Degradation of Poly(ethylene glycol) in Aqueous Solution by Photo-Fenton and H(2)O(2)/UV Processes

This article reports experimental results obtained in a laboratory-scale photochemical reactor on the photodegradation of poly(ethylene glycol) (PEG) in aqueous solutions by means of the photo-Fenton and H(2)O(2)/UV processes. Dilute water solutions of PEG were fed to a batch reactor, mixed with pertinent reactants, and allowed to react under different conditions. Reaction progress was evaluated by sampling and analyzing the concentration of the total organic carbon (TOC) in solution as a function of the reaction time. Organic acids formed during oxidation were determined by HPLC analyses. The main acids detected in both processes were acetic and formic. Glycolic acid was detected only in the photo-Fenton process, and malonic acid was detected only in the H(2)O(2)/UV treatment, indicating that different reaction paths occur in these processes. The characteristics of both processes are discussed, based on the evolution of the TOC-time curves and the concentration profiles of the monitored organic acids. The experimental results constitute a contribution to the design of industrial processes for the treatment of wastewaters containing soluble polymers with similar properties.

Evaluation of the poly-L-lactic acid implant for treatment of the nasolabial fold: 3-year follow-up evaluation

The search for an ideal filler for soft tissue augmentation still continues. Because aging changes are continuous, temporary fillers should be preferred against permanent ones. Since 1999, the poly-L-lactic acid filler (PLA) has been marketed in Europe as Newfill. As a synthetic biocompatible polymer, PLA originally was used in suture materials and screws. In 2004, the U.S. Food and Drug Administration approved PLA under the name of Sculptra for the treatment of human immunodeficiency virus-related facial lipoatrophy. This study aimed to evaluate a 3-year follow-up investigation into the effect of PLA implant injection for the treatment of sunken nasolabial folds. Between October 2003 and February 2004, 10 women with a median age of 54 years (range, 43-60 years) were injected with polylactic acid hydrogel (Newfill) in the nasolabial fold area for aesthetic reasons. All the patients underwent three injections: one injection per month for 3 months. Evaluation of the results based on clinical examination and photography was performed at each session, at 6 months, and then 36 months after the third session. Injectable PLA was able to correct nasolabial folds successfully with a more lasting result than absorbable fillers commonly used in clinical practice, such as hyaluronic acid and collagen. Careful and standardized photographic documentation is indispensable.

Copolymers obtained by the radiation-induced grafting of styrene onto poly(tetrafluoroethylene-co-perfluoropropylvinyl ether) substrates. 1. Preparation and structural investigation

A study has been made to investigate the radiation grafting of styrene onto poly(tetrafluoroethylene-co-perfluoropropylvinyl ether) (PFA) substrates, using the simultaneous irradiation method. Two PFA polymers of different comonomer perfluoropropyl vinyl ether (PPVE) content and degree of crystallinity were used. Effects of grafting conditions such as monomer concentrations, type of solvent, dose rate, and irradiation dose on the grafting yield were investigated. Of the six different solvents used, the most efficient in terms of increasing grafting yield were dichloromethane, benzene, and methanol. The degree of grafting increased with increasing radiation dose up to 500 kGy, stabilizing above this dose. However, the grafting yield decreased with an increase in the dose rate. The grafting of styrene onto the PFA substrates was confirmed by FTIR-ATR and micro-Raman spectroscopy, The increase in the overall grafting yield was accompanied by a proportional increase in the penetration depth of the grafts into the substrate.

Comparative study of the radiation-induced grafting of styrene onto poly(tetrafluoroethylene-co-perfluoropropylvinyl ether) and polypropylene substrates. I: Kinetics and structural investigation

