Formation ranges of icosahedral, amorphous and crystalline phases in rapidly solidified Ti-Zr-Hf-Ni alloys

From the quaternary Ti-Zr-Hf-Ni phase diagram. the cross-section at 20 at % Ni was selected for investigation. The icosahedral quasicrystalline, crystalline and amorphous phases were observed to form in nine kinds of rapidly solidified (TixZryHfz)(80)Ni-20 (x + y + z = 1) alloys at different compositions. The quasilattice constants of 0.519 and 0.531 nm were obtained for the icosahedral phase formed in the melt-spun Ti40Zr20Hf20Ni20 and Ti20Zr40Hf20Ni20 alloys. respectively. The icosahedral phase formed in the melt-spun Ti40Zr20Hf20Ni20 alloy especially is thermodynamically stable. The supercooled liquid region of the Ti20Zr20Hf40Ni20 glassy alloy reached 64 K. From these results a comparison of quasicrystal-forming and glass-forming abilities, was carried out. The quasicrystal-forming ability was reduced and glass-forming ability was improved with an increase in Hf and Zr contents in the (TixZryHfz)(80)Ni-20 alloys. On the other hand. an increase in Ti content caused an improvement in quasicrystal-forming ability.

Creep behaviour of nimonic and R.R. 59 alloys

The Ramberg-Osgood relation which adequately describes the stress-strain curve of a strain-hardening material is extended to formulate the constitutive laws for creep. The constitutive laws which describe primary creep adequately are extended to secondary creep. The results are verified for the case of R.R. 59 at 200°C, Nimonic 80A and Nimonic 90 alloys at 750°C.

Mechanism of low-temperature deformation in quenched aluminium-magnesium alloys

The dislocation mechanisms for plastic flow in quenched AlMg alloys with 0.45, 0.9, 2.7 and 6.4 at. % Mg were investigated using tensile tests and change-in-stress creep experiments in the temperaturhttp://eprints.iisc.ernet.in/cgi/users/home?screen=EPrint::Edit&eprintid=28109&stage=core#te range 87° -473° K. The higher the magnesium content in the alloy, the higher was the temperature dependence of flow stress. The alloys showed no perceptible creep in the vicinity of room temperature, while they crept at lower as well as higher temperatures. The most probable cause of hardening at temperatures below ∼ 200° K was found to be the pinning of dislocations by randomly distributed solute atoms, while athermal locking of dislocations by dynamic strain ageing during creep was responsible for the negligibly small creep rate in the room temperature range.

Clustering kinetics in aluminium-silver alloys

Resistometric studies of isochronal and isothermal annealing of an Al-0.64 at.% Ag alloy have given a value of 0.13 ± 0.02 eV for the silver-vacancy binding energy and 0.55 ± 0.03 eV for the migration energy of solute atoms.

Extraordinary high strain rate superplasticity in electrodeposited nano-nickel and alloys

Superplastic materials exhibit very large elongations to failure,typically >500%, and this enables commercial forming of complex shaped components at slow strain rates of similar to 10(-4) s(-1). We report extraordinary record superplastic elongations to failure of up to 5300% at both high strain rates and low temperature in electrodeposited nanocrystalline Ni and some Ni alloys. Superplasticity is not related to the presence of sulfur or a low melting phase at grain boundaries. (C) 2010 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Steroids and related natural products. VII. Boron trifluoride etherate-lithium aluminum hydride reduction of smilagenin acetate

Reduction of smilagenin acetate (Va) using a boron trifluoride etherate-lithium aluminum hydride reagent, followed by hydrogen peroxide oxidation and acetylation, was found to yield: 3β-ethoxysmilagenin (Vb), 3β-ethoxydihydrosmilagenin acetate (VIa), dihydrosmilagenin diacetate (VIb), and a complex mixture of partially acetylated products. Similar reaction conditions were employed to convert dihydrodiosgenin (II) to dihydrochlorogenin (III). Boron trifluoride etherate-lithium aluminum hydride reduction of 3β-acetoxy-5α-cholestane and 3β-acetoxy-5α-lanostane (VIIIa) was shown to yield the corresponding 3β-ethoxy (e.g., VIIIb) derivatives.

Deformation and crystallization of Zr-based amorphous alloys in homogeneous flow regime

The purpose of this study is to experimentally investigate the interaction of inelastic deformation and microstructural changes of two Zr-based bulk metallic glasses (BMGs): Zr41.25Ti13.75Cu12.5Ni10Be22.5 (commercially designated as Vitreloy 1 or Vit1) and Zr46.75Ti8.25Cu7.5Ni10Be27.5 (Vitreloy 4, Vit4). High-temperature uniaxial compression tests were performed on the two Zr alloys at various strain rates, followed by structural characterization using differential scanning calorimetry (DSC) and transmission electron microscopy (TEM). Two distinct modes of mechanically induced atomic disordering in the two alloys were observed, with Vit1 featuring clear phase separation and crystallization after deformation as observed with TEM, while Vit4 showing only structural relaxation with no crystallization. The influence of the structural changes on the mechanical behaviors of the two materials was further investigated by jump-in-strain-rate tests, and flow softening was observed in Vit4. A free volume theory was applied to explain the deformation behaviors, and the activation volumes were calculated for both alloys.