Graphene-nanocrystalline metal sulphide composites produced by a one-pot reaction starting from graphite oxide

Graphene-nanocrystalline metal sulphide composites were prepared by a one-pot reaction. A dispersion of graphite oxide layers in an aqueous solution of metal ions (Cd2+/Zn2+) was reacted with H2S gas, which acts as a sulphide source as well as a reducing agent, resulting in the formation of metal sulphide nanoparticles and simultaneous reduction of graphite oxide sheets to graphene sheets. The surface defect related emissions shown by free metal sulphide particles are quenched in the composites due to the interaction of the surface of the nanoparticles with graphene sheets.

Kinetics of Extraction of Iron(II1) by Bis(2-ethylhexyl Phosphate in a Laminar Liquid-Liquid Jet Reactor

The kinetics of iron(II1) extraction by bis(Zethylhexy1) phosphate (HDEHP, HA) in kerosene from sulfuric acid solutions has been studied in a liquid-liquid laminar jet reactor. The contact time of the interface in this reacting device is of the same order of magnitude as the surface renewal time in dispersion mixing and much less than that obtained in the relatively quiescent condition of the Lewis cell. Yet the analysis of the data in this study suggested a rate-controlling step involving surface saturation quite in conformity with that obtained in the Lewis cell and not with that in dispersion mixing as reported in the literature. Further, the mechanism suggested a weaker dependence of the rate on hydrogen ion concentration which was reported by other workers.

On the wear of aluminium-corundum composites

The effect of corundum particle content on the wear of aluminium was studied. Composites of different corundum contents were tested for their wear characteristics. Hardness and density measurements were made on specimens before and after test. Specimens were examined by scanning electron microscopy in the as-compacted, sintered and worn states. The wear decreased as the oxide content increased, showing an optimum value at a composition range of 25 wt.%–35 wt.% of corundum. The mechanism of reinforcement and its effect on the operative wear mode are discussed.

Dry sliding wear behaviour of magnesium alloy based hybrid composites in the longitudinal direction

In the present investigation, the wear behaviour of a creep-resistant AE42 magnesium alloy and its composites reinforced with Saffil short fibres and SiC particles in various combinations is examined in the longitudinal direction i.e., the plane containing random fibre orientation is perpendicular to the steel counter-face. Wear tests are conducted on a pin-on-disc set-up under dry sliding condition having a constant sliding velocity of 0.837 m/s for a constant sliding distance of 2.5 km in the load range of 10-40 N. It is observed that the wear rate increases with increase in load for the alloy and the composites, as expected. Wear rate of the composites is lower than the alloy and the hybrid composites exhibit a lower wear rate than the Saffil short fibres reinforced composite at all the loads. Therefore, the partial replacement of Saffil short fibres by an equal volume fraction of SiC particles not only reduces the cost but also improves the wear resistance of the composite. Microstructural investigation of the surface and subsurface of the worn pin and wear debris is carried out to explain the observed results and to understand the wear mechanisms. It is concluded that the presence of SiC particles in the hybrid composites improves the wear resistance because these particles remain intact and retain their load bearing capacity even at the highest load employed, they promote the formation of iron-rich transfer layer and they also delay the fracture of Saffil short fibres to higher loads. Under the experimental conditions used in the present investigation, the dominant wear mechanism is found to be abrasion for the AE42 alloy and its composites. It is accompanied by severe plastic deformation of surface layers in case of alloy and by the fracture of Saffil short fibres as well as the formation of iron-rich transfer layer in case of composites.

Structures of mannose-6-phosphate isomerase from Salmonella typhimurium bound to metal atoms and substrate: implications for catalytic mechanism

Mannose-6-phosphate isomerase (MPI) catalyzes the inter-conversion of mannose 6-phosphate and fructose 6-phosphate. X-ray crystal structures of MPI from Salmonella typhimurium in the apo form (with no metal bound) and in the holo form (with bound Zn2+) and two other structures with yttrium bound at an inhibitory site and complexed with Zn2+ and fructose 6-phosphate (F6P) were determined in order to gain insights into the structure and the isomerization mechanism. Isomerization involves acid/base catalysis with proton transfer between the C1 and C2 atoms of the substrate. His99, Lys132, His131 and Asp270 are close to the substrate and are likely to be the residues involved in proton transfer. The interactions observed at the active site suggest that the ring-opening step is probably catalyzed by His99 and Asp270. An active-site loop consisting of residues 130-133 undergoes conformational changes upon substrate binding. Zn2+ binding induces structural order in the loop consisting of residues 50-54. The metal atom appears to play a role in substrate binding and is probably also important for maintaining the architecture of the active site. Isomerization probably follows the previously suggested cis-enediol mechanism.