A comparative study has been made of the radiation grafting of styrene onto poly(tetrafluoroethylene-co-perfluoropropyl vinyl ether) (PFA) and polypropylene (PP) substrates, using the simultaneous irradiation method. Effects of grafting conditions such as monomer concentrations, type of solvent, dose rate and irradiation dose on the grafting yield were investigated. Under the same grafting conditions it was found that a higher degree of grafting of styrene was obtained using a mixture of dichloromethane/methanol solvents for PFA and methanol for PP and the degree of grafting was higher in PP than in PFA at all doses. However, the micro-Raman spectroscopy analysis of the graft revealed that, for the same degree of grafting, the penetration depth of the grafted polystyrene into the substrate was higher in PFA than in PP substrates. In both polymers the crystallinity was hardly affected by the grafting process and the degree of crystallinity decreased slightly with grafting dose. The dependence of the initial rate of grafting on the dose rate and the monomer concentration was found to be 0.6 and 1.4 order for PFA and 0.15 and 2.2 for PP, respectively. The degree of grafting increased with increasing radiation dose in both polymers. However, the grafting yield decreased with an increase in the dose rate. The increase in the overall grafting yield for PFA and PP was accompanied by a proportional increase in the penetration depth of the graft into the substrates. (C) 2003 Society of Chemical Industry.

Forward osmosis membranes tailored by hydrogel coatings

Dissertação para obtenção do Grau de Mestre em Engenharia Química e Bioquímica

Poly(2-hydroxyethyl methacrylate): A new star polymer

Multiarm star polymers are attractive materials due to their unusual bulk and solution properties. They are considered analogues of dendrimers with a wide range of applications, such as drug delivery, membranes, coatings and lithography.1 The advent of controlled polymerization made possible the existence of this unique class of organic nanoparticles (ONPs).2 Two major synthetic strategies are usually employed in the preparation of star polymers, the core-first and arm-first approaches. The core-first approach involves a controlled living polymerization using a multiarm initiator core while the arm-first methodology is based in the quenching of living polymers with multifunctional coupling agent or bifunctional vinyl compounds. Herein, we present the synthesis and characterization of a new star polymer, the multiarm star poly(2-hydroxyethyl methacrylate). The tetra-armed star polymer was prepared by reversible addition fragmentation chain-transfer (RAFT) polymerization using the core-first approach. The RAFT chain-transfer agent (RAFT CTA) pentaerythritol tetrakis[2-(dodecylthiocarbonothioylthio)-2-methylpropionate] was used as multiarm initiator core were 2-hydroxyethyl methacrylate (HEMA) was polymerized using AIBN as radical initiator. Structural characterization was performed by 1H NMR and FTIR. The new polymer is able to uptake large quantities of organic solvents, forming gels. The rheological behavior of these gels was also investigated.

Cell Adhesion Peptide RGDSP and Laminin Support Proliferation and Migration of Postnatal Retinal Stem Cells in a 3D Hydrogel Culture System

Purpose: Retinal stem cells (RSCs) can be isolated from radial glia population of the newborn mouse retina (Angénieux et al., 2006). These RSCs have great capacity to renew and generate neurons including cells differentiated towards the photoreceptor lineage (Mehri-Soussi et al., 2006). However, our published results showed poor integration and survival rate after cell grafting into the retina. The uncontrollable environment of retina seems to be the problem. To bypass this, we are trying to generate hemi-retinal tissue in vitro that can be used for transplantation. Methods: Expanded RSCs were seeded in a mixture of poly-ethylene-glycol (PEG)-polymer-based hydrogels crosslinked by peptides that also serve as substrates for matrix metalloproteinases. Different doses of crosslinker peptides were tested. Several growth factors were studied to stimulate cell proliferation and differentiation. Results: Cells were trapped in hydrogels and cultured in the presence of FGF2 and EGF. Spherical cell clusters indicating proliferation appeared within several days, but there was no cell migration within the gel. We then added cell adhesion molecules integrin ligand RGDSP, or laminin, or a combination of both, into the gel. Cells grown with laminin showed the best proliferation. Cells grown with RGDSP proliferated a few times and then started to spread out. Cells grown with the combination of RGDSP and laminin showed better proliferation than with RGDSP alone and larger spread-outs than with laminin alone. After stimulations with first FGF2 and EGF, and then only FGF2, some cells showed neuronal morphology after 2 weeks. The neuronal population was assessed by the presence of neuronal marker b-tubulin-III. Glial cells were also present. Further characterizations are undergoing. Conclusions: RSC can grow and migrate in 3D hydrogel with the addition of FGF2, EGF, RGDSP and laminin. Further developments are necessary to form a homogenous tissue containing retinal cells.

