Alloying of pure magnesium with Mg-33.3 wt-%Zr master alloy

To capitalise on the strengthening potential of zirconium as a potent grain refiner for magnesium alloys, the mechanisms of adding zirconium to magnesium and its subsequent grain refining action need to be understood. Using a Mg-33.3Zr master alloy (Zirmax supplied by Magnesium Elektron Ltd) as a zirconium alloying additive, the influence of different alloying conditions on the dissolution of zirconium in magnesium was investigated. It was found that owing to the highly alloyable microstructure of Zirmax, the dissolution of zirconium was generally complete within a few minutes in the temperature range 730 to 780degreesC. Prolonging and/or intensifying stirring were found to have no conspicuous influence on further enhancing the dissolution of zirconium. In all cases studied, the average grain size increased with increasing holding time at temperature while the total zirconium content decreased. The finest grain structure and highest total zirconium content corresponded to sampling immediately after stirring. Pick up of iron by molten magnesium from the mild steel crucibles used for melting and holding, was significantly delayed or avoided in the temperature range 730 to 780degreesC by coating the crucibles with boron nitride. It is therefore feasible to conduct zirconium alloying at 730degreesC without the need of a considerable excess of Zirmax addition using a properly coated or lined steel crucible.

Superplasticity and superplastic forming ability of a Zr-Ti-Ni-Cu-Be bulk metallic glass in the supercooled liquid recgion

The superplastic deformation behavior and superplastic forming ability of the Zr41.25Ti13.75Ni10Cu12.5Be22.5 (at.%) bulk metallic glass (BMG) in the supercooled liquid region were investigated. The isothermal tensile results indicate (hat the BMG exhibits a Newtonian behavior at low strain rates but a non-Newtonian behavior at hiqh-strain rates in the initial deformation stage. The maximum elongation reaches as high as 1624% at 656 K. and nanocrystallization was found to occur during the deformation process. Based cm the analysis on tensile deformation. a gear-like micropart is successfully die-forged via a superplastic forgings process. demonstrating that the BMG has excellent workability in the supercooled liquid region. (C) 2004 Elsevier B.V. All rights reserved.

Effect of over-doped yttrium on the microstructure, mechanical properties and thermal properties of a Zr-based metallic glass

The effects of over-doped yttrium on the microstructure, mechanical properties and thermal behaviour of an oxygen-contaminated Zr51Cu20.7Ni12Al16.3 bulk metallic glass are studied systematically. It has been found that, when yttrium doping is beyond the optimum doping, the glass-forming ability enhancement effect induced by yttrium addition decreases and the mechanical properties are adversely affected. In this study, a new phase with an orthorhombic structure (a = 0.69 nm, b = 0.75 nm and c = 0.74 nm) is identified in the yttrium over-doped alloys. (c) 2006 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Enhanced glass-forming ability of a Zr-based bulk metallic glass with yttrium doping

A significant enhancement in glass formation in a newly developed Zr51Cu20.7Ni12Al16.3 alloy has been achieved by yttrium doping. With just 0.5 at.% yttrium doping, the critical diameter of the as-cast alloys for glass formation has been increased from 3 mm to at least 10 mm. In the undoped, large-sized alloys, massive oxygen stabilized crystalline phases are observed but disappear in yttrium doped alloys. Very small amounts of stable alpha-Y2O3 phases found in the yttrium doped alloys, and their negligible effect on the metallic glasses' properties, provide a superior solution to achieve metallic glasses with a high glass formability. (c) 2006 Elsevier B.V. All rights reserved.