Small nickel metal particles in Ni---Al2O3 metal-ceramic composites

Magnetic measurements have been used in combination with transmission electron microscopy to investigate small nickel metal particles in metal-ceramic composites. Estimates of the average number of atoms in the particles are given for nonmagnetic samples with low Ni content.

Impression creep behaviour of magnesium alloy-based hybrid composites in the transverse direction

The creep behaviour of a creep-resistant AE42 magnesium alloy reinforced with Saffil short fibres and SiC particulates in various combinations has been investigated in the transverse direction, i.e., the plane containing random fibre orientation was perpendicular to the loading direction, in the temperature range of 175-300 degrees C at the stress levels ranging from 60 to 140 MPa using impression creep test technique. Normal creep behaviour, i.e., strain rate decreasing with strain and then reaching a steady state, is observed at 175 degrees C at all the stresses employed, and up to 80 MPa stress at 240 degrees C. A reverse creep behaviour, i.e., strain rate increasing with strain, then reaching a steady state and then decreasing, is observed above 80 MPa stress at 240 degrees C and at all the stress levels at 300 degrees C. This pattern remains the same for all the composites employed. The reverse creep behaviour is found to be associated with fibre breakage. The apparent stress exponent is found to be very high for all the composites. However, after taking the threshold stress into account, the true stress exponent is found to range between 4 and 7, which suggests viscous glide and dislocation climb being the dominant creep mechanisms. The apparent activation energy Q(C) was not calculated due to insufficient data at any stress level either for normal or reverse creep behaviour. The creep resistance of the hybrid composites is found to be comparable to that of the composite reinforced with 20% Saffil short fibres alone at all the temperatures and stress levels investigated. The creep rate of the composites in the transverse direction is found to be higher than the creep rate in the longitudinal direction reported in a previous paper.

Structure of the disodium salt of glucose 1-phosphate hydrate, 2Na+.C6H11O9P2-.3.5H2O

Mr= 367.2, monoclinic, C2, a = 8.429 (1),b= 10.184(2), c= 16.570(2)A, /~= 99.18 (1) °, U= 1404.2 A 3, z = 4, D m = 1.73, D x = 1.74 Mg m -3,Cu K~, 2 = 1.5418 A, g = 2.99 mm -1, F(000) = 764,T= 300K, final R for 1524 observed reflections is0.069. The endocyclic C-O bonds in the glucose ring are nearly equal with C(5)-O(5)= 1.445 (10) and C(1)-O(5)= 1.424(10). The pyranose sugar ring adopts a 4C 1 chair conformation. The conformation about the exocyclic C(5)-C(6) bond is gauche-gauche, in contrast to gauche-trans observed in the structure of the dipotassium salt of glucose 1-phosphate. The phosphate ester bond, P-O(1), is 1.641 (6)A, slightly longer than the 'high-energy' P-,.O bond in the monopotassium salt of phosphoenolpyruvate [1.612 (6)A]. Two sodium ions are six coordinated while the third has only five neighbours.

The structure of the monobarium salt of glucose 6-phosphate heptahydrate

Abstract is not available.

Toughness of as-cast and partially crystallized composites of a bulk metallic glass

The deformation and fracture response of a bulk metallic glass (BMG) post-annealing above the glass transition temperature is examined. The toughness of the glass-matrix composite exhibits a sharp transition beyond a critical volume fraction of crystallization to values as low as that of brittle silicate glass. Instrumented indentation tests supplemented by impact tests were used to study this ductile to brittle transition exhibited by the partially crystallized samples. Indentation on the anneal-embrittled specimens shows lateral cracks in addition to cracks along the corners. The applicability of the Poisson's ratio-toughness correlation with respect to partially crystallized samples is also investigated.