Application of ftir in the determination of acrylate content in poly(sodium acrylate-co-acrylamide) superabsorbent hydrogels

Hydrogels have been prepared by free-radical solution copolymerization of acrylamide and sodium acrylate (NaAc), with molar ratio ranging from 25/75 to 80/20, respectively, using methylene bisacrylamide as the crosslinking agent. A FTIR spectroscopy procedure to determine the acrylate/acrylamide ratio in these hydrogels was proposed based on absorbance at 1410 cm-1 (nCOO-) and 2940 cm-1 (nCH and nCH2). A straight line with a good linear correlation coefficient (0.998) was obtained by plotting the acrylate content (Ac%) versus relative absorbance (Arel = A1410/A2940). Results were confirmed by the amount of sodium cation released in acid medium determined by atomic absorption spectrometry.

Biomechanical and histological evaluation of hydrogel implants in articular cartilage

We evaluated the mechanical behavior of the repaired surfaces of defective articular cartilage in the intercondylar region of the rat femur after a hydrogel graft implant. The results were compared to those for the adjacent normal articular cartilage and for control surfaces where the defects remained empty. Hydrogel synthesized by blending poly(2-hydroxyethyl methacrylate) and poly(methyl methacrylate-co-acrylic acid) was implanted in male Wistar rats. The animals were divided into five groups with postoperative follow-up periods of 3, 5, 8, 12 and 16 weeks. Indentation tests were performed on the neoformed surfaces in the knee joint (with or without a hydrogel implant) and on adjacent articular cartilage in order to assess the mechanical properties of the newly formed surface. Kruskal-Wallis analysis indicated that the mechanical behavior of the neoformed surfaces was significantly different from that of normal cartilage. Histological analysis of the repaired defects showed that the hydrogel implant filled the defect with no signs of inflammation as it was well anchored to the surrounding tissues, resulting in a newly formed articular surface. In the case of empty control defects, osseous tissue grew inside the defects and fibrous tissue formed on the articular surface of the defects. The repaired surface of the hydrogel implant was more compliant than normal articular cartilage throughout the 16 weeks following the operation, whereas the fibrous tissue that formed postoperatively over the empty defect was stiffer than normal articular cartilage after 5 weeks. This stiffness started to decrease 16 weeks after the operation, probably due to tissue degeneration. Thus, from the biomechanical and histological point of view, the hydrogel implant improved the articular surface repair.

Multilayered hydrogel coatings covalently-linked to glass surfaces showing a potential to mimic mucosal tissues

Multilayered hydrogel coatings can be developed on the surface of glass slides via layer-by-layer deposition of hydrogen-bonded interpolymer complexes formed by poly(acrylic acid) and methylcellulose. Chemical modification of the glass surface with (3-aminopropyl)triethoxysilane with subsequent layer-by-layer deposition and cross-linking of interpolymer complexes by thermal treatment allows fabrication of ultrathin hydrogel coatings, not detachable from the substrate. The thickness of these coatings is directly related to the number of deposition cycles and cross-linking conditions. An unusual dependence of the hydrogel swelling properties on the sample thickness is observed and can be interpreted by gradual transitions between two- and three-dimensional networks. The hydrogels exhibit pH-responsive swelling behaviour, achieving higher swelling degrees at pH > 6.0. These coatings can be used as model substrates to study the adhesive properties of pharmaceutical tablets and can potentially mimic the total work of adhesion observed for the detachment of mucoadhesives from porcine buccal mucosa but fail to exhibit identical detachment profiles.

Synthesis of hyperbranched poly(aryl ether)s via carbene insertion processes

Homopolymerization of alkylarylcarbenes derived from diazirine monomers that featured benzyl alcohol or phenol residues was found to lead to the production of soluble hyperbranched poly(aryl ether)s. The polymerization process was influenced by the solvents employed, monomer concentration, and the reaction time. An increase in the monomer concentration and reaction time was found to lead to an increase in the molecular weight characteristics of the resulting polymers as determined by gel permeation chromatography (GPC). The composition and architecture of the polyethers were determined by nuclear magnetic resonance (NMR) spectroscopic analysis and were found to be highly complex and dependent on the structure of the monomers used. All of the polymers were found to contain ether linkages formed via carbene insertion into O-H bonds, although polymers derived from phenolic carbenes also contained linkages arising from C-alkylation.