Preparation and characterization of mesoporous Ni/Zr-laponite for the catalytic deoxygenation of vegetable oils into liquid hydrocarbons

The deoxygenation of vegetable oils was studied over a Ni/Zr-laponite catalyst in various nickel loading composition. Stearic acid has been used as a model compounds. The liquid and gas products were analyzed using gas chromatograph equipped with thermal conductivity detector and flame ionization detector. From product distribution it was determined the effect of catalyst composition on reaction conditions

Zr-containing hybrid organic-inorganic mesoporous materials:hydrophobic acid catalysts for biodiesel production

Zirconium-containing periodic mesoporous organosilicas (Zr-PMOs) with varying framework organic content have been synthesized through a direct synthesis method. These materials display the excellent textural properties of the analogous inorganic solid acid Zr-SBA-15 material. However, the substitution of silica by organosilicon species provides a strong hydrophobic character. This substitution leads to meaningful differences in the environment surrounding the zirconium metal sites, leading the modification of the catalytic properties of these materials. Although lower metal incorporation is accomplished in the final materials, leading to a lower population of metal sites, hydrophobisation leads to an impressive beneficial effect on the intrinsic catalytic activity of the zirconium sites in biodiesel production by esterification/transesterification of free fatty acid -containing feedstock. Moreover, the catalytic activity of the highly hybridised materials is hardly affected in presence of large amounts of water, confirming their very good water-tolerance. This makes Zr-PMO materials interesting catalysts for biodiesel production from highly acidic water-containing feedstock. © 2013 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Synthesis of M2AC (M = Ti, V, Cr, Nb, Zr, A = Al, Sn, S) (MAX) carbide phases and study of their physical behavior under extreme conditions

Materials known as Mn+1AXn phases, where n is 1, 2, or 3, and M represents an early transition metal, A an A-group element, and X is either Carbon and/or Nitrogen [1], are fast becoming technologically important materials due to the interesting combination of unique properties. However, a lot of important information about the high temperature and high pressure behavior of many of these compounds is still missing, which needs to be determined systematically. ^ In this dissertation the synthesis of M2AC (M = Ti, V, Cr, Nb, Zr) and A = (Al, Sn, S) compounds by arc melting, vacuum sintering and piston cylinder synthesis is presented along with the synthesis of Zr 2SC, which has been synthesized for first time in bulk form, by piston cylinder technique. The microstructural analysis by electron microscopy and phase analysis by x-ray diffraction is presented next. Finally, a critical analysis of the behavior of these compounds under the application of extreme pressure (as high as 50 GPa) and temperature (≈ 1000°C) is presented. ^ The high pressure studies, up to 50 GPa, showed that these compounds were structurally intact and their bulk moduli ranged from 140 to 190 GPa. The high temperature studies in the inert atmosphere showed that the M 2SnC compounds were unstable above 650°C and the expansion along the a-axis was higher than that along the c-axis, unlike the other phases. M2SC compounds on the other hand showed negligible difference in the thermal expansion along the two axes. The oxidation study revealed that Ti2AC (Al, S) compounds had highest resistance to oxidation while the M2SnC compounds had the least. Furthermore, from the oxidation study of these compounds, which were short time oxidation experiments, it was found that all of these compounds oxidized to their respective binary oxides. ^

Estudo da deposição de filmes finos de BaTi(1-X)Zr(X)O3 por meio de planejamento Box-Behnken

