, and the interaction between variables. The interaction was analyzed by1-way ANOVA and Tukey's HSD test that showed no significant difference among the coated groups, which had better marginal fit than the groups without coating. Among the groups without coating, CA had significant lower marginal misfit than RP, while RE was not different from CA and RP. For the investment surface roughness, the 1-way ANOVA was significant. CA and RU were smoother than RE and RP (P<.001). Conclusions. The coating technique improved the quality of castings fabricated with phosphate-bonded investments. (J Prosthet Dent 2012;108:51-57)

Effects of type I collagen coating on titanium osseointegration: histomorphometric, cellular and molecular analyses

The investigation of titanium (Ti) surface modifications aiming to increase implant osseointegration is one of the most active research areas in dental implantology. This study was carried out to evaluate the benefits of coating Ti with type I collagen on the osseointegration of dental implants. Acid etched Ti implants (AETi), either untreated or coated with type I collagen (ColTi), were placed in dog mandibles for three and eight weeks for histomorphometric, cellular and molecular evaluations of bone tissue response. While the histological aspects were essentially the same with both implants being surrounded by lamellar bone trabeculae, histomorphometric analysis showed more abundant bone formation in ColTi, mainly at three weeks. Cellular evaluation showed that cells harvested from bone fragments in close contact with ColTi display lower proliferative capacity and higher alkaline phosphatase activity, phenotypic features associated with more differentiated osteoblasts. Confirming these findings, molecular analyses showed that ColTi implants up-regulates the expression of a panel of genes well known as osteoblast markers. Our results present a set of evidences that coating AETi with collagen fastens the osseointegration by stimulating bone formation at the cellular and molecular levels, making this combination of morphological and biochemical modification a promising approach to treat Ti surfaces.

Coating of surfaces of composite materials with enzymatically formed biosilica

Die Bildung kieselsäurehaltiger Spicula in marinen Schwämmen ist nur möglich durch die enzymatische Aktivität des Silicatein- in Verbindung mit der stöchiometrischen Selbstassemblierung des Enzyms mit anderen Schwammproteinen. Die vorliegende Arbeit basiert auf einem biomimetischen Ansatz mit dem Ziel, unterschiedliche Oberflächen für biotechnologische und biomedizinische Anwendungen mit Biosilica und Biotitania zu beschichten und zu funktionalisieren. Für biotechnologische Anwendungen ist dabei das Drucken von Cystein-getaggtem Silicatein auf Gold-Oberflächen von Bedeutung, denn es ermöglichte die Bildung definierter Biotitania-Strukturen (Anatas), welche als Photokatalysator den Abbau eines organischen Farbstoffs bewirkten. Des Weiteren zeigte sich die bio-inspirierte Modifikation von Tyrosin-Resten an rekombinantem Silicatein-(via Tyrosinase) als vielversprechendes Werkzeug zur Beschleunigung der Selbstassemblierung des Enzyms zu mesoskaligen Filamenten. Durch eine solche Modifikation konnte Silicatein auch auf der Oberfläche von anorganischen Partikeln immobilisiert werden, welches die Assemblierung von anorganisch-organischen Verbundwerkstoffen in wäßriger Umgebung förderte. Die resultierenden supramolekularen Strukturen könnten dabei in bio-inspirierten und biotechnologischen Anwendungen genutzt werden. Weiterhin wurde in der vorliegenden Arbeit die Sekundärstruktur von rekombinantem Silicatein- (Monomer und Oligomer) durch Raman Spektroskopie analysiert, nachdem das Protein gemäß einer neu etablierten Methode rückgefaltet worden war. Diese Spektraldaten zeigten insbesondere Änderungen der Proteinkonformation durch Solubilisierung und Oligomerisierung des Enzyms. Außerdem wurden die osteoinduzierenden und osteogenen Eigenschaften unterschiedlicher organischer Polymere, die herkömmlich als Knochenersatzmaterial genutzt werden, durch Oberflächenmodifikation mit Silicatein/Biosilica verbessert: Die bei der Kultivierung knochenbildender Zellen auf derart oberflächenbehandelten Materialien beobachtete verstärkte Biomineralisierung, Aktivierung der Alkalischen Phosphatase, und Ausbildung eines typischen zellulären Phänotyps verdeutlichen das Potential von Silicatein/Biosilica für der Herstellung neuartiger Implantat- und Knochenersatzmaterialien.