Characterization of calcium oxide in root perforation sealer materials

Root perforation represents an undesirable complication that may lead to an unfavorable prognosis. The aims of this study were to characterize and to compare the presence of calcium oxide (CaO) on the chemical composition of materials used for root perforation therapy: gray and white mineral trioxide aggregate (MTA) and Portland cement (PC), gray MTA+5%CaO and gray MTA+10%CaO. The last two materials were analyzed to evaluate the increase of CaO in the final sample. CaO alone was used as a standard. Eighteen polyethylene tubes with an internal diameter of 3 mm and 3 mm in length were prepared, filled and then transferred to a chamber with 95% relative humidity and a temperature of 37ºC. The chemical compounds (particularly CaO) and the main components were analyzed by energy-dispersive X-ray microanalysis (EDX). EDX revealed the following concentrations of CaO: gray MTA: 59.28%, white MTA: 63.09%; PC: 72.51%; gray MTA+5%CaO: 63.48% and gray MTA+10%CaO: 67.55%. The tested materials presented different concentrations of CaO. Even with an increase of 5 and 10% CaO in gray MTA, the CaO levels found in the MTA samples were lower than those found in PC.

Analysis of genetic lineages and their correlation with virulence genes in enterococcus faecalis clinical isolates from root canal and systemic infections

Introduction: Enterococcus faecalis is a member of the mammalian gastrointestinal microbiota but has been considered a leading cause of hospital-acquired infections. In the oral cavity, it is commonly detected from root canals of teeth with failed endodontic treatment. However, little is known about the virulence and genetic relatedness among E. faecalis isolates from different clinical sources. This study compared the presence of enterococcal virulence factors among root canal strains and clinical isolates from hospitalized patients to identify virulent clusters of E. faecalis. Methods: Multilocus sequence typing analysis was used to determine genetic lineages of 40 E. faecalis clinical isolates from different sources. Virulence clusters were determined by evaluating capsule (cps) locus polymorphisms, pathogenicity island gene content, and antibiotic resistance genes by polymerase chain reaction. Results: The clinical isolates from hospitalized patients formed a phylogenetically separate group and were mostly grouped in the clonal complex 2, which is a known virulent cluster of E. faecalis that has caused infection outbreaks globally. The clonal complex 2 group comprised capsule-producing strains harboring multiple antibiotic resistance and pathogenicity island genes. On the other hand, the endodontic isolates were more diverse and harbored few virulence and antibiotic resistance genes. In particular, although more closely related to isolates from hospitalized patients, capsuleproducing E. faecalis strains from root canals did not carry more virulence/antibiotic genes than other endodontic isolates. Conclusions: E. faecalis isolates from endodontic infections have a genetic and virulence profile different from pathogenic clusters of hospitalized patients’ isolates, which is most likely due to niche specialization conferred mainly by variable regions in the genome.

Process for reinforcing SLS parts by epoxy resin

[ES]The purpose of this paper is to report on the use of a combination of selective laser sintering (SLS) and vacuum casting to create plastic composites made by additive manufacturing.

Irrigants for non-surgical root canal treatment in mature permanent teeth

Root canal treatment is carried out on teeth in which irreversible pulpitis has led to necrosis of the dental pulp. As a treatment option it is an alternative to dental extraction. Mechanical preparation and irrigation with antiseptic or antibacterial solutions destroys bacteria and cleans the infected root canal. Irrigants should be effective in deactivating bacteria in the entire root canal space without causing any adverse tissue reactions. Sodium hypochlorite (NaOCl) and chlorhexidine are commonly used but there is uncertainty as to which solution, concentration or combination is the most effective.

Phase behavior, crystallization, and morphology in thermosetting blends of a biodegradable poly(ethylene glycol)-type epoxy resin and poly(ε-caprolactone)

Thermosetting blends of a biodegradable poly(ethylene glycol)-type epoxy resin (PEG-ER) and poly(epsilon-caprolactone) (PCL) were prepared via an in situ curing reaction of poly(ethylene glycol) diglycidyl ether (PEGDGE) and maleic anhydride (MAH) in the presence of PCL. The miscibility, phase behavior, crystallization, and morphology of these blends were investigated. The uncured PCL/PEGDGE blends were miscible, mainly because of the entropic contribution, as the molecular weight of PEGDGE was very low. The crystallization and melting behavior of both PCL and the poly(ethylene glycol) (PEG) segment of PEGDGE were less affected in the uncured PCL/PEGDGE blends because of the very close glass-transition temperatures of PCL and PEGDGE. However, the cured PCL/PEG-ER blends were immiscible and exhibited two separate glass transitions, as revealed by differential scanning calorimetry and dynamic mechanical analysis. There existed two phases in the cured PCL/PEG-ER blends, that is, a PCL-rich phase and a PEG-ER crosslinked phase composed of an MAH-cured PEGDGE network. The crystallization of PCL was slightly enhanced in the cured blends because of the phase-separated nature; meanwhile, the PEG segment was highly restricted in the crosslinked network and was noncrystallizable in the cured blends. The phase structure and morphology of the cured PCL/PEG-ER blends were examined with scanning electron microscopy; a variety of phase morphologies were observed that depended on the blend composition. (C) 2004 Wiley Periodicals, Inc.

Phase separation, porous structure, and cure kinetics in aliphatic epoxy resin containing hyperbranched polyester

Thermosetting blends of an aliphatic epoxy resin and a hydroxyl-functionalized hyperbranched polymer (HBP), aliphatic hyperbranched polyester Boltorn H40, were prepared using 4,4'-diaminodiphenylmethane (DDM) as the curing agent. The phase behavior and morphology of the DDM-cured epoxy/HBP blends with HBP content up to 40 wt% were investigated by differential scanning calorimetry (DSC), dynamic mechanical analysis (DMA), and scanning electron microscopy (SEM). The cured epoxy/HBP blends are immiscible and exhibit two separate glass transitions, as revealed by DMA. The SEM observation showed that there exist two phases in the cured blends, which is an epoxy-rich phase and an HBP-rich phase, which is responsible for the two separate glass transitions. The phase morphology was observed to be dependent on the blend composition. For the blends with HBP content up to 10 wt%, discrete HBP domains are dispersed in the continuous cured epoxy matrix, whereas the cured blend with 40 wt% HBP exhibits a combined morphology of connected globules and bicominuous phase structure. Porous epoxy thermosets with continuous open structures on the order of 100-300 nm were formed after the HBP-rich phase was extracted with solvent from the cured blend with 40 wt% HBP. The DSC study showed that the curing rate is not obviously affected in the epoxy/HBP blends with HBP content up to 40 wt %. The activation energy values obtained are not remarkably changed in the blends; the addition of HBP to epoxy resin thus does not change the mechanism of cure reaction of epoxy resin with DDM. (c) 2006 Wiley Periodicals, Inc.