Microstructural characterization of electron beam evaporated tungsten oxide films for gas sensing applications

Tungsten trioxide is one of the potential semiconducting materials used for sensing NH3, CO, CH4 and acetaldehyde gases. The current research aims at development, microstructural characterization and gas sensing properties of thin films of Tungsten trioxide (WO3). In this paper, we intend to present the microstructural characterization of these films as a function of post annealing heat treatment. Microstructural and elemental analysis of electron beam evaporated WO3 thin films and iron doped WO3 films (WO3:Fe) have been carried out using analytical techniques such as Transmission electron microscopy, Rutherford Backscattered Spectroscopy and XPS analysis. TEM analysis revealed that annealing at 300oC for 1 hour improves cyrstallinity of WO3 film. Both WO3 and WO3:Fe films had uniform thickness and the values corresponded to those measured during deposition. RBS results show a fairly high concentration of oxygen at the film surface as well as in the bulk for both films, which might be due to adsorption of oxygen from atmosphere or lattice oxygen vacancy inherent in WO3 structure. XPS results indicate that tungsten exists in 4d electronic state on the surface but at a depth of 10 nm, both 4d and 4f electronic states were observed. Atomic force microscopy reveals nanosize particles and porous structure of the film. This study shows e-beam evaporation technique produces nanoaparticles and porous WO3 films suitable for gas sensing applications and doping with iron decreases the porosity and particle size which can help improve the gas selectivity.

Electron beam evaporation of tungsten oxide films for gas sensors

Pure and Iron incorporated nanostructured Tungsten Oxide (WO3) thin films were investigated for gas sensing applications using noise spectroscopy. The WO3 sensor was able to detect lower concentrations (1 ppm-10 ppm) of NH3, CO, CH4 and Acetaldehyde gases at higher operating temperatures between 100oC to 250oC. The response of the WO3 sensor to NH3, CH4 and Acetaldehyde at lower temperatures (50oC-100oC) was significant when the sensor was photo-activated using blue-light emitting diode (Blue-LED). The WO3 with Fe (WO3:Fe) was found to show some response to Acetaldehyde gas only at relatively higher operating temperature (250oC) and gas concentration of 10 ppm.

Electron beam evaporation of tungsten oxide films for gas sensors

Pure and Iron incorporated nanostructured Tungsten Oxide (WO3) thin films were investigated for gas sensing applications using noise spectroscopy. The WO3 sensor was able to detect lower concentrations (1 ppm-10 ppm) of NH3, CO, CH4 and Acetaldehyde gases at operating temperatures between 100 degrees celcius to 250 degrees celcius. The iron doped Tungsten Oxide sensor (WO3:Fe) showed some response to Acetaldehyde gas at relatively higher operating temperature (250 degrees celcius) and gas concentration of 10 ppm. The sensitivity of the WO3 sensor towards NH3, CH4 and Acetaldehyde at lower operating temperatures (50 degrees celcius - 100 degrees celcius) was significant when the sensor was photo-activated using blue-light emitting diode (Blue-LED). From the results, photo-activated WO3 thin film that operates at room temperature appeared to be a promising gas sensor. The overall results indicated that the WO3 sensor exhibited reproducibility for the detection of various gases and the WO3:Fe indicated some response towards Acetaldehyde gas.

Mechanical properties of thin sol-gel films

This thesis presents a study of the mechanical properties of thin films. The main aim was to determine the properties of sol-gel derived coatings. These films are used in a range of different applications and are known to be quite porous. Very little work has been carried out in this area and in order to study the mechanical properties of sol-gel films, some of the work was carried out on magnetron sputtered metal coatings in order to validate the techniques developed in this work. The main part of the work has concentrated on the development of various bending techniques to study the elastic modulus of the thin films, including both a small scale three-point bending, as well as a novel bi-axial bending technique based on a disk resting on three supporting balls. The bending techniques involve a load being applied to the sample being tested and the bending response to this force being recorded. These experiments were carried out using an ultra micro indentation system with very sensitive force and depth recording capabilities. By analysing the result of these forces and deflections using existing theories of elasticity, the elastic modulus may be determined. In addition to the bi-axial bending study, a finite element analysis of the stress distribution in a disk during bending was carried out. The results from the bi-axial bending tests of the magnetron sputtered films was confirmed by ultra micro indentation tests, giving information of the hardness and elastic modulus of the films. It was found that while the three point bending method gave acceptable results for uncoated steel substrates, it was very susceptible to slight deformations of the substrate. Improvements were made by more careful preparation of the substrates in order to avoid deformation. However the technique still failed to give reasonable results for coated specimens. In contrast, biaxial bending gave very reliable results even for very thin films and this technique was also found to be useful for determination of the properties of sol-gel coatings. In addition, an ultra micro indentation study of the hardness and elastic modulus of sol-gel films was conducted. This study included conventionally fired films as well as films ion implanted in a range of doses. The indentation tests showed that for implantation of H⁺ ions at doses exceeding 3x10¹⁶ ions/cm², the mechanical properties closely resembled those of films that were conventionally fired to 450°C.

Structural analysis of polymeric scaffolds by Micro-CT

The use of porous structures as tissue engineering scaffolds imposes demands on structural parameters such as porosity, pore size and interconnectivity. For the structural analysis of porous scaffolds, micro-computed tomography (μCT) is an ideal tool. μCT is a 3D X-ray imaging method that has several advantages over scanning electron microscopy (SEM) and other conventional characterisation techniques: • visualisation in 3D • quantitative results • non-destructiveness • minimal sample preparation