Rheological and thermal behaviour of poly(N-isopropylacrylamide)/alginate smart polymeric networks

Interpenetrating polymeric networks based on sodium alginate and poly(N-isopropylacrylamide) (PNIPAAm) covalently crosslinked with N,N′-methylenebisacrylamide have been investigated using rheology, thermogravimetry, differential scanning calorimetry, X-ray diffraction measurements and scanning electron microscopy (SEM). An improved elastic response of the samples with a higher PNIPAAm content and increased amount of crosslinking agent was found. The temperature-responsive behaviour of the hydrogel samples was evidenced by viscoelastic measurements performed at various temperatures. It is shown that the properties of these gels can be tuned according to composition, amount of crosslinking agent and temperature changes. X-ray scattering analysis revealed that the hydrophobic groups are locally segregated even in the swollen state whilst cryo-SEM showed the highly heterogeneous nature of the gels.

Self-assembly of telechelic tyrosine end-capped PEO and poly(alanine) polymers in aqueous solution

The self-assembly in aqueous solution of three novel telechelic conjugates comprising a central hydrophilic polymer and short (trimeric or pentameric) tyrosine end-caps has been investigated. Two of the conjugates have a central poly(oxyethylene) (polyethylene oxide, PEO) central block with different molar masses. The other conjugate has a central poly(l-alanine) (PAla) sequence in a purely amino-acid based conjugate. All three conjugates self-assemble into β-sheet based fibrillar structures, although the fibrillar morphology revealed by cryogenic-TEM is distinct for the three polymers—in particular the Tyr5-PEO6k-Tyr5 forms a population of short straight fibrils in contrast to the more diffuse fibril aggregates observed for Tyr5-PEO2k-Tyr5 and Tyr3-PAla-Tyr3. Hydrogel formation was not observed for these samples (in contrast to prior work on related systems) up to quite high concentrations, showing that it is possible to prepare solutions of peptide–polymer-peptide conjugates with hydrophobic end-caps without conformational constraints associated with hydrogelation. The Tyr5-PEO6k-Tyr5 shows significant PEO crystallization upon drying in contrast to the Tyr5-PEO2k-Tyr5 conjugate. Our findings point to the remarkable ability of short hydrophobic peptide end groups to modulate the self-assembly properties of polymers in solution in model peptide-capped “associative polymers”. Retention of fluidity at high conjugate concentration may be valuable in potential future applications of these conjugates as bioresponsive or biocompatible materials, for example exploiting the enzyme-responsiveness of the tyrosine end-groups

PVP superabsorbent nanogels

Monomer free hydrogel nanoparticles (nanogels) were prepared by crosslinking preformed poly(N-vinyl-2-pyrrolidone) (PVP) entrapped in the aqueous pool of hexadecyltrimethylammonium bromide reverse micelles using the Fenton reaction. The PVP nanoparticles were spherical with a dry diameter of 27 nm. The diameter of the swollen particles was ten times higher, i.e., a swelling ratio, Q, above 900, characterizing this preparation as superabsorbent. PVP nanogel swelling was dependent on bound Fe(3+) and varied with pH and ionic strength. Nanogel deswelling by salt followed the anions lyotropic series, i.e., SCN(-) < HSO(3)(-) < NO(3)(-) < I(-) < Cl(-) < CH(3)COO(-) < CF(3)SO(3)(-). The value of Q reached 6,000 in iron-free PVP nanoparticles at low pH, making this nanogel one of the most efficient swelling systems so far described.

Polymeric electronic gas sensor for determining alcohol content in automotive fuels

In this paper we describe the electrosynthesis of poly[(2-bromo-5-hexyloxy- 1,4-phenylenevinylene)-co-(1,4-phenylenevinylene)] (BHPPV-co-PPV), a novel conducting copolymer, and its application as active layer of a chemiresistive gas sensor suitable for quantification of ethanol present in ethanol-gasoline mixtures normally present in the fuel tanks of flex-fuel vehicles. This information is crucial for the smooth operation of the engine since it permits optimal air:fuel ratio regulation. The sensor consists of an interdigitated electrode coated with a thin polymer film doped with dodecylbenzenesulfonic acid. On exposure to fuel vapours at room temperature, the device presents a linear correlation between its electrical conductance and the ethanol concentration in the fuel. (C) 2008 Elsevier B.V. All rights reserved.