Ferroelectric ceramics with perovskite structure (ABO3) are widely used in solid state memories (FeRAM’s and DRAM's) as well as multilayered capacitors, especially as a thin films. When doped with zirconium ions, BaTiO3-based materials form a solid solution known as barium zirconate titanate (BaTi1-xZrxO3). Also called BZT, this material can undergo significant changes in their electrical properties for a small variation of zirconium content in the crystal lattice. The present work is the study of the effects of deposition parameters of BaTi0,75Zr0,25O3 thin films by spin-coating method on their morphology and physical properties, through an experimental design of the Box-Behnken type. The resin used in the process has been synthesized by the polymeric precursor method (Pechini) and subsequently split into three portions each of which has its viscosity adjusted to 10, 20 and 30 mPa∙s by means of a rotary viscometer. The resins were then deposited on Pt/Ti/SiO2/Si substrates by spin-coating method on 15 different combinations of viscosity, spin speed (3000, 5500 and 8000 rpm) and the number of deposited layers (5, 8 and 11 layers) and then calcined at 800 ° C for 1 h. The phase composition of the films was analyzed by X-ray diffraction (XRD) and indexed with the JCPDS 36-0019. Surface morphology and grain size were observed by atomic force microscopy (AFM) indicating uniform films and average grain size around 40 nm. Images of the cross section of the films were obtained by scanning electron microscopy field emission (SEM-FEG), indicating very uniform thicknesses ranging from 140-700 nm between samples. Capacitance measurements were performed at room temperature using an impedance analyzer. The films presented dielectric constant values of 55-305 at 100kHz and low dielectric loss. The design indicated no significant interaction effects between the deposition parameters on the thickness of the films. The response surface methodology enabled better observes the simultaneous effect of variables.

THE MICROSTRUCTURES OF ZR-EXCEL ALLOY: EFFECTS OF HEAVY ION IRRADIATION, PLASTIC DEFORMATION, THERMAL TREATMENT AND IN-SITU HEATING

Zr-Excel alloy (Zr-3.5Sn-0.8Nb-0.8Mo) is a dual phase (α + β) alloy in the as-received pressure tube condition. It has been proposed to be the pressure tube candidate material for the Generation-IV CANDU-Supercritical Water Reactor (CANDU-SCWR). In this dissertation, the effects of heavy ion irradiation, deformation and heat treatment on the microstructures of the alloy were investigated to enable us to have a better understanding of the potential in-reactor performance of this alloy. In-situ heavy ion (1 MeV) irradiation was performed to study the nucleation and evolution of dislocation loops in both α- and β-Zr. Small and dense type dislocation loops form under irradiation between 80 and 450 °C. The number density tends to saturate at ~ 0.1 dpa. Compared with the α-Zr, the defect yield is much lower in β-Zr. The stabilities of the metastable phases (β-Zr and ω-Zr) and the thermal-dynamically equilibrium phase, fcc Zr(Mo, Nb)2, under irradiation were also studied at different temperatures. Chemi-STEM elemental mapping was carried out to study the elemental redistribution caused by irradiation. The stability of these phases and the elemental redistribution are strongly dependent on irradiation temperature. In-situ time-of-flight neutron diffraction tensile and compressive tests were carried out at different temperatures to monitor lattice strain evolutions of individual grain families during these tests. The β-Zr is the strengthening phase in this alloy in the as-received plate material. Load is transferred to the β-Zr after yielding of the α-Zr grains. The temperature dependence of static strain aging and the yielding sequence of the individual grain families were discussed. Strong tensile/compressive asymmetry was observed in the {0002} grain family at room temperature. The microstructures of the sample deformed at 400 °C and the samples only subjected to heat treatment at the same temperature were characterized with TEM. Concentration of β phase stabilizers in the β grain and the morphology of β grain have significant effect on the stability of β- and ω-Zr under thermal treatment. Applied stress/strain enhances the decomposition of isothermal ω phase but suppresses α precipitation inside the β grains at high temperature. An α → ω/ZrO phase transformation was observed in the thin foils of Zr-Excel alloy and pure Zr during in-situ heating at 700 °C in TEM.

Fenologia kwitnienia i produkcja pyłku w zróżnicowanych warunkach mikroklimatycznych dużego miasta oraz ich wpływ na przebieg sezonu pyłkowego brzozy (Betula spp.) i bylicy (Artemisia spp.) w Poznaniu

Wydział Biologii: Instytut Biologii Środowiska, Pracownia Aeropalinologii

Zróżnicowanie struktury leśnych zgrupowań ślimaków jako efekt uwarunkowań naturalnych i antropogenicznych na przykładzie grądów w Wielkopolsce

Wydział Biologii