Purification of Antibodies Specific to a Dinucleotide Using the Hapten Bound to Deae Cellulose as an Affinity Column

The dinucleotide dpTpA held electrostatically on DEAE cellulose was used as an affinity column for the purification of dpTpA specific antibodies. Chromatography of the y-globulin fraction from dpTpA specific antisera on this column resulted in the retention of dpTpA specific antibodies which were later eluted along with the bound dpTpA using 1M NaC1. Dextran coated charcoal was the method of choice for the dissociation and removal of dpTpA bound to the antibodies. This method may extend itself to the purification of antibodies specific for other oligonucleotides.

Varistors based on barium titanate-graphite-rubber composites

This paper describes the experimental and theoretical studies carried out on particulate composites consisting of BaTiO3, graphite, and rubber. It is shown that such composites exhibit a positive voltage coefficient of resistance beyond a certain voltage. A theoretical model developed to explain the observed V-R characteristics and their dependence on parameters of the composite like composition and grain size of the particles is also described. These composites seem to be useful as varistors with positive voltage coefficient of resistance and may find applications as voltage-regulating devices. Journal of Applied Physics is copyrighted by The American Institute of Physics.

Flotation of calcareous Mussorie phosphate ore

Separation of Mussorie rock phosphate (P2O5 = 20%) from Uttar Pradesh, India, containing pyrite, calcite and other carbonaceous impurities by flotation has been successfully attempted to upgrade the phosphate values. Based on Hallimond cell flotation results of single and synthetic mineral mixtures of calcite and apatite using oleic acid and potassium phosphate, conditions were obtained for the separation of calcite from apatite which is considered to be the most difficult step in the beneficiation of calcareous phosphates. Further studies using 250 g of the mineral (−60 +150 and −150 mesh fractions, deslimed) in laboratory size Fagergren subaeration machine employed a stagewise flotation viz. carbonaceous materials using terpineol, pyrite using potassium-ethyl xanthate and calcite using oleic acid respectively. Separation was, however, found to be unsatisfactory in the absence of a depressant. Among starch, hydrofluosilicic acid and dipotassium hydrogen phosphate, which were tried as depressants for apatite in the final flotation stage, dipotassium hydrogen phosphate proved to be superior to others. However, the tests with the above fractions did not yield the required grade. This was possibly due to insufficient liberation of the phosphate mineral from the ore body and different experimental conditions due to scale up operations. Experiments conducted using −200 mesh deslimed fractions has yielded an acceptable grade of 27.6% P2O5 with a recovery of about 60%. The results have been explained in terms of the specific adsorption characteristics of phosphate ions on apatite and the liberation size of the mineral.

Sequence dependence and role of 5'-phosphate in the B to Z transition

Spectroscopic studies on pd(CG)3 and pd(GC)3 have been carried out to elucidate the sequence dependence and effect of free 5'-phosphate on the B to Z transition. Unlike d(CG)3, pd(CG)3 fails to undergo salt-induced B to Z transition at ambient temperature. Model building studies have been carried out to determine the inhibitory role of the 5'-phosphate group, but have been unsuccessful.

Preparation of cast aluminium alloy-mica particle composites

The optimum conditions for producing cast aluminium alloy-mica particle composites, by stirring mica particles (40 to 120 mgrm) in molten aluminium alloys (above their liquidus temperatures), followed by casting in permanent moulds, are described. Addition of magnesium either as pieces along with mica particles on the surface of the melts or as a previously added alloying element was found to be necessary to disperse appreciable quantities (1.5 to 2 wt.%) of mica particles in the melts and retain them as uniform dispersions in castings under the conditions of present investigation. These castings can be remelted and degassed with nitrogen at least once with the retention of about 80% mica particles in the castings. Electron probe micro-analysis of these cast composites showed that magnesium added to the surface of the melt along with mica has a tendency to segregate around the mica particles, apparently improving the dispersability for mica particles in liquid aluminium alloys. The mechanical properties of the aluminium alloy-mica particle composite decrease with an increase in mica content, however, even at 2.2% the composite has a tensile strength of 14.22 kg mm–2 with 1.1% elongation, a compression strength of 42.61 kg mm–2, and an impact strength of 0.30 kgm cm–2. The properties are adequate for certain bearing applications, and the aluminium-mica composite bearings were found to run under boundary lubrication, semi-dry and dry friction conditions whereas the matrix alloy (without mica) bearings seized or showed stick slip under the same conditions.